CN107687111A - A kind of high intensity green and environmental protection paper and preparation method and application - Google Patents
A kind of high intensity green and environmental protection paper and preparation method and application Download PDFInfo
- Publication number
- CN107687111A CN107687111A CN201710665250.0A CN201710665250A CN107687111A CN 107687111 A CN107687111 A CN 107687111A CN 201710665250 A CN201710665250 A CN 201710665250A CN 107687111 A CN107687111 A CN 107687111A
- Authority
- CN
- China
- Prior art keywords
- paper
- environmental protection
- high intensity
- bamboo pulp
- pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of high intensity green and environmental protection paper and preparation method and application.The preparation method of described high intensity green and environmental protection paper is:To bamboo pulp raw material pulping, it is 30~50 ° of SR bamboo pulps to obtain beating degree;Then bamboo pulp or PLA fibers are pre-processed in cationic guar solution;Pretreated bamboo pulp and undressed PLA fibers, or undressed bamboo pulp and pretreated PLA fibers are pressed 7:3 absolute dry mass ratio is manufactured paper with pulp, you can obtains high intensity green and environmental protection paper.In the present invention, the pretreatment of cationic guar solution improves the fibre strength of bamboo fibre in itself, the chemical polarity of PLA fiber surfaces and interfibrous interface compatibility, the physical property of paper is significantly improved.What the present invention used is all green material, and obtained paper has higher intensity, can be applied to the various fields such as daily life paper, food wrapper well.
Description
Technical field
The invention belongs to technical field of preparation of specialty paper, and in particular to a kind of high intensity green and environmental protection paper and preparation method thereof
With application.
Background technology
PLA (PLA) fiber is a kind of conventional degradation material, it have good biocompatibility, glossiness, thoroughly
Characteristic, its applications such as bright property and heat endurance are more and more extensive.It is if directly fine using PLA using traditional papermaking process
Dimension production high-strength material, has larger cost advantage.But due to can not be formed between PLA fibers as string
Hydrogenbond, adhesion can not meet paper making requirement between PLA fibers, so being only not all right with PLA fiber copy papers.Plant
Fiber is the most abundant renewable environment-friendly materials of nature and cheap, also possesses very excellent biological degradability.If choosing
The bamboo fibre for selecting superior performance mixes with PLA fibers, can significantly improve the intensity of paper.But because PLA fiber surfaces are smooth, and
It is hydrophobic high molecular polymer, have impact on the biocompatibility of it and hydrophily bamboo fibre.Therefore, how to make PLA fibers with
Bamboo fibre preferably combines, it appears special important.
The content of the invention
To solve the shortcomings that prior art and weak point, primary and foremost purpose of the invention is to provide a kind of high intensity green
The preparation method of environment protecting paper, improve the interface binding power between PLA fibers and bamboo fibre, prepared by enhancing PLA fibers and bamboo fibre
The intensity of paper.
Another object of the present invention is to provide high intensity green and environmental protection paper made from above-mentioned preparation method.
It is still another object of the present invention to provide the application of above-mentioned high intensity green and environmental protection paper
For achieving the above object, the present invention adopts the following technical scheme that:
A kind of preparation method of high intensity green and environmental protection paper, comprises the following steps:
(1) it is beaten to starching the dense bamboo pulp raw material for being 10%, obtains bamboo pulp of the beating degree for 30~50 ° of SR;
(2) bamboo pulp in step (1) is added in cationic guar solution, under the conditions of 25~35 DEG C, insulation 20~
30min, bamboo pulp is taken out, pretreated bamboo pulp is obtained after washing;
(3) PLA fibers and pretreated bamboo pulp are pressed 3:7 absolute dry mass ratio is manufactured paper with pulp, you can obtains high intensity
Green and environmental protection paper.
Preferably, the concentration of step (2) described cationic guar solution is 0.5wt%~1.5wt%, the over dry of bamboo pulp
Quality is 6wt%~10wt% of cationic guar solution.
Preferably, according to 80g/m in step (3)2~120g/m2Quantify and manufactured paper with pulp.
