CN107747234A - A kind of cable non-woven fabrics twining package tape and preparation method thereof - Google Patents
A kind of cable non-woven fabrics twining package tape and preparation method thereof Download PDFInfo
- Publication number
- CN107747234A CN107747234A CN201710987758.2A CN201710987758A CN107747234A CN 107747234 A CN107747234 A CN 107747234A CN 201710987758 A CN201710987758 A CN 201710987758A CN 107747234 A CN107747234 A CN 107747234A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven fabrics
- package tape
- twining package
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to cable material field, specifically a kind of cable non-woven fabrics twining package tape and preparation method thereof, its concrete composition composition is as follows:40 45 parts of non-woven fabrics, 25 30 parts of polyvinyl chloride, 15 20 parts of polyethylene, 8 10 parts of polyurethane, 46 parts of magnesia, 12 14 parts of glass fibre, 12 14 parts of Netted flap, 24 parts of antioxidant, 13 parts of thickener, a kind of preparation method of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:(1) melt;(2) silk is organized;(3) weave;(4) brush;(5) low temperature, using polyurethane as face coat, waterproof antiwear, remain unchanged for a long period of time hard;Turn into twining package tape, resistance to good insulation preformance with non-woven fabrics braiding using glass fibre and Netted flap;Relative to non-woven fabrics is directly used, as twining package tape, doing invention has high waterproof antiwear and insulating properties, service life length.
Description
Technical field
The present invention relates to cable material field, specifically a kind of cable non-woven fabrics twining package tape and preparation method thereof.
Background technology
The inside of cable is wrapped usually using non-woven fabrics, non-woven fabrics good insulation preformance, and wrapped certain thickness can also carry
For cushioning effect, but water resistance has certain limitation, it is therefore desirable to processing again is carried out to non-woven fabrics and causes usability
It can be improved.
The content of the invention
In order to solve the above problems, the present invention proposes a kind of cable non-woven fabrics twining package tape and preparation method thereof.
A kind of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:
Non-woven fabrics 40-45 parts, polyvinyl chloride 25-30 parts, polyethylene 15-20 parts, polyurethane 8-10 parts, magnesia 4-6 parts,
Glass fibre 12-14 parts, Netted flap 12-14 parts, antioxidant 2-4 parts, thickener 1-3 parts.
A kind of preparation method of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:
(1) melt:Polyvinyl chloride, polyethylene, magnesia and antioxidant are heated into mixing resulting mixture;
(2) silk is organized:Addition glass fibre and Netted flap are put into extruding strings device after stirring in the mixture
Wire squeeze;
(3) weave:The silk that step (2) is squeezed and non-woven fabrics braiding are got up as twining package tape, while polyurethane and thickening
Agent fusion turns into mixed solution;
(4) brush:Mixed solution is applied on twining package tape using artificial or machine;
(5) low temperature:Carrying out drying using low temperature can wind.
The drying temperature of described step (5) is 30-40 degrees Celsius.
The beneficial effects of the invention are as follows:The present invention, as face coat, waterproof antiwear, is remained unchanged for a long period of time hard using polyurethane;
Turn into twining package tape, resistance to good insulation preformance with non-woven fabrics braiding using glass fibre and Netted flap;Relative to directly making
By the use of non-woven fabrics as twining package tape, doing invention has high waterproof antiwear and insulating properties, service life length.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, below it is right
The present invention is expanded on further.
Embodiment one:
A kind of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:
45 parts of non-woven fabrics, 28 parts of polyvinyl chloride, 15 parts of polyethylene, 10 parts of polyurethane, 5 parts of magnesia, 12 parts of glass fibre,
14 parts of Netted flap, 3 parts of antioxidant, 1 part of thickener.
