CN107698216A - A kind of artificial stone - Google Patents
A kind of artificial stone Download PDFInfo
- Publication number
- CN107698216A CN107698216A CN201710902820.3A CN201710902820A CN107698216A CN 107698216 A CN107698216 A CN 107698216A CN 201710902820 A CN201710902820 A CN 201710902820A CN 107698216 A CN107698216 A CN 107698216A
- Authority
- CN
- China
- Prior art keywords
- parts
- artificial stone
- quartz
- hollow glass
- stone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of artificial stone, fraction proportioning by weight is made up of following components：80 93 parts of white cement, 15 21 parts of low-melting-point glass powder, 24 28 parts of Cab-O-sil, 77 83 parts of quartz sand, 11 22 parts of metakaolin, 22 35 parts of silica flour, 34 45 parts of silicon ash, 132 146 parts of quartz bits, 41 53 parts of water, 69 parts of water reducer, 35 parts of pigment.The advantage of the invention is that：The artificial stone of the present invention, by adding hollow glass microbead in being formulated in artificial stone grains, integrally reduces the relative density of artificial stone grains so that the quality of artificial stone grains is lighter.
Description
Technical field
The present invention relates to building material field, more particularly to a kind of artificial stone.
Background technology
With natural stone on the contrary, artificial stone refers to made stone material.Artificial stone（Such as artificial marble and artificial flower hilllock
Rock）It is used as outside or inside structural material.
Most representational artificial stone is gelling（cementitious）Artificial stone.The artificial stone manufacturing cost that is gelled is low, and
It is typically used as internal structure material
Gelling artificial stone include ground granite or other stone fragments, or a small amount of mirror is considered to be worth doing or chips of glass, and it is showed with this
Outward appearance.However, it is difficult to break away from terrazzo texture, therefore, it is difficult to provide the outward appearance of exclusive engineered stone.
In order to provide the aesthetic appearance of gelling artificial stone, it is necessary to use quartz.However, in the case where using quartz,
Due to the high intensity of quartz, quartz may separate from artificial stone.In addition, if the separation problem for solving quartz and incite somebody to action
The particle size of quartz sets the intensity decreases to 4mm or smaller, then artificial stone, and hair check is formed in artificial stone, and stone
English separation problem is not solved.As a result, it is impossible to show gelling using particle size is 2.5mm or smaller quartz
The outward appearance of artificial stone.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of artificial stone for preventing quartz bits separated.
In order to solve the above technical problems, the technical scheme is that：A kind of artificial stone, its innovative point are：Press
Weight fraction proportioning is made up of following components：
White cement 80-93 parts, pure acryl resin 23-43 parts, Cab-O-sil 24-28 parts, aluminium hydroxide 12-15 parts, metakaolin
11-22 parts, calcium carbonate 22-35 parts, silicon ash 34-45 parts, talcum powder 13-14 parts, water 41-53 parts, hollow glass microbead 6-10 parts,
Water reducer 6-9 parts, Composite acrylic resin 23-43 parts, pigment 3-5 parts, unsaturated-resin 23-43 parts.
Further, the particle size that has of quartz of stating is 0.3 to 4.0mm.
Further, granite is partly contained in the quartz bits.
Further, the compressive strength of the hollow glass microbead is in 25MPa-120MPa, the particle diameter of hollow glass microbead
For 10-100um.
The advantage of the invention is that：It is overall by adding hollow glass microbead in being formulated in artificial stone grains in the present invention
Reduce the relative density of artificial stone grains so that the quality of artificial stone grains is lighter.In addition, by being formulated in Engineered stone products
Middle addition and artificial stone grains similar in other mixed slurry relative densities.On the one hand, the density of Engineered stone products is reduced, is made
The quality for obtaining Engineered stone products is lighter；On the other hand, artificial stone grains and other slurry compatibilities are improved so that artificial stone produces
The intensity of product is higher, and end face is without lamination；And because artificial stone grains and other slurry compatibilities are relatively good so that artificial stone
The defects of appearance pore-free of product, pinprick, Engineered stone products' anti-pollution, chemical-resistance are improved, without increasing
Add face coat or gel coat, be easy to the shape-designing of Engineered stone products.
The artificial stone of the present invention, even if using the quartz with 4mm or smaller particle size, in this case it is still possible to change
The cohesive force entered between quartz bits and other components, so as to prevent quartz bits to be separated.Further, since there is low particle size
, the quartz bits that beautiful outward appearance can be provided can be in the manufacture of gelling artificial stone as single stone fragment, therefore
Artificial stone with engineered stone outward appearance can be manufactured with low price.Furthermore, it is possible to increase the density of artificial stone and
Bending rigidity and water absorption rate are improved, so as to improve the quality of artificial stone.
Embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among described scope of embodiments.
