CN107756910A - A kind of honeycomb fashion fire-retardant heat-insulation material and preparation method thereof - Google Patents
A kind of honeycomb fashion fire-retardant heat-insulation material and preparation method thereof Download PDFInfo
- Publication number
- CN107756910A CN107756910A CN201711057381.7A CN201711057381A CN107756910A CN 107756910 A CN107756910 A CN 107756910A CN 201711057381 A CN201711057381 A CN 201711057381A CN 107756910 A CN107756910 A CN 107756910A
- Authority
- CN
- China
- Prior art keywords
- fire
- insulation material
- retardant heat
- finished product
- honeycomb
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of honeycomb fashion fire-retardant heat-insulation material and preparation method thereof, in hole nest using fire-retardant heat-insulation material finished product press-in honeycomb core, the functional material of once-forming two-in-one body, the cellular material product manufactured using this method, the function of existing original cellular material, there is the function of heat-insulated, sound insulation, insulation and other effects again, overall structure is stable, and foam is uniform in bee-hole, and rate of closed hole is high, thermal conductivity factor is small, easy to operate.After prepared by the method for the present invention, fireproof heat insulating production board, which is pressed onto in the hole nest of honeycomb core, forms dispersed phase, instead of and fire easily combustion-supporting air is met in bee-hole, has blocked honeycomb hole nest wall and has continuously met the condition of fire spread, has improved product entirety fire protecting performance.In addition it is possible to improve heat insulation and preservation effect, production cost is not only saved, simplifies technique, improves efficiency of construction, is added again using space, fully meets the application demand of the high-end occasion such as aircraft, high ferro, car and boat.
Description
Technical field
The present invention relates to cellular composite material technology, more specifically refers to a kind of honeycomb fashion fire-retardant heat-insulation material and its preparation
Method.
Background technology
With the continuous development of modern science, the progress of the mankind proposes higher requirement to material life, technological innovation.
Cellular composite material is exactly a kind of new material, its feature:It is light, intensity is big, rigidity is high and with buffering, anti-
The functions such as shake, heat-insulated, insulation, sound insulation, it is widely used in Aeronautics and Astronautics, track traffic, car and boat manufacture, the neck such as building, furniture
Domain.It can be directly applied to aircraft, bullet train, double train, subway light rail, car and boat ash wall body plate, luggage carrier dividing plate etc. and
Interior trim floor etc..The new material has higher economic value, can largely alternative metals material and the forest reserves, protection and
Improve the ecological environment, be a kind of environment-friendly novel material for meeting 21st century development topic.
As shown in Figure 1, above-mentioned cellular composite material is mainly bonded in honeycomb core 1 by honeycomb core 1 and by adhesive
The covering 2 and sheet material 3 of upper and lower surface, honeycomb core 1 presently the most common generally aluminium honeycomb core and aramid fiber paper honeycomb core.So
And it is either poor using aluminium honeycomb core or the cellular composite material of aramid fiber paper honeycomb core, its anti-flammability, fire-protection rating compared with
It is low, it the defects of obvious is present, in addition, the performance such as its heat-insulated, insulation, sound insulation is also up for further improving.
The content of the invention
It is an object of the invention to provide a kind of honeycomb fashion fire-retardant heat-insulation material and preparation method thereof, honeycomb can be effectively improved
The performances such as the fire prevention of material, insulation, and preparation method is easy and effective.
To achieve these goals, the present invention uses following technical scheme.
On the one hand, a kind of preparation method of honeycomb fashion fire-retardant heat-insulation material, honeycomb is pressed into using fire-retardant heat-insulation material finished product
In-core.
Described press mode includes pushing or rolling mode.
Described rolls the fireproof heat insulating material for using the milling roller of arrangement up and down to will be moved to this and be stacked on honeycomb core
Material finished product is rolled in honeycomb core.
Described fire-retardant heat-insulation material finished product include macromolecule foaming or not expanded material and combinations thereof material, have, nothing
Machine fire-retardant heat-insulation material finished product.
The plastic material and its group in rubber or solidification process in described fire-retardant heat-insulation material finished product sulfidation
The semi-finished product of compound material substitute.
Described high molecular foam material finished product is pnenolic aldehyde foam material finished product.
Described finished product or semi-finished product are sheet material.
Described honeycomb core is papery or metal material.
Described paper material is aramid fiber, brown paper, plastic paper, carbon fiber paper or changes modeling paper material.
