CN107760125A - Wear-resisting timber priming paint - Google Patents
Wear-resisting timber priming paint Download PDFInfo
- Publication number
- CN107760125A CN107760125A CN201710981806.7A CN201710981806A CN107760125A CN 107760125 A CN107760125 A CN 107760125A CN 201710981806 A CN201710981806 A CN 201710981806A CN 107760125 A CN107760125 A CN 107760125A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- priming paint
- acrylic resin
- resisting timber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear-resisting timber priming paint, the raw material of following parts by weight is included：35 45 parts of acrylic resin, 10 15 parts of soya-bean oil lecithin acid, 8 10 parts of titanium dioxide, 8 10 parts of carbon fiber, 6 10 parts of lemon blue, 25 parts of barium white powder, 10 15 parts of polyamide wax, 24 parts of solvent.It has the characteristics of anti-wear performance is high, while its performance such as surface gloss and transparency of constructing is improved.
Description
Technical field
The invention belongs to wood processing technique field, and in particular to a kind of wear-resisting timber priming paint.
Background technology
Priming paint, refer to be directly applied to coating of the body surface as finish paint solid foundation.It is required that the adhesion-tight on object plane,
To increase the adhesive force of upper coating, the dicoration of finish paint is improved.Priming coat, base coat can be divided into according to coating specification
Deng.
The woodenware such as wooden furniture, timber floor, wooden sofa are needed in its surface lacquer, spray painting mostly, first have to primer spray.It is existing
The problem of some priming paint generally existing anti-wear performance differences, after woodenware is rubbed or is cleaned multiple times in use, easily ground
Wear, expose base material, leverage the attractive in appearance of these woodenware.
The content of the invention
The purpose of the present invention is to propose to a kind of wear-resisting timber priming paint, and it has the characteristics of anti-wear performance is high, while it is constructed
The performance such as surface gloss and transparency is improved.
In order to reach above-mentioned purpose of design, under the technical solution adopted by the present invention：
A kind of wear-resisting timber priming paint, include the raw material of following parts by weight：Acrylic resin 35-45 parts, soya-bean oil lecithin acid
10-15 parts, titanium dioxide 8-10 parts, carbon fiber 8-10 parts, lemon blue 6-10 parts, barium white powder 2-5 parts, polyamide wax 10-15 parts,
Solvent 2-4 parts.
Preferably, above-mentioned wear-resisting timber priming paint, the raw material of following parts by weight is included：40 parts of acrylic resin, soya-bean oil ovum
2.5 parts of phosphatase 11,9 parts of titanium dioxide, 9 parts of carbon fiber, 8 parts of lemon blue, 3 parts of barium white powder, 12.5 parts of polyamide wax, 3 parts of solvent.
The glass transition temperature of the acrylic resin is 45 DEG C~60 DEG C；
The acrylic resin is self-drying acrylic resin.
The solvent is ester type compound.
The beneficial effect of wear-resisting timber priming paint of the present invention is：It has the characteristics of anti-wear performance is high, while it is applied
The performance such as work surface gloss and transparency is improved.
Embodiment
Preferred embodiment of the invention is described in further detail below.
Embodiment 1：
The wear-resisting timber priming paint, include the raw material of following parts by weight：35 parts of acrylic resin, soya-bean oil lecithin acid 15
Part, 8 parts of titanium dioxide, 10 parts of carbon fiber, 6 parts of lemon blue, 5 parts of barium white powder, 10 parts of polyamide wax, 4 parts of solvent.
Embodiment 2：
The wear-resisting timber priming paint, include the raw material of following parts by weight：45 parts of acrylic resin, soya-bean oil lecithin acid 10
Part, 10 parts of titanium dioxide, 8 parts of carbon fiber, 10 parts of lemon blue, 2 parts of barium white powder, 15 parts of polyamide wax, 2 parts of solvent.
Embodiment 3：
The wear-resisting timber priming paint, include the raw material of following parts by weight：40 parts of acrylic resin, soya-bean oil lecithin acid 12.5
Part, 9 parts of titanium dioxide, 9 parts of carbon fiber, 8 parts of lemon blue, 3 parts of barium white powder, 12.5 parts of polyamide wax, 3 parts of solvent.
Preferably technical scheme is in specific implementation, in above-described embodiment 1-3, the glass transition temperature of the acrylic resin
For 45 DEG C~60 DEG C；
Preferably technical scheme is in specific implementation, and in above-described embodiment 1-3, the acrylic resin is self-drying type propylene
Acid resin.
Preferably technical scheme is in specific implementation, and in above-described embodiment 1-3, the solvent is ester type compound
Above content is to combine the further description that specific preferred embodiment is done to the present invention, is easy to the skill
The technical staff in art field is understood that and using the present invention, it is impossible to assert that the specific implementation of the present invention is confined to these explanations.
For general technical staff of the technical field of the invention, it can also make without departing from the inventive concept of the premise
Some simple deduction or replace, without by performing creative labour.Therefore, those skilled in the art's taking off according to the present invention
Show, the simple modifications made to the present invention all should be within protection scope of the present invention.
Claims (5)
- A kind of 1. wear-resisting timber priming paint, it is characterised in that：Include the raw material of following parts by weight：Acrylic resin 35-45 parts, beans Oily lecithin acid 10-15 parts, titanium dioxide 8-10 parts, carbon fiber 8-10 parts, lemon blue 6-10 parts, barium white powder 2-5 parts, polyamide wax 10-15 parts, solvent 2-4 parts.
- 2. wear-resisting timber priming paint according to claim 1, it is characterised in that：Include the raw material of following parts by weight：Propylene 40 parts of acid resin, 12.5 parts of soya-bean oil lecithin acid, 9 parts of titanium dioxide, 9 parts of carbon fiber, 8 parts of lemon blue, 3 parts of barium white powder, polyamide 12.5 parts of wax, 3 parts of solvent.
- 3. wear-resisting timber priming paint according to claim 2, it is characterised in that：The glass transition temperature of the acrylic resin is 45 DEG C~60 DEG C.
- 4. wear-resisting timber priming paint according to claim 2, it is characterised in that：The acrylic resin is self-drying acrylic Resin.
- 5. wear-resisting timber priming paint according to claim 2, it is characterised in that：The solvent is ester type compound.