CN107703565A - A kind of anti-high-energy gold-tinted resin lens and its production method - Google Patents
A kind of anti-high-energy gold-tinted resin lens and its production method Download PDFInfo
- Publication number
- CN107703565A CN107703565A CN201710661012.2A CN201710661012A CN107703565A CN 107703565 A CN107703565 A CN 107703565A CN 201710661012 A CN201710661012 A CN 201710661012A CN 107703565 A CN107703565 A CN 107703565A
- Authority
- CN
- China
- Prior art keywords
- tinted
- resin
- grams
- hours
- gold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of anti-high-energy gold-tinted blue light resin lens and its production method, it is by weight, composed of the following components:Resin monomer brominated bisphenol-A diacrylate or 985 991 grams of thio polyurethanes, 0.4 2.0 grams of resin catalyst, 13 grams of resin releasing agent, 7 12 grams of ultraviolet absorber, anti-4 15 milligrams of high energy gold-tinted absorbent.The present invention, detected using ultraviolet specrophotometer UV 2550, high energy gold-tinted 585nm transmitances are down to 30% 70%, it is seen that transmittance reaches 75% 95%, has stronger absorption to 585nm or so high-energy gold-tinted.
Description
Technical field
The invention belongs to eyeglass manufacturing technology field, and in particular to a kind of producer of anti-high-energy gold-tinted resin lens
Method.
Background technology
Correlative study shows, 585nm or so high-energy gold-tinted can cause eyeball ARM, mesh under directly acting on for a long time
The preceding field functional lens are still in space state, therefore it is very to develop a kind of functional health eyeglass for possessing anti-high energy gold-tinted
It is necessary.
The content of the invention
The defects of being existed according to prior art, the present invention propose a kind of anti-high-energy gold-tinted blue light resin lens and its production
Method, the resin lens have absorption to 585nm or so high-energy gold-tinted.
The technical scheme is that be accomplished by the following way:A kind of anti-high-energy gold-tinted blue light resin lens, with
Weight meter, it is composed of the following components:Resin monomer brominated bisphenol-A diacrylate or 985-991 grams of thio polyurethanes, resin
0.4-2.0 grams of catalyst, 1-3 grams of resin releasing agent, 7-12 grams of ultraviolet absorber, anti-high energy gold-tinted absorbent 4-15 milligrams.
Described resin monomer is brominated bisphenol-A diacrylate or thio polyurethane.
Described resin catalyst is dibutyltin dichloride, 1,1- di-t-butyl peroxies -3,3,5- front three basic rings
Hexane or ABVN.
Described resin releasing agent is that organic silicone oil or acidity are even for acid esters.
Described ultraviolet absorber is 2-(2- hydroxyl -5- t-octyl phenyl)BTA or 2-(The tert-butyl group of 2- hydroxyls-3-
5 aminomethyl phenyls)- 5- chlorinated benzotriazoles.
Described anti-high-energy gold-tinted absorbent is copper phthalocyanine blue.
The production method of the present invention comprises the following steps:
1), by resin monomer brominated bisphenol-A diacrylate or 985-991 grams of thio polyurethanes, resin catalyst 0.4-2.0
Gram, 1-3 grams of resin releasing agent, 7-12 grams of ultraviolet absorber, anti-high energy gold-tinted absorbent 4-15 milligrams be proportionally added into sealing
In reactor, fall air using dry nitrogen displacement, form composition;
2), mixed 1 ~ 3 hour at 10-25 DEG C of technological temperature after, degassing is vacuumized to -0.01MPa, after 30-45 minutes
Above-mentioned composition is forced into 0.10---0.25Mpa, is filled to what is fixed with adhesive tape after being filtered with 0.5-5 micron filters
In glass mold, the mould filled is put into progress polymerisation in baking oven;
The reaction temperature of described polymerisation, reaction time is:1)- 35 DEG C of room temperature, 0.5 hour; 2)35 DEG C, 1 hour;3)
35 DEG C -40 DEG C, 2 hours;4)40 DEG C -60 DEG C, 3 hours;5)60 DEG C, 4 hours;6)60 DEG C -120 DEG C, 7 hours;7)120℃、2
Hour;8)120 DEG C -70 DEG C, 1 hour;
3), glass mold is removed when being down to 70 DEG C of temperature, resulting eyeglass carries out annealing stress-removal at a temperature of 120 DEG C
Processing;
4), combine to be heating and curing using dip-coating, spin coating or spraying method the thick stiffened coating of 0.5-5 microns formed on eyeglass;
5), using vacuum coating technology lens surface plates antireflective, waterproof membrane forms anti-high-energy gold-tinted resin lens;
6), detection storage.