Metal material is aluminium or copper or alloy.
If the material self-strength of honeycomb core can not meet the press-in of fire-retardant heat-insulation material finished product when being integrated, using one with
The guided mode of honeycomb core identical high-strength metal material, by honeycomb core, guided mode, fire-retardant heat-insulation material finished product three by from top to bottom
It is overlapping successively, mode is pushed by fire-retardant heat-insulation material finished product through guided mode and being pressed into honeycomb core by punching press.
On the other hand, using the honeycomb fashion fire-retardant heat-insulation material prepared by above-mentioned preparation method, including honeycomb core and pressure
Enter the fire-retardant heat-insulation material finished product in honeycomb core.
Also include the covering for being bonded in the honeycomb core upper and lower surface after being pressed into fire-retardant heat-insulation material finished product.
Also include the decorative cover being bonded in outside upper and lower covering.
Described decorative cover includes one in fire-proof plate, metallic paint, aluminium sheet, calcium silicate board with microporous, true mineral varnish panel, stone material, ceramic tile
Layer or MULTILAYER COMPOSITE.
Honeycomb fashion fire-retardant heat-insulation material using the present invention and preparation method thereof, has following advantage:
1st, in hole nest of the present invention using fire-retardant heat-insulation material finished product press-in honeycomb core, the work(of once-forming two-in-one body
Can property material, the cellular material product manufactured using this method, the function of existing original cellular material, have again it is heat-insulated, every
The function of sound, insulation and other effects, overall structure is stable, and foam is uniform in bee-hole, and rate of closed hole is high, and thermal conductivity factor is small, operation letter
Just.
2nd, traditional single cellular material, only continuous phase do not have dispersed phase, meet the shortcomings that fire burning easily spreads, but through this
After prepared by the method for invention, fireproof heat insulating production board, which is pressed onto in the hole nest of honeycomb core, forms dispersed phase, instead of and fire is met in bee-hole
Easily combustion-supporting air, honeycomb hole nest wall is blocked and has continuously met the condition of fire spread, improved product entirety fire protecting performance.
3rd, due to being filled with the fire-retardant heat-insulation material of low heat conduction in the nest of hole, heat radiation, heat transfer and cross-ventilation are reduced,
Heat insulation and preservation effect is improved, increases the function of original cellular material, eliminates such as aircraft, high ferro, car and boat casing, should use
Cellular material does Insulation again, the two indispensable one cumbersome work, not only saves production cost, simplifies technique, carry
High efficiency of construction, add casing again uses space.
Brief description of the drawings
Fig. 1 is the structural representation of the cellular composite material of prior art;
Fig. 2 is the honeycomb fashion fire-retardant heat-insulation material structural representation of the present invention;
Fig. 3 is a kind of structural representation for rolling setting of the present invention;
Fig. 4 is the structural representation of another rolling apparatus of the present invention;
Fig. 5 is the structural representation of the honeycomb fashion guided mode of the present invention;
The punching press using honeycomb fashion guided mode that Fig. 6 is the present invention is stacked schematic diagram.
Embodiment
Technical scheme is further illustrated below in conjunction with the accompanying drawings.
The preparation method of the honeycomb fashion fire-retardant heat-insulation material of the present invention, honeycomb core 1 is pressed into using fire-retardant heat-insulation material finished product
Hole nest in.
Described press mode can use and push or roll mode, or other press modes.
Wherein, the mode of press-in, hydraulic test can be used, the fire-retardant heat-insulation material finished product 4 being stacked on honeycomb core 1 is straight
Connect and push in press-in honeycomb core 1.The mode rolled, then the milling roller arranged up and down can be used to will be moved to this and be stacked in honeycomb
Fire-retardant heat-insulation material finished product 4 on core 1 is rolled in honeycomb core 1.Fig. 3,4 show two kinds be used to rolling preparation roll dress
Put, stacked up and down fire-retardant heat-insulation material finished product 4 and honeycomb core 1 can be conveyed by rollgang 7, by milling roller
After 5 roll, the honeycomb fashion fire-retardant heat-insulation material 6 of both unifications is formed.
Described fire-retardant heat-insulation material finished product 4 may include macromolecule foaming or not expanded material and combinations thereof material, have,
The finished products such as inorganic fireproofing insulation material.
Described fire-retardant heat-insulation material finished product 4 also can use plastic material in rubber or solidification process in sulfidation and
The semi-finished product of its composition material are substituted.
