CN107757062A - The preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge - Google Patents
The preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge Download PDFInfo
- Publication number
- CN107757062A CN107757062A CN201710997449.3A CN201710997449A CN107757062A CN 107757062 A CN107757062 A CN 107757062A CN 201710997449 A CN201710997449 A CN 201710997449A CN 107757062 A CN107757062 A CN 107757062A
- Authority
- CN
- China
- Prior art keywords
- fluororesin
- cloth
- sponge
- agent
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge, comprise the following steps that:Prepare fluoro-resin emulsion dipping agent, tieed up using glass pricker, by twisting Split Down plain weave into grid Woven glass cloth cloth, fabric cloth is sent to the dipping tank equipped with fluoro-resin emulsion dipping agent by roller, pass through scraping off residual emulsion, sintered into hot-fluid oven for drying, form fluororesin coated glass fiber fabric cloth;Fabric cloth is sent to the dipping tank of surface conditioning agent by roller, ensure that it is just drying at room temperature after dipping to transmit cloth with drum shaft pressure, then be transferred to next rinse bath and embathe residual surface inorganic agent, room temperature or baking oven air-dry, and form one side absorbent-type fluororesin glass fabric cloth.Present invention introduces sponge surface adhesion type fluororesin Garment Steamer Machine curtain pad to have a comfortable feel, and surface elastic constant strengthens, while has insulation, it is shockproof the features such as, greatly reduce damage of the high temperature apparatus for textile material.
Description
Technical field
The present invention relates to a kind of Garment Steamer Machine curtain pad, the specifically compound fluororesin-type glass fibre Garment Steamer Machine curtain of sponge
The preparation method of pad.
Background technology
Fluororesin high temperature cord fabric has high temperature resistant, and chemically stable, coefficient of friction is low, surface non-stick, nontoxic pollution-free
The advantages that, but hardness is high, and heat insulating ability is poor, it is coarse to feel the deficiencies of, because the specific chemical stability of fluororesin is strong, surface is not
It is viscous, therefore the adhesion of the foam sponge material such as polyurethanes is poor.
The content of the invention
It is an object of the invention to provide a kind of compound fluororesin-type glass fibre Garment Steamer Machine curtain of sponge of heat-insulating shockproof
The preparation method of pad, to solve the problems mentioned in the above background technology.
To achieve the above object, the present invention provides following technical scheme:
A kind of preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge, is comprised the following steps that:
(1)Prepare fluoro-resin emulsion dipping agent, the fluoro-resin emulsion dipping agent according to weight than raw material include:Fluororesin
40-60%, surfactant 3-5%, pigment agent 0.5-5%, alkaline regulator 0.5-3.5%, remaining be deionized water;Take fluorine tree
Fat, surfactant, pigment agent, alkaline regulator and water are mixed evenly with 70-100r/min rotating speed, and stirring is to without heavy
Form sediment;
(2)Tieed up, twisted with the fingers by twisting Split Down plain weave into grid Woven glass cloth cloth, twisting count for 150-250, fabric cloth leads to using glass pricker
Cross roller and be sent to the dipping tank equipped with fluoro-resin emulsion dipping agent, by scraping off residual emulsion, burnt into hot-fluid oven for drying
Knot, sintering temperature are 370-390 DEG C, rotating speed 0.5-4m/min, repeat 2-4 times, form fluororesin coated glass fiber fabric
Cloth;
(3)Fabric cloth is sent to the dipping tank of surface conditioning agent by roller, the upper liquid level of holding surface inorganic agent is positioned at leaching
At the perpendicular diameter height 1/3-1/5 of stain roller, and ensure that it is just drying at room temperature after dipping to transmit cloth with drum shaft pressure, then
The rinse bath for being transferred to next 60-70 DEG C of hot water embathes residual surface inorganic agent, and room temperature or baking oven air-dry, and forms one side absorption
Type fluororesin glass fabric cloth;
(4)Commercially available high temperature resistant sponge room temperature is sent to the fitting machine cylinder covered with waterproof solidification glue, after coating glue-line, with
The fluororesin glass fabric cloth of one side processing, carry out high temperature and be bonded to obtain the compound fluororesin-type glass fibre extension of coiled sponge
Machine curtain lining cloth is scalded, the temperature of fitting is 180 DEG C;
(5)By the compound fluororesin-type glass fibre Garment Steamer Machine curtain lining cloth of the coiled sponge prepared, arbitrary shape is cut into, is cut out
Cut place and carry out edge sealing, punching two ends with temperature pressure sensitive band, hole is affiliated in formation.
