CN107805949A - Multi-functional summer is with refrigerant sense fabric - Google Patents
Multi-functional summer is with refrigerant sense fabric Download PDFInfo
- Publication number
- CN107805949A CN107805949A CN201710918138.3A CN201710918138A CN107805949A CN 107805949 A CN107805949 A CN 107805949A CN 201710918138 A CN201710918138 A CN 201710918138A CN 107805949 A CN107805949 A CN 107805949A
- Authority
- CN
- China
- Prior art keywords
- refrigerant sense
- functional
- parts
- fabric
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is with refrigerant sense fabric, the composition and parts by weight of the fabric the invention discloses multi-functional summer：Multi-functional 40 60 parts of refrigerant sense fiber, 5 15 parts of flaxen fiber, 15 25 parts of cotton fiber, 8 15 parts of cocoon fiber.The preparation method of the fabric includes the preparation of peppermint oil microcapsule, prepared by multi-functional refrigerant sense fibre section, prepared by multi-functional refrigerant sense fiber, multi-functional summer is prepared with refrigerant sense fabric.Have the beneficial effect that：The present invention multi-functional summer has refreshing, anti-inflammation with refrigerant sense fabric, wear refrigerant advantage, and be easy to colour, absorbing sweat effect is good, have no stimulation of the skin, glossiness and soft-touch are good；The fabric has the feel of smooth, soft, wash resistant, there is the presence of peppermint oil microcapsule in its surface and fiber gap, and the form of microcapsules is complete, there is no a broken wall phenomenon, the slow releasing function of peppermint oil microcapsule can extend fabric refrigerant sense and mint flavored it is ageing.
Description
Technical field
The present invention relates to garment material field, more particularly to multi-functional summer is with refrigerant sense fabric.
Background technology
Human body is an airframe systems open, with compared with strong adaptability.When environment changes, human body is most fast
Adaptation reaction is the change of the circulatory system, and caused heat in vivo is carried to skin by it, and by perspiring, evaporation is scattered to increase
Heat.If sweat effectively can not be transmitted and evaporated so that the substantial amounts of heat of aggregation in vivo, will have influence on the comfort of human body, also
Probably due to hyperpyrexia triggers fatigue and reaction of trembling, or even reduce Human Stamina.Human body is passing through gaseous state sweat always
Moisture is lost, this is extremely important to keeping human body thermal balance and comfortableness, and this process depends on body state and the gas of surrounding
Environment is waited, is also largely influenceed by clothes physical property, clothes are the interaction media of environment and human body hot and humid area.
Clothes are not only to be covered in one on skin by kinetoplast, and can be adjusted with the skin heat to be changed because motion state is different
Function interaction is saved, and the latter is played regulatory role, the heat-moisture transfer attribute of clothes is to determine that human body gathers in motion
Heat and caused sweat actively can be delivered to outside clothes, so as to radiating and humidifying, are improved comfortableness, are still stopped in clothes
In dress-human body microenvironment, the key factor of human heat and wet comfort sense is reduced.It is especially all in the case where environment temperature is higher
When enclosing environment temperature close to body surface temperature, human body sweat in motion process flashes to as important factor, and
As human body and the clothes of surrounding environment heat-moisture transfer medium, its wet transitive attribute has non-to the radiating and humidifying of human body in motion
Often important meaning.Therefore, how lasting cooling feeling is kept in outdoor high temperature, turns into the problem of ordinary people is of interest.
Facing to such a demand from terminal consumer, function cool feeling absorbing sweat garment material just arises at the historic moment, in addition, summer weather is scorching
Heat, skin are easily perspired and sensitive, therefore it is required that fabric pliability is high, has no stimulation of the skin.