The present invention, detected using ultraviolet specrophotometer UV-2550, high energy gold-tinted 585nm transmitances are down to 30%-
70%, it is seen that transmittance reaches 75%-95%, has stronger absorption to 585nm or so high-energy gold-tinted.
Embodiment
Embodiment 1:
1st, anti-high-energy gold-tinted blue light resin lens, 1KG formulas:Thio 990 grams of polyurethane, catalyst dibutyltin dichloride 2
Gram, releasing agent it is acid even for 1 gram of acid esters, ultraviolet absorber 2-(The aminomethyl phenyl of -3 tert-butyl group of 2- hydroxyls -5)- 5- chloro benzos three
7 grams of azoles, anti-4.5 milligrams of high energy gold-tinted absorbent copper phthalocyanine blue.
2nd, production method:Add in the reactor of sealing after above-mentioned monomer is weighed by formula, put using dry nitrogen
Air is changed, after then being mixed 2 hours at 15 DEG C, degassing is vacuumized afterwards to -0.01MPa 30 minutes, is finally filled with
Air pressurized is filled to the glass molds fixed with adhesive tape after combinations of the above thing is filtered with 1 micron filter to 0.15Mpa
In tool, the mould filled is put into baking oven by following heating schedule progress polymerisation:
Reactions steps:Reaction temperature, reaction time is:1)- 35 DEG C of room temperature, 0.5 hour; 2)35 DEG C, 1 hour;3)35℃-40
DEG C, 2 hours;4)40 DEG C -60 DEG C, 3 hours;5)60 DEG C, 4 hours;6)60 DEG C -120 DEG C, 7 hours;7)120 DEG C, 2 hours;8)
120 DEG C -70 DEG C, 1 hour;
Then glass mold is removed at 70 DEG C, resulting eyeglass carries out stress-removal processing of annealing at a temperature of 120 DEG C.
Prepared eyeglass, through silane coupler containing hydrolysis on over cleaning and surface dip-coating, Ludox dispersion liquid
Coating simultaneously solidifies the stiffened film layer for obtaining 2.0 microns of thickness, lens surface is obtained containing silica using vacuum vapour deposition
With the anti-reflective film layer of zirconia film.
Performance test
3rd, performance measurement:Refractive index 1.558, abbe number 43, it is seen that transmittance 89.0%,
High energy gold-tinted 585nm transmitances 68%.
Embodiment 2:
1st, 1KG is formulated:985 grams of brominated bisphenol-A diacrylate gram, 0.5 gram of catalyst ABVN, releasing agent are acid
Occasionally for 3 grams of acid esters, ultraviolet absorber 2-(The aminomethyl phenyl of -3 tert-butyl group of 2- hydroxyls -5)12 grams of -5- chlorinated benzotriazoles, 585 anti-height
Can 10 milligrams of gold-tinted absorbent.
2nd, production method:Added after monomer is weighed by formula in the reactor of sealing, then mix 2 at room temperature
After hour, vacuum outgas afterwards 30 minutes, be finally filled with air pressurized to 0.2Mpa by combinations of the above thing with 1 micron filter
It is filled to after filtering in the glass mold fixed with adhesive tape, the mould filled is put into baking oven and carried out by following heating schedule
Polymerisation:
Reactions steps:Reaction temperature, reaction time is:1)- 35 DEG C of room temperature, 0.5 hour; 2)35 DEG C, 1 hour;3)35℃-40
DEG C, 2 hours;4)40 DEG C -60 DEG C, 3 hours;5)60 DEG C, 4 hours;6)60 DEG C -120 DEG C, 7 hours;7)120 DEG C, 2 hours;8)
120 DEG C -70 DEG C, 1 hour;
Then glass mold is removed at 70 DEG C, resulting eyeglass carries out stress-removal processing of annealing at a temperature of 120 DEG C.Institute
The eyeglass of preparation, through the silane coupler containing hydrolysis, the coating of Ludox dispersion liquid and solidification in over cleaning and surface dip-coating
The stiffened film layer of 2.0 microns of thickness is obtained, obtains lens surface using vacuum vapour deposition thin containing silica and zirconium oxide
The anti-reflective film layer of film.
