CN107868565A - A kind of production method of the polyaniline epoxy resin corrosion-inhibiting coating of sericite toughness reinforcing - Google Patents
A kind of production method of the polyaniline epoxy resin corrosion-inhibiting coating of sericite toughness reinforcing Download PDFInfo
- Publication number
- CN107868565A CN107868565A CN201710984118.6A CN201710984118A CN107868565A CN 107868565 A CN107868565 A CN 107868565A CN 201710984118 A CN201710984118 A CN 201710984118A CN 107868565 A CN107868565 A CN 107868565A
- Authority
- CN
- China
- Prior art keywords
- sericite
- polyaniline
- epoxy resin
- curing agent
- toughness reinforcing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The polyaniline epoxy resin corrosion-inhibiting coating of a kind of sericite toughness reinforcing, it is characterised in that prepare sericite Polyaniline in sericite surface aggregate polyaniline in the method using mechanochemistry polymerization first;Then the curing agent with certain flexibility chain is prepared;Finally, using epoxy resin E571 as raw material, component A is mixed into the epoxy resin of different epoxide numbers, curing agent, accelerator, modified pitch and the mixing of other auxiliary agents, sericite Polyaniline is toughener, adds curing agent and other auxiliary agents, mix, coating, solidification, obtains the polyaniline epoxy resin corrosion-inhibiting coating of sericite toughness reinforcing.Corrosion-inhibiting coating provided by the invention, there is the good characteristics such as adhesive force is strong, intensity is high, chemicals-resistant, wear-resisting, anti-corrosion loss is strong, cost is cheap.
Description
Technical field
The present invention relates to a kind of corrosion-inhibiting coating, the polyaniline epoxy resin corrosion-inhibiting coating of especially a kind of sericite toughness reinforcing
Production method.
Background technology
Epoxy coating is a kind of coating being used widely, in epoxy resin it is average it is each be divided to give containing two or
Two or more epoxy radicals.The constituent of epoxy coating mainly has epoxy resin and its curing agent, and the composition of auxiliary then has
Pigment, filler etc..Epoxy coating has excellent resistance to aquation, chemical-resistant(Acidproof, alkaline-resisting and organic solvent), and have
There is good adhesion property, suitable for the application of steel under all kinds of corrosive environments etc., the application on especially all kinds of storage tank surfaces.
But the weatherability difference of epoxy coating causes to ftracture, and limits the application of epoxy coating to a certain extent.
The content of the invention
It is an object of the invention to provide a kind of polyaniline epoxy resin corrosion-inhibiting coating of the sericite toughness reinforcing of good weatherability
Production method.
To achieve these goals, present invention employs following technical scheme:
The polyaniline epoxy resin corrosion-inhibiting coating of a kind of sericite toughness reinforcing, it is characterised in that polymerize first using mechanochemistry
Method prepare sericite-Polyaniline in sericite surface aggregate polyaniline;Then prepare with certain flexibility chain
Curing agent;Finally, using epoxy resin E571 as raw material, component A, curing agent, rush are mixed into the epoxy resin of different epoxide numbers
Entering agent, modified pitch and the mixing of other auxiliary agents, sericite-Polyaniline is toughener, adds curing agent and other auxiliary agents,
Mix, apply, solidification, obtain the polyaniline epoxy resin corrosion-inhibiting coating of sericite toughness reinforcing.
The polyaniline epoxy resin corrosion-inhibiting coating of described sericite toughness reinforcing, it is characterised in that its preparation that has the following steps
Form:
(1)By sericite and aniline with 1:2.5-3 mass ratio is added in reaction vessel, sealing, is vacuumized, under nitrogen protection
Soak 20-24h;It is transferred in mortar and grinds 30-40min to uniform;Ammonium persulfate is added, continues to grind 6-8h, uses water successively
Washed 2-3 times with absolute ethyl alcohol, decompression spontaneously dries overnight after filtering, then is dried with 60-70 DEG C of air dry oven, obtains thin,tough silk cloud
Mother-Polyaniline;
(2)Diethylenetriamine is added in reaction vessel, opens stirring, it is 200-250r/min to control stir speed (S.S.), rise temperature
Degree starts that the octyl glycidyl ether of 0.75-0.85 times of parts by weight is added dropwise, controls and be added dropwise in 3-4h to 45-50 DEG C,
Temperature is raised to 65-70 DEG C, continues magnetic agitation reaction 3-4h, reduces temperature to room temperature, obtain curing agent;
(3)By epoxy resin E571 and deionized water with 1:0.7-0.72 mass ratio mixing, after mechanical agitation is uniform, adds thin,tough silk
Mica-Polyaniline, continue mechanical agitation to uniform;Curing agent, DMP-30 and organic silicon defoamer are added, is added
The deionized water of 0.6-0.65 times of parts by weight, continue to be stirred until homogeneous, deaeration, obtain coating;
(4)Coating even application is dried under the conditions of working interface, 60-70 DEG C, obtains the polyaniline epoxy of sericite toughness reinforcing
Resin resistant coating.