Described high molecular foam material finished product preferably selects pnenolic aldehyde foam material finished product, due to pnenolic aldehyde foam material into
It has certain crisp brittleness to product, is especially suitable for the preparation method being pressed directly into, and has the property such as insulation well, fire prevention again
Energy.
Described finished product or semi-finished product can preferably use broad form, can also select other section bars certainly.
Described honeycomb core 1 can use papery or metal material or other materials, wherein, described paper material specifically may be used
Using aramid paper, brown paper, plastic paper, carbon fiber paper or change the paper materials such as modeling paper material.And metal material can be selected aluminium or
Copper or its alloy or other metal or alloy materials.
If in addition, when the material self-strength of honeycomb core 1 can not meet fire-retardant heat-insulation material finished product 4 press-in be integrated when,
The guided mode 7 with the identical high-strength metal material of honeycomb core 1 as shown in Figure 5 can be used, by honeycomb core 1, guided mode 7, fire prevention
The three of insulation material finished product 4 by overlapping (see Fig. 6) successively from top to bottom, by punching press push mode by fire-retardant heat-insulation material into
Product are through guided mode and are pressed into honeycomb core.The paper honeycomb core that the method is relatively large in diameter particularly suitable for hole nest pushes life
Production.
Using the honeycomb fashion fire-retardant heat-insulation material prepared by above-mentioned preparation method, including honeycomb core 1 and press-in honeycomb core 1
Interior fire-retardant heat-insulation material finished product 4.The honeycomb fashion fire-retardant heat-insulation material can be used as finished product direct marketing, can also be used as base material,
Continue corresponding compound:
As one embodiment, the honeycomb fashion fire-retardant heat-insulation material also includes being bonded in press-in fire-retardant heat-insulation material finished product 4
The covering of the upper and lower surface of honeycomb core 1 afterwards.
As another embodiment, the honeycomb fashion fire-retardant heat-insulation material also includes the decorative cover being bonded in outside upper and lower covering,
The decorative cover may include in fire-proof plate, metallic paint, aluminium sheet, calcium silicate board with microporous, true mineral varnish panel, stone material, ceramic tile one or more layers is multiple
Close.
What is needed is:Applicant of the present invention was once considered using following several schemes in R&D process:
1st, to being filled foamed phenolic resin (fluent material) in the hole nest of aramid fiber paper honeycomb core 1 or other honeycomb cores 1,
The problem of being prepared by way of heating foamed solidification, but being existed in this way be:Usual aramid fiber cellular material
Or it is unit that other cellular materials, which are all several cubes, that is to say, that by taking aramid fiber cellular material as an example, the diameter of general bee-hole
For five or six millimeters, the depth in hole is one meter or so, if immersing foamed phenolic resin in the bee-hole of so tiny depth
If, just to Foamex viscosity, solid content requires very high, and one meter or so deep hole is difficult the degree of hanging from above for controlling resin, nothing
Method ensures the uniformity consistency above and below resin.In addition, foamed phenolic resin is in one meter or so deep hole, by heating, foaming,
Solidification, can be by the great foaming resistance of bee-hole wall, so that foam is obstructed up and down, uneven percent opening is high, does not reach certain
Effective rate of closed hole, directly affects heat insulation effect.
2nd, first large-scale aramid fiber cellular material is cut into slices, then is soaked phenolic foam resin, then heat foamed solidification again.Such as
This effect is worse, this be due to the uncontrollable phenolic foam in cellular two it is resin expanded overflow phenomenon, honeycomb can be higher by and put down
Face, the Foamex as hard as iron that is cured be difficult handle it is smooth.
3rd, a kind of a kind of powder of organic or inorganic less than bee-hole is filled in honeycomb hole, or it is a kind of organic foamable
Precursor Powder or the microballons such as polyimides, aeroge, polyurethane, expandable polystyrene (EPS), then by heating, the side of pressurization
It can reach ideal effect.But this method is too time-consuming, power consumption, is only capable of realizing in laboratory, can not arrive scale, continuous production,
Especially there is the material product of certain length and width.General finished product cellular material plate is all long at nearly two meters, and that just processes sets
Standby and processing difficulty is well imagined.