As the further scheme of the present invention:The fluororesin is ptfe emulsion, polytetrafluoroethylene (PTFE), Teflon system
Any one of row, poly- fluorine vinyl chloride, the pigment agent is any one of aluminium silver powder, copper powder, carbon black, organic dyestuff, described
Surfactant is commercial surfactant, and alkaline conditioner is the weak base such as ammoniacal liquor, triethylamine.
As the further scheme of the present invention:The fluororesin is ptfe emulsion.
As the further scheme of the present invention:The alkaline conditioner is ammoniacal liquor.
As the further scheme of the present invention:The glass fibre ties up one-ply yarn, Kai Fu for the glass pricker of E- type 5-9 microns
To tow one kind of dimension, Carbon fibe or ceramic fibre, the sizing grid of the grid Woven glass cloth cloth is 0.5 × 0.5mm, 1 ×
1mm、2×2mm、3×3mm、5×5mm。
As the further scheme of the present invention:The glass fibre ties up one-ply yarn for the glass pricker of E- type 5-9 microns.
As the further scheme of the present invention:The surface conditioning agent according to weight than raw material include:Metallic sodium 1-
10%th, smart sodium 1-10%, remaining be tetrahydrofuran.
As the further scheme of the present invention:The preparation method of the surface conditioning agent, be by metallic sodium by batch slowly plus
Enter in the tetrahydrofuran solution at the uniform velocity stirred, after abundant dissolving, add smart sodium, after solid gradually dissolving, be cooled to room temperature
It is standby.
As the further scheme of the present invention:It is 95 that the waterproof solidification glue, which includes ratio,:5 marine glue and curing agent,
The marine glue is commercially available PS glue, PA glue, PC glue, PE glue, PP glue, rubber cement, polyurethane glue it is any
One kind, curing agent are commercially available curing agent.
As further scheme of the invention:The sponge is polyurethanes foam sponge, polyethers, polyvinyl alcohol
Any one.
Compared with prior art, the beneficial effects of the invention are as follows:
Present invention introduces sponge surface adhesion type fluororesin Garment Steamer Machine curtain pad to have comfortable feel, and surface elastic constant increases
By force, while there is the features such as insulation, shockproof, greatly reduces damage of the high temperature apparatus for textile material.
Embodiment
The technical scheme of this patent is described in more detail with reference to embodiment.
Embodiment 1
A kind of preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge, is comprised the following steps that:
(1)Prepare fluoro-resin emulsion dipping agent, the fluoro-resin emulsion dipping agent according to weight than raw material include:Fluororesin
60%th, surfactant 3%, pigment agent 0.5%, alkaline regulator 0.5%, remaining be deionized water;Take fluororesin, surface-active
Agent, pigment agent, alkaline regulator and water are mixed evenly with 70r/min rotating speed, and stirring is to without precipitation;
(2)Using E- type 5-9 microns glass pricker tie up one-ply yarn, through twisting Split Down plain weave into sizing grid be 0.5 × 0.5mm
Grid Woven glass cloth cloth, twisting count are 150 sth. made by twisting, and fabric cloth is sent to the dipping tank equipped with fluoro-resin emulsion dipping agent by roller,
By scraping off residual emulsion, being sintered into hot-fluid oven for drying, sintering temperature is 370 DEG C, rotating speed 0.5m/min, is repeated 2 times,
Form fluororesin coated glass fiber fabric cloth;
(3)Fabric cloth is sent to the dipping tank of surface conditioning agent by roller, the upper liquid level of holding surface inorganic agent is positioned at leaching
At the perpendicular diameter height 1/3/5 of stain roller, and ensure that it is just drying at room temperature after dipping to transmit cloth with drum shaft pressure, then turn
The rinse bath for entering next 60 DEG C of hot water embathes residual surface inorganic agent, and room temperature or baking oven air-dry, and forms one side absorbent-type fluorine
