CN107661763A - The forming method and hydrocarbon dehydrogenation reaction method of nano-carbon material formed body and its preparation method and application and nano-carbon material - Google Patents
The forming method and hydrocarbon dehydrogenation reaction method of nano-carbon material formed body and its preparation method and application and nano-carbon material Download PDFInfo
- Publication number
- CN107661763A CN107661763A CN201610602659.3A CN201610602659A CN107661763A CN 107661763 A CN107661763 A CN 107661763A CN 201610602659 A CN201610602659 A CN 201610602659A CN 107661763 A CN107661763 A CN 107661763A
- Authority
- CN
- China
- Prior art keywords
- nano
- weight
- carbon material
- formed body
- range
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The forming method and hydrocarbon dehydrogenation reaction method of nano-carbon material formed body and its preparation method and application and nano-carbon material.The invention discloses a kind of nano-carbon material formed body and its preparation method and application and using hydrocarbon dehydrogenation reaction method of the formed body as catalyst, the formed body contains nano-carbon material and for the heat-resistant inorganic oxide of the nano-carbon material molding bonded, the nano-carbon material to be contained into O elements and N element.According to the nano-carbon material formed body of the present invention using heat-resistant inorganic oxide as binding agent by nano-carbon material molding bonded, not only there is higher crushing strength, and there is higher porosity, the catalyst for being adapted as catalyst, particularly hydrocarbon dehydrogenation reaction uses.
Description
Technical field
The present invention relates to nano-carbon material field shaping technique, in particular it relates to which a kind of nano-carbon material is molded
Body and preparation method thereof, the invention further relates to the application of catalyst of the nano-carbon material formed body as hydrocarbon dehydrogenation reaction,
The invention further relates to a kind of hydrocarbon dehydrogenation reaction method using the nano-carbon material formed body as catalyst.
Background technology
The dehydrogenation reaction of hydrocarbons is a kind of important reaction type, such as most of low-carbon olefine is to pass through low-carbon
The dehydrogenation reaction of alkane and obtain.Whether dehydrogenation reaction participates in that direct dehydrogenation reaction (that is, oxygen can be divided into according to oxygen
Gas is not involved in) and oxidative dehydrogenation (that is, oxygen participates in) two classes.
Polytype nano-carbon material has been demonstrated equal to the direct dehydrogenation reaction of hydrocarbons and oxidative dehydrogenation
With catalytic effect.
Hydrocarbon oxidative dehydrogenation process using nano-carbon material as catalyst, need to be by nano-sized carbon as used fixed bed reaction technique
Material is molded, and formed body needs the requirement for meeting following two aspects：(1) there is certain intensity, to avoid in course of reaction
Middle formed body occurs to crush, and on the one hand broken the fine grained formed or powder can cause beds pressure drop to raise, so as to carry
High production run cost, increase the danger of production；On the other hand if the broken fine grained formed or powder are by reaction product band
Go out, catalyst loss and product can be caused to separate and complicate；(2) there is certain porosity, to improve the ratio table of formed body
Area so that the nano-carbon material in formed body can be contacted more fully with reaction mass.
As an example for being molded nano-carbon material, researcher attempts CNT (CNT) being supported on SiC bubbles
The surface of foam, form CNT/SiC foams.Although CNT can preferably be anchored on SiC foam surface, CNT load capacity compared with
It is low, it is typically only capable to reach 0.5-4 weight %.
Therefore, how nano-carbon material is shaped in wide in range nano-carbon material content range still with higher
The formed body of intensity is still a technical problem urgently to be resolved hurrily.
The content of the invention
It is an object of the invention to provide a kind of nano-carbon material formed body and preparation method thereof, nano-carbon material shaping
Body not only has higher intensity, and the content of nano-carbon material can be adjusted in wider scope.
According to an aspect of the present invention, the invention provides a kind of nano-carbon material formed body, the formed body, which contains, to be received
Rice carbon material and for the heat-resistant inorganic oxide of the nano-carbon material molding bonded, the nano-carbon material to be contained into O
Element and N element.
According to the second aspect of the invention, the invention provides a kind of nano-carbon material formed body, the formed body to contain
Nano-carbon material and for by the heat-resistant inorganic oxide of the nano-carbon material molding bonded；
The nano-carbon material is made using the method comprised the following steps：By one kind be dispersed with raw material nano carbon material,
The aqueous dispersions of at least one nitrogen-containing compound and at least one organic base are reacted in closed container, the nitrogen
Compound is selected from NH3, hydrazine and urea, the organic base is selected from amine and quaternary ammonium base, and in course of reaction, the temperature of the aqueous dispersions is protected
Hold in the range of 80-250 DEG C.
According to the third aspect of the present invention, should the invention provides a kind of preparation method of nano-carbon material formed body
Method include nano-carbon material is mixed with binding agent source, obtained mixture is molded, obtains article shaped, by it is described into
Type thing is dried and is optionally calcined, and the binding agent source is selected from heat-resistant inorganic oxide and/or heat-resistant inorganic oxide
Precursor, the nano-carbon material is not surface treated nano-carbon material and/or surface treated nano-carbon material,
Determined through x-ray photoelectron power spectrum, the surface treated nano-carbon material contains O elements and N element.
According to the fourth aspect of the present invention, the invention provides a kind of method system as described in third aspect of the present invention
Standby nano-carbon material formed body.
According to the fifth aspect of the present invention, the invention provides a kind of forming method of nano-carbon material, this method bag
Include and nano-carbon material is subjected to hydro-thermal process in a kind of aqueous dispersions, the sizing material forming that hydro-thermal process is obtained, be molded
Thing, the article shaped is dried and is optionally calcined, the aqueous dispersions contain binding agent source, the binding agent source choosing
From the precursor of heat-resistant inorganic oxide and/or heat-resistant inorganic oxide, the nano-carbon material is received to be not surface treated
Rice carbon material and/or surface treated nano-carbon material, is determined through x-ray photoelectron power spectrum, described surface treated to receive
Rice carbon material contains O elements and N element.
According to the sixth aspect of the invention, the invention provides as the method preparation described in the 5th aspect of the present invention
Nano-carbon material formed body.
According to the seventh aspect of the present invention, the invention provides according to the present invention nano-carbon material formed body as hydrocarbon
The application of the catalyst of dehydrogenation reaction.
According to the eighth aspect of the present invention, the invention provides a kind of hydrocarbon dehydrogenation reaction method, this method, which is included in, deposits
Under conditions of oxygen, under hydrocarbon dehydrogenation reaction conditions, by hydrocarbon with the present invention the on one side, second aspect,
Nano-carbon material formed body contact described in 4th aspect or the 6th aspect.
Nano-carbon material is glued using heat-resistant inorganic oxide as binding agent according to the nano-carbon material formed body of the present invention
Form type, not only there is higher crushing strength, and there is higher porosity, be adapted as catalyst, particularly hydrocarbon
The catalyst of dehydrogenation reaction uses.
Embodiment
The embodiment of the present invention is described in detail below.It is it should be appreciated that described herein specific
Embodiment is merely to illustrate and explain the present invention, and is not intended to limit the invention.
The end points of disclosed scope and any value are not limited to the accurate scope or value herein, these scopes or
Value should be understood to comprising the value close to these scopes or value.For number range, between the endpoint value of each scope, respectively
It can be combined with each other between the endpoint value of individual scope and single point value, and individually between point value and obtain one or more
New number range, these number ranges should be considered as specific open herein.In the present invention, nano-carbon material refers to disperse
The phase yardstick at least one-dimensional carbon material less than 100nm.In the present invention, " at least one " represents one or more kinds of.This hair
In bright, when representing number range, " ×-× in the range of " include two binary values.