Prior art such as Authorization Notice No. is CN103184603B Chinese invention patent, discloses a kind of super cool feeling polyester
Fiber blend yarn and its spinning method for genuine, the mixed yarn is by super cool feeling polyester fiber 30%-100% and other fiber 70%-0% groups
It is the fibers such as tencel, Modal, viscose glue, cotton, bamboo fibre, terylene into, other fibers, by blowing, cotton carding, simultaneously on cotton spinning equipment
Bar, rove, spun yarn, the special process spinning of winding procedure.Multiple fiber blending in the mixed yarn, have complementary advantages between fiber,
With changeable style, not only with ventilative, comfortable and easy to wear, feel cunning the is glutinous characteristic of moisture absorption, and there is instantaneous temperature reduction effect, connect
There is 1-2 ° of moment is nice and cool, sunshine irradiates to have the 5-6 ° of cool feeling temperature difference after touching skin, skin can be wet by skin surface sweat after perspiring
Aspiration is transported to fabric face and dissipated, but the fabric flexibility is inadequate, and it is inadequate to wear comfort.
The content of the invention
It is an object of the invention to provide one kind have refrigerant sense and mint flavored, be easy to coloring, absorbing sweat effect it is good, to skin
Have no stimulation, multi-functional summer that glossiness and soft-touch are good is with refrigerant sense fabric.
The present invention is directed to the problem of being mentioned in above-mentioned technology, and the technical scheme taken is：Multi-functional summer is with refrigerant sense face
Material, its composition and parts by weight are：Multi-functional refrigerant sense fiber 40-60 parts, flaxen fiber 5-15 parts, cotton fiber 15-25 parts, silk are fine
Tie up 8-15 parts.The fabric has refreshing, anti-inflammation, wears refrigerant advantage, and the fabric is easy to coloring, absorbing sweat effect
Get well, have no stimulation of the skin, glossiness and soft-touch it is good, it is water-fastness.
Multi-functional summer is with the preparation method of refrigerant sense fabric, including prepared by peppermint oil microcapsule, multi-functional refrigerant sense is fine
Prepared by dimension section, prepared by multi-functional refrigerant sense fiber, multi-functional summer is prepared with refrigerant sense fabric, and it is concretely comprised the following steps：
It is prepared by peppermint oil microcapsule：Peppermint oil 20-30 parts, wall material 42-55 parts, emulsifying agent 2-3 parts, crosslinking agent are taken by weight
0.01-0.02 parts, the wall material solution that concentration is 1.3-1.7% and the emulsifier solution that concentration is 0.4-0.7% are first prepared, then will be thin
Lotus oil and emulsifier solution pre-emulsification 50-70s, then add wall material solution and continue to emulsify 2-4min, then adjust pH to 3-4, after
Continue and react 12-16min under conditions of temperature is 35-45 DEG C, stir speed (S.S.) is 500-700r/min, be then cooled to 2-10
DEG C, pH is adjusted to 9-10, is eventually adding crosslinking agent reaction 10-20min, spray drying, produces the microcapsules that fineness is 1-5 μm, on
It is that weight ratio is 1 to state wall material:0.9-1.1 gelatin and Arabic gum, the gelatin in the wall material is in the solution with polycation
Form is present, and it can be with producing electrostatic interaction in solution with Arabic gum existing for polyanion, and electric charge attracts each other and shape
Into negative ions complex compound, solubility reduces and condenses encystation, and the microencapsulated forms for the peppermint oil microcapsule that the step obtains are steady
Fixed, distinct, its surface is smooth, and cyst wall densification does not rupture, and wall material can not only play a protective role to peppermint oil, makes thin
Lotus oil high temperature resistant, delays its decomposition, reaches the effect of embedding, and can significantly reduce the rate of volatilization of peppermint oil, more has
Continue muchly to play its effect beneficial to essential oil, the effect of sustained release can be reached；
It is prepared by multi-functional refrigerant sense fibre section：It is 100 by weight ratio:0.7-1:0.28-0.35 polyamide, jade powder and thin
Lotus oil microcapsule is added in batch mixer and premixed, then raw material is put into melting extrusion in double screw extruder, cool drying, i.e., much
