CN107699065A - A kind of composite coating of vacuum filter - Google Patents

A kind of composite coating of vacuum filter Download PDF

Info

Publication number
CN107699065A
CN107699065A CN201711087165.7A CN201711087165A CN107699065A CN 107699065 A CN107699065 A CN 107699065A CN 201711087165 A CN201711087165 A CN 201711087165A CN 107699065 A CN107699065 A CN 107699065A
Authority
CN
China
Prior art keywords
parts
vacuum filter
agent
composite coating
filter according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711087165.7A
Other languages
Chinese (zh)
Inventor
邵莹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711087165.7A priority Critical patent/CN107699065A/en
Publication of CN107699065A publication Critical patent/CN107699065A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of composite coating of vacuum filter, it is prepared by the component of following parts by weight：100 120 parts of Kynoar glue, 30 50 parts of modified high chlorinated polyethylene resin, 10 15 parts of turpentine oil, 140 58 parts of mesh mica powders, 35 parts of organosilicon fluorescein polymer, 35 parts of cellulose, 5 12 parts of corn flour, 12 parts of sulfide lime, 36 parts of diatomite, 0.5 1 parts of melamine, 12 parts of curing agent, 12 parts of adhesion promoter, viscosity adjusts 15 parts of solvent, 12 parts of dispersant, 12 parts of levelling agent, 12 parts of coupling agent, 12 parts of defoamer, 58 parts of auxiliary agent.The present invention selects rational raw material and proportioning, each raw material synergy, complements each other, and adhesive force is splendid, and closure is fabulous, and film is fine and close in neat formation, does not ftracture, does not rise swollen, resistance to corrosion-resistant, can extend the service life of vacuum filter.