According to the first aspect of the invention, the invention provides a kind of nano-carbon material formed body, the formed body to contain
Nano-carbon material and for by the heat-resistant inorganic oxide of the nano-carbon material molding bonded.
According to the nano-carbon material formed body of the present invention, the nano-carbon material can be pure nano-carbon material,
It can be the nano-carbon material containing oxygen atom and nitrogen-atoms.
From the further angle for improving nano-carbon material formed body as the catalyst of hydrocarbon dehydrogenation reaction, the nanometer
Carbon material preferably comprises O elements and N element (being also referred to as nano-carbon material containing hetero atom sometimes below).It is highly preferred that with institute
State on the basis of the total amount of nano-carbon material and in terms of element, the content of O elements can be 1-8 weight %, preferably 2.5-7.5 weights
Measure %, more preferably more preferably 3-7 weight %, 4.5-7 weight %；The content of N element can be 1-8 weight %, excellent
Elect 2-6 weight %, more preferably 3-5 weight %, more preferably 3.5-4.5 weight % as；The content of C element can be
84-98 weight %, preferably 86.5-95.5 weight %, more preferably 88-94 weight %, more preferably 88.5-92 weights
Measure %.
In the present invention, the content of each element is determined using X-ray photoelectron spectroscopy in nano-carbon material.Sample is being tested
It is preceding to be dried 3 hours in helium atmosphere at a temperature of 150 DEG C.Wherein, X-ray photoelectron spectroscopic analysis are in Thermo
The ESCALab250 type x-ray photoelectron power spectrums equipped with Thermo Avantage V5.926 softwares of Scientific companies
Tested on instrument, excitaton source is monochromatization Al K α X ray, energy 1486.6eV, power 150W, is led to used in narrow scan
Can be thoroughly 30eV, base vacuum when analysis is tested is 6.5 × 10-10Mbar, the C1s peaks of electron binding energy simple substance carbon
(284.0eV) is corrected, and carries out data processing on Thermo Avantage softwares, sensitivity factor is used in analysis module
Method carries out quantitative analysis.
In the nano-carbon material, the O determined by the peak in the range of 531.0-532.5eV in x-ray photoelectron power spectrum is first
The amount of plain (that is, C=O) is IO c, the O elements determined by the peak in the range of 532.6-533.5eV in x-ray photoelectron power spectrum are (i.e.,
C-O amount) is IO e, IO c/IO eCan be in the range of 0.2-2.5, preferably in the range of 1.2-2.5, more preferably in 1.3-
In the range of 2.2, further preferably in the range of 1.4-2.In the present invention, by the O1s spectral peaks in x-ray photoelectron power spectrum
Area AO 1The total amount of O elements is determined, the O1s spectral peaks in x-ray photoelectron power spectrum are divided into two groups of peaks, i.e., in 531.0-
Spectral peak (corresponding to C=O species) in the range of 532.5eV and the spectral peak in the range of 532.6-533.5eV (correspond to C-O
Species), the area of the spectral peak in the range of 531.0-532.5eV is designated as AO 2, by the spectral peak in the range of 532.6-533.5eV
Area be designated as AO 3, IO c/IO e=AO 2/AO 3。
In the nano-carbon material, using the total amount of C element determined in nano-carbon material by x-ray photoelectron power spectrum as base
Standard, the content of the C element determined by the peak in the range of 284.7-284.9eV in x-ray photoelectron power spectrum can be 60-98 weights
Measure %, more preferably preferably 65-95 weight %, 70-90 weight %；By 286.0-288.8eV models in x-ray photoelectron power spectrum
The total content for the C element that peak in enclosing determines can be 2-40 weight %, and preferably 5-35 weight %, more preferably 10-30 are heavy
Measure %.In the present invention, by the area A of the C1s spectral peaks in x-ray photoelectron power spectrumC 1The total amount of C element is determined, by X ray photoelectricity
C1s spectral peaks in sub- power spectrum are divided into two groups of peaks, i.e., the spectral peak (corresponding to graphite mould carbon species) in the range of 284.7-284.9eV
And the spectral peak (corresponding to non-graphite type carbon species) in the range of 286.0-288.8eV, will be in the range of 284.7-284.9eV
The area of spectral peak be designated as AC 2, the area of the spectral peak in the range of 286.0-288.8eV is designated as AC 3, by x-ray photoelectron energy
Content=the A for the C element that peak in spectrum in the range of 284.7-284.9eV determinesC 2/AC 1, by x-ray photoelectron power spectrum
Total content=the A for the C element that peak in the range of 286.0-288.8eV determinesC 3/AC 1。
In the nano-carbon material, the C determined by the peak in the range of 288.6-288.8eV in x-ray photoelectron power spectrum is first
The amount of element is IC c, the amount of the C element determined by the peak in the range of 286.0-286.2eV in x-ray photoelectron power spectrum is IC e, IC c/
IC eMore preferably in the range of 1.5-3.5, can further preferably it exist in the range of 0.3-4, in the range of preferably 1.5-4
In the range of 1.55-3.In the present invention, the spectral peak in x-ray photoelectron power spectrum in the range of 286.0-288.8eV (is corresponded to
Agraphitic carbon species) be further divided into two groups of peaks, i.e., the spectral peak in the range of 286.0-286.2eV (corresponds to hydroxyl and ether
Type carbon species) and spectral peak (corresponding to carboxyl, acid anhydride and ester type carbon species) in the range of 288.6-288.8eV, will be
286.0-286.2eV the area of spectral peak in the range of is designated as AC 4, the area of the spectral peak in the range of 288.6-288.8eV is designated as
AC 5, IC c/IC e=AC 5/AC 4。
In the nano-carbon material, the total amount that the N element in nano-carbon material is determined by x-ray photoelectron power spectrum is IN t,
The amount of the N element determined by the peak in the range of 398.5-400.1eV in x-ray photoelectron power spectrum is IN c, IN c/IN tCan be
In the range of 0.7-1, preferably in the range of 0.75-0.98, more preferably in the range of 0.8-0.95.
In the nano-carbon material, the N determined by the peak in the range of 400.6-401.5eV in x-ray photoelectron power spectrum is first
Cellulose content is relatively low not to be contained even.Usually, the N members determined by the peak in the range of 400.6-401.5eV in x-ray photoelectron power spectrum
The amount of element is IN g, IN g/IN tFor not higher than 0.3, typically in the range of 0.02-0.25, preferably in the range of 0.05-0.2.
In the present invention, the total amount A of N element is determined by the area of the N1s spectral peaks in x-ray photoelectron power spectrumN 1, by X ray
N1s spectral peaks in photoelectron spectroscopy are divided into two groups of peaks, i.e., the spectral peak in the range of 400.6-401.5eV (corresponds to graphite mould nitrogen
Species) and 398.5-400.1eV in the range of spectral peak (nitrogen species in addition to graphite mould nitrogen), determine this respective face in two groups of peaks
Product, A is designated as by the area of the spectral peak in the range of 400.6-401.5eVN 2, by the spectral peak in the range of 398.5-400.1eV
Area is designated as AN 3, IN c/IN t=AN 3/AN 1, IN g/IN t=AN 2/AN 1, when obtained ratio is less than 0.01, it is believed that without such
Species, and the content of such species is designated as 0.