In summary, using honeycomb fashion fire-retardant heat-insulation material of the present invention and preparation method thereof, possesses following advantage:
1st, cellular board production procedure is not changed, it is not necessary to cellular board is immersed foamed phenolic resin and carried out again in honeycomb
Heat the cumbersome techniques such as foamed solidification.It is large-scale in this way to be difficult to a kind of warming-up device, small-sized fine of this warming-up device
Realize.
2nd, the materials such as powder, microballon need not be loaded in honeycomb hole, then enter the trouble process such as temperature-pressure shaping, are saved
Energy;
3rd, finished product phenolic foam board, or other organic foam production boards, completely by prefabrication it is good its produce into
Product plate, the stable foam of product quality is uniform, and rate of closed hole is high, and thermal conductivity factor is low, good effect of heat insulation, and this is all the elder generation of production board
Its advantage.
4th, phenol formaldehyde foam production board, with aramid fiber honeycomb production board or other honeycomb production boards, through double-roller rolling apparatus
It is processed, the multi-functional honeycomb board that the once-forming Innovative process technology being combined into one manufactures, without adding again
Work, pressurization, heating, solidification and again cutting etc. trouble process.
5th, with the honeycomb board that manufactures of the present invention, can process can grow, can it is short, can greatly, various sheet materials that can be small, consume
Energy level is low, and process is easy, greatly reduces working strength, reduces recruitment quantity and working environment.
Those of ordinary skill in the art it should be appreciated that the embodiment of the above be intended merely to explanation the present invention,
And be not used as limitation of the invention, as long as in the spirit of the present invention, the change to embodiment described above
Change, modification will all fall in the range of claims of the present invention.
Claims (14)
- A kind of 1. preparation method of honeycomb fashion fire-retardant heat-insulation material, it is characterised in that:Honeybee is pressed into using fire-retardant heat-insulation material finished product Nest in-core.
- 2. the preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 1, it is characterised in that:Described press mode Including pushing or rolling mode.
- 3. its preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 1, it is characterised in that described rolling is adopted The fire-retardant heat-insulation material finished product that will be moved to this with the milling roller arranged up and down and be stacked on honeycomb core is rolled in honeycomb core.
- 4. its preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 1, it is characterised in that:Described fire prevention is protected Adiabator finished product include macromolecule foaming or not expanded material and combinations thereof material, have, inorganic fireproofing insulation material finished product.
- 5. its preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 1, it is characterised in that:Described fire prevention is protected The semi-finished product of the plastic material in rubber or solidification process in adiabator finished product sulfidation and combinations thereof material substitute.
- 6. its preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 4, it is characterised in that:Described macromolecule Expanded material finished product is pnenolic aldehyde foam material finished product.
- 7. its preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 5, it is characterised in that described finished product or Semi-finished product are sheet material.
- 8. its preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 1, it is characterised in that described honeycomb core For papery or metal material.
- 9. its preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 8, it is characterised in that described papery material Expect for aramid fiber, brown paper, plastic paper, carbon fiber paper or change modeling paper material.
- 10. the preparation method of honeycomb fashion fire-retardant heat-insulation material as claimed in claim 1, it is characterised in that if the material of honeycomb core When material self-strength can not meet that the press-in of fire-retardant heat-insulation material finished product is integrated, then using one and honeycomb core identical high intensity gold Belong to the guided mode of material, by honeycomb core, guided mode, fire-retardant heat-insulation material finished product three by overlapping successively from top to bottom, pass through punching press Mode is pushed fire-retardant heat-insulation material finished product is passed through into guided mode and is pressed into honeycomb core.
- 11. the honeycomb fashion fire-retardant heat-insulation material as prepared by preparation method according to any one of claims 1 to 10, it is special Sign is:Including the fire-retardant heat-insulation material finished product in honeycomb core and press-in honeycomb core.
- 12. honeycomb fashion fire-retardant heat-insulation material as claimed in claim 11, it is characterised in that:Also include being bonded in press-in fire prevention guarantor The covering of honeycomb core upper and lower surface after adiabator finished product.
- 13. honeycomb fashion fire-retardant heat-insulation material as claimed in claim 12, it is characterised in that:Also include being bonded in upper and lower covering Outer decorative cover.
- 14. honeycomb fashion fire-retardant heat-insulation material as claimed in claim 13, it is characterised in that:Described decorative cover includes fire prevention One or more layers in plate, metallic paint, aluminium sheet, calcium silicate board with microporous, true mineral varnish panel, stone material, ceramic tile is compound.