CN107814983A - A kind of full steel engineering radial-type tyre colliery tread glue formula - Google Patents
A kind of full steel engineering radial-type tyre colliery tread glue formula Download PDFInfo
- Publication number
- CN107814983A CN107814983A CN201710682948.3A CN201710682948A CN107814983A CN 107814983 A CN107814983 A CN 107814983A CN 201710682948 A CN201710682948 A CN 201710682948A CN 107814983 A CN107814983 A CN 107814983A
- Authority
- CN
- China
- Prior art keywords
- colliery
- age resistor
- sizing material
- full steel
- tyre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of full steel engineering radial-type tyre colliery tread glue formula, it is characterised in that each component of its sizing material includes:Natural rubber, butadiene rubber, carbon black, zinc oxide, stearic acid, age resistor OK2122, anti-aging agent RD, age resistor 3100, the benzothiazole sulfenamide of anti-recovery agent PK900, N tert-butyl group 2, vulcanizing agent DTDM, tackifying resin TYC0411, hydrocarbon oil and insoluble sulfur etc..It is good to roll the sizing material wearability of refining, ageing-resistant, anti-puncture excellent performance, manufactured Life of Tyre extends.
Description
Technical field
The present invention relates to a kind of full steel engineering radial-type tyre colliery tread glue formula, be mainly used in 30.00R51,
33.00R51 wait the tread rubber sizing material of full steel engineering radial-type tyre.
Background technology
Nineteen forty-six, radial was invented by company of Michelin of France, and revolutionary change is brought for tire industry.Thereafter
Again by this Technique Popularizing into all kinds of tires, and the first in the world meridian tire is produced in nineteen fifty-nine.Radial
Appearance, incomparable superiority is shown compared with bias tire.Therefore, in West Europe, radial develops earliest, development
Speed is also most fast.Early in almost 100% meridian of France in 1972, to year ends 1989, West Europe tire market 100% son
Noon.Full steel engineering radial-type tyre has fuel-economizing, low-heat-generation, distance travelled is high, load-bearing capacity is big, anti-wear performance is good, resistance to cuts
Cut, the performance such as resistance to puncture, driving safety are comfortable, advantage is fairly obvious compared with bias tire.The actual travel in colliery and iron ore
Mileage and service life are 2.5-3 times of bias tire, and remarkable in economical benefits, depth are welcome by user.
Full steel engineering radial-type tyre has excellent performance, and higher want is proposed to the performance of tire formulation sizing material
Ask.Therefore company is according to the actual investigation of the road conditions to major mine and tire used situation, and foundation is in the viviparity of Traditional project wheel
The experience of production, constantly brings forth new ideas, and have developed the various formulas needed for new tire.Full steel engineering radial-type tyre colliery tread rubber
Effect of the sizing material in tire is extremely important, and colliery majority is open work, but existing sizing material heat resistance, resistance to ag(e)ing
Energy, anti-puncture poor-performing, therefore develop a kind of brand-new full steel engineering radial-type tyre colliery tread glue formula.
The content of the invention
It is an object of the invention to provide a kind of full steel engineering radial-type tyre colliery tread glue formula, the formula uses day
The paste system that T PNR coordinates with butadiene rubber.Sizing material is demonstrated by good wear-resisting and heat resistance, the manufactured anti-thorn of tire
Prick, heat-resisting, ageing-resistant performance is good, service life length.The purpose of the present invention is realized by following technical scheme, a kind of all steel work
Journey radial colliery tread glue formula, it is characterised in that:It is formulated by weight by following raw materials:
Natural rubber 70-100;
Butadiene rubber 0-30;
Zinc oxide 3-6;
Stearic acid 1-4;
Carbon black 40-65;
Anti-recovery agent PK900 0-2;
Age resistor OK2122 1-3.5;
Anti-aging agent RD 0.5-2;
The 0.5-1 of age resistor 3100;
N tert butyl benzothiazole 2 sulfenamide 0.5-3.0;
Insoluble sulfur 1-2.5;
Vulcanizing agent DTDM 0-2;
Tackifying resin TYC0411 0-4;
Hydrocarbon oil 0-10;
The technical principle of the present invention is using the excellent super abrasive carbon black of reinforcing property(Code name N220)Make an addition to combination property most
In the excellent butadiene rubber paralled system of good natural rubber and anti-wear performance, sizing material is increased using the vulcanizing system of high sulphur
Wearability and high-intensity performance, and increase sulfuration resistant with the insoluble sulfur of high-temperature stable to increase the technology stability of sizing material
Agent revert to ensure that tire keeps good physical property in use.