In the present invention, the position at each peak can determine that as the combination corresponding to the summit at the peak, and scope determines by mentioned earlier
The peak combination that refers to corresponding to summit can be within that range peak, a peak can be included within the range, can also be wrapped
Include more than two peaks.Such as：Peak in the range of 398.5-400.1eV refers to that the combination corresponding to summit can be in 398.5-
Whole peaks in the range of 400.1eV.
The nano-carbon material can by it is common it is various in the form of exist, be specifically as follows but be not limited to CNT, stone
Group more than one or both of black alkene, thin layer graphite, nano carbon particle, carbon nano-fiber, Nano diamond and fullerene
Close.The CNT can be one or both of single-walled carbon nanotube, double-walled carbon nano-tube and multi-walled carbon nanotube with
On combination, preferably multi-walled carbon nanotube.
Preferably, the specific surface area of the multi-walled carbon nanotube is 50-500m2/ g, it so can further improve nano-sized carbon
The catalytic performance of material molded compact, especially as the catalytic performance of the catalyst of hydrocarbons dehydrogenation reaction.More wall carbon
The specific surface area of nanotube is more preferably 80-300m2/ g, more preferably 90-150m2/ g, it is still more preferably 95-
140m2/g.In the present invention, specific surface area is determined by nitrogen adsorption BET method.
Weight-loss ratio of the multi-walled carbon nanotube in 400-800 DEG C of temperature range is w800, in 400-500 DEG C of temperature
The weight-loss ratio spent in section is w500, w500/w800It is preferred that in the range of 0.01-0.5, preferably catalysis effect can be so obtained
Fruit, during catalyst particularly as hydrocarbons dehydrogenation reaction, more preferable catalytic effect can be obtained.w500/w800More preferably exist
In the range of 0.02-0.2.In the present invention, w800=W800- W400, w500=W500- W400, W400To be surveyed at a temperature of 400 DEG C
Fixed mass loss rate, W800For the mass loss rate determined at a temperature of 800 DEG C, W500To be determined at a temperature of 500 DEG C
Mass loss rate；The weight-loss ratio is determined using thermogravimetric analyzer in air atmosphere, and test initial temperature is 25 DEG C, heating
Speed is 10 DEG C/min；Sample is depressed in 150 DEG C of temperature and 1 normal atmosphere dried 3 hours in helium atmosphere before testing.
According to the nano-carbon material formed body of the present invention, the other nonmetallic heteroatoms contents of such as sulphur atom and phosphorus atoms can
Think customary amount.Usually, in the nano-carbon material, other nonmetallic heteroatoms outside oxygen atom and nitrogen-atoms are (such as
Sulphur atom and phosphorus atoms) total amount can be below 0.5 weight %, preferably below 0.2 weight %.The nano-carbon material is also
A small amount of metallic atom can be contained, these metallic atoms are typically derived from the catalyst used when preparing nano-carbon material, described
The content of metallic atom is generally below 0.5 weight %, preferably below 0.2 weight %.
According to the nano-carbon material formed body of the present invention, also contain and be used for the heat-resisting of the nano-carbon material molding bonded
Inorganic oxide.In the present invention, term " heat-resistant inorganic oxide " refers to that under oxygen or oxygen-containing atmosphere decomposition temperature is not less than
300 DEG C (such as：Decomposition temperature be 300-1000 DEG C) inorganic oxygen-containing compound.
According to the present invention nano-carbon material formed body, the heat-resistant inorganic oxide be preferably aluminum oxide, silica and
It is more than one or both of titanium oxide.In an example, the heat-resistant inorganic oxide is aluminum oxide, according to the example
Nano-carbon material shaping physical efficiency obtains higher feed stock conversion.
In a preferred embodiment, at least part heat-resistant inorganic oxide is silica, according to the preferable reality
The nano-carbon material formed body of mode is applied in the catalyst as hydrocarbon dehydrogenation reaction, can be in feed stock conversion and selectivity of product
Between obtain preferably balance.It is described on the basis of the total amount of the heat-resistant inorganic oxide in the preferred embodiment
The content of silica can be 10-100 weight %, more preferably preferably 20-99 weight %, 50-99 weight %, silicon
Outside the content of heat-resistant inorganic oxide can be 0-90 weight %, preferably 1-80 weight %, more preferably 1-50 weight
Measure %.In the preferred embodiment, the instantiation of the heat-resistant inorganic oxide outside silicon can be included but not
It is limited to aluminum oxide and/or titanium oxide.As an example of the preferred embodiment, the heat resistant inorganic oxygen outside silicon
Compound is titanium oxide.
According to the nano-carbon material formed body of the present invention, the content of the nano-carbon material can become in wider scope
It is dynamic, still such that the nano-carbon material formed body has higher intensity.Usually, with the nano-carbon material formed body
On the basis of total amount, the content of the nano-carbon material can be 6-94 weight %, preferably 8-92 weight %, more preferably 10-
90 weight %, more preferably 20-90 weight %, it is still more preferably 40-90 weight %, particularly preferably 70-90 weight
% is measured, the content of the heat-resistant inorganic oxide can be 6-94 weight %, preferably 8-92 weight %, more preferably 10-90
Weight %, more preferably 10-80 weight %, it is still more preferably 10-60 weight %, particularly preferably 10-30 weight
Measure %.The composition of formed body can use x-ray fluorescence spectrometry.In embodiment disclosed by the invention, by the gauge that feeds intake
The composition of the composition and the formed body using x-ray fluorescence spectrometry of obtained formed body is basically identical, and error is 5%
Within.
According to the second aspect of the invention, the invention provides a kind of nano-carbon material formed body, the formed body to contain
Nano-carbon material and for by the heat-resistant inorganic oxide of the nano-carbon material molding bonded.
According to the formed body described in second aspect of the present invention, the nano-carbon material is using the method comprised the following steps
It is made：A kind of moisture for being dispersed with raw material nano carbon material, at least one nitrogen-containing compound and at least one organic base is dissipated
Liquid is reacted in closed container.
The nitrogen-containing compound is selected from NH3, hydrazine and urea.
The organic base is selected from amine and quaternary ammonium base.
The quaternary ammonium base is specifically as follows the compound shown in Formulas I：
In Formulas I, R1、R2、R3And R4Can be each C1-C20Alkyl (including C1-C20Straight chained alkyl and C3-C20Branch
Alkyl group) or C6-C12Aryl.The C1-C20The instantiation of alkyl can include but is not limited to：Methyl, ethyl, just
Propyl group, isopropyl, normal-butyl, sec-butyl, isobutyl group, the tert-butyl group, n-pentyl, neopentyl, isopentyl, tertiary pentyl, n-hexyl, just
Octyl group, n-nonyl, positive decyl, n-undecane base, dodecyl, n-tridecane base, n-tetradecane base, n-pentadecane base, just
One or more in cetyl, n-octadecane base and n-eicosane base.The C6-C12The instantiation of aryl can wrap
Include but be not limited to phenyl, naphthyl, 4- aminomethyl phenyls and 4- ethylphenyls.R1、R2、R3And R4It is preferred that it is respectively C1-C10Alkyl
(including C1-C10Straight chained alkyl and C3-C10Branched alkyl), more preferably respectively C1-C6Alkyl (including C1-C6Straight chain
Alkyl and C3-C6Branched alkyl).