A kind of preparation method of high intensity green and environmental protection paper, comprises the following steps:
(a) it is beaten to starching the dense bamboo pulp raw material for being 10%, obtains bamboo pulp of the beating degree for 30~50 ° of SR;
(b) PLA fibers are added in cationic guar solution, under the conditions of 25~35 DEG C, is incubated 20~30min, takes
Go out PLA fibers, pretreated PLA fibers are obtained after washing;
(c) by the bamboo pulp obtained in step (a) and pretreated PLA fibers by 7:3 absolute dry mass ratio is manufactured paper with pulp,
It can obtain high intensity green and environmental protection paper.
Preferably, the concentration of step (b) cationic guar solution is 0.5wt%~1.5wt%, PLA fibers
Absolute dry mass is 6wt%~10wt% of cationic guar solution.
Preferably, according to 80g/m in step (c)2~120g/m2Quantify and manufactured paper with pulp.
A kind of high intensity green and environmental protection paper, it can be obtained by the preparation method of above-mentioned high intensity green and environmental protection paper.
Application of the above-mentioned high intensity green and environmental protection paper in paper for daily use and wrapping paper field.
Compared with prior art, the present invention has advantages below and beneficial effect:
The present invention uses guar hydroxypropyltrimonium ammonium chloride (cation guar gum) as the pre- of bamboo fibre and PLA fibers
Solvent is handled, it has the advantages of very big in security, stability, film forming, the feature of environmental protection etc..
Guar xanthan molecule contains substantial amounts of hydroxyl in itself, meanwhile, there is certain cohesive action, fiber surface can be increased
Hydroxyl value, assign PLA Hydrophilic Fiber energy, be so advantageous to the combination between PLA fibers and bamboo fibre;And bamboo fibre surface
Containing great amount of hydroxy group, what guar gum can be suitably reduces the chemical polarity on bamboo fibre surface, and it is fine with PLA to be equally beneficial for bamboo fibre
The interface cohesion of dimension.But if guar gum is directly added in fiber solution, the process of discongesting can produce substantial amounts of foam,
Fiber skewness is caused during sheet formation;If add guar gum after fiber is discongested, it is difficult to make fiber and Guar
Glue efficiently combines, and guar gum also can waste material with a part is lost in into gauze.
And the present invention pre-processes bamboo fibre, PLA fibers by guar gum, above mentioned problem was both avoided, plant can be improved again
Binding ability between fibres and synthetic fibers, the intensity of composite paper is significantly improved, solved between two kinds of fibers because of material
Hydrophilic, hydrophilic polar it is different and caused by the problem of can not combining.Meanwhile PLA fibers, bamboo fibre and cation guar gum are
The green material of fully biodegradable under field conditions (factors), paper prepared therefrom not only meet people to the high thing of paper
The requirement of rationality energy, also comply with requirement of the country to Product Green sustainable development.
Embodiment
With reference to embodiment, the present invention is described in further detail, but the implementation of the present invention is not limited to this.
Each initiation material is commercially available or prepared according to art methods in preparation method of the present invention.
Embodiment 1
A kind of preparation method of high intensity green and environmental protection paper, comprises the following steps:
(1) 300g is starched into the dense bamboo pulp raw material for being 10% be placed in PFI mills and be beaten, obtain bamboo pulp of the beating degree for 30 ° of SR;
(2) weigh the bamboo pulp obtained in a certain amount of step (1) and add the cationic guar solution that concentration is 0.5wt%
In, the absolute dry mass of bamboo pulp is the 6wt% of cationic guar solution quality, under the conditions of 25 DEG C, after being incubated 20min, is taken out
Bamboo pulp, washed 3 times with 3000ml distilled water, that is, the pretreated bamboo pulp used in being tested;
(3) by the pretreated bamboo pulp in step (2) and the PLA fibers without cationic guar solution processing with 7:
3 absolute dry mass ratio is on a papermaking machine according to 80g/m2Quantify and manufactured paper with pulp, you can obtain high intensity green and environmental protection paper.