Function refrigerant sense fibre section, above-mentioned jade powder are surface-treated with silane coupler and titanate coupling agent, surface treatment
The particle diameter reduction of jade powder and distribution narrow afterwards so that the oil factor of jade powder is decreased obviously, and can effectively reduce the table of jade powder
Face can, so as to reduce the generation of jade powder agglomeration, polyamide in the step, jade powder and peppermint oil microcapsule it is reasonable
Proportioning enables jade powder and peppermint oil microcapsule dispersed in polyamide melt, and agglomeration will not occur, and to poly-
The mobility and spinnability of acid amides melt influence less, while jade powder and the compounding use of peppermint oil microcapsule additive can be big
The big refrigerant sense for improving polyamide, effect is far better than single additive；
It is prepared by multi-functional refrigerant sense fiber：Multi-functional refrigerant sense fibre section and auxiliary agent are put into screw rod, component, spinneret temperature
Respectively 245-255 DEG C, 260-270 DEG C, 235-245 DEG C, winding speed is to be carried out in 380-420m/min screw extruder
Melt spinning, multi-functional refrigerant sense fiber being produced, above-mentioned additive dosage is the 0.3-0.5% of multi-functional refrigerant sense fibre section,
Auxiliary agent is that weight ratio is 1:0.7-0.9:0.13-0.15 calcium chloride, rare earth ion and lactic acid, D-lactic acid and dextrorotation in lactic acid
The weight ratio of lactic acid is 1:0.2-0.3, D-lactic acid and L-lactic acid rational proportion can enable lactic acid as chlorination in lactic acid
The carrier agent of calcium and rare earth ion, the dispersiveness and stabilizer of calcium chloride and rare earth ion are improved, can preferably be acted on poly-
Amide molecule, the in addition addition of lactic acid can also make fiber be easy to colour, increase gloss and soft-touch, the controllability of the auxiliary agent
Good, the addition of auxiliary agent can hinder or destroy the formation of hydrogen bond between polyamide molecule, by reducing polyamide molecule interphase interaction
To reduce its melt viscosity, the addition of trace assistant can improve the processing characteristics of multi-functional refrigerant sense fibre section, make more work(
Can refrigerant sense fibre section obtain can spinnability greatly improve, and be not easy fracture of wire, finally improve the performance of multi-functional refrigerant sense fiber,
The peppermint oil microcapsule and jade powder that are prepared are coated in fiber by the multi-functional refrigerant sense fiber, have fiber refrigerant
Sense and mint flavored, also with the slow releasing function of peppermint oil microcapsule, the timeliness of long stapled refrigerant sense and mint flavored can be prolonged
Property；
Multi-functional summer is prepared with refrigerant sense fabric：Multi-functional refrigerant sense fiber, flaxen fiber, cotton fiber, silk are measured by formula
Fiber, blending by mixed yarn looming weaving, thermal finalization, are finally put into dressing liquid and post-processed into mixed yarn, i.e. much work(
Can summer be with refrigerant sense fabric, the composition and its parts by weight of above-mentioned dressing liquid：Peppermint oil microcapsule 3-5 parts, propane diols shrink
Glycerin ether 19-22 parts, aziridine 5-10 parts, ethylene urea 2-3 parts, polyurethane 0.8-1.2 parts, Tween-20 1-2 parts, water
80-90 parts, the arrangement liquid energy crosslink with fiber, effectively keep fibre-forming polymer chain molecule to be connected to each other, and make to divide on chain
It can be maintained between son on relative position, strengthen the wrinkle resistance of fabric, and peppermint oil microcapsule is readily adsorbed in fabric table
Face, it is strong to fabric affinity, make fabric have the feel of smooth, soft, wash resistant, and collated web surface and fiber empty
There is the presence of peppermint oil microcapsule in gap, and form is complete, does not have broken wall phenomenon, further enhances the refrigerant sense of fabric,
The fabric has refreshing, anti-inflammation, wears refrigerant advantage, and the fabric be easy to coloring, absorbing sweat effect it is good, to skin
Have no stimulation, glossiness and soft-touch it is good, also with the slow releasing function of peppermint oil microcapsule, fabric can be extended
Refrigerant sense and mint flavored it is ageing.
