CN107721294A - Sandwich benzene board compound wall - Google Patents
Sandwich benzene board compound wall Download PDFInfo
- Publication number
- CN107721294A CN107721294A CN201710819441.8A CN201710819441A CN107721294A CN 107721294 A CN107721294 A CN 107721294A CN 201710819441 A CN201710819441 A CN 201710819441A CN 107721294 A CN107721294 A CN 107721294A
- Authority
- CN
- China
- Prior art keywords
- parts
- sandwich
- wall
- board compound
- benzene board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Sandwich benzene board compound wall, is related to combined wall technical field；Sandwich benzene board compound wall of the present invention is made up of exterior wall, benzene plate and interior wall, and exterior wall is by portland cement, polyacrylic resin, lignocellulosic, cellulose ether, animal bone powder, titanium dioxide, bentonite, polyurethane and water；Exterior wall of the present invention has stronger toughness, and sturdy and durable, material is light, and waterproof fireproofing, heat-proof quality is strong, easy for construction, and various aspects of performance is superior to Sandwich benzene board compound wall of the prior art.
Description
Technical field
The present invention relates to combined wall technical field, especially a kind of Sandwich benzene board compound wall.
Background technology
Sandwich benzene board compound wall, typically it is combined, is had by clay brick, polystyrene foam plate, hollow cinder brick
Heat transfer coefficient is reduced, thermal resistance is improved, reduces the characteristics of construction costs；However, existing Sandwich benzene board compound wall still suffers from one
A little shortcomings, such as：Clay brick robustness and water proofing property are poor, and the combination property of its wall filler is poor, and construction is loaded down with trivial details, with wall
Combination it is not close, the adaptability of hollow cinder brick and steelframe is poor, ventilative to leak out, and water absorption rate is high, and whole Sandwich benzene board is answered
There is also the problem of robustness and less stable in itself for the structure of conjunction wall.
The content of the invention
It is an object of the invention to provide a kind of Sandwich benzene board compound wall, this Sandwich benzene board compound wall can solve existing
There is the problem of wall robustness is poor.
In order to solve the above problems, the technical solution adopted by the present invention is：
A kind of this Sandwich benzene board compound wall is made up of exterior wall, benzene plate and interior wall, exterior wall by following parts by weight raw material system
It is standby to form：30~50 parts of portland cements, 2~3.5 parts of polyacrylic resins, 2~3 parts of lignocellulosics, 1.5~3.5 parts of fibres
Tie up plain ether, 2~5 parts of animal bone powders, 0.5~2 part of titanium dioxide, 5~10 parts of bentonites, 1~3 part of polyurethane, 10~16 parts of water.
In above-mentioned technical proposal, more specifically technical scheme can also be：Cellulose ether is methylcellulose or hydroxyl second
Ylmethyl cellulose.
Further, the viscosity of cellulose ether is 50000mpas~65000mpas.
Further, exterior wall is prepared by the raw material of following parts by weight：30 parts of portland cements, 2 parts of polyacrylic acid
Resin, 2 parts of lignocellulosics, 1.5 parts of cellulose ethers, 2 parts of animal bone powders, 0.5 part of titanium dioxide, 5 parts of bentonites, 3 parts of polyurethane,
10 parts of water.
Further, exterior wall is prepared by the raw material of following parts by weight：40 parts of portland cements, 3.5 parts of polypropylene
Acid resin, 3 parts of lignocellulosics, 2 parts of cellulose ethers, 3 parts of animal bone powders, 2 parts of titanium dioxides, 10 parts of bentonites, 2 parts of polyurethane,
16 parts of water.
Further, exterior wall is prepared by the raw material of following parts by weight：50 parts of portland cements, 3 parts of polyacrylic acid
Resin, 2.5 parts of lignocellulosics, 3.5 parts of cellulose ethers, 5 parts of animal bone powders, 1 part of titanium dioxide, 7.5 parts of bentonites, 1 part of poly- ammonia
Ester, 13 parts of water.
By adopting the above-described technical solution, the present invention has the advantages that compared with prior art：
Sandwich benzene board compound wall of the present invention is made up of exterior wall, benzene plate and interior wall, and exterior wall is by portland cement, polyacrylic acid tree
Fat, lignocellulosic, cellulose ether, animal bone powder, titanium dioxide, bentonite, polyurethane and water；Exterior wall of the present invention has stronger
Toughness, sturdy and durable, material is light, and waterproof fireproofing, heat-proof quality is strong, easy for construction, and various aspects of performance is superior to prior art
In Sandwich benzene board compound wall.