The amine refers to the material that the one, two or three hydrogen in amino molecule is substituted and formed by organic group, described
Organic group can form cyclic structure with nitrogen atom bonding.The organic group can be substitution (such as hydroxyl substitution) or not take
The aliphatic alkyl in generation and/or substitution (such as hydroxyl substitution) or unsubstituted aromatic hydrocarbyl, the aliphatic alkyl can be
Substitute (such as hydroxyl substitution) or unsubstituted representative examples of saturated aliphatic chain alkylene, substitution (such as hydroxyl substitution) or unsubstituted unsaturated lipid
Fat race chain alkylene, substitution (such as hydroxyl substitution) or unsubstituted saturated alicyclic hydrocarbon base and substitution (such as hydroxyl substitution) do not take
It is more than one or both of the unsaturated lipid cyclic hydrocarbon radical in generation.Specifically, the amine can be substitution (such as hydroxyl substitution) or not
Substituted representative examples of saturated aliphatic amine, substitution (such as hydroxyl substitution) or unsubstituted unsaturated aliphatic amine, substitution (such as hydroxyl substitution)
Or unsubstituted saturation aliphatic cyclic amine, substitution (such as hydroxyl substitution) or unsubstituted unsaturated lipid cyclammonium, substitution (such as hydroxyl substitution)
Or more than unsubstituted heterocyclic amine and substitution one or both of (such as hydroxyl substitution) or unsubstituted arylamine.
The representative examples of saturated aliphatic amine is preferably the compound shown in Formula II, the compound shown in formula III and general formula R12
(NH2)2It is more than one or both of material of expression,
In Formula II, R5、R6And R7Respectively H or C1-C6Alkyl, and R5、R6And R7It is asynchronously H.In the present invention, C1-
C6The instantiation of alkyl can include but is not limited to：Methyl, ethyl, n-propyl, isopropyl, normal-butyl, sec-butyl, isobutyl
Base, the tert-butyl group, n-pentyl, isopentyl, tertiary pentyl, neopentyl and n-hexyl.
In formula III, R8、R9And R10Respectively-R11OH or hydrogen, and R8、R9And R10In it is at least one be-R11OH, R11
For C1-C4Alkylidene.In the present invention, C1-C4Alkylidene include C1-C4Straight-chain alkyl-sub and C3-C4Branched alkylidene,
Its instantiation can include but is not limited to：Methylene, ethylidene, sub- n-propyl, isopropylidene, sub- normal-butyl, isobutylidene
With the sub- tert-butyl group.
General formula R12(NH2)2In, R12Can be C1-C6Alkylidene.In the present invention, C1-C6Alkylidene include C1-C6's
Straight-chain alkyl-sub and C3-C6Branched alkylidene, its instantiation can include but is not limited to：Methylene, ethylidene, Asia positive third
Base, isopropylidene, sub- normal-butyl, isobutylidene, the sub- tert-butyl group, sub- n-pentyl and sub- n-hexyl.
The unsaturated aliphatic amine refers to the aliphatic streptamine containing unsaturated group, the unsaturation in molecular structure
Group is preferably alkenyl (that is ,-C=C-).The quantity of the unsaturated group and amino can be one or more, not have
It is particularly limited to.
The instantiation of the organic base can include but is not limited to methylamine, dimethylamine, trimethylamine, ethamine, diethylamine, three
Ethamine, n-propylamine, di-n-propylamine, Tri-n-Propylamine, isopropylamine, diisopropylamine, n-butylamine, di-n-butyl amine, tri-n-butyl amine,
Sec-butylamine, diisobutyl amine, triisobutyl amine, tert-butylamine, n-amylamine, two n-amylamines, tri-n-amyl amine, neopentyl amine, isoamyl
Amine, di-iso-amylamine, triisoamylamine, tertiary amylamine, hexylamine, octylame, nonyl amine, decyl amine, undecyl amine, lauryl amine, dodecane
It is base dimethyl amine, tridecyl amine, tetradecylamine, pentadecyl amine, hexadecylamine, monoethanolamine, triethanolamine, three different
Propanolamine, diethanol amine, dipropanolamine, tripropanol amine, two butanolamines, three butanolamines, dodecyl-dimethyl amine, myristyl
Dimethyl amine, hexadecyldimethyl benzyl ammonium amine, ethylenediamine, propane diamine, butanediamine, pentanediamine, hexamethylene diamine, substituted or unsubstituted pyrrole
Cough up, substituted or unsubstituted nafoxidine, substituted or unsubstituted pyridine, substituted or unsubstituted hexahydropyridine, substitution or not
Substituted imidazoles, substituted or unsubstituted pyrazoles, substituted or unsubstituted quinoline, substituted or unsubstituted EEDQ, substitution
It is or unsubstituted tetrahydroquinoline, substituted or unsubstituted decahydroquinoline, substituted or unsubstituted isoquinolin, substituted or unsubstituted
Pyrimidine, aniline, diphenylamines, benzidine, o-phenylenediamine, m-phenylene diamine (MPD), p-phenylenediamine, o-toluidine, m-toluidine, to first
Base aniline, 23 dimethyl aniline, 2,4- dimethylanilines, 2,5- dimethylanilines, 2,6- dimethylanilines, 3,4- dimethyl
Aniline, 3,5- dimethylanilines, 2,4,6- trimethylanilines, o ethyl aniline, N- butylanilines, 2,6- diethylanilines, ring
Hexylamine, cyclopentamine, hexamethylenetetramine, diethylenetriamine, triethylene tetramine, TMAH, tetraethyl ammonium hydroxide,
TPAOH (including its various isomers, such as four n-propyl ammonium hydroxide and tetra isopropyl ammonium hydroxide), the tetrabutyl
Ammonium hydroxide (including its various isomers, such as 4-n-butyl ammonium hydroxide, four sec-butyl ammonium hydroxide, four isobutyl group hydroxides
Ammonium and tetra-tert ammonium hydroxide) and one or both of four pentyl ammonium hydroxide (including its various isomers) more than.
Raw material nano carbon material：Nitrogen-containing compound：The weight ratio preferably 1 of organic base：0.01-20：0.01-20, so
Catalytic effect of the nano-carbon material formed body in the catalyst as hydrocarbon dehydrogenation reaction can further be improved.It is it is highly preferred that former
Expect nano-carbon material：Nitrogen-containing compound：The weight ratio of organic base is 1：0.02-10：0.02-15.
The mol ratio of the nitrogen-containing compound and the organic base is preferably 1：0.05-100.The nitrogen-containing compound and institute
The mol ratio for stating organic base is more preferably 1：0.1-90, more preferably 1：0.4-80.
Preferably, raw material nano carbon material：H2O weight ratio is 1：2-1000, water dosage be in should within the scope of
When, structural form retentivity of the nano-carbon material in processing procedure is more preferable, such as：Raw material nano carbon material is CNT
When, it will not be cut off substantially in processing procedure.Raw material nano carbon material：H2O weight ratio more preferably 1：5-500, enter one
Step is preferably 1：10-300, it is still more preferably 1：20-200.Furthermore it is also possible to according to nitrogen-containing compound and organic base
Species is adjusted to the dosage of water, so that the nitrogen-containing compound can be uniformly dispersed in water and be defined.