Description

A kind of composite coating of vacuum filter
Technical field
The present invention relates to filter technical field, more particularly to a kind of composite coating of vacuum filter.
Background technology
Filter (pressure filter) is the equipment that separation of solid and liquid is realized using porous filter material.Filter Applied to departments such as chemical industry, oil, pharmacy, light industry, food, ore dressing, coal and water process.Filter is a kind of new filtering System, structure novelty, small volume, convenient and flexible operation, efficient, closed work, be strong applicability multipurpose filter plant.
The paper that ancient Chinese has made using filtering technique in production, B.C. 200 years existing strings, Christian era Cai Lun improves paper process within 105 years, and he swings process of plant fiber pulp on the thin bamboo curtain splint of densification in paper-making process, and water is through bamboo curtain splint Gap is filtered, and a thin layer wet pulp is stayed on bamboo curtain splint face, after doing paper.
Vacuum filter is that motive force of the negative pressure as filtering is formed at filtrate (liquid, existing vacuum filter, its Inner-wall paint uses common coating, and after long-term use, the easy aging of coating comes off, so as to cause filter plant by corrosion, contracting The short service life of vacuum filter.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of composite coating of vacuum filter.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of composite coating of vacuum filter, is prepared by the component of following parts by weight：Kynoar glue Liquid 100-120 parts, modified high chlorinated polyethylene resin 30-50 parts, turpentine oil 10-15 parts, 140 mesh mica powder 5-8 parts, organosilicon Fluorescein polymer 3-5 parts, cellulose 3-5 parts, corn flour 5-12 parts, sulfide lime 1-2 parts, diatomite 3-6 parts, melamine 0.5-1 parts, curing agent 1-2 parts, adhesion promoter 1-2 parts, viscosity adjustment solvent 1-5 parts, dispersant 1-2 parts, levelling agent 1-2 Part, coupling agent 1-2 parts, defoamer 1-2 parts, auxiliary agent 5-8 parts.
Further, the preferred weight number of each component is：110 parts of Kynoar glue, modified high chlorinated polyethylene 35 parts of resin, 12 parts of turpentine oil, 140 6 parts of mesh mica powders, 3 parts of organosilicon fluorescein polymer, 4 parts of cellulose, corn flour 10 Part, 1.5 parts of sulfide lime, 4 parts of diatomite, 0.8 part of melamine, 1 part of curing agent, 1 part of adhesion promoter, viscosity adjustment solvent 3 parts, 1 part of dispersant, 2 parts of levelling agent, 2 parts of coupling agent, 1 part of defoamer, 7 parts of auxiliary agent.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the viscosity adjustment solvent is toluene, dimethylbenzene, trimethylbenzene, butyl acetate, polyethylene glycol, dichloro It is one or more than one kinds of in ethane.
Further, the dispersant is lignin sulfonate, sulfonated polystyrene, PVP and poly- third Olefin(e) acid presses 6:5:2:1 ratio mixes.
Further, one kind that the levelling agent is selected in acrylic resin, Lauxite and melamine resin Or multiple combinations.
Further, the defoamer is Silica hydrogel.
Further, the auxiliary agent is that polymeric acrylic acid esters flow control agent and benzoin class degasser press 1:4 ratio Example mixes.
Beneficial effects of the present invention：The present invention selects rational raw material and proportioning, each raw material synergy, complements each other, Adhesive force is splendid, and closure is fabulous, and film is fine and close in neat formation, does not ftracture, does not rise swollen, resistance to corrosion-resistant, can extend vacuum filter Service life.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
A kind of composite coating of vacuum filter, is prepared by the component of following parts by weight：Kynoar glue 110 parts of liquid, 35 parts of modified high chlorinated polyethylene resin, 12 parts of turpentine oil, 140 6 parts of mesh mica powders, organosilicon fluorescein polymer 3 parts, 4 parts of cellulose, 10 parts of corn flour, 1.5 parts of sulfide lime, 4 parts of diatomite, 0.8 part of melamine, 1 part of curing agent, adhesive force 1 part of accelerator, viscosity 3 parts of solvent of adjustment, 1 part of dispersant, 2 parts of levelling agent, 2 parts of coupling agent, 1 part of defoamer, 7 parts of auxiliary agent.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the viscosity adjustment solvent is toluene, dimethylbenzene, trimethylbenzene, butyl acetate, polyethylene glycol, dichloro It is one or more than one kinds of in ethane.
Further, the dispersant is lignin sulfonate, sulfonated polystyrene, PVP and poly- third Olefin(e) acid presses 6:5:2:1 ratio mixes.
Further, one kind that the levelling agent is selected in acrylic resin, Lauxite and melamine resin Or multiple combinations.
Further, the defoamer is Silica hydrogel.
Further, the auxiliary agent is that polymeric acrylic acid esters flow control agent and benzoin class degasser press 1:4 ratio Example mixes.
Embodiment 2
A kind of composite coating of vacuum filter, is prepared by the component of following parts by weight：Kynoar glue 100 parts of liquid, 50 parts of modified high chlorinated polyethylene resin, 12 parts of turpentine oil, 140 7 parts of mesh mica powders, organosilicon fluorescein polymer 4 parts, 4 parts of cellulose, 10 parts of corn flour, 2 parts of sulfide lime, 4 parts of diatomite, 0.5 part of melamine, 1 part of curing agent, attachment is made every effort to promote Enter 1 part of agent, viscosity 1 part of solvent of adjustment, 2 parts of dispersant, 2 parts of levelling agent, 1 part of coupling agent, 1 part of defoamer, 6 parts of auxiliary agent.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the viscosity adjustment solvent is toluene, dimethylbenzene, trimethylbenzene, butyl acetate, polyethylene glycol, dichloro It is one or more than one kinds of in ethane.
