CN107722660A - A kind of high intensity liquid detergent bottle and preparation method - Google Patents
A kind of high intensity liquid detergent bottle and preparation method Download PDFInfo
- Publication number
- CN107722660A CN107722660A CN201710832882.1A CN201710832882A CN107722660A CN 107722660 A CN107722660 A CN 107722660A CN 201710832882 A CN201710832882 A CN 201710832882A CN 107722660 A CN107722660 A CN 107722660A
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid detergent
- detergent bottle
- coupling agent
- bottle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high intensity liquid detergent bottle and preparation method, constitutive material component by weight is divided into：60 70 parts of plastic raw materials, 15 19 parts of Tissuemat E, 1.2 1.6 parts of lead sulfate, 1 1.2 parts of lead stearate, 8 10 parts of fines of filling, 13 parts of coupling agent, 35 parts of auxiliary agent, 24 parts of toughener.Liquid detergent bottle of the present invention is mixed by plastic raw materials with Tissuemat E collocation, strengthen the intensity of liquid detergent bottle in addition lead sulfate, lead stearate, filling fines, so that liquid detergent bottle impact resistance strengthens, the liquid detergent bottle of high-intensity performance is advantageous to production and sales use.
Description
Technical field
The present invention relates to liquid detergent bottle production technical field, more particularly to a kind of high intensity liquid detergent bottle and preparation method.
Background technology
Liquid detergent is articles for use essential in every household daily life production, and present liquid detergent is all to use plastics
Bottle packs liquid detergent, and therefore, in use, different placement environment often produces certain influence to it, is transporting
It is defeated or in use, bottle for handling liquid toilet or cosmetic substance receives impact force deformation, the sale of product is often influenceed, is brought to liquid detergent bottle producer certain
Limitation, therefore, it is necessary to propose a kind of high intensity liquid detergent bottle and preparation method.
The content of the invention
To solve the defects of prior art, the invention discloses a kind of high intensity liquid detergent bottle and preparation method.
The invention discloses a kind of environment-friendly type liquid detergent bottle, constitutive material component by weight is divided into：Plastic raw materials 60-70
Part, Tissuemat E 15-19 parts, lead sulfate 1.2-1.6 parts, lead stearate 1-1.2 parts, filling fines 8-10 parts, coupling agent 1-3
Part, auxiliary agent 3-5 parts, toughener 2-4 parts.
Preferably, constitutive material component by weight is divided into：Constitutive material component by weight is divided into：65 parts of plastic raw materials, gather
17 parts of ethylene waxes, 1.4 parts of lead sulfate, 1.1 parts of lead stearate, 9 parts of fines of filling, 2 parts of coupling agent, 4 parts of auxiliary agent, 3 parts of toughener.
Preferably, the filling fines is calcium phosphate 3-5 parts, boron carbide 1-3 parts, chrome green 1-3 part components, is ground
The combination mixture crossed afterwards after 900-1000 mesh sieves.
Preferably, the coupling agent is zirconium ester coupling agent.
Preferably, the auxiliary agent is the mixture of catalyst and dispersant, and catalyst is sodium hydroxide solution, dispersant
For stearmide.
Preferably, the plasticizer is ATBC.
Preferably, the toughener is MBS.
A kind of preparation method of high intensity liquid detergent bottle, its processing step are as follows：
Step 1：It is standby by lead sulfate, lead stearate, the filling ground 800-900 mesh sieves of fines；
Step 2：Put into plastic raw materials, Tissuemat E in shearing equipment, and the abrasive added in step 1, coupling agent,
Auxiliary agent, toughener, under collective effect, when device temperature rises to 100-120 DEG C, it is thoroughly mixed, in rotating speed 1500-2000
Under rev/min rotating speed, 1-2h is handled, obtains compound；
Step 3：By obtained compound in step 2 beforehand through extruding machine extrusion moulding；
Step 4：The raw material of extrusion moulding is put into blow moulding machine, blow molding passes sequentially through bottle blowing, prolongs modeling, cooling and pressurize
Process is completed；
Step 5：By the liquid detergent bottle after being cooled down in step 4 by manually carrying out flash polishing；
Step 6：The good liquid detergent bottle of film will be played to be sent at side leakage machine, check whether the sealing of liquid detergent bottle is intact.
Beneficial effect is：Mixed by plastic raw materials with Tissuemat E collocation, in addition lead sulfate, lead stearate, filling
Fines strengthens the intensity of liquid detergent bottle so that liquid detergent bottle impact resistance strengthens, and the liquid detergent bottle of high-intensity performance is advantageous to
Production and sales use.
