CN107779155A - A kind of nitrile rubber blanking cover adhesive Nian Jie with jet pipe and process - Google Patents

A kind of nitrile rubber blanking cover adhesive Nian Jie with jet pipe and process Download PDF

Info

Publication number
CN107779155A
CN107779155A CN201711136353.4A CN201711136353A CN107779155A CN 107779155 A CN107779155 A CN 107779155A CN 201711136353 A CN201711136353 A CN 201711136353A CN 107779155 A CN107779155 A CN 107779155A
Authority
CN
China
Prior art keywords
blanking cover
parts
jet pipe
adhesive
nitrile rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711136353.4A
Other languages
Chinese (zh)
Inventor
包乐
王纪霞
张海鹏
张新航
秦锋
周旭旭
张崇耿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xi'an Changfeng Electromechanical Research Institute
Original Assignee
Xi'an Changfeng Electromechanical Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xi'an Changfeng Electromechanical Research Institute filed Critical Xi'an Changfeng Electromechanical Research Institute
Priority to CN201711136353.4A priority Critical patent/CN107779155A/en
Publication of CN107779155A publication Critical patent/CN107779155A/en
Pending legal-status Critical Current

Abstract

The invention provides a kind of nitrile rubber blanking cover adhesive Nian Jie with jet pipe and process, adhesive includes following component in parts by weight:45~70 parts of epoxy E, 51,8~12 parts of toluene di-isocyanate(TDI)s, 1.5~5 parts of aerosils, 30~45 parts of polysulfide rubber of JLY 121,1~3 part of KH 550 and 6~8 part of 2 methylimidazole of ethyl 4.After cleaning Nozzle Lining and blanking cover gluing of surfaces using acetone and dry, using above-mentioned adhesive applicating blanking cover and inner lining surface, and pressing and stoving.The present invention can improve the reliability of product bonding.