Compared with prior art, the advantage of the invention is that：1）The present invention multi-functional summer has clear with refrigerant sense fabric
It is cool to refresh oneself, anti-inflammation, wear refrigerant advantage, and the fabric be easy to coloring, absorbing sweat effect is good, have no stimulation of the skin,
Glossiness and soft-touch are good；2）The fabric has the feel of smooth, soft, wash resistant, and collated web surface and fibre
There is the presence of peppermint oil microcapsule in dimension space, the form of microcapsules is complete, does not have broken wall phenomenon, and the fabric utilizes peppermint oil
The slow releasing function of microcapsules, can extend fabric refrigerant sense and mint flavored it is ageing；3）It is multi-functional refrigerant in the fabric
Jade powder and peppermint oil microcapsule are embedded with sense fiber, the water-wash resistance of fiber can be improved, and then improve the water-fastness of fabric
Property；4）The multi-functional summer refrigerant sense fabric improves the added value of Fypro, and processing technology is simple, operational control side
Just, steady quality, production efficiency is high, is easy to large-scale industrial production.
Embodiment
The present invention program is described further below by embodiment：
Embodiment 1：
Multi-functional summer is with refrigerant sense fabric, its composition and parts by weight：Multi-functional 55 parts of refrigerant sense fiber, 6 parts of flaxen fiber, cotton
23 parts of fiber, 8 parts of cocoon fiber.
Multi-functional summer is with the preparation method of refrigerant sense fabric, including prepared by peppermint oil microcapsule, multi-functional refrigerant sense is fine
Prepared by dimension section, prepared by multi-functional refrigerant sense fiber, multi-functional summer is prepared with refrigerant sense fabric, and it is concretely comprised the following steps：
1）It is prepared by peppermint oil microcapsule：30 parts of peppermint oil, 45 parts of wall material, 3 parts of emulsifying agent, 0.012 part of crosslinking agent are taken by weight,
The wall material solution that concentration is 1.7% and the emulsifier solution that concentration is 0.45% are first prepared, then peppermint oil and emulsifier solution is pre-
65s is emulsified, wall material solution is then added and continues to emulsify 2min, then adjusts pH to 3.8, it is 38 DEG C, stir speed (S.S.) to continue in temperature
To react 12min under conditions of 700r/min, 10 DEG C are then cooled to, pH is adjusted to 9.2, is eventually adding crosslinking agent reaction 20min,
Spray drying, the microcapsules that fineness is 1-5 μm are produced, above-mentioned wall material is that weight ratio is 1:0.92 gelatin and Arabic gum, should
Gelatin in wall material exists in the form of polycation in the solution, it can with solution with Arabic existing for polyanion
Glue produces electrostatic interaction, and electric charge attracts each other and forms negative ions complex compound, and solubility reduces and condenses encystation, and the step obtains
The microencapsulated forms of the peppermint oil microcapsule arrived are stable, and distinct, its surface is smooth, and cyst wall densification does not rupture, and wall material is not
Peppermint oil can only be played a protective role, make peppermint oil high temperature resistant, delay its decomposition, reach the effect of embedding, and can be with
The rate of volatilization of peppermint oil is significantly reduced, essential oil is more beneficial for and continues muchly to play its effect, the effect of sustained release can be reached
Fruit；
2）It is prepared by multi-functional refrigerant sense fibre section：It is 100 by weight ratio:1:0.28 polyamide, jade powder and peppermint oil are micro-
Capsule is added in batch mixer and premixed, then raw material is put into melting extrusion in double screw extruder, cool drying, is produced multi-functional clear
Cool fiber is cut into slices, and above-mentioned jade powder is surface-treated with silane coupler and titanate coupling agent, jade after surface treatment
The particle diameter of powder reduces and distribution narrow so that and the oil factor of jade powder is decreased obviously, and can effectively reduce the surface energy of jade powder, from
