CN107696659A - A kind of manufacture craft of environmentally friendly laser transfer paper - Google Patents
A kind of manufacture craft of environmentally friendly laser transfer paper Download PDFInfo
- Publication number
- CN107696659A CN107696659A CN201711126666.1A CN201711126666A CN107696659A CN 107696659 A CN107696659 A CN 107696659A CN 201711126666 A CN201711126666 A CN 201711126666A CN 107696659 A CN107696659 A CN 107696659A
- Authority
- CN
- China
- Prior art keywords
- environmentally friendly
- transfer paper
- coated
- manufacture craft
- basement membranes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of manufacture craft of environmentally friendly laser transfer paper, pass through the improvement and innovation of technique, OPP film transfers technology and UV curing technologies are combined, make the laser information layer on OPP films be transferred to PET it is epilamellar it is photosensitive it is transfer coated on, avoid the caused deformation stretching due to hot press moulding of PET basement membranes, therefore PET basement membranes are physical diminishes, OPP films can be repeatedly utilized so that with PET basement membranes, the purpose of economical environment-protective is reached, the setting of aluminium lamination also makes environmentally friendly citicall limited aluminium paper possess metallic luster.
Description
Technical field
The present invention relates to field of packaging material, more particularly to a kind of manufacture craft of environmentally friendly laser transfer paper.
Background technology
Laser transfer paper is a kind of new, attractive in appearance packaging material, is shown with its advantage such as rich and varied, environmentally friendly, inexpensive
Good development prospect.Laser transfer paper is quite varied in the application of Yan Bao, cosmetic package, food packaging applications.
However, laser transfer paper in the market in manufacturing process, is bonded using PET basement membranes with high temperature nickel plate substantially
And the technique of laser effect is formed, cause the stretcher strain due to high temperature of PET basement membranes, destroy the substantially physical of PET basement membranes
Can so that PET basement membranes can not subsequently reuse and cause the wasting of resources.
The content of the invention
A kind of manufacture craft for environmentally friendly laser transfer paper that the purpose of the present invention is in view of the shortcomings of the prior art and provided,
It not only possesses the characteristics of existing laser transfer paper printing is good, light inexpensive, rich and varied, and has been also equipped with basement membrane physics
Deformation is small, it is repeatable utilize, the feature such as the simple, economical environment-protective of manufacturing process.
The object of the present invention is achieved like this：
A kind of environmentally friendly laser transfer paper is from top to bottom provided with photosensitive transfer coated, laser information layer, aluminium lamination and base paper, this
A kind of manufacture craft of environmentally friendly laser transfer paper of invention comprises the following steps：
Step 1：The pre- hot-rolling of die press, then passes through middle pressing mold pressure by preheated OPP films during OPP films are passed through
The radium-shine roller of machine is molded, and makes to form laser information layer on OPP films；
Step 2：PET basement membranes are coated with photosensitive transfer coatings by UV curing, formation is photosensitive transfer coated, will be coated with
There are photosensitive transfer coated PET basement membranes to dry in an oven；
Step 3：By on the epilamellar photosensitive transfer coated OPP films with step 1 of the PET after being dried in step 2
Laser information layer be bonded, so as to by laser information layer be transferred to it is photosensitive it is transfer coated on；
Step 4：By UV light source irradiated region of the PET basement membranes being bonded in step 3 with OPP films Jing Guo UV curing, make painting
Cloth is in the epilamellar photosensitive transfer coated solidifications of PET；
Step 5：OPP films are individually peeled off from being coated with photosensitive transfer coated PET basement membranes by stripping machine, and led to
Film rewinding machine is crossed to wind the OPP films stripped down；
Step 6：Be transferred to it is photosensitive it is transfer coated on laser information layer on aluminized by vacuum aluminum-plating machine, shape
Into aluminium lamination；
Step 7：Adhesive is coated in base paper on compounding machine, then by adhesive by the aluminium lamination in step 6
It is bonded with base paper, then is dried by baking oven；
Step 8：PET basement membranes are individually peeled off by stripping machine, PET basement membranes are wound using film rewinding operation machine and arranged, it is whole
PET basement membranes after reason are reused when making environmentally friendly laser transfer paper next time in step 2 into step 8.
A kind of manufacture craft of above-mentioned environmentally friendly laser transfer paper, wherein, have in the radium-shine roller in step 1 radium-shine
The design temperature of radium-shine roller in light beam effect and step 1 is 120 DEG C.
A kind of manufacture craft of above-mentioned environmentally friendly laser transfer paper, wherein, the design temperature of the pre- hot-rolling in step 1 is
100℃。
A kind of manufacture craft of above-mentioned environmentally friendly laser transfer paper, wherein, the start car of the middle die press in step 1
Speed is 40m/min.