From the angle of catalytic activity of the further raising nano-carbon material in as hydrocarbon dehydrogenation reaction, a kind of excellent
In the embodiment of choosing, the nitrogen-containing compound is ammonia, and the organic base is selected from the compound shown in formula III, is preferably selected from second
Hydramine, diethanol amine and triethanolamine, nano-carbon material formed body so can be further improved in urging as hydrocarbon dehydrogenation reaction
Catalytic reaction effect during agent.In the preferred embodiment, raw material nano carbon material：Nitrogen-containing compound：Organic base
Weight ratio is preferably 1：0.02-10：In the range of 0.05-8, more preferably 1：0.03-5：It is further excellent in the range of 0.1-6
It is selected in 1：0.05-2：In the range of 0.2-5.In the preferred embodiment, nitrogen-containing compound：The mol ratio of organic base is preferred
1：In the range of 0.05-5, more preferably 1：In the range of 0.1-2.5, further preferably 1：In the range of 0.4-0.8.
In the preferred embodiment, raw material nano carbon material：H2O weight ratio is preferably 1：In the range of 5-100, more preferably 1：
In the range of 10-90, further preferably 1：In the range of 40-80.
In another preferred embodiment, the nitrogen-containing compound is hydrazine, and the organic base is selected from the season shown in Formulas I
Ammonium alkali, it so can further improve catalytic reaction effect of the nano-carbon material formed body in the catalyst as hydrocarbon dehydrogenation reaction
Fruit.In the preferred embodiment, raw material nano carbon material：Nitrogen-containing compound：The weight ratio of organic base is 1：0.01-5：
In the range of 0.02-10, preferably 1：0.02-2.5：In the range of 1-9, more preferably 1：0.02-1.5：4.5-8 scope
It is interior.In the preferred embodiment, nitrogen-containing compound：The mol ratio of organic base is preferably 1：0.5-100, more preferably 1：1-
90, more preferably 1：1.1-80.In the preferred embodiment, raw material nano carbon material：H2O weight ratio is preferably
1：10-400, more preferably 1：20-250.
In another preferred embodiment, the nitrogen-containing compound is urea, and the organic base is selected from shown in Formula II
Compound and general formula R12(NH2)2The material of expression, it is preferably selected from ethylenediamine, n-butylamine and diamines, so energy is further
Improve catalytic reaction effect of the nano-carbon material formed body in the catalyst as hydrocarbon dehydrogenation reaction.In the preferable embodiment party
In formula, raw material nano carbon material：Nitrogen-containing compound：The weight ratio of organic base is 1：0.02-10：0.05-20, preferably 1：0.1-
8：0.5-15, more preferably 1：1-5：1-10.In the preferred embodiment, nitrogen-containing compound：The mol ratio of organic base is excellent
Elect 1 as：0.1-5, more preferably 1：0.5-2.In the preferred embodiment, raw material nano carbon material：H2O weight is than excellent
Elect 1 as：5-200, more preferably 1：20-150.
Preferably, in course of reaction, the temperature of the aqueous dispersions is in the range of 80-250 DEG C.In the aqueous dispersions
Temperature when being within above range, the oxygen atom and/or nitrogen-atoms in raw material nano carbon material can not only be effectively improved
Content, and the structural form of raw material nano carbon material will not be produced and significantly affected.It is highly preferred that in course of reaction, it is described
The temperature of aqueous dispersions is in the range of 100-180 DEG C.The duration of the reaction can be selected according to the temperature of reaction
Select, so that enough oxygen atoms can be introduced in raw material nano carbon material and nitrogen-atoms is defined.Usually, the reaction continues
Time can be in the range of 0.5-96 hours, preferably in the range of 2-72 hours, the scope more preferably in 10-40 hours
It is interior.
The aqueous dispersions can be formed using conventional various methods, such as raw material nano carbon material can be disperseed
In water (being preferably deionized water), then mixed with the nitrogen-containing compound and the organic base, so as to obtain the moisture
Dispersion liquid.In order to further improve the dispersion effect of raw material nano carbon material, while shorten the scattered time, can be shaken using ultrasound
Raw material nano carbon material is dispersed in water by the method swung.The condition of the sonic oscillation can be conventional selection, usually, institute
The frequency for stating sonic oscillation can be 10-100kHz, and the duration of the sonic oscillation can be 0.1-6 hours, be preferably
0.5-2 hours.The nitrogen-containing compound and the organic base can each be provided in the form of solution (being preferably the aqueous solution),
It can be provided, be not particularly limited in the form of pure material.
According to the formed body described in second aspect of the present invention, oxygen element and nitrogen in the raw material nano carbon material
Content is not particularly limited, and can be conventional selection.Usually, the content of oxygen element is not high in the raw material nano carbon material
In 1.5 weight %, preferably not higher than 0.5 weight %, more preferably not above 0.3 weight %；The content of nitrogen is not high
In 0.2 weight %, preferably not higher than 0.1 weight %, more preferably not above 0.05 weight %, more preferably it is not higher than
0.02 weight %.Remaining nonmetallic heteroatoms (such as phosphorus atoms in the raw material nano carbon material outside oxygen atom and nitrogen-atoms
And sulphur atom) total amount (in terms of element) can be customary amount.Usually, in the raw material nano carbon material except oxygen element and
The total amount (in terms of element) of remaining nonmetallic heteroatoms outside nitrogen is not higher than 0.5 weight %, preferably not higher than 0.2 weight
Measure %, more preferably not above 0.1 weight %, more preferably not higher than 0.05 weight %.The raw material nano carbon material
According to the difference in source, some metallic elements may be contained, such as the catalysis used during from preparing raw material nano-carbon material
Metallic atom in agent.In the raw material nano carbon material content of metallic atom be generally (in terms of element) 2.5 weight % with
Under, preferably below 1.8 weight %, more preferably below 0.5 weight %.
According to the formed body described in second aspect of the present invention, raw material nano carbon material can use this area before use
Conventional method is pre-processed (as washed), to remove some impurity of raw material nano carbon material surface；Can also be without
Pretreatment, directly use.In preparation example disclosed by the invention, raw material nano carbon material is not pre-processed using preceding.
According to the formed body described in second aspect of the present invention, the raw material nano carbon material can be but be not limited to carbon and receive
One or both of mitron, graphene, Nano diamond, thin layer graphite, nano carbon particle, Nano carbon fibers peacekeeping fullerene with
On combination.The CNT can be single-walled carbon nanotube, double-walled carbon nano-tube and multi-walled carbon nanotube in one kind or
Two or more combinations.Preferably, the raw material nano carbon material is CNT, more preferably multi-walled carbon nanotube.
According to the formed body described in second aspect of the present invention, in a preferred embodiment, the raw material nano
Carbon material is multi-walled carbon nanotube, and the specific surface area of the multi-walled carbon nanotube can be 50-500m2/ g, preferably 80-
300m2/ g, more preferably 100-260m2/ g, more preferably 120-190m2/g。
When the raw material nano carbon material is multi-walled carbon nanotube, temperature of the multi-walled carbon nanotube at 400-800 DEG C
The weight-loss ratio spent in section is w800, the weight-loss ratio in 400-500 DEG C of temperature range is w500, w500/w800Can be in 0.01-
In the range of 0.5, preferably in the range of 0.02-0.4.
According to the formed body described in second aspect of the present invention, the reaction is carried out in closed container.The reaction can
To be carried out under self-generated pressure (that is, not applying pressure additionally), can also carry out under pressure.Preferably, it is described anti-
It should carry out at autogenous pressures.The closed container can be the common reactor that can realize sealing and heating, as high pressure is anti-
Answer kettle.