And reducing the generation of jade powder agglomeration, the rational proportion of polyamide, jade powder and peppermint oil microcapsule makes in the step
Obtain jade powder and peppermint oil microcapsule can be dispersed in polyamide melt, agglomeration will not occur, and polyamide is melted
The mobility and spinnability of body influence less, while jade powder and the compounding use of peppermint oil microcapsule additive can greatly improve
The refrigerant sense of polyamide, effect is far better than single additive；
3）It is prepared by multi-functional refrigerant sense fiber：Multi-functional refrigerant sense fibre section and auxiliary agent are put into screw rod, component, spinneret temperature
Degree is respectively 255 DEG C, 260 DEG C, 245 DEG C, and winding speed is to carry out melt spinning in 380m/min screw extruder, i.e., much
Function refrigerant sense fiber, above-mentioned additive dosage are the 0.5% of multi-functional refrigerant sense fibre section, and auxiliary agent is that weight ratio is 1:
0.7:0.15 calcium chloride, rare earth ion and lactic acid, the weight of D-lactic acid and L-lactic acid ratio is 1 in lactic acid:0.2, lactic acid
Middle D-lactic acid and L-lactic acid rational proportion can enable lactic acid improve chlorination as calcium chloride and the carrier agent of rare earth ion
The dispersiveness and stabilizer of calcium and rare earth ion, can preferably act on polyamide molecule, and the addition of lactic acid in addition can also make
Fiber is easy to colour, increases gloss and soft-touch, and the controllability of the auxiliary agent is good, and the addition of auxiliary agent can hinder or destroy polyamides
The formation of hydrogen bond between amine molecule, its melt viscosity is reduced by reducing polyamide molecule interphase interaction, trace assistant adds
The processing characteristics of multi-functional refrigerant sense fibre section can be improved by entering, make multi-functional refrigerant sense fibre section obtain can spinnability significantly
Improve, and be not easy fracture of wire, finally improve the performance of multi-functional refrigerant sense fiber, the multi-functional refrigerant sense fiber will be prepared
Peppermint oil microcapsule and jade powder are coated in fiber, fiber is had refrigerant sense and mint flavored so that its woven face prepared
Material with refreshing, anti-inflammation, wear refrigerant advantage, and the fabric lining is easy to colour, absorbing sweat effect is good, to skin
Have no stimulation, glossiness and soft-touch it is good, also with the slow releasing function of peppermint oil microcapsule, can prolong long stapled
Refrigerant sense and mint flavored it is ageing；
4）Multi-functional summer is prepared with refrigerant sense fabric：Multi-functional refrigerant sense fiber, flaxen fiber, cotton fiber, true is measured by formula
Much silk fiber, blending, by mixed yarn looming weaving, thermal finalization, finally put into dressing liquid and post-processed, i.e., into mixed yarn
Function summer is with refrigerant sense fabric, the composition and its parts by weight of above-mentioned dressing liquid：5 parts of peppermint oil microcapsule, propane diols shrink
19 parts of glycerin ether, 10 parts of aziridine, 2 parts of ethylene urea, 1.2 parts of polyurethane, 1 part of Tween-20,90 parts of water, the dressing liquid
It can be crosslinked with fiber, effectively keep fibre-forming polymer chain molecule to be connected to each other, make that phase can be maintained on chain between molecule
To position on, strengthen the wrinkle resistance of fabric, and peppermint oil microcapsule is readily adsorbed in web surface, to fabric affinity
By force, make fabric that there is the feel of smooth, soft, wash resistant, and have peppermint oil micro- in collated web surface and fiber gap
The presence of capsule, and form is complete, does not have broken wall phenomenon, further enhances the refrigerant sense of fabric, and the fabric has refrigerant carry
God, anti-inflammation, refrigerant advantage is worn, and the fabric is easy to coloring, absorbing sweat effect is good, has no stimulation of the skin, gloss
Degree and soft-touch are good, also with the slow releasing function of peppermint oil microcapsule, can extend the refrigerant sense and mint flavored of fabric
It is ageing.