The preparation method of the polyaniline epoxy resin corrosion-inhibiting coating of described sericite toughness reinforcing, it is characterised in that step(1)
The mass ratio of middle aniline and ammonium persulfate is 1:0.32-0.35.
The preparation method of the polyaniline epoxy resin corrosion-inhibiting coating of described sericite toughness reinforcing, it is characterised in that step(3)
Epoxy resin E571, sericite-Polyaniline, curing agent, the mass ratio of DMP-30 and organic silicon defoamer are 1:
0.06-0.08:0.75-0.8:0.12-0.15:0.03-0.04.
By using above-mentioned technical scheme, the present invention has the advantages that:
The present invention prepares sericite-polyaniline in the method using mechanochemistry polymerization in sericite surface aggregate polyaniline first
Compound;Then the curing agent with certain flexibility chain is prepared;Finally, using epoxy resin E571 as raw material, with different epoxide numbers
Epoxy resin be mixed into component A, curing agent, accelerator, modified pitch and the mixing of other auxiliary agents, sericite-polyaniline are compound
Thing is toughener, adds curing agent and other auxiliary agents, is mixed, and is applied, and solidification, obtains the polyaniline epoxy of sericite toughness reinforcing
Resin resistant coating.Polyaniline is a kind of novel high polymer material, have cost it is cheap, chemically and thermally excellent in stability, synthesis
The characteristics such as simply, anti-corrosion loss is strong.And epoxy resin then has the characteristics that adhesive force is strong, intensity is high, chemicals-resistant, wear-resisting, sheet
The antiseptic property of the excellent filming performance of epoxy resin and polyaniline is combined by the corrosion-inhibiting coating of invention, and it has preferably anti-
Rotten effect.Sericite is the silicate of scale sheet superfine in muscovite mineral suite, not only aboundresources, it is widely distributed and
It is cheap, and with many excellent performances, such as chemical property is stable, can acid-alkali-corrosive-resisting, and with high resiliency, high-ductility
Property, shielding ultraviolet rays and counter infrared ray radiation etc.;Sericite is added in corrosion-inhibiting coating, on the one hand can substantially reduce cost, separately
On the one hand, in the coating, sericite tends to arrange parallel to coating surface, forms one layer of inert, resist chemical and sun
The protective layer of light radiation, make it that air and moisture can be prevented to enter, can also prevent coating stress from concentrating to produce cracking, improve painting
The critical film Cracking Thickness of layer.Corrosion-inhibiting coating provided by the invention, has that adhesive force is strong, intensity is high, chemicals-resistant, wear-resisting, anti-
The good characteristics such as corrosionization is strong, cost is cheap.