Embodiment
Embodiment 1
The invention discloses a kind of environment-friendly type liquid detergent bottle, constitutive material component by weight is divided into：60 parts of plastic raw materials, polyethylene
15 parts of wax, 1.2 parts of lead sulfate, 1 part of lead stearate, 8 parts of fines of filling, 1 part of coupling agent, 3 parts of auxiliary agent, 2 parts of toughener.
The filling fines is 1 part of 3 parts of calcium phosphate, 1 part of boron carbide, chrome green component, after crossing 900 mesh sieves after grinding
Combination mixture.
The coupling agent is zirconium ester coupling agent.
The auxiliary agent is the mixture of catalyst and dispersant, and catalyst is sodium hydroxide solution, and dispersant is tristearin
Acid amides.
The plasticizer is ATBC.
The toughener is MBS.
A kind of preparation method of high intensity liquid detergent bottle, its processing step are as follows：
Step 1：It is standby by lead sulfate, lead stearate, filling ground 800 mesh sieve of fines；
Step 2：Put into plastic raw materials, Tissuemat E in shearing equipment, and the abrasive added in step 1, coupling agent,
Auxiliary agent, toughener, under collective effect, when device temperature rises to 100 DEG C, it is thoroughly mixed, in rotating speed, 1500 revs/min turn
Under speed, 1h is handled, obtains compound；
Step 3：By obtained compound in step 2 beforehand through extruding machine extrusion moulding；
Step 4：The raw material of extrusion moulding is put into blow moulding machine, blow molding passes sequentially through bottle blowing, prolongs modeling, cooling and pressurize
Process is completed；
Step 5：By the liquid detergent bottle after being cooled down in step 4 by manually carrying out flash polishing；
Step 6：The good liquid detergent bottle of film will be played to be sent at side leakage machine, check whether the sealing of liquid detergent bottle is intact.
Embodiment 2
The invention discloses a kind of environment-friendly type liquid detergent bottle, constitutive material component by weight is divided into：Constitutive material component by weight
It is divided into：65 parts of plastic raw materials, 17 parts of Tissuemat E, 1.4 parts of lead sulfate, 1.1 parts of lead stearate, 9 parts of fines of filling, coupling agent 2
Part, 4 parts of auxiliary agent, 3 parts of toughener.
The filling fines is 2 parts of 4 parts of calcium phosphate, 2 parts of boron carbide, chrome green components, after crossing 950 mesh sieves after grinding
Combination mixture.
The coupling agent is zirconium ester coupling agent.
The auxiliary agent is the mixture of catalyst and dispersant, and catalyst is sodium hydroxide solution, and dispersant is tristearin
Acid amides.
The plasticizer is ATBC.
The toughener is MBS.
A kind of preparation method of high intensity liquid detergent bottle, its processing step are as follows：
Step 1：It is standby by lead sulfate, lead stearate, filling ground 850 mesh sieve of fines；
Step 2：Put into plastic raw materials, Tissuemat E in shearing equipment, and the abrasive added in step 1, coupling agent,
Auxiliary agent, toughener, under collective effect, when device temperature rises to 110 DEG C, it is thoroughly mixed, in rotating speed, 1800 revs/min turn
Under speed, 1.5h is handled, obtains compound；
Step 3：By obtained compound in step 2 beforehand through extruding machine extrusion moulding；
Step 4：The raw material of extrusion moulding is put into blow moulding machine, blow molding passes sequentially through bottle blowing, prolongs modeling, cooling and pressurize
Process is completed；
Step 5：By the liquid detergent bottle after being cooled down in step 4 by manually carrying out flash polishing；
Step 6：The good liquid detergent bottle of film will be played to be sent at side leakage machine, check whether the sealing of liquid detergent bottle is intact.
Embodiment 3
The invention discloses a kind of environment-friendly type liquid detergent bottle, constitutive material component by weight is divided into：70 parts of plastic raw materials, polyethylene
19 parts of wax, 1.6 parts of lead sulfate, 1.2 parts of lead stearate, 10 parts of fines of filling, 3 parts of coupling agent, 5 parts of auxiliary agent, 4 parts of toughener.
The filling fines is 3 parts of 5 parts of calcium phosphate, 3 parts of boron carbide, chrome green components, and 1000 mesh sieves are crossed after grinding
Combination mixture afterwards.