Plexiglas fibre fabric;The surface conditioning agent according to weight than raw material include:Metallic sodium 1%, smart sodium 1%, remaining be
Tetrahydrofuran, the preparation method of the surface conditioning agent, it is that metallic sodium is molten by batch tetrahydrofuran for being slowly added at the uniform velocity stir
In liquid, after abundant dissolving, smart sodium is added, after solid gradually dissolving, it is standby to be cooled to room temperature;
(4)Commercially available high temperature resistant sponge room temperature is sent to the fitting machine cylinder covered with waterproof solidification glue, after coating glue-line, with
The fluororesin glass fabric cloth of one side processing, carry out high temperature and be bonded to obtain the compound fluororesin-type glass fibre extension of coiled sponge
Machine curtain lining cloth is scalded, the temperature of fitting is 180 DEG C;
(5)By the compound fluororesin-type glass fibre Garment Steamer Machine curtain lining cloth of the coiled sponge prepared, arbitrary shape is cut into, is cut out
Cut place and carry out edge sealing, punching two ends with temperature pressure sensitive band, hole is affiliated in formation.
Embodiment 2
A kind of preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge, is comprised the following steps that:
(1)Prepare fluoro-resin emulsion dipping agent, the fluoro-resin emulsion dipping agent according to weight than raw material include:Fluororesin
50%th, surfactant 4%, pigment agent 3%, alkaline regulator 2%, remaining be deionized water;Take fluororesin, surfactant, face
Material agent, alkaline regulator and water are mixed evenly with 85r/min rotating speed, and stirring is to without precipitation;
(2)Using triumphant dimension of not towing, by twisting Split Down plain weave into the grid Woven glass cloth cloth that sizing grid is 1 × 1mm, twisting count
Twisted with the fingers for 200, fabric cloth is sent to the dipping tank equipped with fluoro-resin emulsion dipping agent by roller, by scraping off residual emulsion, entered
Enter hot-fluid oven for drying sintering, sintering temperature is 380 DEG C, rotating speed 2m/min, is repeated 3 times, and it is fine to form fluororesin coating glass
Dimensional fabric cloth;
(3)Fabric cloth is sent to the dipping tank of surface conditioning agent by roller, the upper liquid level of holding surface inorganic agent is positioned at leaching
At the perpendicular diameter height 1/4 of stain roller, and ensure that it is just drying at room temperature after dipping to transmit cloth with drum shaft pressure, then be transferred to
The rinse bath of next 65 DEG C of hot water embathes residual surface inorganic agent, and room temperature or baking oven air-dry, and forms one side absorbent-type fluorine tree
Fat glass fabric cloth;The surface conditioning agent according to weight than raw material include:Metallic sodium 5%, smart sodium 5%, remaining be four
Hydrogen furans, the preparation method of the surface conditioning agent, it is by the tetrahydrofuran solution for batch being slowly added at the uniform velocity to stir by metallic sodium
In, after abundant dissolving, smart sodium is added, after solid gradually dissolving, it is standby to be cooled to room temperature;
(4)Commercially available high temperature resistant sponge room temperature is sent to the fitting machine cylinder covered with waterproof solidification glue, after coating glue-line, with
The fluororesin glass fabric cloth of one side processing, carry out high temperature and be bonded to obtain the compound fluororesin-type glass fibre extension of coiled sponge
Machine curtain lining cloth is scalded, the temperature of fitting is 180 DEG C;
(5)By the compound fluororesin-type glass fibre Garment Steamer Machine curtain lining cloth of the coiled sponge prepared, arbitrary shape is cut into, is cut out
Cut place and carry out edge sealing, punching two ends with temperature pressure sensitive band, hole is affiliated in formation.