Embodiment
With reference to embodiment, the invention will be further described：
Embodiment 1
The present embodiment Sandwich benzene board compound wall is made up of exterior wall, benzene plate and interior wall, exterior wall by following parts by weight raw material system
It is standby to form：30 parts of portland cements, 2 parts of polyacrylic resins, 2 parts of lignocellulosics, 1.5 parts of methylcellulose, 2 parts of Animal Bones
Powder, 0.5 part of titanium dioxide, 5 parts of bentonites, 3 parts of polyurethane, 10 parts of water；The viscosity of the present embodiment methylcellulose is
50000mpa·s。
Embodiment 2
The present embodiment Sandwich benzene board compound wall is made up of exterior wall, benzene plate and interior wall, exterior wall by following parts by weight raw material system
It is standby to form：40 parts of portland cements, 3.5 parts of polyacrylic resins, 3 parts of lignocellulosics, 2 parts of methylcellulose, 3 parts of Animal Bones
Powder, 2 parts of titanium dioxides, 10 parts of bentonites, 2 parts of polyurethane, 16 parts of water, the viscosity of the present embodiment methylcellulose are
60000mpa·s。
Embodiment 3
The present embodiment Sandwich benzene board compound wall is made up of exterior wall, benzene plate and interior wall, exterior wall by following parts by weight raw material system
It is standby to form：50 parts of portland cements, 3 parts of polyacrylic resins, 2.5 parts of lignocellulosics, 3.5 parts of hydroxyethylmethylcelluloses, 5
Part animal bone powder, 1 part of titanium dioxide, 7.5 parts of bentonites, 1 part of polyurethane, 13 parts of water；The present embodiment hydroxyethylmethylcellulose
Viscosity is 65000mpas.
The bending strength and impact strength of Sandwich benzene board compound wall prepared by embodiment 1~3 are detected, testing result is shown in Table
1：
The intensity of the Sandwich benzene board compound wall of table 1
Claims (6)
1. a kind of Sandwich benzene board compound wall, it is characterised in that the Sandwich benzene board compound wall is by exterior wall, benzene plate and interior wall group
Into the exterior wall is prepared by the raw material of following parts by weight：30~50 parts of portland cements, 2~3.5 parts of polyacrylic acid trees
Fat, 2~3 parts of lignocellulosics, 1.5~3.5 parts of cellulose ethers, 2~5 parts of animal bone powders, 0.5~2 part of titanium dioxide, 5~10 parts
Bentonite, 1~3 part of polyurethane, 10~16 parts of water.
2. the cellulose ether according to claim 1 is methylcellulose or hydroxyethylmethylcellulose.
3. Sandwich benzene board compound wall according to claim 1 or 2, it is characterised in that the viscosity of the cellulose ether is
50000mpas~65000mpas.
4. Sandwich benzene board compound wall according to claim 1, it is characterised in that the exterior wall is by following parts by weight
Raw material is prepared：30 parts of portland cements, 2 parts of polyacrylic resins, 2 parts of lignocellulosics, 1.5 parts of cellulose ethers, 2 parts dynamic
Thing bone meal, 0.5 part of titanium dioxide, 5 parts of bentonites, 3 parts of polyurethane, 10 parts of water.
5. Sandwich benzene board compound wall according to claim 1, it is characterised in that the exterior wall is by following parts by weight
Raw material is prepared：40 parts of portland cements, 3.5 parts of polyacrylic resins, 3 parts of lignocellulosics, 2 parts of cellulose ethers, 3 parts dynamic
Thing bone meal, 2 parts of titanium dioxides, 10 parts of bentonites, 2 parts of polyurethane, 16 parts of water.
6. Sandwich benzene board compound wall according to claim 1, it is characterised in that the exterior wall is by following parts by weight
Raw material is prepared：50 parts of portland cements, 3 parts of polyacrylic resins, 2.5 parts of lignocellulosics, 3.5 parts of cellulose ethers, 5 parts
Animal bone powder, 1 part of titanium dioxide, 7.5 parts of bentonites, 1 part of polyurethane, 13 parts of water.