The coupling agent is zirconium ester coupling agent.
The auxiliary agent is the mixture of catalyst and dispersant, and catalyst is sodium hydroxide solution, and dispersant is tristearin
Acid amides.
The plasticizer is ATBC.
The toughener is MBS.
A kind of preparation method of high intensity liquid detergent bottle, its processing step are as follows：
Step 1：It is standby by lead sulfate, lead stearate, filling ground 900 mesh sieve of fines；
Step 2：Put into plastic raw materials, Tissuemat E in shearing equipment, and the abrasive added in step 1, coupling agent,
Auxiliary agent, toughener, under collective effect, when device temperature rises to 120 DEG C, it is thoroughly mixed, in rotating speed, 2000 revs/min turn
Under speed, 2h is handled, obtains compound；
Step 3：By obtained compound in step 2 beforehand through extruding machine extrusion moulding；
Step 4：The raw material of extrusion moulding is put into blow moulding machine, blow molding passes sequentially through bottle blowing, prolongs modeling, cooling and pressurize
Process is completed；
Step 5：By the liquid detergent bottle after being cooled down in step 4 by manually carrying out flash polishing；
Step 6：The good liquid detergent bottle of film will be played to be sent at side leakage machine, check whether the sealing of liquid detergent bottle is intact.
Finally it should be noted that：Above example only not limits technology described in the invention to illustrate the present invention
Scheme；Therefore, although this specification with reference to above-mentioned each embodiment to present invention has been detailed description, this
Field it is to be appreciated by one skilled in the art that still can be modified to the present invention or equivalent substitution；And all do not depart from this
The technical scheme of the spirit and scope of invention and its improvement, it all should cover in scope of the presently claimed invention.
Claims (7)
1. a kind of high intensity liquid detergent bottle, it is characterised in that constitutive material component by weight is divided into：Plastic raw materials 60-70 parts, gather
Ethylene waxes 15-19 parts, lead sulfate 1.2-1.6 parts, lead stearate 1-1.2 parts, filling fines 8-10 parts, coupling agent 1-3 parts, auxiliary agent
3-5 parts, toughener 2-4 parts.
2. according to a kind of environment-friendly type liquid detergent bottle of claim 1, it is characterised in that a kind of high intensity liquid detergent bottle, constitutive material
Component is divided into by weight：65 parts of plastic raw materials, 17 parts of Tissuemat E, 1.4 parts of lead sulfate, 1.1 parts of lead stearate, filling fines 9
Part, 2 parts of coupling agent, 4 parts of auxiliary agent, 3 parts of toughener.
3. according to a kind of environment-friendly type liquid detergent bottle of claim 1, it is characterised in that the filling fines is calcium phosphate 3-5 parts, carbon
Change boron 1-3 parts, chrome green 1-3 part components, the combination mixture crossed after grinding after 900-1000 mesh sieves.
4. according to a kind of environment-friendly type liquid detergent bottle of claim 1, it is characterised in that the coupling agent is zirconium ester coupling agent.
5. according to a kind of environment-friendly type liquid detergent bottle of claim 1, it is characterised in that the auxiliary agent is the mixed of catalyst and dispersant
Compound, and catalyst is sodium hydroxide solution, dispersant is stearmide.
6. according to a kind of environment-friendly type liquid detergent bottle of claim 1, it is characterised in that the toughener be methyl methacrylate-
BS.
7. a kind of preparation method of high intensity liquid detergent bottle, it is characterised in that its processing step is as follows：
Step 1：It is standby by lead sulfate, lead stearate, the filling ground 800-900 mesh sieves of fines；
Step 2：Put into plastic raw materials, Tissuemat E in shearing equipment, and the abrasive added in step 1, coupling agent,
Auxiliary agent, toughener, under collective effect, when device temperature rises to 100-120 DEG C, it is thoroughly mixed, in rotating speed 1500-2000
Under rev/min rotating speed, 1-2h is handled, obtains compound；
Step 3：By obtained compound in step 2 beforehand through extruding machine extrusion moulding；
Step 4：The raw material of extrusion moulding is put into blow moulding machine, blow molding passes sequentially through bottle blowing, prolongs modeling, cooling and pressurize
Process is completed；
Step 5：By the liquid detergent bottle after being cooled down in step 4 by manually carrying out flash polishing；
Step 6：The good liquid detergent bottle of film will be played to be sent at side leakage machine, check whether the sealing of liquid detergent bottle is intact.