CN107805430A - A kind of reflective heat-insulation paint used for textiles - Google Patents
A kind of reflective heat-insulation paint used for textiles Download PDFInfo
- Publication number
- CN107805430A CN107805430A CN201711113210.1A CN201711113210A CN107805430A CN 107805430 A CN107805430 A CN 107805430A CN 201711113210 A CN201711113210 A CN 201711113210A CN 107805430 A CN107805430 A CN 107805430A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat
- paint used
- insulation paint
- textiles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of reflective heat-insulation paint used for textiles, includes the raw material composition of following parts by weight：20 ~ 40 parts of water-based acrylic resin；8 ~ 15 parts of Acrylic Adhesive Modified with Silicone；2 ~ 6 parts of nano-hollow microballon；3 ~ 10 parts of inorganic filler；0.5 ~ 1 part of dispersant；0.2 ~ 0.8 part of wetting agent；0.5 ~ 1 part of levelling agent；0.3 ~ 0.6 part of defoamer；0.1 ~ 0.5 part of coalescents.Coating proposed by the present invention is used for textile, and it has the effect of reflection red line line, is effectively reduced absorption of the textile to infrared ray, the heat absorption capacity of yarn fabric is reduced, plays the effect of heat-insulation and heat-preservation, simultaneously, energy-conserving and environment-protective, adhesive force is strong, weatherability is strong, and improves its service life.
Description
Technical field
The present invention relates to functional coating technical field, and in particular to a kind of reflective heat-insulation paint used for textiles.
Background technology
Heat insulating coat fabric is that one layer of coating with effect of heat insulation is coated on fabric, by obstructing, reflecting or radiate
Solar energy reaches the purpose for reducing fabric cover internal temperature, can play the purpose for reducing energy resource consumption.Have in textile industry
Good application prospect.Weaving heat insulating coat is used primarily in the fabric of army personnel's dress, by the anti-of infra-red radiation
The difference for eliminating or reducing infrared external reflection characteristic between fabric and background such as penetrate, obstruct, radiating, realizing to the infrared of army personnel
Camouflage.Then it is applied in civil area, according to infrared emanation mode is resisted, fabric heat insulating coat can be divided into barrier
Type heat insulating coat, reflection type thermal insulation coating and radiation type heat-insulation coating.Heat-proof coating material for fabric mainly have resin and
Functional particles, wherein functional particles play main function.
It is infrared-reflecting coated as conventional one kind, refer to be coated on body surface, to the infrared band tool in radiation
There is high reflectance, so as to suppress Coated Surface Temperature rising and reduce the coating of covering internal temperature, heat-reflective coating simultaneously
Reflectivity depend on coating in color stuffing optical properties total reflection and scattering, color stuffing is mainly based on scattering.Color stuffing
Refraction index differ bigger with the refraction index of resin, it is stronger to the albedo of sunshine.Color stuffing and resin it is this
The relation of refraction index, there is certain associate with the covering power of color stuffing.Obviously, the covering power of color stuffing is stronger, scattering heat
Ability it is stronger.
The content of the invention
It is an object of the invention to provide a kind of with excellent effect of heat insulation while corrosion-resistant, the weaving of service life length
Product reflective heat-insulation paint.
The present invention is achieved through the following technical solutions：
A kind of reflective heat-insulation paint used for textiles, include the raw material composition of following parts by weight：
20 ~ 40 parts of water-based acrylic resin；
8 ~ 15 parts of Acrylic Adhesive Modified with Silicone；
2 ~ 6 parts of nano-hollow microballon；
3 ~ 10 parts of inorganic filler；
0.5 ~ 1 part of dispersant；
0.2 ~ 0.8 part of wetting agent；
0.5 ~ 1 part of levelling agent；
0.3 ~ 0.6 part of defoamer；
0.1 ~ 0.5 part of coalescents.
Further, the inorganic filler includes silica, zinc oxide, titanium dioxide, graphene.
Further, the silica, zinc oxide, titanium dioxide, the mass ratio of graphene are 2：1~1.5：1.5~2.5：
0.8~1.2。
Further, the particle diameter of the nano-hollow microballon is 1 ~ 3um.
Further, the silica, zinc oxide, titanium dioxide, the particle diameter of graphene are 1 ~ 3um.