According to the formed body described in second aspect of the present invention, isolated in the mixture that can also include obtaining from reaction
It is dried after solid matter, so as to obtain nano-carbon material.It can use what conventional solid-liquid separating method obtained from reaction
Solid matter is isolated in mixture, such as combination more than one or both of centrifugation, filtering and decantation.The bar of the drying
Part can be conventional selection, be defined by that can remove the volatile materials in the solid matter isolated.Usually, the drying can
To be carried out at a temperature of 50-400 DEG C, carried out preferably at a temperature of 80-180 DEG C.The duration of the drying can root
Selected according to dry temperature and mode.Usually, the duration of the drying can be no more than 48 hours, be preferably
4-24 hours, more preferably 6-12 hours.The drying can be carried out under normal pressure (that is, 1 standard atmospheric pressure), can also subtracted
Carried out under conditions of pressure.From the further angle for improving dry efficiency, the drying is preferably entered at reduced pressure
OK.Also spray drying etc. is without by solid matter is isolated in mixture the step of can be used, drying now can be
Carried out at a temperature of 120-400 DEG C, carry out preferably at a temperature of 150-350 DEG C, more preferably enter at a temperature of 180-300 DEG C
OK, the duration of the drying can be selected according to dry degree, be such as no more than 0.5 hour, preferably no more than
0.2 hour, more preferably less than 0.1 hour.
According to the formed body described in second aspect of the present invention, also contain and be used for the nano-carbon material molding bonded
Heat-resistant inorganic oxide.The species and its content of the heat-resistant inorganic oxide with it is heat-resisting described in one side of the invention
The species and content of inorganic oxide are identical, are no longer described in detail herein.
Nano-carbon material formed body according to one side of the invention and second aspect can have as needed
There is variously-shaped such as spherical, bar shaped.
There is nano-carbon material formed body according to one side of the invention and second aspect higher resisting to break
Broken intensity.Usually, can be more than 4N/mm according to the radial direction crushing strength of the nano-carbon material formed body of the present invention, typically
For more than 5N/mm.Specifically, the footpath of the nano-carbon material formed body according to one side of the invention and second aspect
It is 5-25N/mm, preferably 6-25N/mm, more preferably 10-25N/mm to crushing strength.In the present invention, radial direction crushing strength is pressed
According to《Petrochemical Engineering Analysis method》In RIPP 25-90 described in (Science Press, the nineteen ninety first edition, Yang Cui are waited and compiled surely)
Defined method measure.
Nano-carbon material formed body according to one side of the invention and second aspect has higher hole
Rate.Usually, according to the present invention nano-carbon material formed body porosity can be more than 5%, it might even be possible to for 10% with
On, such as can be in the range of 5-50%, preferably in the range of 10-30%, more preferably in the range of 12-25%.This
In invention, porosity refers to all interstitial space volume sums and the body of the nano-carbon material formed body in nano-carbon material formed body
Long-pending ratio, the porosity of the nano-carbon material formed body is referred to as, is expressed as a percentage, using mercury injection method (with reference to text
Offer《Graphite porosity of porous material study on determination method》,《Lubrication and sealing》, 2010,35 (10)：99-101) method determines.
According to the third aspect of the present invention, should the invention provides a kind of preparation method of nano-carbon material formed body
Method include nano-carbon material is mixed with binding agent source, obtained mixture is molded, obtains article shaped, by it is described into
Type thing is dried and is optionally calcined.
Method according to third aspect of the present invention, the binding agent source are selected from heat-resistant inorganic oxide and/or resistance to
The precursor of hot inorganic oxide.The heat-resistant inorganic oxide be preferably one kind in aluminum oxide, silica and titanium oxide or
It is two or more.In an example, the heat-resistant inorganic oxide is aluminum oxide, according to the nano-carbon material formed body of the example
Higher feed stock conversion can be obtained.
In a preferred embodiment, at least part heat-resistant inorganic oxide is silica, according to the preferable reality
Nano-carbon material formed body prepared by the mode of applying can select in the catalyst as hydrocarbon dehydrogenation reaction in feed stock conversion and product
Preferably balance is obtained between selecting property.In the preferred embodiment, on the basis of the total amount of the heat-resistant inorganic oxide,
The content of the silica can be 10-100 weight %, more preferably preferably 20-99 weight %, 50-99 weight %, deoxygenation
The content of heat-resistant inorganic oxide outside SiClx can be 0-90 weight %, preferably 1-80 weight %, more preferably 1-50
Weight %.In the preferred embodiment, the instantiation of the heat-resistant inorganic oxide outside silicon can include but
It is not limited to aluminum oxide and/or titanium oxide.As an example of the preferred embodiment, the heat resistant inorganic outside silicon
Oxide is titanium oxide.
The heat-resistant inorganic oxide can by it is common it is various in the form of provide, such as (such as Ludox, titanium is molten with colloidal sol
Glue, Alumina gel) form provide.The precursor of the heat-resistant inorganic oxide can be according to expected heat-resistant inorganic oxide
Species is selected.
For example, when the heat-resistant inorganic oxide is aluminum oxide, the precursor of the heat-resistant inorganic oxide can be
The material of aluminum oxide can be transformed into, the material of aluminum oxide can be such as formed by hydrolysis-condensation reaction and/or roasting, for example, it is organic
Aluminium salt and inorganic aluminate, its instantiation can include but is not limited to hydrated alumina (such as boehmite), aluminium hydroxide, sulphur
Sour aluminium, sodium metaaluminate, aluminium chloride, aluminum nitrate and C1-C10Organic aluminium salt (such as aluminium isopropoxide, isobutanol aluminum, three isopropoxies
Aluminium, three tert-butoxy aluminium and isooctanol aluminium) one or both of more than.
For another example when the heat-resistant inorganic oxide is silica, the precursor of the heat-resistant inorganic oxide can be with
For the material of silica can be transformed into, the material of silica can be such as formed by hydrolysis-condensation reaction and/or roasting, its is specific
Example can include but is not limited to the organo-silicon compound that hydrolysis-condensation reaction can occur.It is described that hydrolysis-condensation reaction can occur
Organo-silicon compound can be the common various materials that silica can be formed by hydrolysis-condensation reaction.As an example,
The organo-silicon compound that hydrolysis-condensation reaction can occur can be more than one or both of compound shown in formula IV：
In formula IV, R13、R14、R15And R16Respectively C1-C4Alkyl.The C1-C4Alkyl include C1-C4Straight chain alkane
Base and C3-C4Branched alkyl, its instantiation can include but is not limited to：Methyl, ethyl, n-propyl, isopropyl, normal-butyl,
Sec-butyl, isobutyl group and the tert-butyl group.Preferably, organic silicon source is selected from methyl silicate, tetraethyl orthosilicate, positive silicic acid positive third
Ester, positive isopropyl silicate and positive silicic acid N-butyl.
In another example when the heat-resistant inorganic oxide is titanium oxide, the precursor of the heat-resistant inorganic oxide can be with
For organic titanate and/or inorganic titanium salt, its instantiation can include but is not limited to TiCl4、Ti(SO4)2、TiOCl2, hydrogen-oxygen
Change titanium, nitric acid titanium salt, phosphoric acid titanium salt, fatty alcohol titanium and organic titanate (such as tetraisopropyl titanate, the n-propyl of metatitanic acid four, metatitanic acid
One or more in four butyl esters and tetraethyl titanate) in one or more.
