CN107686660A - A kind of high-temperature resistant rubber sole - Google Patents
A kind of high-temperature resistant rubber sole Download PDFInfo
- Publication number
- CN107686660A CN107686660A CN201711006236.6A CN201711006236A CN107686660A CN 107686660 A CN107686660 A CN 107686660A CN 201711006236 A CN201711006236 A CN 201711006236A CN 107686660 A CN107686660 A CN 107686660A
- Authority
- CN
- China
- Prior art keywords
- parts
- sole
- rubber
- temperature resistant
- fluorubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of shoe making, especially a kind of high-temperature resistant rubber sole, the sizing material for preparing sole is made up of following components, specifically included:Silicon rubber, fluorubber, neoprene, natural rubber, carbon black, calcium carbonate, age resistor, clay, antiscorching agent, Methyl Benzene-o-dicarboxylate, zinc oxide;The mass fraction of above each component is:60 80 parts of silicon rubber, 50 60 parts of fluorubber, 40 50 parts of neoprene, 30 40 parts of natural rubber, 10 15 parts of carbon black, 35 parts of calcium carbonate, 24 parts of age resistor, 25 parts of clay, 34 parts of antiscorching agent, 8 10 parts of Methyl Benzene-o-dicarboxylate, 35 parts of zinc oxide.A kind of high-temperature resistant rubber sole obtained by the present invention, it has good resistance to elevated temperatures, is chronically under higher temperature state situations such as aging, deformation will not also occur, improves the performance and service life of sole.
Description
Technical field
The present invention relates to technical field of shoe making, especially a kind of high-temperature resistant rubber sole.
Background technology
In the prior art, for some special work posts, its environment temperature is higher, especially ground, then causes rubber
Rubber sole all the time be in higher temperature state under, then cause sole easily aging, deformation, damage situations such as.
The content of the invention
One kind is provided and is not easy under long term high temperature environment the invention aims to solve the deficiency of above-mentioned technology
Aging, the high-temperature resistant rubber sole of deformation.
In order to achieve the above object, a kind of high-temperature resistant rubber sole designed by the present invention, prepare the sizing material of sole by with
Lower component is formed, and is specifically included:It is silicon rubber, fluorubber, neoprene, natural rubber, carbon black, calcium carbonate, age resistor, clay, anti-
Burnt agent, Methyl Benzene-o-dicarboxylate, zinc oxide;The mass fraction of above each component is:Silicon rubber 60-80 parts, fluorubber 50-60
Part, neoprene 40-50 parts, natural rubber 30-40 parts, carbon black 10-15 parts, calcium carbonate 3-5 parts, age resistor 2-4 parts, clay 2-5
Part, antiscorching agent 3-4 parts, Methyl Benzene-o-dicarboxylate 8-10 parts, zinc oxide 3-5 parts.
Preferably, a kind of high-temperature resistant rubber sole, the sizing material for preparing sole are made up of following components, specifically included:Silicon
Rubber, fluorubber, neoprene, natural rubber, carbon black, calcium carbonate, age resistor, clay, antiscorching agent, Methyl Benzene-o-dicarboxylate, oxygen
Change zinc;The mass fraction of above each component is:68 parts of silicon rubber, 56 parts of fluorubber, 43 parts of neoprene, 37 parts of natural rubber, charcoal
Black 12 parts, 4 parts of calcium carbonate, 3 parts of age resistor, 4 parts of clay, 3 parts of antiscorching agent, 9 parts of Methyl Benzene-o-dicarboxylate, 4 parts of zinc oxide.
A kind of high-temperature resistant rubber sole obtained by the present invention, it has good resistance to elevated temperatures, is chronically at higher
Also situations such as aging, deformation will not occur under state of temperature, the performance and service life of sole are improved.
Embodiment
The present invention is further described by the following embodiment.
Embodiment 1:
A kind of high-temperature resistant rubber sole of the present embodiment description, the sizing material for preparing sole are made up of following components, specifically included:Silicon
Rubber, fluorubber, neoprene, natural rubber, carbon black, calcium carbonate, age resistor, clay, antiscorching agent, Methyl Benzene-o-dicarboxylate, oxygen
Change zinc;The mass fraction of above each component is:60 parts of silicon rubber, 50 parts of fluorubber, 40 parts of neoprene, 30 parts of natural rubber, charcoal
Black 10 parts, 3 parts of calcium carbonate, 2 parts of age resistor, 2 parts of clay, 3 parts of antiscorching agent, 8 parts of Methyl Benzene-o-dicarboxylate, 3 parts of zinc oxide.
Embodiment 2:
A kind of high-temperature resistant rubber sole of the present embodiment description, the sizing material for preparing sole are made up of following components, specifically included:Silicon
Rubber, fluorubber, neoprene, natural rubber, carbon black, calcium carbonate, age resistor, clay, antiscorching agent, Methyl Benzene-o-dicarboxylate, oxygen
Change zinc;The mass fraction of above each component is:80 parts of silicon rubber, 60 parts of fluorubber, 50 parts of neoprene, 40 parts of natural rubber, charcoal
Black 15 parts, 5 parts of calcium carbonate, 4 parts of age resistor, 5 parts of clay, 4 parts of antiscorching agent, 10 parts of Methyl Benzene-o-dicarboxylate, 5 parts of zinc oxide.
Embodiment 3:
A kind of high-temperature resistant rubber sole of the present embodiment description, the sizing material for preparing sole are made up of following components, specifically included:Silicon
Rubber, fluorubber, neoprene, natural rubber, carbon black, calcium carbonate, age resistor, clay, antiscorching agent, Methyl Benzene-o-dicarboxylate, oxygen
Change zinc;The mass fraction of above each component is:68 parts of silicon rubber, 56 parts of fluorubber, 43 parts of neoprene, 37 parts of natural rubber, charcoal
Black 12 parts, 4 parts of calcium carbonate, 3 parts of age resistor, 4 parts of clay, 3 parts of antiscorching agent, 9 parts of Methyl Benzene-o-dicarboxylate, 4 parts of zinc oxide.
Claims (1)
1. a kind of high-temperature resistant rubber sole, it is characterized in that:The sizing material for preparing sole is made up of following components, is specifically included:Silicon rubber
Glue, fluorubber, neoprene, natural rubber, carbon black, calcium carbonate, age resistor, clay, antiscorching agent, Methyl Benzene-o-dicarboxylate, oxidation
Zinc;The mass fraction of above each component is:Silicon rubber 60-80 parts, fluorubber 50-60 parts, neoprene 40-50 parts, natural rubber
30-40 parts, carbon black 10-15 parts, calcium carbonate 3-5 parts, age resistor 2-4 parts, clay 2-5 parts, antiscorching agent 3-4 parts, phthalic acid
Methyl esters 8-10 parts, zinc oxide 3-5 parts.