A kind of manufacture craft of above-mentioned environmentally friendly laser transfer paper, wherein, the UV light sources in step 4 are UV lamp pipe；UV lamp
Tube current is 8A, and power 20kW, intensity 100W/cm, wavelength is between 150-300nm.
A kind of manufacture craft of above-mentioned environmentally friendly laser transfer paper, wherein, the OPP films stripped down in step 5 are in next time
Reused when making environmentally friendly laser transfer paper in step 1 into step 5.
A kind of manufacture craft of above-mentioned environmentally friendly laser transfer paper, wherein, by made from vacuum aluminum-plating machine in step 6
Aluminum layer thickness is 300-550 Ethylmercurichlorendimides.
A kind of manufacture craft of above-mentioned environmentally friendly laser transfer paper, wherein, the design temperature of the baking oven in step 7 is 80-
140 DEG C, baking oven is 4 section baking ovens or 5 section baking ovens.
OPP film transfers technology and UV curing technologies are combined, with existing skill by the present invention by the improvement and innovation of technique
Art is compared, in addition to common apparent and physicochemical property is maintained, also with manufacturing process is simple, basement membrane physical deformation is small, repeatable
The characteristics of using, economical environment-protective.
Brief description of the drawings
Fig. 1 is the structural representation of the environmentally friendly laser transfer paper made by the present invention.
Embodiment
Fig. 1 shows the structural representation of the environmentally friendly laser transfer paper made by the present invention, the environmentally friendly laser transfer paper
Including base paper 1, aluminium lamination 2, laser information layer 3 and photosensitive transfer coated 4；Base paper 1 is arranged on the lower surface of aluminium lamination 2；Aluminium lamination 2 is set
In the lower surface of laser information layer 3；Laser information layer 3 is arranged on photosensitive transfer coated 4 lower surface.
Below in conjunction with embodiment, a kind of manufacture craft of environmentally friendly laser transfer paper of the present invention is described further.
Embodiment 1
A kind of manufacture craft of environmentally friendly laser transfer paper comprises the following steps：
Step 1：The pre- hot-rolling of die press, makes OPP films have initial temperature, the setting of pre- hot-rolling during OPP films are passed through
Temperature is 100 DEG C, and then preheated OPP films are molded by the radium-shine roller of middle die press, make to be formed on OPP films
Laser information layer, it is 120 DEG C to have the design temperature of radium-shine light beam effect and radium-shine roller in radium-shine roller, middle die press
Start speed is 40m/min；
Step 2：PET basement membranes are coated with photosensitive transfer coatings by UV curing, formation is photosensitive transfer coated, will be coated with
There are photosensitive transfer coated PET basement membranes to dry in an oven；The line number of the anilox roll of UV curing is 300 mesh, and photosensitive transfer applies
The viscosity of material is 8 seconds (painting 4- cups, 25 DEG C), and photosensitive transfer coated coating dry measure is 1.8g/m2, the design temperature of baking oven is 80
℃；
Step 3：By on the epilamellar photosensitive transfer coated OPP films with step 1 of the PET after being dried in step 2
Laser information layer is in 5kg/cm2Pressure under be bonded, so as to by laser information layer be transferred to it is photosensitive it is transfer coated on；
Step 4：By UV light source irradiated region of the PET basement membranes being bonded in step 3 with OPP films Jing Guo UV curing, make painting
Cloth is in the epilamellar photosensitive transfer coated solidifications of PET；The UV lamp tube current of UV light sources is set as 8A, power 20kW, intensity
100W/cm, for wavelength between 150-300nm, the start speed of UV curing is 50m/min；
Step 5：OPP films are individually peeled off from being coated with photosensitive transfer coated PET basement membranes by stripping machine, and led to
Cross film rewinding machine to wind the OPP films stripped down, the OPP films stripped down make environmentally friendly laser transfer paper in next time
When reused in step 1 into step 5；
Step 6：Be transferred to it is photosensitive it is transfer coated on laser information layer on aluminized by vacuum aluminum-plating machine, shape
Into aluminium lamination, the thickness of aluminium lamination is 300-550 Ethylmercurichlorendimides；
Step 7：Adhesive is coated in base paper on compounding machine, then by adhesive by the aluminium lamination in step 6
It is bonded with base paper, then is dried by the baking oven of 4 to 5 sections；The design temperature of baking oven is 80-140 DEG C, the start car of compounding machine
Speed is 120m/min；
Step 8：PET basement membranes are individually peeled off by stripping machine, PET basement membranes are wound using film rewinding operation machine and arranged, it is whole
PET basement membranes after reason are reused when making environmentally friendly laser transfer paper next time in step 2 into step 8.