Further, the dispersant is lignin sulfonate, sulfonated polystyrene, PVP and poly- third Olefin(e) acid presses 6:5:2:1 ratio mixes.
Further, one kind that the levelling agent is selected in acrylic resin, Lauxite and melamine resin Or multiple combinations.
Further, the defoamer is Silica hydrogel.
Further, the auxiliary agent is that polymeric acrylic acid esters flow control agent and benzoin class degasser press 1:4 ratio Example mixes.
Embodiment 3
A kind of composite coating of vacuum filter, is prepared by the component of following parts by weight：Kynoar glue 115 parts of liquid, 45 parts of modified high chlorinated polyethylene resin, 12 parts of turpentine oil, 140 6 parts of mesh mica powders, organosilicon fluorescein polymer 5 parts, 3 parts of cellulose, 8 parts of corn flour, 1 part of sulfide lime, 4 parts of diatomite, 0.8 part of melamine, 1 part of curing agent, attachment is made every effort to promote Enter 2 parts of agent, viscosity 4 parts of solvent of adjustment, 1 part of dispersant, 2 parts of levelling agent, 2 parts of coupling agent, 1 part of defoamer, 6 parts of auxiliary agent.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the viscosity adjustment solvent is toluene, dimethylbenzene, trimethylbenzene, butyl acetate, polyethylene glycol, dichloro It is one or more than one kinds of in ethane.
Further, the dispersant is lignin sulfonate, sulfonated polystyrene, PVP and poly- third Olefin(e) acid presses 6:5:2:1 ratio mixes.
Further, one kind that the levelling agent is selected in acrylic resin, Lauxite and melamine resin Or multiple combinations.
Further, the defoamer is Silica hydrogel.
Further, the auxiliary agent is that polymeric acrylic acid esters flow control agent and benzoin class degasser press 1:4 ratio Example mixes.
Embodiment 4
A kind of composite coating of vacuum filter, is prepared by the component of following parts by weight：Kynoar glue 120 parts of liquid, 45 parts of modified high chlorinated polyethylene resin, 12 parts of turpentine oil, 140 7 parts of mesh mica powders, organosilicon fluorescein polymer 4 parts, 4 parts of cellulose, 10 parts of corn flour, 2 parts of sulfide lime, 4 parts of diatomite, 0.9 part of melamine, 2 parts of curing agent, attachment is made every effort to promote Enter 1 part of agent, viscosity 3 parts of solvent of adjustment, 1 part of dispersant, 1 part of levelling agent, 2 parts of coupling agent, 1 part of defoamer, 6 parts of auxiliary agent.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the viscosity adjustment solvent is toluene, dimethylbenzene, trimethylbenzene, butyl acetate, polyethylene glycol, dichloro It is one or more than one kinds of in ethane.
Further, the dispersant is lignin sulfonate, sulfonated polystyrene, PVP and poly- third Olefin(e) acid presses 6:5:2:1 ratio mixes.
Further, one kind that the levelling agent is selected in acrylic resin, Lauxite and melamine resin Or multiple combinations.
Further, the defoamer is Silica hydrogel.
Further, the auxiliary agent is that polymeric acrylic acid esters flow control agent and benzoin class degasser press 1:4 ratio Example mixes.
Embodiment 5
A kind of composite coating of vacuum filter, is prepared by the component of following parts by weight：Kynoar glue 105 parts of liquid, 35 parts of modified high chlorinated polyethylene resin, 11 parts of turpentine oil, 140 6 parts of mesh mica powders, organosilicon fluorescein polymer 4 parts, 4 parts of cellulose, 7 parts of corn flour, 2 parts of sulfide lime, 4 parts of diatomite, 1 part of melamine, 2 parts of curing agent, adhesive force promotion 2 parts of agent, viscosity 1 part of solvent of adjustment, 2 parts of dispersant, 1 part of levelling agent, 1 part of coupling agent, 2 parts of defoamer, 5 parts of auxiliary agent.
Further, the curing agent is polymerization macromolecule amine reagent.
Further, the adhesion promoter is compound bifunctional silane.
Further, the viscosity adjustment solvent is toluene, dimethylbenzene, trimethylbenzene, butyl acetate, polyethylene glycol, dichloro It is one or more than one kinds of in ethane.
Further, the dispersant is lignin sulfonate, sulfonated polystyrene, PVP and poly- third Olefin(e) acid presses 6:5:2:1 ratio mixes.
Further, one kind that the levelling agent is selected in acrylic resin, Lauxite and melamine resin Or multiple combinations.
Further, the defoamer is Silica hydrogel.
Further, the auxiliary agent is that polymeric acrylic acid esters flow control agent and benzoin class degasser press 1:4 ratio Example mixes.
The general principle and principal character of the present invention has been shown and described above.It should be understood by those skilled in the art that The present invention is not limited to the above embodiments, merely illustrating the principles of the invention described in above-described embodiment and specification, Without departing from the spirit and scope, various changes and modifications of the present invention are possible, and these changes and improvements all fall Enter in scope of the claimed invention.The scope of the present invention is defined by the appended claims and its equivalents.