Embodiment 2
A kind of preparation method of high intensity green and environmental protection paper, comprises the following steps:
(1) 300g is starched into the dense bamboo pulp raw material for being 10% be placed in PFI mills and be beaten, obtain bamboo pulp of the beating degree for 40 ° of SR;
(2) bamboo pulp obtained in a certain amount of step (1) is weighed to add in the cationic guar solution that concentration is 1wt%,
The absolute dry mass of bamboo pulp is the 8wt% of cationic guar solution quality, under the conditions of 30 DEG C, after being incubated 25min, takes out bamboo
Slurry, washed 3 times with 3000ml distilled water, that is, the pretreated bamboo pulp used in being tested;
(3) by the pretreated bamboo pulp in step (2) and the PLA fibers without cationic guar solution processing with 7:
3 absolute dry mass ratio is on a papermaking machine according to 100g/m2Quantify and manufactured paper with pulp, you can obtain high intensity green and environmental protection paper.
Embodiment 3
A kind of preparation method of high intensity green and environmental protection paper, comprises the following steps:
(1) 300g is starched into the dense bamboo pulp raw material for being 10% be placed in PFI mills and be beaten, obtain bamboo pulp of the beating degree for 50 ° of SR;
(2) weigh the bamboo pulp obtained in a certain amount of step (1) and add the cationic guar solution that concentration is 1.5wt%
In, the absolute dry mass of bamboo pulp is the 10wt% of cationic guar solution quality, under the conditions of 35 DEG C, after being incubated 30min, is taken out
Bamboo pulp, washed 3 times with 3000ml distilled water, that is, the pretreated bamboo pulp used in being tested;
(3) by the pretreated bamboo pulp in step (2) and the PLA fibers without cationic guar solution processing with 7:
3 absolute dry mass ratio, on a papermaking machine according to 120g/m2Quantify and manufactured paper with pulp, you can obtain high intensity green and environmental protection paper.
Embodiment 4
A kind of preparation method of high intensity green and environmental protection paper, comprises the following steps:
(1) 300g is starched into the dense bamboo pulp raw material for being 10% be placed in PFI mills and be beaten, obtain bamboo pulp of the beating degree for 30 ° of SR;
(2) a certain amount of PLA fibers are weighed to add in the cationic guar solution that concentration is 0.5wt%, PLA fibers
Absolute dry mass is the 6wt% of cationic guar solution quality, under the conditions of 25 DEG C, after being incubated 20min, takes out PLA fibers, uses
3000ml distilled water is washed 3 times, that is, the pretreated PLA fibers used in being tested;
(3) by the pretreated PLA fibers in the bamboo pulp and step (2) that are obtained in step (1) with 7:3 absolute dry mass
Than on a papermaking machine according to 80g/m2Quantify and manufactured paper with pulp, you can obtain high intensity green and environmental protection paper.
Embodiment 5
A kind of preparation method of high intensity green and environmental protection paper, comprises the following steps:
(1) 300g is starched into the dense bamboo pulp raw material for being 10% be placed in PFI mills and be beaten, obtain bamboo pulp of the beating degree for 40 ° of SR;
(2) a certain amount of PLA fibers are weighed to add in the cationic guar solution that concentration is 1wt%, PLA fibers it is exhausted
Dry mass is the 8wt% of cationic guar solution quality, under the conditions of 30 DEG C, after being incubated 25min, takes out PLA fibers, respectively
Washed respectively 3 times with 3000ml distilled water, that is, the pretreated PLA fibers used in being tested;
(3) by the pretreated PLA fibers in the bamboo pulp and step (2) that are obtained in step (1) with 7:3 absolute dry mass
Than on a papermaking machine according to 100g/m2Quantify and manufactured paper with pulp, you can obtain high intensity green and environmental protection paper.
Embodiment 6
A kind of preparation method of high intensity green and environmental protection paper, comprises the following steps:
(1) 300g is starched into the dense bamboo pulp raw material for being 10% be placed in PFI mills and be beaten, obtain bamboo pulp of the beating degree for 50 ° of SR;
(2) a certain amount of PLA fibers are weighed to add in the cationic guar solution that concentration is 1.5wt%, PLA fibers
Absolute dry mass is the 10wt% of cationic guar solution quality, under the conditions of 35 DEG C, after being incubated 30min, takes out PLA fibers,
Washed 3 times with 3000ml distilled water, that is, the pretreated PLA fibers used in being tested;
(3) by the pretreated PLA fibers in the bamboo pulp and step (2) that are obtained in step (1) with 7:3 absolute dry mass
Than on a papermaking machine according to 120g/m2Quantify and manufactured paper with pulp, you can obtain high intensity green and environmental protection paper.