Embodiment
Embodiment 1:
Natural rubber(Code name SMR 10#) 90;
Butadiene rubber(Code name BR9000) 10;
Zinc oxide 3.0;
Stearic acid 2.0;
Carbon black 58;
Anti-recovery agent PK900 1.0;
Age resistor OK2122 2.5;
Anti-aging agent RD 1.1;
Age resistor 3,100 0.75;
N tert butyl benzothiazole 2 sulfenamide 0.9;
Insoluble sulfur 2.1;
Vulcanizing agent DTDM 0.5;
Tackifying resin TYC0411 3.0;
Hydrocarbon oil 5.0;
1 in the present embodiment, described anti-aging agent RD is 2,2,4- trimethyl -1,2 dihyaroquinoline condensates, described age resistor
3100 be N, N '-DTPD di tolyl p phenylenediamine (mixture);
In the present embodiment 1, the calendering process of sizing material is:
1. dispensing:
Above each group is weighed successively according to standard weights respectively standby;
2. it is kneaded:
The charging sequence of mixing is:
2.1 will carry out rolling refining in natural rubber and butadiene rubber addition banbury, and rotating speed is 45 revs/min, and the time is 20 seconds;
2.2 add stearic acid, zinc oxide, age resistor OK2122, anti-aging agent RD, age resistor 3100, anti-recovery agent PK900,
Tackifying resin TYC0411, carbon black N220 are kneaded, and rotating speed is 40 revs/min, and the time is 60 seconds;
2.3 addition hydrocarbon oils are kneaded, and rotating speed is 35 revs/min, and the time is 80 seconds;
2.4 temperature reach 155 DEG C, and sizing material is discharged, and roll into film and pile up;
2.5 sizing materials must cool down more than 24 hours, standby;
2.6 add sizing material in banbury again, addition N tert butyl benzothiazole 2 sulfenamide, vulcanizing agent DTDM and not
Dissolubility sulphur is kneaded, and rotating speed is 20 revs/min, and the time is 140 seconds, dumping, and dump temperature is 102 DEG C, and extrusion film is cold
But;
Performance test data using tyre stock made of the present embodiment 1 is as follows:
Tensile strength/MPa 23.5;
300% stress at definite elongation/MPa 10.1;
Elongation at break/% 590;
Shore A type hardness testers/degree 63;
Compression fatigue heat/DEG C 22.5;
Rebound value/% normal temperature 75.2;
Thermoresilience value/100 DEG C 71.5 of %;
Akron abrasion (cm3/1.61km) 0.092;
There is preferable anti-puncture anti-wear performance in mine use using 33.00R51 tires made of the present embodiment 1, tyre surface is resistance to be collapsed
Block is used up, Life of Tyre is obviously prolonged.
Embodiment 2:
Natural rubber(Code name SMR 10#) 85;
Butadiene rubber(Code name BR9000) 15;
Zinc oxide 3.0;
Stearic acid 2.2;
Carbon black 62;
Anti-recovery agent PK900 0.8;
Age resistor OK2122 2.5;
Anti-aging agent RD 1.0;
Age resistor 3,100 0.75;
N tert butyl benzothiazole 2 sulfenamide 1.0;
Insoluble sulfur 2.2;
Vulcanizing agent DTDM 0.5;
Tackifying resin TYC0411 3.0;
Hydrocarbon oil 6.0;
In the present embodiment 2, the calendering process of sizing material is:
1. dispensing:
Above each group is weighed successively according to standard weights respectively standby;
2. it is kneaded:
The charging sequence of mixing is:
2.1 will carry out rolling refining in natural rubber and butadiene rubber addition banbury, and rotating speed is 45 revs/min, and the time is 20 seconds;
2.2 add stearic acid, zinc oxide, age resistor OK2122, anti-aging agent RD, age resistor 3100, anti-recovery agent PK900,
Tackifying resin TYC0411, carbon black N220 are kneaded, and rotating speed is 40 revs/min, and the time is 60 seconds;
2.3 addition hydrocarbon oils are kneaded, and rotating speed is 35 revs/min, and the time is 80 seconds;
2.4 temperature reach 155 DEG C, and sizing material is discharged, and roll into film and pile up;
2.5 sizing materials must cool down more than 24 hours, standby;
2.6 add sizing material in banbury again, addition N tert butyl benzothiazole 2 sulfenamide, vulcanizing agent DTDM and not
Dissolubility sulphur is kneaded, and rotating speed is 20 revs/min, and the time is 140 seconds, dumping, and dump temperature is 102 DEG C, and extrusion film is cold
But;
Performance test data using tyre surface formula sizing material made of the present embodiment 2 is as follows:
Tensile strength/MPa 22.5;
300% stress at definite elongation/MPa 9.6;
Elongation at break/% 589;
Shore A type hardness testers/degree 64;
Compression fatigue heat/DEG C 23.6;
Rebound value/% normal temperature 79.2;
Thermoresilience value/100 DEG C 72.6 of %;
Akron abrasion (cm3/1.61km) 0.082;
In above example 1,2, Life of Tyre made of sizing compound formula used improves nearly 2.5 times compared with cross-ply,
The wearability of tire improves a lot.
Claims (1)
- A kind of 1. full steel engineering radial-type tyre colliery tread glue formula, it is characterised in that the weight ratio of each component of its sizing material It is as follows:Natural rubber 70-100;Butadiene rubber 0-30;Zinc oxide 3-6;Stearic acid 1-4;Carbon black 40-65;Anti-recovery agent PK900 0-2;Age resistor OK2122 1-3.5;Anti-aging agent RD 0.5-2;The 0.5-1 of age resistor 3100;N tert butyl benzothiazole 2 sulfenamide 0.5-3.0;Insoluble sulfur 1-2.5;Vulcanizing agent DTDM 0-2;Tackifying resin TYC0411 0-4;Hydrocarbon oil 0-10.