Embodiment 1
The artificial stone of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
80 parts of white cement, pure 23 parts of acryl resin, 24 parts of Cab-O-sil, 12 parts of aluminium hydroxide, 11 parts of metakaolin, calcium carbonate 22
Part, 34 parts of silicon ash, 13 parts of talcum powder, 41 parts of water, 6 parts of hollow glass microbead, 6 parts of water reducer, 23 parts of Composite acrylic resin, face
3 parts of material, 23 parts of unsaturated-resin.
In above-mentioned formula, the particle size that stating quartz has is 0.3 to 4.0mm, partly containing flower hilllock in quartz bits
Rock, in 25MPa-120MPa, the particle diameter of hollow glass microbead is 10-100um for the compressive strength of hollow glass microbead.
Embodiment 2
The artificial stone of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
93 parts of white cement, pure 43 parts of acryl resin, 28 parts of Cab-O-sil, 15 parts of aluminium hydroxide, 22 parts of metakaolin, calcium carbonate 35
Part, 45 parts of silicon ash, 14 parts of talcum powder, 53 parts of water, 10 parts of hollow glass microbead, 9 parts of water reducer, 43 parts of Composite acrylic resin,
5 parts of pigment, 43 parts of unsaturated-resin.
In above-mentioned formula, the particle size that stating quartz has is 0.3 to 4.0mm, partly containing flower hilllock in quartz bits
Rock, in 25MPa-120MPa, the particle diameter of hollow glass microbead is 10-100um for the compressive strength of hollow glass microbead.
Embodiment 3
The artificial stone of present invention fraction proportioning by weight is made up of following components：
Fraction proportioning by weight is made up of following components：
87 parts of white cement, pure 33 parts of acryl resin, 26 parts of Cab-O-sil, 13 parts of aluminium hydroxide, 17 parts of metakaolin, calcium carbonate 28
Part, 39 parts of silicon ash, 13 parts of talcum powder, 47 parts of water, 8 parts of hollow glass microbead, 7 parts of water reducer, 33 parts of Composite acrylic resin, face
4 parts of material, 33 parts of unsaturated-resin.
In above-mentioned formula, the particle size that stating quartz has is 0.3 to 4.0mm, partly containing flower hilllock in quartz bits
Rock, in 25MPa-120MPa, the particle diameter of hollow glass microbead is 10-100um for the compressive strength of hollow glass microbead.
By adding hollow glass microbead in being formulated in artificial stone grains, the relatively close of artificial stone grains is integrally reduced
Degree so that the quality of artificial stone grains is lighter.It is in addition, relative with other mixed slurries by being added in being formulated in Engineered stone products
The artificial stone grains of similar density.On the one hand, the density of Engineered stone products is reduced so that the quality of Engineered stone products is lighter；
On the other hand, artificial stone grains and other slurry compatibilities are improved so that the intensity of Engineered stone products is higher, and end face is without layering
Phenomenon；And because artificial stone grains and other slurry compatibilities are relatively good so that appearance pore-free, the pinprick of Engineered stone products
The defects of, Engineered stone products' anti-pollution, chemical-resistance are improved, without increase face coat or gel coat, is easy to
The shape-designing of Engineered stone products.
The artificial stone of the present invention, even if using the quartz with 4mm or smaller particle size, in this case it is still possible to change
The cohesive force entered between quartz bits and other components, so as to prevent quartz bits to be separated.Further, since there is low particle size
, the quartz bits that beautiful outward appearance can be provided can be in the manufacture of gelling artificial stone as single stone fragment, therefore
Artificial stone with engineered stone outward appearance can be manufactured with low price.Furthermore, it is possible to increase the density of artificial stone and
Bending rigidity and water absorption rate are improved, so as to improve the quality of artificial stone.
It should be understood by those skilled in the art that the present invention is not limited to the above embodiments, above-described embodiment and explanation
Merely illustrating the principles of the invention described in book, without departing from the spirit and scope of the present invention, the present invention also have
Various changes and modifications, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention
By appended claims and its equivalent thereof.
Claims (4)
- A kind of 1. artificial stone, it is characterised in that：Fraction proportioning by weight is made up of following components：White cement 80-93 parts, pure acryl resin 23-43 parts, Cab-O-sil 24-28 parts, aluminium hydroxide 12-15 parts, metakaolin 11-22 parts, calcium carbonate 22-35 parts, silicon ash 34-45 parts, talcum powder 13-14 parts, water 41-53 parts, hollow glass microbead 6-10 parts, Water reducer 6-9 parts, Composite acrylic resin 23-43 parts, pigment 3-5 parts, unsaturated-resin 23-43 parts.
- 2. artificial stone according to claim 1, it is characterised in that：The particle size that has of quartz of stating is 0.3 To 4.0mm.
- 3. artificial stone according to claim 1, it is characterised in that：Partly contain granite in the quartz bits Stone.
- 4. artificial stone according to claim 1, it is characterised in that：The compressive strength of the hollow glass microbead exists 25MPa-120MPa, the particle diameter of hollow glass microbead is 10-100um.