CN107774881A - Easy gas permeability precoated sand - Google Patents
Easy gas permeability precoated sand Download PDFInfo
- Publication number
- CN107774881A CN107774881A CN201610744539.7A CN201610744539A CN107774881A CN 107774881 A CN107774881 A CN 107774881A CN 201610744539 A CN201610744539 A CN 201610744539A CN 107774881 A CN107774881 A CN 107774881A
- Authority
- CN
- China
- Prior art keywords
- sand
- precoated sand
- gas permeability
- mixed grind
- precoated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of easily gas permeability precoated sand, key step includes that mulling, heating, mixed grind, cooling, charging, mixed grind be broken, screening obtains precoated sand.Resistance to water soak of the present invention is preferably, roughness is smaller, is not easy in casting scab.
Description
Technical field
The invention belongs to casting technology field, and in particular to a kind of easily gas permeability precoated sand.
Background technology
Precoated sand refers to the molding sand or core sand for being covered with one layer of hard resin film before moulding on sand grain surface.Have cold process and
Heat two kinds of coating techniques of hair:Cold process is dissolved resin with ethanol, and methenamine is added during mulling, makes the two bag
Sand grain surface is overlayed on, ethanol volatilization, obtains precoated sand;Sand is preheating to certain temperature by hot method, adds resin to make its melting, and stirring makes tree
Fat is coated on sand grain surface, adds the methenamine aqueous solution and lubricant, cools down, crushes, sieving and to obtain precoated sand.For steel-casting,
Ironcasting.Because precoated sand has, intensity is high, gas forming amount is low, production casting dimension accuracy height, any surface finish, is easy to preservation etc. excellent
Point, in recent years using increasingly extensive.Precoated sand of the prior art there is heat resistance is poor, roughness is larger, easily in casting
The defects of upper scab and problem.
The content of the invention
In order to overcome above-mentioned technical problem existing for prior art, it is an object of the present invention to provide a kind of easily saturating
Gas precoated sand, resistance to water soak is preferably, roughness is smaller, is not easy the scab on casting.
Easily gas permeability precoated sand provided by the invention, comprises the following steps:
(1)100 parts of roughing sand are put into blade mixer, are heated to 170-280 DEG C;
(2)13-17 part phenolic resin mixed grind times 47-58S is put into roughing sand;
(3)When roughing sand temperature is reduced to 110-120 DEG C, 5-8 part curing agent, mixed grind 10S are added;
(4)Add 6-9 parts lubricant and 15-19 part additive mixed grinds 46-55S;
(5)When roughing sand is down to below 80 DEG C, broken, screening obtains precoated sand.
Easily gas permeability precoated sand, its advantage provided by the invention are that this precoated sand is removed with Conventional coverlay film sand
Outside performance, also have and delay raising rate 4-5S, performance caused by suppression nitrogen, can effectively reduce casting and produce nitrogen pore, greatly
The big yield rate for improving austenitic iron casting.
Embodiment
With reference to one embodiment, easily gas permeability precoated sand provided by the invention is described in detail.
Embodiment
The easy gas permeability precoated sand of the present embodiment, comprises the following steps:
(1)100 parts of roughing sand are put into blade mixer, are heated to 190 DEG C;
(2)17 parts of phenolic resin mixed grind time 58S are put into roughing sand;
(3)When roughing sand temperature is reduced to 110 DEG C, 8 parts of curing agent, mixed grind 10S are added;
(4)Add 9 parts of lubricants and 15 parts of additive mixed grind 55S;
(5)When roughing sand is down to 78 DEG C, broken, screening obtains precoated sand.
Claims (1)
- A kind of 1. easily gas permeability precoated sand, it is characterised in that:Comprise the following steps:(1)100 parts of roughing sand are put into blade mixer, are heated to 170-280 DEG C;(2)13-17 part phenolic resin mixed grind times 47-58S is put into roughing sand;(3)When roughing sand temperature is reduced to 110-120 DEG C, 5-8 part curing agent, mixed grind 10S are added;(4)Add 6-9 parts lubricant and 15-19 part additive mixed grinds 46-55S;(5)When roughing sand is down to below 80 DEG C, broken, screening obtains precoated sand.