CN107721185A - A kind of preparation technology for the safety glass that can be imaged - Google Patents
A kind of preparation technology for the safety glass that can be imaged Download PDFInfo
- Publication number
- CN107721185A CN107721185A CN201710004540.0A CN201710004540A CN107721185A CN 107721185 A CN107721185 A CN 107721185A CN 201710004540 A CN201710004540 A CN 201710004540A CN 107721185 A CN107721185 A CN 107721185A
- Authority
- CN
- China
- Prior art keywords
- glass
- nano particle
- heated
- preparation technology
- particle implantation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation technology for the safety glass that can be imaged, it is related to the preparing technical field of glass.Nano particle implantation is entered by nanometer implanted prosthetics first in glass deep layer, specific nano particle implantation process is:After first glass is heated 23 hours in 180 DEG C of 200 DEG C of high temperature, after then glass is cooled down, inside glass produces cellular Fine holes, and now nano particle implantation is entered;Then glass is heated to 650 DEG C 700 DEG C, in glass surface spraying, showering optics raw material, is sprayed again after glass is heated, the light transmittance of glass can be increased.This technique is by nanometer technology, fuel factor implanted prosthetics and anti-oxidation tech, high temperature resistant paint vehicle technology is combined into one, preparation technology is simple, and cost is low, and it is good that the safety glass of the imaging prepared penetrates light enhancing effect, three-dimensional imaging performance is strong, 180 degree visible angle can be reached, picture reproduction color and luster saturation degree is preferable, and glass transparent degree is preferable.
Description
Technical field
A kind of preparation technology for the safety glass being imaged the present invention relates to energy, belong to the preparing technical field of glass.
Background technology
At present, the glassware that glass processing field typically processes is by carrying specific pattern in glass article surface printing
The pattern of shape, but it the defects of be that thickness sense is not strong, simple plane visual effect can only be showed.
In recent years, the typography of glass prints the plane pattern of special pattern just for glass surface, can not meet
Manufacture the technological requirement of three-dimensional imaging glass.And the glass of planar imaging is not very superior in eyeshield field, therefore need
Study the technique that a kind of technique is simple and can produce the good three-dimensional imaging glass of eyeshield effect.
The content of the invention
In view of the above-mentioned problems, the technical problem to be solved in the present invention is to provide a kind of preparation method is simple, and prepare
Safety glass can not only realize the function of three-dimensional imaging, the performance also very superior glass preparation technique in eyeshield field.
The preparation technology of the safety glass that can be imaged of the present invention is:Step 1:Pass through nanometer in glass deep layer first
Implanted prosthetics enters nano particle implantation, and specific nano particle implantation process is:First by glass in 180 DEG C of -200 DEG C of high temperature
After middle heating 2-3 hours, after then glass is cooled down, inside glass produces cellular Fine holes, now by nano particle be implanted into
Go;
Step 2:Then glass is heated to 650 DEG C -700 DEG C, it is former in glass surface spraying, showering or silk-screen optics
Material, sprayed again after glass is heated, the light transmittance of glass can be increased.
Beneficial effects of the present invention:It can overcome the drawbacks of prior art, and nanometer technology, fuel factor are implanted into by this technique
Technology and anti-oxidation tech, high temperature resistant paint vehicle technology are combined into one, and preparation technology is simple, and cost is low, the imaging prepared
Safety glass penetrates that light enhancing effect is good, and three-dimensional imaging performance is strong, can reach 180 degree visible angle, and picture reappears color and luster saturation degree
Preferably, glass transparent degree is preferable.
Brief description of the drawings:
For ease of explanation, the present invention is described in detail by following specific implementations and accompanying drawing.
Fig. 1 is the structural representation of the curved steel glass of imaging prepared by the present invention.
Embodiment:
Present embodiment uses following technical scheme:Step 1:Will by nanometer implanted prosthetics first in glass deep layer
Nano particle implantation is entered, and specific nano particle implantation process is:Glass is first heated into 2-3 in 180 DEG C of -200 DEG C of high temperature
After hour, after then glass is cooled down, inside glass produces cellular Fine holes, and now nano particle implantation is entered;
Step 2:Then glass is heated to 650 DEG C -700 DEG C, it is former in glass surface spraying, showering or silk-screen optics
Material, sprayed again after glass is heated, the light transmittance of glass can be increased.
Embodiment 1:Nano particle implantation is entered by nanometer implanted prosthetics in glass deep layer, specific nano particle
Implantation process is:After first glass is heated 3 hours in 200 DEG C of high temperature, after then glass is cooled down, inside glass produces honeycomb
Formula Fine holes, now nano particle implantation is entered;Then glass is heated to 700 DEG C, light is sprayed in glass surface
It can be the plastic safety glass that can be imaged, the safety glass that this embodiment is prepared and common imaging afterwards to learn raw material
Glass carries out transparency difference pictures contrast, and the two difference transparency is 88 to 92=95.6%, it can be seen that this implementation
Glass transparent degree prepared by example is stronger.
Embodiment 2:Glass is first molded into curved steel glass, then in glass deep layer by nanometer implanted prosthetics by nanometer
Particle implantation is entered, and specific nano particle implantation process is:After first glass is heated 2 hours in 180 DEG C of high temperature, then will
After glass cooling, inside glass produces cellular Fine holes, and now nano particle implantation is entered;Then glass is heated and risen
Temperature sprays the curved steel safety glass that optics raw material can be plastic energy imaging afterwards, the institute of reference picture 1 to 680 DEG C, in glass surface
Show, described curved steel safety glass can reach 180 degree visible angle.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
- A kind of 1. preparation technology for the safety glass that can be imaged, it is characterised in that:It is concretely comprised the following steps:First in glass deep layer Nano particle implantation is entered by nanometer implanted prosthetics, specific nano particle implantation process is:First by glass 180 DEG C- After heating 2-3 hours in 200 DEG C of high temperature, after then glass is cooled down, inside glass produces cellular Fine holes, now by nanometer Grain implantation is entered;Step 2:Then glass is heated to 650 DEG C -700 DEG C, will in glass surface spraying, showering optics raw material Sprayed again after glass heating, the light transmittance of glass can be increased.
- 2. according to a kind of preparation technology of safety glass that can be imaged described in claim 1, it is characterised in that:Described step Glass surface spraying described in two, showering optics raw material can be replaced described glass surface silk-screen optics raw material.