Beneficial effects of the present invention：
OPP film transfers technology and UV curing technologies are combined by the improvement and innovation of technique, make OPP films by the present invention
On laser information layer be transferred to PET it is epilamellar it is photosensitive it is transfer coated on, avoid PET basement membranes and produced due to hot press moulding
Deformation stretching, therefore PET basement membranes are physical diminishes, and OPP films can be repeatedly utilized so that with PET basement membranes, reach economical environment-protective
Purpose, the setting of aluminium lamination also make environmentally friendly citicall limited aluminium paper possess metallic luster.
Above example is used for illustrative purposes only, rather than limitation of the present invention, the technology people about technical field
Member, without departing from the spirit and scope of the present invention, can also make various conversion or modification, therefore all equivalent
Technical scheme should also belong to scope of the invention, should be limited by each claim.
Claims (8)
1. a kind of manufacture craft of environmentally friendly laser transfer paper, the environmentally friendly laser transfer paper is from top to bottom provided with photosensitive transfer and applied
Layer, laser information layer, aluminium lamination and base paper, it is characterised in that the manufacture craft of the environmentally friendly laser transfer paper comprises the following steps：
Step 1：The pre- hot-rolling of die press, then passes through middle die press by preheated OPP films during OPP films are passed through
Radium-shine roller is molded, and makes to form laser information layer on OPP films；
Step 2：PET basement membranes are coated with photosensitive transfer coatings by UV curing, formation is photosensitive transfer coated, is coated with feeling
The transfer coated PET basement membranes of light are dried in an oven；
Step 3：By the epilamellar photosensitive transfer coated OPP films with the step 1 of the PET after being dried in the step 2
On laser information layer fitting, so as to by laser information layer be transferred to it is photosensitive it is transfer coated on；
Step 4：By UV light source irradiated region of the PET basement membranes being bonded in the step 3 with OPP films Jing Guo UV curing, make painting
Cloth is in the epilamellar photosensitive transfer coated solidifications of PET；
Step 5：OPP films are individually peeled off from being coated with photosensitive transfer coated PET basement membranes by stripping machine, and by thin
Film rewinding machine is wound to the OPP films stripped down；
Step 6：Be transferred to it is photosensitive it is transfer coated on laser information layer on aluminized by vacuum aluminum-plating machine, form aluminium
Layer；
Step 7：Adhesive is coated in base paper on compounding machine, then by adhesive by the aluminium lamination in the step 6
It is bonded with base paper, then is dried by baking oven；
Step 8：PET basement membranes are individually peeled off by stripping machine, PET basement membranes are wound using film rewinding operation machine and arranged, after arrangement
PET basement membranes next time make the environmentally friendly laser transfer paper when, reused in the step 2 into step 8.
2. a kind of manufacture craft of environmentally friendly laser transfer paper as claimed in claim 1, it is characterised in that in the step 1
It is 100-150 DEG C to have the design temperature of radium-shine light beam effect and the radium-shine roller in the step 1 in radium-shine roller.
3. a kind of manufacture craft of environmentally friendly laser transfer paper as claimed in claim 1, it is characterised in that in the step 1
The design temperature of pre- hot-rolling is 100-150 DEG C.
4. a kind of manufacture craft of environmentally friendly laser transfer paper as claimed in claim 1, it is characterised in that in the step 1
The start speed of middle die press is 40m/min.
5. a kind of manufacture craft of environmentally friendly laser transfer paper as claimed in claim 1, it is characterised in that in the step 4
UV light sources are UV lamp pipe；The UV lamp tube current is 8A, power 20kW, intensity 100W/cm, wavelength be 150-300nm it
Between.
6. a kind of manufacture craft of environmentally friendly laser transfer paper as claimed in claim 1, it is characterised in that shelled in the step 5
Repeat to make into the step 5 in the step 1 when making the environmentally friendly laser transfer paper next time from the OPP films to get off
With.
7. a kind of manufacture craft of environmentally friendly laser transfer paper as claimed in claim 1, it is characterised in that lead in the step 6
It is 300-550 Ethylmercurichlorendimides to cross aluminum layer thickness made from vacuum aluminum-plating machine.
8. a kind of manufacture craft of environmentally friendly laser transfer paper as claimed in claim 1, it is characterised in that in the step 7
The design temperature of baking oven is 80-140 DEG C, and the baking oven is 4 section baking ovens or 5 section baking ovens.