Description

A kind of nitrile rubber blanking cover adhesive Nian Jie with jet pipe and process
Technical field
The present invention relates to a kind of solid propellant rocket nitrile rubber blanking cover adhesive bonding with jet pipe and technique.
Background technology
Blanking cover is the critical component of solid rocket motor nozzle, and sealed damp-proof effect is played in storage, during work, is held It is complete to open by certain pressure.Mainly it is molded between blanking cover and jet pipe using technique for sticking, the bonding quality of blanking cover is to starting The integrality of machine product structure plays an important role.Application of the nitrile rubber blanking cover in solid propellant rocket is less, often Adhesive and technology can not meet performance needs:It is required that the shearing of carbon fibre composite plate-laminated rubber-metal Adhesive strength satisfaction >=2.0MPa under test specimen high/low temperature condition, adhesive strength satisfaction >=3.0MPa under normal temperature condition, blanking cover are opened It is complete to test bonding plane.Nozzle Lining is carbon fibre composite, the rubber used in blanking cover for vulcanization after nitrile rubber, jet pipe Liner differs larger with the modulus and linear expansion coefficient of blanking cover material, and carbon fibre composite belongs to nitrile rubber after vulcanization The viscous material of hardly possible, and engine use condition harshness under+65 DEG C and -45 DEG C of environmental conditions, it is necessary to work, therefore adhesive needs There is good adhesive strength, and have preferable high and low temperature resistance.Common mainly rubber is Nian Jie with metal material, due to The influence of the factors such as the mobility of rubber, morphotropism, its bonding mechanism are more complicated.The rubber side generally used Nian Jie with metal Method has adhesive method, direct Method for bonding, vulcanie method.
Certain model adhesive is the adhesive that early stage metal blanking cover uses, and nitrile rubber blanking cover uses the adhesive with jet pipe After bonding, during product testing, it is found that its adhesive strength is poor, high and low temperature resistance is poor, has certain fragility, its is airtight Property pass the test rate it is low, and the adhesive has certain tack, is easy to be stuck after blanking cover fitting, can not position, Technical requirements can not be met.Therefore it is necessary to using the higher adhesive of adhesive strength.
During technique for sticking, glued material and adhesive and the aspect joint effect of bonding interface situation three bonding Intensity, it is therefore desirable to improve to bonding interface.Early stage metal blanking cover ensures adhesive strength using hard pressurization frock.Due to Rubber is the taper soft material that small end carries cambered surface, after being pressurizeed using hard metal material, easily causes blanking cover pressurizing attaching Property it is poor, blanking cover port can not be pressed onto position, and glue-line is uneven, intensity decreases, it is therefore necessary to process is improved, ensured viscous The stickiness connect.
The content of the invention
For overcome the deficiencies in the prior art, the present invention provides a kind of nitrile rubber blanking cover the adhesive Nian Jie with jet pipe, The reliability of product bonding can be improved.
The technical solution adopted for the present invention to solve the technical problems is:A kind of nitrile rubber blanking cover glue Nian Jie with jet pipe Stick, in parts by weight including following component:45~70 parts of epoxy E-51,8~12 parts of toluene di-isocyanate(TDI)s, 1.5~5 parts of gas Aerosil, 30~45 parts of JLY-121 polysulfide rubber, 1~3 part of KH-550 and 6~8 part of 2-ethyl-4-methylimidazole.
The present invention also provides a kind of technique for sticking of nitrile rubber blanking cover and jet pipe, comprises the following steps:
(1) using sand paper polishing Nozzle Lining and blanking cover surface;
(2) using acetone cleaning Nozzle Lining and blanking cover gluing of surfaces, 15min is then stood;
(3) Nozzle Lining and blanking cover are dried into 30~40min at 50 DEG C ± 2 DEG C;
(4) in parts by weight, 45~70 parts of epoxy E-51,8~12 parts of toluene di-isocyanate(TDI)s, 1.5~5 parts of gas phases are weighed Silica, 30~45 parts of JLY-121 polysulfide rubber, 1~3 part of KH-550 and 6~8 part of 2-ethyl-4-methylimidazole, stirring 3 ~5min, is made adhesive;
(5) blanking cover is placed in inner lining surface, bonding plane is rule;
(6) adhesive is respectively applied in blanking cover and inner lining surface, bondline thickness is 0.15~0.3mm;
(7) blanking cover and jet pipe are bonded, dries 110~150min after pressurization at 70 DEG C ± 2 DEG C.
Twice of adhesive is respectively applied in blanking cover and inner lining surface in described step (6), every to be not less than 0.07mm all over thickness.
Described step (7) is put 5~7Kg flexible materials after bonding blanking cover and jet pipe and pressurizeed.
The cold curing pressure of described step (7) is not less than 0.1MPa, and intermediate temperature setting pressure is 0.1~0.3MPa.
The beneficial effects of the invention are as follows:The blanking cover adhesive strength of preparation improves positive effect, specifically see the table below:
It is filled with nitrogen, pressurize 15 minutes, air-tight test qualification rate 100%.Blanking cover is opened checking test and see the table below
Sequence number Experiment quantity Test period As a result
1 5 + 60 DEG C of insulations, constant temperature 24 hours Blanking cover destroys, and bonding plane is complete
2 5 25 DEG C of insulations, constant temperature 24 hours Blanking cover destroys, and bonding plane is complete
3 5 - 45 DEG C of insulations, constant temperature 24 hours Blanking cover destroys, and bonding plane is complete
Embodiment
With reference to embodiment, the present invention is further described, and the present invention includes but are not limited to following embodiments.
Adhesive provided by the invention is mainly used in being bonded nitrile rubber and carbon fibre composite, in order to avoid solidification temperature Spending height causes ageing of rubber, and selected adhesive matrix formula must be a kind of adhesive for being capable of middle low-temperature setting, and And adhesive is in itself to possessing good compatibility between rubber and carbon fiber.Blanking cover small end is cambered surface, and adhesive is due to viscosity It is low, easily occur gummosis situation in the curing process, increase the toughness and temperature tolerance of adhesive by adding filler.Blanking cover Belong to soft material, therefore under conditions of ensureing to shear mechanical property, the toughness of adhesive plays vital to resin Effect, addition coupling agent make adhesive while toughness is improved, the shearing that there is higher modulus also to make adhesive after crosslinking Performance is improved.
The adhesive formulation of the present invention is as follows:
Sequence number Recipe ingredient title Recipe ingredient matches (weight) Remarks