Claims (9)

1. a kind of composite coating of vacuum filter, it is characterised in that be prepared by the component of following parts by weight：It is poly- inclined PVF glue 100-120 parts, modified high chlorinated polyethylene resin 30-50 parts, turpentine oil 10-15 parts, 140 mesh mica powder 5-8 Part, organosilicon fluorescein polymer 3-5 parts, cellulose 3-5 parts, corn flour 5-12 parts, sulfide lime 1-2 parts, diatomite 3-6 parts, Melamine 0.5-1 parts, curing agent 1-2 parts, adhesion promoter 1-2 parts, viscosity adjustment solvent 1-5 parts, dispersant 1-2 parts, Levelling agent 1-2 parts, coupling agent 1-2 parts, defoamer 1-2 parts, auxiliary agent 5-8 parts.
A kind of 2. composite coating of vacuum filter according to claim 1, it is characterised in that each component it is preferred heavy Measuring number is：110 parts of Kynoar glue, 35 parts of modified high chlorinated polyethylene resin, 12 parts of turpentine oil, 140 mesh mica powders 6 Part, 3 parts of organosilicon fluorescein polymer, 4 parts of cellulose, 10 parts of corn flour, 1.5 parts of sulfide lime, 4 parts of diatomite, melamine 0.8 part, 1 part of curing agent, 1 part of adhesion promoter, viscosity 3 parts of solvent of adjustment, 1 part of dispersant, 2 parts of levelling agent, coupling agent 2 Part, 1 part of defoamer, 7 parts of auxiliary agent.
A kind of 3. composite coating of vacuum filter according to claim 1 or 2, it is characterised in that the curing agent For polymerization macromolecule amine reagent.
A kind of 4. composite coating of vacuum filter according to claim 1 or 2, it is characterised in that the adhesive force Accelerator is compound bifunctional silane.
5. the composite coating of a kind of vacuum filter according to claim 1 or 2, it is characterised in that the viscosity is adjusted Whole solvent is one or more than one kinds of in toluene, dimethylbenzene, trimethylbenzene, butyl acetate, polyethylene glycol, dichloroethanes.
A kind of 6. composite coating of vacuum filter according to claim 1 or 2, it is characterised in that the dispersant It is lignin sulfonate, sulfonated polystyrene, PVP and polyacrylic acid by 6:5:2:1 ratio mixing and Into.
A kind of 7. composite coating of vacuum filter according to claim 1 or 2, it is characterised in that the levelling agent Combined from the one or more in acrylic resin, Lauxite and melamine resin.
A kind of 8. composite coating of vacuum filter according to claim 1 or 2, it is characterised in that the defoamer For Silica hydrogel.
9. the composite coating of a kind of vacuum filter according to claim 1 or 2, it is characterised in that the auxiliary agent is Polymeric acrylic acid esters flow control agent and benzoin class degasser press 1:4 ratio mixes.
CN201711087165.7A 2017-11-07 2017-11-07 A kind of composite coating of vacuum filter Withdrawn CN107699065A (en)