3rd, performance measurement:Refractive index 1.597, abbe number 33, it is seen that transmittance 80%, high energy gold-tinted 585nm are saturating
Cross rate 35%.
Claims (7)
1. a kind of anti-high-energy gold-tinted blue light resin lens, by weight, composed of the following components:Resin monomer brominated bisphenol-A
Diacrylate or 985-991 grams of thio polyurethanes, 0.4-2.0 grams of resin catalyst, 1-3 grams of resin releasing agent, ultraviolet suction
Receive 7-12 grams of agent, anti-high energy gold-tinted absorbent 4-15 milligrams.
A kind of 2. anti-high-energy gold-tinted blue light resin lens according to claim 1, it is characterised in that:Described resin list
Body is brominated bisphenol-A diacrylate or thio polyurethane.
A kind of 3. anti-high-energy gold-tinted blue light resin lens according to claim 1, it is characterised in that:Described resin is urged
Agent is dibutyltin dichloride, 1,1- di-t-butyl peroxies -3,3,5- trimethyls thiacyclohexane or ABVN.
A kind of 4. anti-high-energy gold-tinted blue light resin lens according to claim 1, it is characterised in that:Described resin takes off
Mould agent is that organic silicone oil or acidity are even for acid esters.
Described ultraviolet absorber is 2-(2- hydroxyl -5- t-octyl phenyl)BTA or 2-(The first of -3 tert-butyl group of 2- hydroxyls -5
Base phenyl)- 5- chlorinated benzotriazoles.
A kind of 5. anti-high-energy gold-tinted blue light resin lens according to claim 1, it is characterised in that:Described anti-high energy
It is copper phthalocyanine blue to measure gold-tinted absorbent.
A kind of 6. method for producing the anti-high-energy gold-tinted blue light resin lens described in claim 1, it is characterised in that including such as
Lower step:
1), by resin monomer brominated bisphenol-A diacrylate or 985-991 grams of thio polyurethanes, resin catalyst 0.4-2.0
Gram, 1-3 grams of resin releasing agent, 7-12 grams of ultraviolet absorber, anti-high energy gold-tinted absorbent 4-15 milligrams be proportionally added into sealing
In reactor, fall air using dry nitrogen displacement, form composition;
2), mixed 1 ~ 3 hour at 10-25 DEG C of technological temperature after, degassing is vacuumized to -0.01MPa, after 30-45 minutes
Above-mentioned composition is forced into 0.10---0.25Mpa, is filled to what is fixed with adhesive tape after being filtered with 0.5-5 micron filters
In glass mold, the mould filled is put into progress polymerisation in baking oven;
The reaction temperature of described polymerisation, reaction time is:1)- 35 DEG C of room temperature, 0.5 hour; 2)35 DEG C, 1 hour;3)
35 DEG C -40 DEG C, 2 hours;4)40 DEG C -60 DEG C, 3 hours;5)60 DEG C, 4 hours;6)60 DEG C -120 DEG C, 7 hours;7)120℃、2
Hour;8)120 DEG C -70 DEG C, 1 hour;
3), glass mold is removed when being down to 70 DEG C of temperature, resulting eyeglass carries out annealing stress-removal at a temperature of 120 DEG C
Processing;
4), combine to be heating and curing using dip-coating, spin coating or spraying method the thick stiffened coating of 0.5-5 microns formed on eyeglass;
5), using vacuum coating technology lens surface plates antireflective, waterproof membrane forms anti-high-energy gold-tinted resin lens;
6), detection storage.
A kind of 7. production method of anti-high-energy gold-tinted blue light resin lens according to claim 6, it is characterised in that:Institute
The step 2 stated)In the reaction temperature of polymerisation, the reaction time be:1)- 35 DEG C of room temperature, 0.5 hour; 2)35 DEG C, it is 1 small
When;3)35 DEG C -40 DEG C, 2 hours;4)40 DEG C -60 DEG C, 3 hours;5)60 DEG C, 4 hours;6)60 DEG C -120 DEG C, 7 hours;7)
120 DEG C, 2 hours;8)120 DEG C -70 DEG C, 1 hour.