Embodiment 2：
Multi-functional summer is with refrigerant sense fabric, its composition and parts by weight：Multi-functional 43 parts of refrigerant sense fiber, 15 parts of flaxen fiber,
15 parts of cotton fiber 15-256 parts, cocoon fiber.
Multi-functional summer, it was concretely comprised the following steps with the preparation method of refrigerant sense fabric：
1）It is prepared by peppermint oil microcapsule：20 parts of peppermint oil, 55 parts of wall material, 2 parts of emulsifying agent, 0.02 part of crosslinking agent are taken by weight,
First prepare the wall material solution that concentration is 1.3% and the emulsifier solution that concentration is 0.7%, then by peppermint oil and the pre- breast of emulsifier solution
Change 50s, then add wall material solution and continue to emulsify 4min, then adjust pH to 3, continue temperature be 45 DEG C, stir speed (S.S.) be
16min is reacted under conditions of 500r/min, is then cooled to 3 DEG C, pH is adjusted to 10, is eventually adding crosslinking agent reaction 13min, spraying
Dry, produce the microcapsules that fineness is 1-5 μm, above-mentioned wall material is that weight ratio is 1:1.1 gelatin and Arabic gum；
2）It is prepared by multi-functional refrigerant sense fibre section：It is 100 by weight ratio:0.7:0.35 polyamide, jade powder and peppermint oil
Microcapsules are added in batch mixer and premixed, then raw material is put into melting extrusion in double screw extruder, cool drying, are produced multi-functional
Refrigerant sense fibre section, above-mentioned jade powder are surface-treated with silane coupler and titanate coupling agent；
3）It is prepared by multi-functional refrigerant sense fiber：Multi-functional refrigerant sense fibre section and auxiliary agent are put into screw rod, component, spinneret temperature
Degree is respectively 245 DEG C, 270 DEG C, 235 DEG C, and winding speed is to carry out melt spinning in 420m/min screw extruder, i.e., much
Function refrigerant sense fiber, above-mentioned additive dosage are the 0.3% of multi-functional refrigerant sense fibre section, and auxiliary agent is that weight ratio is 1:
0.9:0.13 calcium chloride, rare earth ion and lactic acid, the weight of D-lactic acid and L-lactic acid ratio is 1 in lactic acid:0.3；
4）Multi-functional summer is prepared with refrigerant sense fabric：Multi-functional refrigerant sense fiber, flaxen fiber, cotton fiber, true is measured by formula
Much silk fiber, blending, by mixed yarn looming weaving, thermal finalization, finally put into dressing liquid and post-processed, i.e., into mixed yarn
Function summer is with refrigerant sense fabric, the composition and its parts by weight of above-mentioned dressing liquid：3 parts of peppermint oil microcapsule, propane diols shrink
22 parts of glycerin ether, 5 parts of aziridine, 3 parts of ethylene urea, 0.8 part of polyurethane, 2 parts of Tween-20,80 parts of water.
Embodiment 3：
Multi-functional summer is with refrigerant sense fabric, its composition and parts by weight：Multi-functional 50 parts of refrigerant sense fiber, 10 parts of flaxen fiber,
20 parts of cotton fiber, 12 parts of cocoon fiber.