Embodiment
The polyaniline epoxy resin corrosion-inhibiting coating of the sericite toughness reinforcing of the present embodiment, it, which has the following steps, is prepared:
(1)By sericite and aniline with 1:3 mass ratio is added in reaction vessel, sealing, is vacuumized, and nitrogen protection is lower to soak
24h;It is transferred in mortar and grinds 40min to uniform;Ammonium persulfate is added, continues to grind 8h, is washed successively with water and absolute ethyl alcohol
Wash 3 times, decompression spontaneously dries overnight after filtering, then is dried with 60-70 DEG C of air dry oven, and it is compound to obtain sericite-polyaniline
Thing;
(2)Diethylenetriamine is added in reaction vessel, opens stirring, it is 250r/min to control stir speed (S.S.), and rise temperature is extremely
50 DEG C, start that the octyl glycidyl ether of 0.85 times of parts by weight is added dropwise, control and be added dropwise in 4h, rise temperature to 70
DEG C, continue magnetic agitation reaction 4h, reduce temperature to room temperature, obtain curing agent;
(3)By epoxy resin E571 and deionized water with 1:0.72 mass ratio mixing, after mechanical agitation is uniform, adds thin,tough silk cloud
Mother-Polyaniline, continue mechanical agitation to uniform;Curing agent, DMP-30 and organic silicon defoamer are added, is added
The deionized water of 0.65 times of parts by weight, continue to be stirred until homogeneous, deaeration, obtain coating;
(4)Coating even application is dried under the conditions of working interface, 70 DEG C, obtains the polyaniline epoxy resin of sericite toughness reinforcing
Corrosion-inhibiting coating.
The step of the present embodiment(1)The mass ratio of middle aniline and ammonium persulfate is 1:0.32.
The step of the present embodiment(3)Epoxy resin E571, sericite-Polyaniline, curing agent, DMP-30 and
The mass ratio of organic silicon defoamer is 1:0.07:0.75:0.15:0.03.
Claims (4)
1. the polyaniline epoxy resin corrosion-inhibiting coating of a kind of sericite toughness reinforcing, it is characterised in that gather first using mechanochemistry
The method of conjunction prepares sericite-Polyaniline in sericite surface aggregate polyaniline;Then prepare with certain flexibility chain
Curing agent;Finally, using epoxy resin E571 as raw material, component A is mixed into the epoxy resin of different epoxide numbers, curing agent,
Accelerator, modified pitch and the mixing of other auxiliary agents, sericite-Polyaniline is toughener, adds curing agent and other are helped
Agent, mix, apply, solidification, obtain the polyaniline epoxy resin corrosion-inhibiting coating of sericite toughness reinforcing.
2. the polyaniline epoxy resin corrosion-inhibiting coating of sericite toughness reinforcing according to claim 1, it is characterised in that its just like
Lower step is prepared:
(1)By sericite and aniline with 1:2.5-3 mass ratio is added in reaction vessel, sealing, is vacuumized, under nitrogen protection
Soak 20-24h;It is transferred in mortar and grinds 30-40min to uniform;Ammonium persulfate is added, continues to grind 6-8h, uses water successively
Washed 2-3 times with absolute ethyl alcohol, decompression spontaneously dries overnight after filtering, then is dried with 60-70 DEG C of air dry oven, obtains thin,tough silk cloud
Mother-Polyaniline;
(2)Diethylenetriamine is added in reaction vessel, opens stirring, it is 200-250r/min to control stir speed (S.S.), rise temperature
Degree starts that the octyl glycidyl ether of 0.75-0.85 times of parts by weight is added dropwise, controls and be added dropwise in 3-4h to 45-50 DEG C,
Temperature is raised to 65-70 DEG C, continues magnetic agitation reaction 3-4h, reduces temperature to room temperature, obtain curing agent;
(3)By epoxy resin E571 and deionized water with 1:0.7-0.72 mass ratio mixing, after mechanical agitation is uniform, adds thin,tough silk
Mica-Polyaniline, continue mechanical agitation to uniform;Curing agent, DMP-30 and organic silicon defoamer are added, is added
The deionized water of 0.6-0.65 times of parts by weight, continue to be stirred until homogeneous, deaeration, obtain coating;
(4)Coating even application is dried under the conditions of working interface, 60-70 DEG C, obtains the polyaniline epoxy of sericite toughness reinforcing
Resin resistant coating.
3. the preparation method of the polyaniline epoxy resin corrosion-inhibiting coating of sericite toughness reinforcing according to claim 2, its feature
It is, step(1)The mass ratio of middle aniline and ammonium persulfate is 1:0.32-0.35.
4. the preparation method of the polyaniline epoxy resin corrosion-inhibiting coating of sericite toughness reinforcing according to claim 2, its feature
It is, step(3)Epoxy resin E571, sericite-Polyaniline, curing agent, DMP-30 and organic silicon defoamer
Mass ratio is 1:0.06-0.08:0.75-0.8:0.12-0.15:0.03-0.04.