CN107746229A - A kind of insulation powder of lacquer putty for use on and preparation method thereof - Google Patents
A kind of insulation powder of lacquer putty for use on and preparation method thereof Download PDFInfo
- Publication number
- CN107746229A CN107746229A CN201711166874.4A CN201711166874A CN107746229A CN 107746229 A CN107746229 A CN 107746229A CN 201711166874 A CN201711166874 A CN 201711166874A CN 107746229 A CN107746229 A CN 107746229A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- lacquer putty
- insulation
- kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of insulation powder of lacquer putty for use on and preparation method thereof.A kind of insulation powder of lacquer putty for use on, including following raw material：600 700 parts of dicalcium powder, 50 parts of halloysite nanotubes, 50 parts of kaolin, 50 parts of glass fibre, 150 250 parts of white cement, 30 parts of redispersible latex powder, 35 parts of carboxymethyl cellulose, 35 parts of modified starch ether.A kind of preparation method of insulation powder of lacquer putty for use on, is crushed emphatically, is mixed respectively to inorganic component, organic component.The powder of lacquer putty for use on materials environmental protection of the present invention, preparation technology is simple, and easily construction polishing, adhesion strength is high, especially with insulation effect, belongs to functional form powder of lacquer putty for use on product, has good market prospects.
Description
Technical field
It is especially a kind of for the insulation powder of lacquer putty for use on of interior wall and its preparation the present invention relates to building material technical field
Method.
Background technology
Heat energy in air transmits by three kinds of conduction, convection current and radiation modes, wherein having more than 90% to come from spoke
Penetrate the transmission of heat.The influence lived to slow down the transmission of these heats to people is protected, it is necessary to be used in building surface
Warm heat-barrier material so that materials for wall can improve heat-proof quality in summer, can improve heat-insulating property in the winter time.And putty is
A kind of building and ornament materials of smooth surface of wall, are a kind of thick slurry coating materials, and the purpose of brushing putty is to fill construction surface
Hole, depression and correct construction surface curve deviation.In addition, putty can also play waterproof, antibacterial, enhancing, mould proof
Etc. a variety of special efficacies.
The heat-insulating material in China is by heat insulating coatings and its product and both products of facing putty mostly at present
Collective effect is in surface of wall, hence it is evident that occur structure loosely, service life is short, easy peeling cracking and space-consuming are big etc. asks
Topic.Therefore, a kind of powder of lacquer putty for use on insulation effect is studied to have great importance.
The content of the invention
A kind of in view of the above-mentioned problems, the present invention is intended to provide insulation powder of lacquer putty for use on and preparation method thereof.
In order to solve the above problems, scheme of the present invention is：
A kind of insulation powder of lacquer putty for use on, it is composed of the following raw materials by weight：
Dicalcium powder 600-700 parts, 50 parts of halloysite nanotubes, 50 parts of kaolin, 50 parts of glass fibre, white cement 150-250 parts,
30 parts of redispersible latex powder, carboxymethyl cellulose 3-5 parts, modified starch ether 3-5 parts.
Further, the dicalcium powder particle diameter is in 3-5 microns, dicalcium powder of the whiteness in 80-82%.
Further, the halloysite nanotubes length is about 500-800 nanometers, and external diameter is about 80-120 nanometers, interior
Footpath is about 20-30 nanometers.
Further, the kaolin is calcined kaolin, and particle diameter is more than 60% in 2-5 microns, dioxide-containing silica.
Further, the glass fibre is alkali-free short glass fiber, and dimensions is 1-2 centimetres.
A kind of preparation method of above-mentioned insulation powder of lacquer putty for use on, comprises the following steps：
A, the dicalcium powder of above-mentioned parts by weight, halloysite nanotubes, kaolin, glass fibre, white cement are respectively placed in pulverizer
In pulverize and sieve it is rear standby；
B, under high speed shear effect, the halloysite nanotubes after sieving, kaolin is first mixed, sequentially add glass fibers
Dimension, dicalcium powder, white cement；After inorganic filler mixing after, sequentially add redispersible latex powder, carboxymethyl cellulose and
Modified starch ether；Keep 5000r/min shear rate scattered 10 minutes, it is final to obtain target compound.
Relative to prior art, beneficial effects of the present invention：
（1）Raw material sources used in the powder of lacquer putty for use on of the present invention are extensive, and innovative design with the addition of heat-insulation and heat-preservation filler, greatly promote
The feature and added value of powder of lacquer putty for use on.The environmental protection of powder of lacquer putty for use on materials, preparation technology is simple, and it is low to prepare cost.