Embodiment 3
A kind of preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge, is comprised the following steps that:
(1)Prepare fluoro-resin emulsion dipping agent, the fluoro-resin emulsion dipping agent according to weight than raw material include:Fluororesin
40%th, surfactant 5%, pigment agent 5%, alkaline regulator 3.5%, remaining be deionized water;Take fluororesin, surfactant,
Pigment agent, alkaline regulator and water are mixed evenly with 100r/min rotating speed, and stirring is to without precipitation;
(2)Using Carbon fibe, it is into the grid Woven glass cloth cloth that sizing grid is 2 × 2mm, twisting count by twisting Split Down plain weave
250 twist with the fingers, and fabric cloth is sent to the dipping tank equipped with fluoro-resin emulsion dipping agent by roller, by scraping off residual emulsion, enter
Hot-fluid oven for drying sinters, and sintering temperature is 390 DEG C, rotating speed 4m/min, is repeated 4 times, and forms fluororesin coated glass fiber
Fabric cloth;
(3)Fabric cloth is sent to the dipping tank of surface conditioning agent by roller, the upper liquid level of holding surface inorganic agent is positioned at leaching
At the perpendicular diameter height 1/1/5 of stain roller, and ensure that it is just drying at room temperature after dipping to transmit cloth with drum shaft pressure, then turn
The rinse bath for entering next 70 DEG C of hot water embathes residual surface inorganic agent, and room temperature or baking oven air-dry, and forms one side absorbent-type fluorine
Plexiglas fibre fabric;The surface conditioning agent according to weight than raw material include:Metallic sodium 10%, smart sodium 10%, remaining
The preparation method of the surface conditioning agent, it is by the tetrahydrofuran for batch being slowly added at the uniform velocity to stir by metallic sodium for tetrahydrofuran
In solution, after abundant dissolving, smart sodium is added, after solid gradually dissolving, it is standby to be cooled to room temperature;
(4)Commercially available high temperature resistant sponge room temperature is sent to the fitting machine cylinder covered with waterproof solidification glue, after coating glue-line, with
The fluororesin glass fabric cloth of one side processing, carry out high temperature and be bonded to obtain the compound fluororesin-type glass fibre extension of coiled sponge
Machine curtain lining cloth is scalded, the temperature of fitting is 180 DEG C;
(5)By the compound fluororesin-type glass fibre Garment Steamer Machine curtain lining cloth of the coiled sponge prepared, arbitrary shape is cut into, is cut out
Cut place and carry out edge sealing, punching two ends with temperature pressure sensitive band, hole is affiliated in formation.
The fluororesin be ptfe emulsion, polytetrafluoroethylene (PTFE), serial, the poly- fluorine vinyl chloride of Teflon it is any one
Kind, the pigment agent is any one of aluminium silver powder, copper powder, carbon black, organic dyestuff, and the surfactant is lived for commercial surface
Property agent, alkaline conditioner is the weak base such as ammoniacal liquor, triethylamine;The glass fibre for E- type 5-9 microns glass pricker tie up one-ply yarn,
Kai Fu tows one kind of dimension, Carbon fibe or ceramic fibre, and the sizing grid of the grid Woven glass cloth cloth is 0.5 × 0.5mm, 1
×1mm、2×2mm、3×3mm、5×5mm;It is 95 that the waterproof solidification glue, which includes ratio,:5 marine glue and curing agent, it is described
Marine glue is commercially available PS glue, PA glue, PC glue, PE glue, PP glue, rubber cement, polyurethane glue any one,
Curing agent is commercially available curing agent.The sponge is any one of polyurethanes foam sponge, polyethers, polyvinyl alcohol.
Present invention introduces sponge surface adhesion type fluororesin Garment Steamer Machine curtain pad to have comfortable feel, surface elastic constant
Enhancing, while has insulation, it is shockproof the features such as, greatly reduce damage of the high temperature apparatus for textile material.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be on the premise of this patent objective not be departed from one skilled in the relevant art's possessed knowledge
Various changes can be made.