1 Epoxy E-51 (618) 45-70 Matrix resin
2 Toluene di-isocyanate(TDI) 8-12 Crosslinking agent
3 Aerosil 1.5-5 Filler
4 JLY-121 polysulfide rubber 30-45 Toughener
5 KH-550 1-3 Coupling agent
6 2-ethyl-4-methylimidazole 6-8 Curing agent
Blanking cover and jet pipe gluing of surfaces, which carry out surface treatment, can obtain good surface-active, increase adhesive resin and base The affinity in body surface face.Surface treatment mainly decontaminates, the demoulding in nitrile rubber and carbon fibre composite forming process Greasy dirt in agent, mechanical processing process can have a strong impact on the intensity of bonding.To rubber and carbon fibre composite before bonding Processing is dried, adhesive property can be improved.With the progressive additive of glue-line, adhesive strength is gradually reduced adhesive shear strength, Glue-line thickeies, and glue layer defect has exponent relation increase, causes glue-line cohesion force intensity to decline, and glue-line is thicker by temperature change Caused by internal stress it is also bigger, also bigger in shrinkage stress caused by solidification, but bondline thickness hour, internal lack of fill Defect, internal stress increase, therefore bondline thickness control are between 0.15~0.3mm.The main control parameters of solidification are pressure, temperature Degree and time.Flexible material covers in blanking cover outer surface, sturdy closely sealed with material, and the size of unit pressure is by influenceing glue-line thickness Degree etc. factor and have influence on glue-joint strength.General cold curing pressure is not less than 0.1MPa, intermediate temperature setting pressure 0.1~ Between 0.3MPa.Solidification temperature uses and is heating and curing and in higher temperature-curable cross-linking reaction can be made more abundant.
The present invention technique for sticking flow be:
(1) Nozzle Lining and blanking cover surface are polished using sand paper;
(2) using acetone cleaning gluing of surfaces, 15min is stood;
(3) Nozzle Lining and blanking cover are put into baking oven, 50 DEG C ± 2 DEG C of drying temperature, 30~40min of time;
(4) often hair product weighs 50g~80g, weighs adhesive components in proportion, is put into jar, stirs evenly 3~5min;
(5) blanking cover is placed in inner lining surface, bonding plane is rule;
(6) gluing is carried out in blanking cover and inner lining surface, respectively smeared twice, it is every to be not less than 0.07mm all over thickness;
(7) blanking cover and jet pipe are bonded, puts 5Kg-7Kg flexible materials pressurization frock;
(8) baking oven, 70 DEG C ± 2 DEG C of oven temperature, 110~150min of time are put into.
Example 1
(1) recipe ingredient is weighed
Recipe ingredient is weighed according to following table.
Sequence number Recipe ingredient title Recipe ingredient matches (weight) Remarks
1 Epoxy E-51 (618) 45 Matrix resin
2 Toluene di-isocyanate(TDI) 8 Crosslinking agent
3 Aerosil 1.5 Filler
4 JLY-121 polysulfide rubber 30 Toughener
5 KH-550 1 Coupling agent
6 2-ethyl-4-methylimidazole 6 Curing agent
(2) blanking cover is bonded
(a) Nozzle Lining and blanking cover surface are polished using sand paper;
(b) acetone cleaning gluing of surfaces, stands 15min;
(c) Nozzle Lining and blanking cover are put into baking oven, 50 DEG C ± 2 DEG C of drying temperature, time 30min;
(d) often hair product weighs 50g, weighs adhesive components in proportion, is put into jar, stirs evenly 3min;
(e) blanking cover is placed in inner lining surface, bonding plane is rule;
(f) gluing is carried out in blanking cover and inner lining surface, respectively smeared twice, it is every to be not less than 0.07mm all over thickness;
(g) blanking cover and jet pipe are bonded, puts 5Kg flexible materials pressurization frock;
(h) baking oven, 70 DEG C ± 2 DEG C of oven temperature, time 110min are put into;;
(3) blanking cover opens experiment
Blanking cover after bonding carries out+60 DEG C of insulations after being assemblied in combustion chamber, constant temperature 24 hours, unsticking does not occur after experiment and shows As it is 1.6MPa that blanking cover, which opens intensity, and blanking cover crushes in itself.
Example 2
(1) recipe ingredient is weighed
Recipe ingredient is weighed according to following table.
Sequence number Recipe ingredient title Recipe ingredient matches (weight) Remarks
1 Epoxy E-51 (618) 70 Matrix resin
2 Toluene di-isocyanate(TDI) 12 Crosslinking agent
3 Aerosil 5 Filler
4 JLY-121 polysulfide rubber 45 Toughener
5 KH-550 3 Coupling agent
6 2-ethyl-4-methylimidazole 8 Curing agent
(2) blanking cover is bonded
(a) Nozzle Lining and blanking cover surface are polished using sand paper;
(b) acetone cleaning gluing of surfaces, stands 15min;
(c) Nozzle Lining and blanking cover are put into baking oven, 50 DEG C ± 2 DEG C of drying temperature, time 40min;
(d) often hair product weighs 80g, weighs adhesive components in proportion, is put into jar, stirs evenly 5min;
(e) blanking cover is placed in inner lining surface, bonding plane is rule;
(f) gluing is carried out in blanking cover and inner lining surface, respectively smeared twice, it is every to be not less than 0.07mm all over thickness;
(g) blanking cover and jet pipe are bonded, puts 7Kg flexible materials pressurization frock;
(h) baking oven, 70 DEG C ± 2 DEG C of oven temperature, time 150min are put into;;
(3) blanking cover opens experiment
Blanking cover after bonding carries out -45 DEG C of insulations after being assemblied in combustion chamber, constant temperature 24 hours, unsticking does not occur after experiment and shows As it is 1.8MPa that blanking cover, which opens intensity, and blanking cover crushes in itself.
Example 3
(1) recipe ingredient is weighed
Recipe ingredient is weighed according to following table.
Sequence number Recipe ingredient title Recipe ingredient matches (weight) Remarks
1 Epoxy E-51 (618) 55 Matrix resin
2 Toluene di-isocyanate(TDI) 10 Crosslinking agent
3 Aerosil 3 Filler
4 JLY-121 polysulfide rubber 40 Toughener
5 KH-550 2 Coupling agent
6 2-ethyl-4-methylimidazole 7 Curing agent
(2) blanking cover is bonded
(a) Nozzle Lining and blanking cover surface are polished using sand paper;
(b) acetone cleaning gluing of surfaces, stands 15min;
(c) Nozzle Lining and blanking cover are put into baking oven, 50 DEG C ± 2 DEG C of drying temperature, time 35min;
(d) often hair product weighs 70g, weighs adhesive components in proportion, is put into jar, stirs evenly 4min;
(e) blanking cover is placed in inner lining surface, bonding plane is rule;
(f) gluing is carried out in blanking cover and inner lining surface, respectively smeared twice, it is every to be not less than 0.07mm all over thickness;
(g) blanking cover and jet pipe are bonded, puts 6Kg flexible materials pressurization frock;
(h) baking oven, 70 DEG C ± 2 DEG C of oven temperature, time 120min are put into;;
(3) blanking cover opens experiment
Blanking cover after bonding carries out 25 DEG C of insulations after being assemblied in combustion chamber, constant temperature 24 hours, unsticking does not occur after experiment and shows As it is 1.5MPa that blanking cover, which opens intensity, and blanking cover crushes in itself.