Method according to third aspect of the present invention, in one embodiment, the binding agent source are selected from heat-resisting
Inorganic oxide, such as the heat-resistant inorganic oxide provided with solation.In this embodiment, by nano-carbon material with gluing
It is molded after knot agent source is well mixed.In another embodiment, at least part binding agent source is heat resistant inorganic oxygen
The precursor of compound.In this embodiment, after nano-carbon material is mixed with binding agent source, entered according to the species in binding agent source
Row processing, is transformed into heat-resistant inorganic oxide by the precursor of the heat-resistant inorganic oxide in binding agent source.
Method according to third aspect of the present invention, the mixture preferably also contain at least one alkali, such energy
Further improve catalytic activity of the nano-carbon material formed body finally prepared in the catalyst as hydrocarbon dehydrogenation reaction.It is described
Alkali can be organic base and/or inorganic base.The inorganic base can be that ammonia, the alkali that cation is alkali metal and cation are alkaline earth
It is more than one or both of alkali of metal.The organic base can be one or both of hydrazine, urea, amine and quaternary ammonium base with
On.The amine and quaternary ammonium base have been carried out being described in detail in second aspect formed body of the present invention, herein no longer
It is described in detail.
Preferably, the alkali is organic base (such as Formulas I, Formula II, formula III and general formula R12(NH2)2The material of expression), more
Preferably quaternary ammonium base (quaternary ammonium base shown in formula I), more preferably synthesis of titanium silicon molecular sieve template, the nanometer thus prepared
Carbon material formed body has higher crushing strength, and shows in the catalyst as hydrocarbon dehydrogenation reaction and further carry
High catalytic activity.
The dosage of the alkali can be selected according to the dosage in binding agent source.Usually, the alkali and the binding agent
The mol ratio in source can be 0.05-15：1, preferably 0.1-12：1, the binding agent source is in terms of oxide.
Method according to third aspect of the present invention, various decentralized media can be used by nano-carbon material and bonding
Agent source and optional alkali are well mixed.Preferably, the decentralized medium is water.The dosage of the decentralized medium is with can be by nanometer
Carbon material, binding agent source and optional alkali are well mixed to be defined.As an example, when the decentralized medium is water, water
Mol ratio with the binding agent source can be 1-150：1, preferably 4-120：1, the binding agent source is in terms of oxide.
The present inventor has found that molecular sieve preparation solution generally contains caused by molecular sieve preparation process in research process
There are the required binding agent source of the present invention and alkali, while also contain water, above-mentioned molecular sieve preparation solution is mixed with nano-carbon material
One of water, binding agent source and alkali, both or three are alternatively supplemented afterwards, nano-carbon material can not only be molded, and are made
Standby nano-carbon material also shows higher crushing strength, while still shows preferable catalytic activity, also real in addition
Recycling of the system with molecular sieve for preparing for process waste is showed.
The molecular sieve preparation solution can be the common various required binding agent sources of the present invention and optional of providing
The molecular sieve preparation solution of alkali.Preferably, the molecular sieve preparation solution is the crystallization mother liquor and siliceous molecular sieve of siliceous molecular sieve
Reset mixed liquor more than one or both of modified mother liquor.The siliceous molecular sieve can be silica zeolite, containing miscellaneous original
It is more than one or both of sub- molecular sieve (such as HTS) and Si-Al molecular sieve.The crystallization mother liquor refers to passing through water
When thermal crystallisation prepares molecular sieve, the mixture obtained to hydrothermal crystallizing carries out the liquid that separation of solid and liquid obtains, i.e., from hydrothermal crystallizing
Isolate the liquid mixture remained after the molecular sieve to be formed in obtained mixture, also referred to as synthesis mother liquid, filtering waste liquid or
Filter raw liquid.The rearrangement modified mother liquor refers to when preparing modified molecular screen by hydrothermal modification rearrangement, to hydrothermal modification weight
The mixture that is obtained after row carries out the liquid that separation of solid and liquid obtains, i.e., is isolated in the mixture for resetting to obtain from hydrothermal modification point
The liquid mixture remained after son sieve, also referred to as reset mother liquor, modified mother liquor, reset filtering waste liquid, modified filtering waste liquid, modification
Filter raw liquid resets filter raw liquid.The crystallization mother liquor and rearrangement solution can be mixed directly with nano-carbon material, as needed
It can also be concentrated or be mixed after being diluted with nano-carbon material, can enable binding agent source, alkali and the dosage of water
Meet to require, proportion requirement as previously described is defined.
It is highly preferred that the siliceous molecular sieve preparation solution is the crystallization mother liquor (crystallization of such as silica zeolite of si molecular sieves
Mother liquor), crystallization mother liquor (crystallization mother liquor of such as HTS), the crystallization mother liquor of Si-Al molecular sieve of the si molecular sieves containing hetero atom
One or both of with the modification rearrangement solution (rearrangement solution of such as silica zeolite and HTS) of above-mentioned siliceous molecular sieve
Mixed liquor above.
The concrete composition of the crystallization mother liquor and rearrangement solution is not particularly limited, as long as binding agent source and optional can be provided
Alkali.As an example, in the crystallization mother liquor of siliceous molecular sieve, with SiO2The content of the element silicon of meter is generally
0.05-10 weight %, preferably 0.1-5 weight %, more preferably 1-4 weight %；The content of alkali is generally 0.05-15 weights
Measure %, more preferably preferably 0.1-15 weight %, 1.5-14 weight %.As another example, the rearrangement of HTS
In liquid, with SiO2The content of the element silicon of meter is generally 0.01-10 weight %, preferably 0.02-5 weight %, more preferably
0.5-2 weight %；With TiO2The content of the titanium elements of meter is generally 0.0001-0.2 weight %, preferably 0.001-0.1 weights
Measure %, more preferably 0.01-0.08 weight %；The content of alkali is generally 0.01-10 weight %, preferably 0.05-5 weight %,
More preferably 1-4 weight %.As there is an example, in the crystallization mother liquor of Si-Al molecular sieve, with SiO2The element silicon of meter contains
Amount is generally 0.05-10 weight %, more preferably preferably 0.1-8 weight %, 1-4 weight %；With Al2O3The aluminium element of meter
Content is generally 0.01-5 weight %, preferably 0.05-2 weight %, more preferably 0.1-0.5 weight %, and the content of alkali is general
For 0.05-15 weight %, preferably 0.1-14 weight %, more preferably 8-13 weight %.
Method according to third aspect of the present invention, in a preferred embodiment, by the mixture
Before being molded, the mixture is subjected to hydro-thermal process (that is, mixture hydro-thermal process obtained is molded), such energy
Further improve catalytic activity during catalyst of the nano-carbon material formed body finally prepared as hydrocarbon dehydrogenation reaction.It is excellent at this
In the embodiment of choosing, nano-carbon material, binding agent source and optional alkali can be dispersed in water, aqueous dispersions are carried out
Hydro-thermal process.
In the preferred embodiment, the condition of hydro-thermal process is not particularly limited, as long as enter in closed environment
Row high-temperature process.Specifically, the temperature of the hydro-thermal process can be 100-200 DEG C, preferably 120-180 DEG C.It is described
The time of hydro-thermal process can be selected according to the temperature for carrying out hydro-thermal process, typically can be 0.5-24 hours, be preferably
6-12 hours.The hydro-thermal process can carry out (that is, in hydrothermal treatment process, not applying pressure additionally at autogenous pressures
Power), it can also be carried out under conditions of pressure is additionally applied.Preferably, the hydro-thermal process is carried out at autogenous pressures.