Multi-functional summer is with the preparation method of refrigerant sense fabric：
1）25 parts of peppermint oil, 48 parts of wall material, 2.5 parts of emulsifying agent, 0.015 part of crosslinking agent are taken by weight, and wall material is that weight ratio is
1:1 gelatin and Arabic gum, the wall material solution that concentration is 1.5% and the emulsifier solution that concentration is 0.5% are first prepared, then will be thin
Lotus oil and emulsifier solution pre-emulsification 60s, then add wall material solution and continue to emulsify 3min, then adjust pH to 3.5, continue in temperature
Spend for 40 DEG C, stir speed (S.S.) be 600r/min under conditions of react 14min, be then cooled to 6 DEG C, pH is adjusted to 9.5, is eventually adding
Crosslinking agent reacts 15min, spray drying, produces the peppermint oil microcapsule that fineness is 1-5 μm；
2）It is 100 by weight ratio:0.8:0.3 polyamide, it is surface-treated with silane coupler and titanate coupling agent
Jade powder and peppermint oil microcapsule, which are added in batch mixer, to be premixed, then raw material is put into melting extrusion in double screw extruder, is cooled down
Dry, produce multi-functional refrigerant sense fibre section；
3）By multi-functional refrigerant sense fibre section and auxiliary agent be put into screw rod, component, spinneret temperature be respectively 250 DEG C, 265 DEG C,
240 DEG C, winding speed is to carry out melt spinning in 400m/min screw extruder, produces multi-functional refrigerant sense fiber, above-mentioned
Additive dosage is the 0.4% of multi-functional refrigerant sense fibre section, and auxiliary agent is that weight ratio is 1:0.8:0.14 calcium chloride, rare earth
Ion and lactic acid, the weight of D-lactic acid and L-lactic acid ratio is 1 in lactic acid:0.25；
4）Multi-functional refrigerant sense fiber, flaxen fiber, cotton fiber, cocoon fiber are measured by formula, blending is into mixed yarn, by mixed yarn
Looming weaving, thermal finalization, finally input containing 4 parts of peppermint oil microcapsule, 20 parts of propylene glycol glycidyl ether, 8 parts of aziridine,
2.5 parts of ethylene urea, 1 part of polyurethane, 1.5 parts of Tween-20,85 parts of water dressing liquid in post-processed, produce multi-functional
Summer is with refrigerant sense fabric.
Embodiment 4：
Multi-functional summer is with the performance test of refrigerant sense fabric：
The fabric of embodiment 1, embodiment 2 and embodiment 3 is set to test group, common commercially available polyamide fabric is set to control group 1,
Common commercially available refrigerant fabric is set to control group 2, carries out refrigerant sense test respectively.
Refrigerant sense is tested：Changes in temperature sensing tester is contacted using instantaneous touch cool feeling Q-max as index：By simulating hand contact surface
The change of caused heat calculates the degree of cool feeling after material, and result of calculation is as shown in table 1.
Table 1：Refrigerant sense test result
As shown in Table 1, the refrigerant sense Q-max of the embodiment of the present invention 1, embodiment 2 and the fabric of embodiment 3 is more than control group 1 and right
According to group 2, illustrate that the present invention multi-functional summer is good with the cooling effect of refrigerant sense fabric.
Routine operation in the operating procedure of the present invention is well known to those skilled in the art, herein without repeating.
Technical scheme is described in detail embodiment described above, it should be understood that it is described above only
For the specific embodiment of the present invention, it is not intended to limit the invention, all any modifications made in the spirit of the present invention,
Supplement or similar fashion replacement etc., should be included in the scope of the protection.
Claims (10)
1. multi-functional summer is with refrigerant sense fabric, it is characterised in that：Described multi-functional summer with the composition of refrigerant sense fabric and
Its parts by weight is：Multi-functional refrigerant sense fiber 40-60 parts, flaxen fiber 5-15 parts, cotton fiber 15-25 parts, cocoon fiber 8-15 parts.
