CN107746577A - A kind of preparation technology for building organic fire prevention calking - Google Patents
A kind of preparation technology for building organic fire prevention calking Download PDFInfo
- Publication number
- CN107746577A CN107746577A CN201710863619.9A CN201710863619A CN107746577A CN 107746577 A CN107746577 A CN 107746577A CN 201710863619 A CN201710863619 A CN 201710863619A CN 107746577 A CN107746577 A CN 107746577A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicone oil
- fire prevention
- preparation technology
- phenyl silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of preparation technology for building organic fire prevention calking of the present invention, step are as follows:(1)Prepare fire retardant, count in parts by weight, by 4 12 parts of 25 45 parts of methyl phenyl silicone oil, 15 27 parts of hydroxy phenyl silicone oil, 20 35 parts of magnesium hydroxide, 16 35 parts of expansile graphite particle, 13 25 parts of red phosphorus, APP mixing, incorporation time 30min, fire retardant is obtained;(2)Count in parts by weight, by 40 55 parts of 107 base rubber, 10 35 parts of kaolin, 14 45 parts of natural diatomaceous earth, 15 25 parts of talcum powder, 10 25 parts of bentonite are added in Multi-functional dispersion mixer and mixed, 40min is mixed, is put into after the completion of mixing in extruder, extrusion molding, extrusion obtains finished product no less than secondary.The fire retardant performance of the fire prevention calking of gained of the invention is splendid.
Description
Technical field
The present invention relates to a kind of preparation technology for building organic fire prevention calking.
Background technology
Flexible organic putty is widely used in the fields such as power plant, power transmission and transformation, smelting industry, while is also used for preventing cable, electricity
Line, optical cable occur fire and spread from hole to adjacent room, to reducing fire damage, avoiding fault spread from serving great role.
However, the flexible organic putty of most domestic is mainly that excellent anti-flammability is obtained with halogen adhesive.But halogen containing material
Substantial amounts of smog and hydrogen chloride gas can be discharged in burning, these smog and hydrogen chloride gas, which are known from experience to stimulate human eye and breathe, is
System, the work of the fighting and rescue operations of fire fighter and rescue personnel is hindered, environment can also be damaged.
The content of the invention
The present invention proposes a kind of preparation technology for building organic fire prevention calking regarding to the issue above.
Specific technical scheme is as follows:
A kind of preparation technology for building organic fire prevention calking, it is characterised in that step is as follows:
(1)Fire retardant is prepared, is counted in parts by weight, by methyl phenyl silicone oil 25-45 parts, hydroxy phenyl silicone oil 15-27 parts, hydrogen-oxygen
Change magnesium 20-35 parts, expansile graphite particle 16-35 parts, red phosphorus 13-25 parts, the mixing of APP 4-12 parts, incorporation time is
30min, obtain fire retardant;
(2)Count in parts by weight, by 107 base rubber 40-55 parts, kaolin 10-35 parts, natural diatomaceous earth 14-45 parts, talcum powder
15-25 parts, bentonite 10-25 parts are added in Multi-functional dispersion mixer and mixed, and mix 40min, are put into after the completion of mixing crowded
Go out in machine, extrusion molding, extrusion obtains finished product no less than secondary.
Above-mentioned a kind of preparation technology for building organic fire prevention calking, it is characterised in that the particle diameter of expansile graphite particle is
50-120nm。
Above-mentioned a kind of preparation technology for building organic fire prevention calking, it is characterised in that methyl phenyl silicone oil and hydroxy phenyl
Silicone oil is with weight than 5:3 ratio mixing.
The fire retardant performance of the fire prevention calking of gained of the invention is splendid.
Embodiment
To make technical scheme become apparent from clearly, below the present invention is described further, it is any to this
The scheme that the technical characteristic progress equivalencing of inventive technique scheme and conventional reasoning are drawn each falls within the scope of the present invention.
Embodiment 1
A kind of preparation technology for building organic fire prevention calking, it is characterised in that step is as follows:
(1)Fire retardant is prepared, is counted in parts by weight, by 25 parts of methyl phenyl silicone oil, 15 parts of hydroxy phenyl silicone oil, magnesium hydroxide 20
4 parts of part, 16 parts of expansile graphite particle, 13 parts of red phosphorus, APP mixing, incorporation time 30min, obtain fire retardant;
(2)Count in parts by weight, by 40 parts of 107 base rubber, 10 parts of kaolin, 14 parts of natural diatomaceous earth, 15 parts of talcum powder, bentonite
10 parts are added in Multi-functional dispersion mixer and mix, and mix 40min, are put into after the completion of mixing in extruder, extrusion molding, squeeze
Go out no less than secondary, obtain finished product.
The particle diameter of expansile graphite particle is 50nm.
Embodiment 2
A kind of preparation technology for building organic fire prevention calking, it is characterised in that step is as follows:
(1)Fire retardant is prepared, is counted in parts by weight, by 45 parts of methyl phenyl silicone oil, 27 parts of hydroxy phenyl silicone oil, magnesium hydroxide 35
12 parts of part, 35 parts of expansile graphite particle, 25 parts of red phosphorus, APP mixing, incorporation time 30min, obtain fire retardant;
(2)Count in parts by weight, by 55 parts of 107 base rubber, 35 parts of kaolin, 45 parts of natural diatomaceous earth, 25 parts of talcum powder, bentonite
25 parts are added in Multi-functional dispersion mixer and mix, and mix 40min, are put into after the completion of mixing in extruder, extrusion molding, squeeze
Go out no less than secondary, obtain finished product.
The particle diameter of expansile graphite particle is 120nm.
Claims (3)
1. a kind of preparation technology for building organic fire prevention calking, it is characterised in that step is as follows:
(1)Fire retardant is prepared, is counted in parts by weight, by methyl phenyl silicone oil 25-45 parts, hydroxy phenyl silicone oil 15-27 parts, hydrogen-oxygen
Change magnesium 20-35 parts, expansile graphite particle 16-35 parts, red phosphorus 13-25 parts, the mixing of APP 4-12 parts, incorporation time is
30min, obtain fire retardant;
(2)Count in parts by weight, by 107 base rubber 40-55 parts, kaolin 10-35 parts, natural diatomaceous earth 14-45 parts, talcum powder
15-25 parts, bentonite 10-25 parts are added in Multi-functional dispersion mixer and mixed, and mix 40min, are put into after the completion of mixing crowded
Go out in machine, extrusion molding, extrusion obtains finished product no less than secondary.
A kind of 2. preparation technology for building organic fire prevention calking as claimed in claim 1, it is characterised in that expansile graphite
The particle diameter of grain is 50-120nm.
A kind of 3. preparation technology for building organic fire prevention calking as claimed in claim 1, it is characterised in that methyl phenyl silicone oil
With hydroxy phenyl silicone oil with weight than 5:3 ratio mixing.