Claims (5)

1. a kind of nitrile rubber blanking cover adhesive Nian Jie with jet pipe, it is characterised in that in parts by weight including following component:45 ~70 parts of epoxy E-51,8~12 parts of toluene di-isocyanate(TDI)s, 1.5~5 parts of aerosils, 30~45 parts of JLY-121 polysulfides Rubber, 1~3 part of KH-550 and 6~8 part of 2-ethyl-4-methylimidazole.
2. a kind of process Nian Jie with jet pipe using the nitrile rubber blanking cover of adhesive described in claim 1, its feature exist In comprising the steps:
(1) using sand paper polishing Nozzle Lining and blanking cover surface;
(2) using acetone cleaning Nozzle Lining and blanking cover gluing of surfaces, 15min is then stood;
(3) Nozzle Lining and blanking cover are dried into 30~40min at 50 DEG C ± 2 DEG C;
(4) in parts by weight, 45~70 parts of epoxy E-51,8~12 parts of toluene di-isocyanate(TDI)s, 1.5~5 parts of gas phase dioxies are weighed SiClx, 30~45 parts of JLY-121 polysulfide rubber, 1~3 part of KH-550 and 6~8 part of 2-ethyl-4-methylimidazole, stirring 3~ 5min, adhesive is made;
(5) blanking cover is placed in inner lining surface, bonding plane is rule;
(6) adhesive is respectively applied in blanking cover and inner lining surface, bondline thickness is 0.15~0.3mm;
(7) blanking cover and jet pipe are bonded, dries 110~150min after pressurization at 70 DEG C ± 2 DEG C.
3. the nitrile rubber blanking cover according to claim 2 process Nian Jie with jet pipe, it is characterised in that:Described step Suddenly twice of adhesive is respectively applied in blanking cover and inner lining surface in (6), every to be not less than 0.07mm all over thickness.
4. the nitrile rubber blanking cover according to claim 2 process Nian Jie with jet pipe, it is characterised in that:Described step Suddenly (7) are put 5~7Kg flexible materials after bonding blanking cover and jet pipe and pressurizeed.
5. the nitrile rubber blanking cover according to claim 2 process Nian Jie with jet pipe, it is characterised in that:Described step Suddenly the cold curing pressure of (7) is not less than 0.1MPa, and intermediate temperature setting pressure is 0.1~0.3MPa.
CN201711136353.4A 2017-11-16 2017-11-16 A kind of nitrile rubber blanking cover adhesive Nian Jie with jet pipe and process Pending CN107779155A (en)