CN107760150A - A kind of anti-aging coating - Google Patents

A kind of anti-aging coating Download PDF

Info

Publication number
CN107760150A
CN107760150A CN201710903998.XA CN201710903998A CN107760150A CN 107760150 A CN107760150 A CN 107760150A CN 201710903998 A CN201710903998 A CN 201710903998A CN 107760150 A CN107760150 A CN 107760150A
Authority
CN
China
Prior art keywords
parts
aging
coating
aging coating
kaolin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201710903998.XA
Other languages
Chinese (zh)
Inventor
吴江
陈秀兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhenjiang Ze Lin Lin Building Materials Co Ltd
Original Assignee
Zhenjiang Ze Lin Lin Building Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhenjiang Ze Lin Lin Building Materials Co Ltd filed Critical Zhenjiang Ze Lin Lin Building Materials Co Ltd
Priority to CN201710903998.XA priority Critical patent/CN107760150A/en
Publication of CN107760150A publication Critical patent/CN107760150A/en
Withdrawn legal-status Critical Current

Abstract

A kind of anti-aging coating of the present invention, it is characterised in that constituent is counted as follows in parts by weight：45 85 parts of epoxy resin；35 68 parts of polystyrene；25 45 parts of titanium dioxide；15 35 parts of polyester fiber；18 28 parts of propane diols；5 28 parts of kaolin.The present invention uses unique formula, uses ultrafine kaolin as additive, and the anti-aging coating of gained has anti-aging a, high temperature resistant, the characteristic such as corrosion-resistant.

Description

A kind of anti-aging coating
Technical field
The present invention relates to a kind of coating, more particularly to a kind of anti-aging coating.
Background technology
With the rapid development built with modern society, requirement more and more higher of the people for construction material, coating is made For one kind of modern architecture material, it researches and develops the concern that people are constantly subjected to improving, and the ageing resistace of coating is always Its important one side, the coating of ageing resistace difference can produce discoloration, decortication etc. now by sternly during long-term use Service life is have impact on again, although existing coating is provided with certain guarantee at anti-aging aspect, but in special applications condition Ageing resistace under lower such as high temperature or super-humid conditions is poor.
The content of the invention
The present invention proposes a kind of anti-aging coating regarding to the issue above.
Specific technical scheme is as follows：
A kind of anti-aging coating, it is characterised in that constituent is counted as follows in parts by weight：
Epoxy resin 45-85 parts
Polystyrene 35-68 parts
Titanium dioxide 25-45 parts
Polyester fiber 15-35 parts
Propane diols 18-28 parts
Kaolin 5-28 parts.
Above-mentioned a kind of anti-aging coating, it is characterised in that the kaolin is nano-scale particle.
Above-mentioned a kind of anti-aging coating, it is characterised in that the kaolinic particle diameter is 50-100 nanometers.
Beneficial effects of the present invention are：
The present invention uses unique formula, uses ultrafine kaolin as additive, the anti-aging coating of gained has anti-aging, resistance to height Temperature, the characteristic such as corrosion-resistant.
Embodiment
To make technical scheme become apparent from clearly, below the present invention is described further, it is any to this The scheme that the technical characteristic progress equivalencing of inventive technique scheme and conventional reasoning are drawn each falls within the scope of the present invention.
Embodiment 1
A kind of anti-aging coating, it is characterised in that constituent is counted as follows in parts by weight：
45 parts of epoxy resin
35 parts of polystyrene
25 parts of titanium dioxide
15 parts of polyester fiber
18 parts of propane diols
5 parts of kaolin.
The kaolinic particle diameter is 50 nanometers.
Embodiment 2
A kind of anti-aging coating, it is characterised in that constituent is counted as follows in parts by weight：
85 parts of epoxy resin
68 parts of polystyrene
45 parts of titanium dioxide
35 parts of polyester fiber
28 parts of propane diols
28 parts of kaolin.
The kaolinic particle diameter is 100 nanometers.
Embodiment 3
A kind of anti-aging coating, it is characterised in that constituent is counted as follows in parts by weight：
55 parts of epoxy resin
55 parts of polystyrene
34 parts of titanium dioxide
22 parts of polyester fiber
21 parts of propane diols
13 parts of kaolin.
The kaolinic particle diameter is 66 nanometers.
Beneficial effects of the present invention are：
The present invention uses unique formula, uses ultrafine kaolin as additive, the anti-aging coating of gained has anti-aging, resistance to height Temperature, the characteristic such as corrosion-resistant.

Claims (3)

1. a kind of anti-aging coating, it is characterised in that constituent is counted as follows in parts by weight：
Epoxy resin 45-85 parts
Polystyrene 35-68 parts
Titanium dioxide 25-45 parts
Polyester fiber 15-35 parts
Propane diols 18-28 parts
Kaolin 5-28 parts.
2. a kind of anti-aging coating as claimed in claim 1, it is characterised in that the kaolin is nano-scale particle.
3. a kind of anti-aging coating as claimed in claim 1, it is characterised in that the kaolinic particle diameter is received for 50-100 Rice.
CN201710903998.XA 2017-09-29 2017-09-29 A kind of anti-aging coating Withdrawn CN107760150A (en)