High intensity green and environmental protection paper obtained in above-described embodiment 1-6 is put down in national standard laboratory with constant temperature and constant humidity
24h is divided in Hengshui, detects paper indices with testers such as tensile strength instrument, tearability instrument, as a result as shown in table 1.
The paper performance of table 1 detects
Note:Paper 1# is that extrusion coating paper is by being beaten without beater and without the bamboo pulp and PLA fibers of guar gum pretreatment
By 7:3 absolute dry mass ratio, copy the quantification of 100g/m of system2Extrusion coating paper;
Paper 2# is the bamboo pulp by being beaten without beater and being pre-processed without guar gum, copies the quantification of 100g/m of system2
Paper;
Paper 3# is the PLA fibers by being beaten without beater and being pre-processed without guar gum, copies the quantification of 100g/ of system
m2Paper.
The cationic guar solution of selection suitable concn and appropriate is can be seen that from the embodiments of the invention of table 1
Paper making scheme, the tensile strength and tear angle value of paper can be significantly improved.
Above-described embodiment is for the preferable embodiment of the present invention, but embodiments of the present invention are not by above-described embodiment
Limitation, other any Spirit Essences without departing from the present invention with made under principle change, modification, replacement, combine, letter
Change, should be equivalent substitute mode, be included within protection scope of the present invention.
Claims (8)
1. a kind of preparation method of high intensity green and environmental protection paper, it is characterised in that comprise the following steps:
(1) it is beaten to starching the dense bamboo pulp raw material for being 10%, obtains beating degree as 30~50oSR bamboo pulp;
(2) bamboo pulp obtained in step (1) is added in cationic guar solution, under the conditions of 25~35 DEG C, insulation 20~
30min, bamboo pulp is taken out, pretreated bamboo pulp is obtained after washing;
(3) pretreated bamboo pulp in PLA fibers and step (2) is pressed 3:7 absolute dry mass ratio is manufactured paper with pulp, you can obtains height
Intensity green and environmental protection paper.
2. the preparation method of high intensity green and environmental protection paper according to claim 1, it is characterised in that step (2) described sun
The concentration of cationic guar solution is 0.5wt%~1.5wt%, and the absolute dry mass of bamboo pulp is cationic guar solution
6wt%~10wt%.
3. the preparation method of high intensity green and environmental protection paper according to claim 1, it is characterised in that in step (3) according to
80g/m2~120g/m2Quantify and manufactured paper with pulp.
4. a kind of preparation method of high intensity green and environmental protection paper, it is characterised in that comprise the following steps:
(a) it is beaten to starching the dense bamboo pulp raw material for being 10%, obtains beating degree as 30~50oSR bamboo pulp;
(b) PLA fibers are added in cationic guar solution, under the conditions of 25~35 DEG C, is incubated 20~30min, takes out PLA
Fiber, pretreated PLA fibers are obtained after washing;
(c) by pretreated PLA fibers in the bamboo pulp obtained in step (a) and step (b) by 7:3 absolute dry mass is than carrying out
Manufacture paper with pulp, you can obtain high intensity green and environmental protection paper.
5. the preparation method of high intensity green and environmental protection paper according to claim 4, it is characterised in that step (b) sun
The concentration of cationic guar solution is 0.5wt%~1.5wt%, and the absolute dry mass of PLA fibers is cationic guar solution
6wt%~10wt%.
6. the preparation method of high intensity green and environmental protection paper according to claim 4, it is characterised in that in step (c) according to
80g/m2~120g/m2Quantify and manufactured paper with pulp.
7. a kind of high intensity green and environmental protection paper, it is characterised in that it is as the high intensity green described in any one of claim 1 to 6
The preparation method of environment protecting paper obtains.
8. high intensity green and environmental protection paper described in claim 7 is in the application in paper for daily use and wrapping paper field.