A kind of preparation method of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:
(1) melt:Polyvinyl chloride, polyethylene, magnesia and antioxidant are heated into mixing resulting mixture;
(2) silk is organized:Addition glass fibre and Netted flap are put into extruding strings device after stirring in the mixture
Wire squeeze;
(3) weave:The silk that step (2) is squeezed and non-woven fabrics braiding are got up as twining package tape, while polyurethane and thickening
Agent fusion turns into mixed solution;
(4) brush:Mixed solution is applied on twining package tape using artificial or machine;
(5) low temperature:Carrying out drying using low temperature can wind.
The drying temperature of described step (5) is 30-40 degrees Celsius.
Embodiment two:
A kind of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:
40 parts of non-woven fabrics, 30 parts of polyvinyl chloride, 18 parts of polyethylene, 8 parts of polyurethane, 6 parts of magnesia, 13 parts of glass fibre,
12 parts of Netted flap, 4 parts of antioxidant, 2 parts of thickener.
A kind of preparation method of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:
(1) melt:Polyvinyl chloride, polyethylene, magnesia and antioxidant are heated into mixing resulting mixture;
(2) silk is organized:Addition glass fibre and Netted flap are put into extruding strings device after stirring in the mixture
Wire squeeze;
(3) weave:The silk that step (2) is squeezed and non-woven fabrics braiding are got up as twining package tape, while polyurethane and thickening
Agent fusion turns into mixed solution;
(4) brush:Mixed solution is applied on twining package tape using artificial or machine;
(5) low temperature:Carrying out drying using low temperature can wind.
The drying temperature of described step (5) is 30-40 degrees Celsius.
Embodiment three:
A kind of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:
43 parts of non-woven fabrics, 25 parts of polyvinyl chloride, 20 parts of polyethylene, 9 parts of polyurethane, 4 parts of magnesia, 14 parts of glass fibre,
13 parts of Netted flap, 2 parts of antioxidant, 3 parts of thickener.
A kind of preparation method of cable non-woven fabrics twining package tape, its concrete composition composition are as follows:
(1) melt:Polyvinyl chloride, polyethylene, magnesia and antioxidant are heated into mixing resulting mixture;
(2) silk is organized:Addition glass fibre and Netted flap are put into extruding strings device after stirring in the mixture
Wire squeeze;
(3) weave:The silk that step (2) is squeezed and non-woven fabrics braiding are got up as twining package tape, while polyurethane and thickening
Agent fusion turns into mixed solution;
(4) brush:Mixed solution is applied on twining package tape using artificial or machine;
(5) low temperature:Carrying out drying using low temperature can wind.
The drying temperature of described step (5) is 30-40 degrees Celsius.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
For personnel it should be appreciated that the present invention is not limited to the above embodiments, that described in above-described embodiment and specification is the present invention
Principle, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these change and
Improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appended claims and its equivalent
Thing defines.
Claims (3)
- A kind of 1. cable non-woven fabrics twining package tape, it is characterised in that:Its concrete composition composition is as follows:Non-woven fabrics 40-45 parts, polychlorostyrene Ethene 25-30 parts, polyethylene 15-20 parts, polyurethane 8-10 parts, magnesia 4-6 parts, glass fibre 12-14 parts, netted polypropylene Fiber 12-14 parts, antioxidant 2-4 parts, thickener 1-3 parts.
- A kind of 2. preparation method of cable non-woven fabrics twining package tape according to claim 1, it is characterised in that:Its specific group It is as follows into composition:(1) melt:Polyvinyl chloride, polyethylene, magnesia and antioxidant are heated into mixing resulting mixture;(2) silk is organized:Addition glass fibre and Netted flap are put into wire squeeze in extruding strings device after stirring in the mixture;(3) weave:The silk that step (2) is squeezed and non-woven fabrics braiding are got up as twining package tape, while polyurethane and thickener are melted Synthesize mixed solution;(4) brush:Mixed solution is applied on twining package tape using artificial or machine;(5) low temperature:Carrying out drying using low temperature can wind.
- A kind of 3. preparation method of cable non-woven fabrics twining package tape according to claim 2, it is characterised in that:Described step Suddenly the drying temperature of (5) is 30-40 degrees Celsius.