2. multi-functional summer according to claim 1 is with refrigerant sense fabric, it is characterised in that：The preparation side of described fabric
Method is：
1）It is prepared by peppermint oil microcapsule：Again by peppermint oil and emulsifier solution pre-emulsification, then add wall material solution and continue to emulsify,
It is stirred for reacting, then cooling, adds crosslinking agent reaction, spray drying, produce microcapsules；
2）It is prepared by multi-functional refrigerant sense fibre section：Polyamide, jade powder and peppermint oil microcapsule are added in batch mixer and premixed,
Raw material is put into melting extrusion in double screw extruder again, cool drying, produces multi-functional refrigerant sense fibre section；
3）It is prepared by multi-functional refrigerant sense fiber：Multi-functional refrigerant sense fibre section and auxiliary agent are put into out in machine and carry out melting spinning
Silk, produces multi-functional refrigerant sense fiber；
4）Multi-functional summer is prepared with refrigerant sense fabric：Multi-functional refrigerant sense fiber, flaxen fiber, cotton fiber, true is measured by formula
Much silk fiber, blending, by mixed yarn looming weaving, thermal finalization, finally put into dressing liquid and post-processed, i.e., into mixed yarn
Function summer is with refrigerant sense fabric.
3. multi-functional summer according to claim 2 is with the preparation method of refrigerant sense fabric, it is characterised in that：Described step
The screw rod of screw extruder, component, spinneret temperature are respectively 245-255 DEG C, 260-270 DEG C, 235-245 DEG C in rapid 3, winding
Speed is 380-420m/min.
4. multi-functional summer according to claim 2 is with the preparation method of refrigerant sense fabric, it is characterised in that：Described step
Additive dosage is the 0.3-0.5% of multi-functional refrigerant sense fibre section in rapid 3, and auxiliary agent is that weight ratio is 1:0.7-0.9:0.13-
0.15 calcium chloride, rare earth ion and lactic acid.
5. multi-functional summer according to claim 4 is with the preparation method of refrigerant sense fabric, it is characterised in that：Described step
The weight of D-lactic acid and L-lactic acid ratio is 1 in lactic acid in rapid 3:0.2-0.3.
6. multi-functional summer according to claim 2 is with the preparation method of refrigerant sense fabric, it is characterised in that：Described step
The composition of peppermint oil microcapsule and its parts by weight are in rapid 1：Peppermint oil 20-30 parts, wall material 42-55 parts, emulsifying agent 2-3 parts, friendship
Join agent 0.01-0.02 parts, wall material is that weight ratio is 1:0.9-1.1 gelatin and Arabic gum.
7. multi-functional summer according to claim 2 is with the preparation method of refrigerant sense fabric, it is characterised in that：Described step
The concentration of wall material solution is 1.3-1.7% in rapid 1, and the concentration of emulsifier solution is 0.4-0.7%.
8. multi-functional summer according to claim 2 is with the preparation method of refrigerant sense fabric, it is characterised in that：Described step
The pH of stirring reaction is 3-4 in rapid 1, and temperature is 35-45 DEG C, stir speed (S.S.) 500-700r/min, time 12-16min；Hand over
The temperature of connection reaction is 2-10 DEG C, pH 9-10, time 10-20min.
9. multi-functional summer according to claim 2 is with the preparation method of refrigerant sense fabric, it is characterised in that：Described step
The weight ratio of polyamide, jade powder and peppermint oil microcapsule is 100 in rapid 2:0.7-1:0.28-0.35, jade powder are even with silane
Connection agent and titanate coupling agent are surface-treated.
10. multi-functional summer according to claim 2 is with the preparation method of refrigerant sense fabric, it is characterised in that：Described
The composition of dressing liquid and its parts by weight are in step 4：Peppermint oil microcapsule 3-5 parts, propylene glycol glycidyl ether 19-22 parts, second
Alkene imines 5-10 parts, ethylene urea 2-3 parts, polyurethane 0.8-1.2 parts, Tween-20 1-2 parts, water 80-90 parts.