Claims (10)
- A kind of 1. preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge, it is characterised in that specific step It is rapid as follows:(1)Prepare fluoro-resin emulsion dipping agent, the fluoro-resin emulsion dipping agent according to weight than raw material include:Fluororesin 40-60%, surfactant 3-5%, pigment agent 0.5-5%, alkaline regulator 0.5-3.5%, remaining be deionized water;Take fluorine tree Fat, surfactant, pigment agent, alkaline regulator and water are mixed evenly with 70-100r/min rotating speed, and stirring is to without heavy Form sediment;(2)Tieed up, twisted with the fingers by twisting Split Down plain weave into grid Woven glass cloth cloth, twisting count for 150-250, fabric cloth leads to using glass pricker Cross roller and be sent to the dipping tank equipped with fluoro-resin emulsion dipping agent, by scraping off residual emulsion, burnt into hot-fluid oven for drying Knot, sintering temperature are 370-390 DEG C, rotating speed 0.5-4m/min, repeat 2-4 times, form fluororesin coated glass fiber fabric Cloth;(3)Fabric cloth is sent to the dipping tank of surface conditioning agent by roller, the upper liquid level of holding surface inorganic agent is positioned at leaching At the perpendicular diameter height 1/3-1/5 of stain roller, and ensure that it is just drying at room temperature after dipping to transmit cloth with drum shaft pressure, then The rinse bath for being transferred to next 60-70 DEG C of hot water embathes residual surface inorganic agent, and room temperature or baking oven air-dry, and forms one side absorption Type fluororesin glass fabric cloth;(4)Commercially available high temperature resistant sponge room temperature is sent to the fitting machine cylinder covered with waterproof solidification glue, after coating glue-line, with The fluororesin glass fabric cloth of one side processing, carry out high temperature and be bonded to obtain the compound fluororesin-type glass fibre extension of coiled sponge Machine curtain lining cloth is scalded, the temperature of fitting is 180 DEG C;(5)By the compound fluororesin-type glass fibre Garment Steamer Machine curtain lining cloth of the coiled sponge prepared, arbitrary shape is cut into, is cut out Cut place and carry out edge sealing, punching two ends with temperature pressure sensitive band, hole is affiliated in formation.
- 2. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 1, its Be characterised by, the fluororesin be ptfe emulsion, polytetrafluoroethylene (PTFE), serial, the poly- fluorine vinyl chloride of Teflon it is any one Kind, the pigment agent is any one of aluminium silver powder, copper powder, carbon black, organic dyestuff, and the surfactant is lived for commercial surface Property agent, alkaline conditioner is the weak base such as ammoniacal liquor, triethylamine.
- 3. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 1 or 2, Characterized in that, the fluororesin is ptfe emulsion.
- 4. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 1 or 2, Characterized in that, the alkaline conditioner is ammoniacal liquor.
- 5. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 1, its It is characterised by, dimension that the glass fibre ties up one-ply yarn for the glass pricker of E- type 5-9 microns, Kai Fu tows, Carbon fibe or ceramics are fine One kind of dimension, the sizing grid of the grid Woven glass cloth cloth is 0.5 × 0.5mm, 1 × 1mm, 2 × 2mm, 3 × 3mm, 5 × 5mm。
- 6. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 1 or 5, Characterized in that, the glass fibre ties up one-ply yarn for the glass pricker of E- type 5-9 microns.
- 7. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 1, its Be characterised by, the surface conditioning agent according to weight than raw material include:Metallic sodium 1-10%, smart sodium 1-10%, remaining be tetrahydrochysene Furans.
- 8. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 7, its It is characterised by, the preparation method of the surface conditioning agent, is that metallic sodium is molten by batch tetrahydrofuran for being slowly added at the uniform velocity stir In liquid, after abundant dissolving, smart sodium is added, after solid gradually dissolving, it is standby to be cooled to room temperature.
- 9. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 1, its It is characterised by, it is 95 that the waterproof solidification glue, which includes ratio,:5 marine glue and curing agent, the marine glue are commercially available PS glue, PA glue, PC glue, PE glue, PP glue, rubber cement, polyurethane glue any one, curing agent is commercially available curing agent.
- 10. the preparation method of the compound fluororesin-type glass fibre Garment Steamer Machine curtain pad of sponge according to claim 1, its It is characterised by, the sponge is any one of polyurethanes foam sponge, polyethers, polyvinyl alcohol.