The beneficial effects of the invention are as follows：Coating proposed by the present invention is used for textile, and it has the effect of reflection red line line,
Absorption of the textile to infrared ray is effectively reduced, reduces the heat absorption capacity of yarn fabric, plays the effect of heat-insulation and heat-preservation, together
When, energy-conserving and environment-protective, adhesive force is strong, weatherability is strong, and improves its service life.
Embodiment
The present invention is described further with reference to embodiment.
Embodiment 1
A kind of reflective heat-insulation paint used for textiles, include the raw material composition of following parts by weight：
20 parts of water-based acrylic resin；
8 parts of Acrylic Adhesive Modified with Silicone；
2 parts of nano-hollow microballon；
3 parts of inorganic filler；
0.5 part of dispersant；
0.2 part of wetting agent；
0.5 part of levelling agent；
0.3 part of defoamer；
0.1 part of coalescents.
In the present embodiment, inorganic filler includes silica, zinc oxide, titanium dioxide, graphene；Silica, oxidation
Zinc, titanium dioxide, the mass ratio of graphene are 2：1：1.5：0.8；The particle diameter of nano-hollow microballon is 1um；The silica, oxygen
It is 1um to change zinc, titanium dioxide, the particle diameter of graphene.
Embodiment 2
A kind of reflective heat-insulation paint used for textiles, include the raw material composition of following parts by weight：
30 parts of water-based acrylic resin；
10 parts of Acrylic Adhesive Modified with Silicone；
4 parts of nano-hollow microballon；
6 parts of inorganic filler；
0.8 part of dispersant；
0.5 part of wetting agent；
0.7 part of levelling agent；
0.4 part of defoamer；
0.3 part of coalescents.
In the present embodiment, inorganic filler includes silica, zinc oxide, titanium dioxide, graphene；Silica, oxidation
Zinc, titanium dioxide, the mass ratio of graphene are 2：1.2：2：1；The particle diameter of nano-hollow microballon is 2um；The silica, oxidation
Zinc, titanium dioxide, the particle diameter of graphene are 2um.
Embodiment 3
A kind of reflective heat-insulation paint used for textiles, include the raw material composition of following parts by weight：
40 parts of water-based acrylic resin；
15 parts of Acrylic Adhesive Modified with Silicone；
6 parts of nano-hollow microballon；
10 parts of inorganic filler；
1 part of dispersant；
0.8 part of wetting agent；
1 part of levelling agent；
0.6 part of defoamer；
0.5 part of coalescents.
In the present embodiment, inorganic filler includes silica, zinc oxide, titanium dioxide, graphene；Silica, oxidation
Zinc, titanium dioxide, the mass ratio of graphene are 2： 1.5： 2.5： 1.2；The particle diameter of nano-hollow microballon is 3um；The titanium dioxide
Silicon, zinc oxide, titanium dioxide, the particle diameter of graphene are 3um.
It is described above, only it is embodiments of the invention, is not the limitation for making any other form to the present invention, and
Any modification or equivalent variations that technical spirit according to the present invention is made, still fall within scope of the present invention.
Claims (5)
- A kind of 1. reflective heat-insulation paint used for textiles, it is characterised in that：Raw material composition including following parts by weight：20 ~ 40 parts of water-based acrylic resin；8 ~ 15 parts of Acrylic Adhesive Modified with Silicone；2 ~ 6 parts of nano-hollow microballon；3 ~ 10 parts of inorganic filler；0.5 ~ 1 part of dispersant；0.2 ~ 0.8 part of wetting agent；0.5 ~ 1 part of levelling agent；0.3 ~ 0.6 part of defoamer；0.1 ~ 0.5 part of coalescents.
- A kind of 2. reflective heat-insulation paint used for textiles according to claim 1, it is characterised in that：The inorganic filler includes two Silica, zinc oxide, titanium dioxide, graphene.
- A kind of 3. reflective heat-insulation paint used for textiles according to claim 2, it is characterised in that：The silica, oxidation Zinc, titanium dioxide, the mass ratio of graphene are 2：1~1.5：1.5~2.5：0.8~1.2.
- A kind of 4. reflective heat-insulation paint used for textiles according to claim 1, it is characterised in that：The nano-hollow microballon Particle diameter is 1 ~ 3um.
- A kind of 5. reflective heat-insulation paint used for textiles according to Claims 2 or 3, it is characterised in that：The silica, oxygen It is 1 ~ 3um to change zinc, titanium dioxide, the particle diameter of graphene.