（2）A certain proportion of white cement and redispersible latex powder are with the addition of in the powder of lacquer putty for use on of the present invention, it is possible to increase
The adhesion strength and structural strength of putty；The glass fibre of certain part by weight is with the addition of, there is excellent effect of heat insulation, as greasy
The aggregate element of insulation in sub- powder, it can effectively obstruct the transmission of heat in air；Modified starch ether is with the addition of, can conduct
Thickener adjusts the mobility of putty, and prevents putty sagging.
Embodiment
The invention will be further described with the following Examples.
Embodiment 1
A kind of insulation powder of lacquer putty for use on and preparation method thereof：
A, in parts by weight, weigh 600 parts of dicalcium powders, 50 parts of halloysite nanotubes, 50 parts of kaolin, 50 parts of glass fibres and
250 parts of white cements be respectively placed in pulverizer pulverize and sieve it is rear standby；
B, under high speed shear effect, the halloysite nanotubes after being sieved in step A, kaolin are first mixed, Ran Houyi
Secondary addition glass fibre, dicalcium powder, white cement；After inorganic filler mixing after, sequentially add 30 parts of redispersible latex powders,
5 parts of carboxymethyl celluloses and 5 parts of modified starch ethers；Keep 5000r/min shear rate scattered 10 minutes, it is final to obtain target
Compound.
Embodiment 2
A kind of Thermal insulation putty powder and preparation method：
A, in parts by weight, weigh 650 parts of dicalcium powders, 50 parts of halloysite nanotubes, 50 parts of kaolin, 50 parts of glass fibres and
200 parts of white cements be respectively placed in pulverizer pulverize and sieve it is rear standby；
B, under high speed shear effect, the halloysite nanotubes after being sieved in step A, kaolin are first mixed, Ran Houyi
Secondary addition glass fibre, dicalcium powder, white cement；After inorganic filler mixing after, sequentially add 30 parts of redispersible latex powders,
4 parts of carboxymethyl celluloses and 4 parts of modified starch ethers；Keep 5000r/min shear rate scattered 10 minutes, it is final to obtain target
Compound.
Embodiment 3
A kind of Thermal insulation putty powder and preparation method：
A, in parts by weight, weigh 700 parts of dicalcium powders, 50 parts of halloysite nanotubes, 50 parts of kaolin, 50 parts of glass fibres and
150 parts of white cements be respectively placed in pulverizer pulverize and sieve it is rear standby；
B, under high speed shear effect, the halloysite nanotubes after being sieved in step A, kaolin are first mixed, Ran Houyi
Secondary addition glass fibre, dicalcium powder, white cement；After inorganic filler mixing after, sequentially add 30 parts of redispersible latex powders,
3 parts of carboxymethyl celluloses and 3 parts of modified starch ethers；Keep 5000r/min shear rate scattered 10 minutes, it is final to obtain target
Compound.
To sum up, Thermal insulation putty powder provided by the invention, materials environmental protection, preparation technology is simple, easily construction polishing, bonds
Intensity is high, especially with insulation effect, belongs to functional form powder of lacquer putty for use on product, has good market prospects.
Claims (6)
1. a kind of insulation powder of lacquer putty for use on, it is characterised in that including following raw material：Dicalcium powder 600-700 parts, galapectite
50 parts of nanotube, 50 parts of kaolin, 50 parts of glass fibre, white cement 150-250 parts, 30 parts of redispersible latex powder, carboxylic first
Base cellulose 3-5 parts, modified starch ether 3-5 parts.
2. a kind of insulation powder of lacquer putty for use on according to claim 1, it is characterised in that the dicalcium powder is particle diameter in 3-5
Micron, dicalcium powder of the whiteness in 80-82%.
A kind of 3. insulation powder of lacquer putty for use on according to claim 1, it is characterised in that institute
It is 500-800 nanometers to state halloysite nanotubes length, and external diameter is 80-120 nanometers, and internal diameter is 20-30 nanometers.
A kind of 4. insulation powder of lacquer putty for use on according to claim 1, it is characterised in that institute
It is calcined kaolin to state kaolin, and particle diameter is more than 60% in 2-5 microns, dioxide-containing silica.
A kind of 5. insulation powder of lacquer putty for use on according to claim 1, it is characterised in that institute
It is alkali-free short glass fiber to state glass fibre, and dimensions is 1-2 centimetres.
6. prepare the method for the insulation powder of lacquer putty for use on described in claim 1, it is characterised in that
Comprise the following steps：
A, the dicalcium powder of above-mentioned parts by weight, halloysite nanotubes, kaolin, glass fibre, white cement are respectively placed in pulverizer
In pulverize and sieve it is rear standby；
B, under high speed shear effect, the halloysite nanotubes after sieving, kaolin is first mixed, sequentially add glass fibers
Dimension, dicalcium powder, white cement；After inorganic filler mixing after, sequentially add redispersible latex powder, carboxymethyl cellulose and
Modified starch ether；Keep 5000r/min shear rate scattered 10 minutes, it is final to obtain target compound.