CN107793104A - A kind of frost resistance is non-burning brick - Google Patents
A kind of frost resistance is non-burning brick Download PDFInfo
- Publication number
- CN107793104A CN107793104A CN201610774832.8A CN201610774832A CN107793104A CN 107793104 A CN107793104 A CN 107793104A CN 201610774832 A CN201610774832 A CN 201610774832A CN 107793104 A CN107793104 A CN 107793104A
- Authority
- CN
- China
- Prior art keywords
- cement
- frost resistance
- burning brick
- activator
- lime
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of frost resistance is non-burning brick, the concrete is formed using the uniform mix of raw material of following match ratio：Cement 5 10, lime 30 40, flyash 35 50, activator 0.1 0.2, straw 0.5 1, water 25 35, the cement is that silicon breaks salt cement as cementitious matter, with slag cements or pulverized fuel ash cement, activator is sodium sulphate, the lime is carbide slag, and the present invention can be suitable for the overall pouring of the cast-in-place concretes such as the basis of skyscraper, beam, post, framework, bridge, and T connector.The quality of monolithic architecture can be ensured, meet building standard, improve concrete grade, reduce energy consumption, improve yield.
Description
Technical field
Design building technical field of concrete of the present invention, and in particular to a kind of frost resistance is non-burning brick.
Background technology
Concrete, refer to the general designation for the cementing integral engineered composite material that gathers materials by binder materials.That generally says is mixed
Coagulate one word of soil to refer to make binder materials with cement, sand, masonry gather materials；With water（Additive and admixture can be contained）Match somebody with somebody by a certain percentage
Close, it is agitated obtained by cement concrete, also referred to as normal concrete.Concrete is that purposes is most wide in civil engineering, dosage is maximum
A kind of construction material.Concrete is designed and made by pre-determined characteristics, develops lightweight, high intensity, multi-functional concrete new product
Kind.
Existing mix Design is unreasonable, it is impossible to high suitable for the needs of existing production and living, cost.
The content of the invention
The problem to be solved in the present invention is overcome the deficiencies in the prior art, there is provided a kind of frost resistance is non-burning brick.
A kind of frost resistance of the present invention is non-burning brick, and the concrete is formed using the uniform mix of raw material of following match ratio：Water
Mud 5-10, lime 30-40, flyash 35-50, activator 0.1-0.2, straw 0.5-1, water 25-35.
Preferably, the cement is that silicon breaks salt cement as cementitious matter, with slag cements or pulverized fuel ash cement.
Activator is sodium sulphate.
The lime is carbide slag.
The flyash is wet ash and dry ash.
Containing 40% silica, 15 % alundum (Al2O3)s in the flyash, containing 15 % carbon amounts, 5 % content of magnesia
The present invention compared with prior art, has advantages below.
The mix-design of concrete of the present invention is reasonable, applied widely, can be applied to the basis of skyscraper, beam,
The cast-in-place concretes such as post, framework, bridge, and the overall pouring of T connector.The quality of monolithic architecture can be ensured, meet and build
Standard is built, improves concrete grade, reduces energy consumption, improves yield.
Embodiment
With reference to embodiment the present invention will be further explained explanation.
Embodiment 1
A kind of frost resistance is non-burning brick, and the concrete is formed using the uniform mix of raw material of following match ratio：Cement 5-10, lime
30-40, flyash 35-50, activator 0.1-0.2, straw 0.5-1, water 25-35.
The cement is that silicon breaks salt cement as cementitious matter, with slag cements or pulverized fuel ash cement.Activator is sodium sulphate.
The lime is carbide slag.The flyash is wet ash and dry ash.Contain 40% silica, the oxygen of 15 % tri- in the flyash
Change two aluminium, containing 15 % carbon amounts, 5 % content of magnesia
Embodiment 2
The concrete is formed using the uniform mix of raw material of following match ratio：Cement 5, lime 30, flyash 35, activator 0.1,
Straw 0.5, water 25.
Embodiment 3
The concrete is formed using the uniform mix of raw material of following match ratio：Cement 10, lime 40, flyash 50, activator
0.2, straw 1, water 35.
The above is example and explanation of the invention, but does not mean that the obtainable advantage of the present invention is so limited, all
It is wherein the one of may be to being realized in the simple transformation of structure, and/or some embodiments in practice process of the present invention the advantages of
It is individual or multiple in the protection domain of the application.
Claims (6)
1. a kind of frost resistance is non-burning brick, it is characterised in that：The concrete is formed using the uniform mix of raw material of following match ratio：Water
Mud 5-10, lime 30-40, flyash 35-50, activator 0.1-0.2, straw 0.5-1, water 25-35.
2. frost resistance according to claim 1 is non-burning brick, it is characterised in that：The cement is that silicon breaks salt cement as cementing
Material, with slag cements or pulverized fuel ash cement.
3. frost resistance according to claim 1 is non-burning brick, it is characterised in that：Activator is sodium sulphate.
4. frost resistance according to claim 1 is non-burning brick, it is characterised in that：The lime is carbide slag.
5. frost resistance according to claim 1 is non-burning brick, it is characterised in that：The flyash is wet ash and dry ash.
6. frost resistance according to claim 1 is non-burning brick, it is characterised in that：In the flyash containing 40% silica,
15 % alundum (Al2O3)s, containing 15 % carbon amounts, 5 % content of magnesia.