Method according to third aspect of the present invention, the dosage in binding agent source can be according to expected nano-carbon material
The content of binding agent is selected in formed body.Usually, the dosage in the binding agent source causes in the formed body that finally prepares,
The content of nano-carbon material can be more than 5 weight % (such as more than 6 weight %), preferably more than 10 weight %, more preferably
More than 50 weight %, it is still more preferably more than 70 weight %, still more preferably more preferably more than 60 weight %
For more than 75 weight %, particularly preferably more than 80 weight %, the content of the nano-carbon material is generally below 95 weight %,
Preferably below 94 weight %, more preferably below 90 weight %.In an example, with the nano-carbon material formed body
On the basis of total amount, the content of the nano-carbon material can be 5-95 weight %, preferably 6-94 weight %, more preferably 8-92
Weight %, more preferably 10-90 weight %, it is still more preferably 20-90 weight %, particularly preferably 40-90 weight
% is measured, particularly preferably 70-90 weight %, the content of the heat-resistant inorganic oxide can be 5-95 weight %, be preferably
6-94 weight %, more preferably 8-92 weight %, more preferably 10-90 weight %, it is still more preferably 10-80 weights
%, particularly preferably 10-60 weight % are measured, particularly preferably 10-30 weight %.When carrying out hydro-thermal process before the forming, i.e.,
Make under relatively low binder content, can also obtain higher intensity.Usually, when carrying out hydro-thermal process before the forming, with institute
On the basis of the total amount for stating formed body, the content of the nano-carbon material is preferably 75-95 weight %, and more preferably 85-95 is heavy
% is measured, the content of the heat-resistant inorganic oxide is preferably 5-25 weight %, more preferably 5-15 weight %.
Method according to third aspect of the present invention, conventional method can be used to contain nano-carbon material and bonding
The mixture in agent source is molded, and obtains article shaped., can be by way of mediating and/or extruding by institute as an example
State mixture shaping.The article shaped can have common variously-shaped such as spherical, bar shaped.
Method according to third aspect of the present invention, the article shaped can be dried under normal conditions,
To remove the volatile materials in the article shaped.Usually, the drying can be carried out at a temperature of 50-200 DEG C, preferably
Carry out at a temperature of 80-180 DEG C, carried out more preferably at a temperature of 120-180 DEG C.The duration of the drying can root
Selected according to dry temperature, typically can be preferably 3-24 hours, more preferably 5-15 hours no more than 48 hours.
It is able to can also be calcined without roasting through dry article shaped.The present invention does not have for the condition of roasting yet
It is particularly limited to, can carries out under normal conditions.Usually, the roasting can 300-800 DEG C, preferably not higher than
Carried out at a temperature of 650 DEG C.The roasting can be carried out in oxygen-containing atmosphere (such as air, oxygen), can also be non-oxygenous
Carried out in atmosphere (such as nitrogen, group 0 element gas).When the roasting is carried out in oxygen-containing atmosphere, the roasting is preferably in 300-
Carry out at a temperature of 500 DEG C, more preferably carried out at a temperature of not higher than 450 DEG C.Enter in the roasting in non-oxygen-containing atmosphere
During row, the roasting is more preferably carried out preferably at 400-800 DEG C at a temperature of the temperature not higher than 750 DEG C.The roasting
Duration can be 1-12 hours, preferably 2-4 hours.
Method according to third aspect of the present invention, the nano-carbon material in various sources can be handled, can
Think not surface treated nano-carbon material, or surface treated nano-carbon material.In the present invention, penetrated using X
Photoelectron Spectroscopy detects to the surface of nano-carbon material, if removing C in nano-carbon material surface-element after testing
The total content of element outside element is below 2 weight %, then the nano-carbon material is considered as into not surface treated nano carbon material
Material, conversely, the nano-carbon material then is considered as into surface treated nano-carbon material.
In one embodiment, the nano-carbon material is not surface treated nano-carbon material.In the embodiment party
In formula, before the mixture is molded, the mixture is preferably subjected to hydro-thermal process, can not only so be significantly improved
The intensity of the formed body finally prepared, and the catalytic performance of the formed body finally prepared can be obviously improved.It is it is highly preferred that described
Binding agent source and optional alkali source come from molecular sieve preparation solution, by the nano-carbon material of non-modified surface treatment in molecule
Catalytic performance of the formed body finally prepared in hydrocarbon dehydrogenation reaction can further be improved by carrying out hydro-thermal process in sieve preparation solution.
In the embodiment, the nano-carbon material can by it is common it is various in the form of exist, be specifically as follows but be not limited to carbon nanometer
It is more than one or both of pipe, graphene, thin layer graphite, nano carbon particle, carbon nano-fiber, Nano diamond and fullerene
Combination.The CNT can be one kind or two in single-walled carbon nanotube, double-walled carbon nano-tube and multi-walled carbon nanotube
The combination of the kind above, preferably multi-walled carbon nanotube.The specific surface area of the multi-walled carbon nanotube can be 50-500m2/ g, it is excellent
Elect 80-300m as2/ g, more preferably 100-250m2/ g, more preferably 120-180m2/g.The multi-walled carbon nanotube exists
Weight-loss ratio in 400-800 DEG C of temperature range is w800, the weight-loss ratio in 400-500 DEG C of temperature range is w500, w500/
w800It is preferred that in the range of 0.01-0.5, more preferably in the range of 0.02-0.3, the model further preferably in 0.05-0.15
In enclosing.As an example, described without surface treating nano carbon material can be second aspect formed body of the present invention
In raw material nano carbon material.
In another embodiment, the nano-carbon material is surface treated nano-carbon material, by X ray photoelectricity
Sub- power spectrum determines that the surface treated nano-carbon material is selected from O elements and N element.Preferably, with the nano carbon material
On the basis of the total amount of material and in terms of element, the content of O elements is 1-8 weight %, preferably 2.5-7.5 weight %, is more preferably
3-7 weight %, more preferably 4.5-7 weight %；The content of N element is 2-8 weight %, preferably 2-6 weight %, more excellent
Elect 3-5 weight %, more preferably 3.5-4.5 weight % as.
Specifically, the surface treated nano-carbon material can be in the present invention one side formed body
Nano-carbon material in second aspect formed body of nano-carbon material and/or the present invention.
According to the fourth aspect of the present invention, the invention provides a kind of method system as described in third aspect of the present invention
Standby nano-carbon material formed body.
Nano-carbon material formed body according to the 4th aspect of the present invention has higher crushing strength.Typically
Ground, the radial direction crushing strength according to the nano-carbon material formed body of the present invention can be more than 4N/mm, generally more than 5N/mm.
Specifically, the radial direction crushing strength of the nano-carbon material formed body according to one side of the invention and second aspect is
5-25N/mm, preferably 6-25N/mm, more preferably 10-25N/mm.
Nano-carbon material formed body according to the 4th aspect of the present invention has higher porosity.Usually, root
Porosity according to the nano-carbon material formed body described in the 4th aspect of the present invention can be more than 5%, it might even be possible to be 10%
More than, such as can be in the range of 5-50%, preferably in the range of 10-30%, more preferably in the range of 12-25%.
According to the fifth aspect of the present invention, the invention provides a kind of forming method of nano-carbon material, this method bag
Include in closed container, nano-carbon material is subjected to hydro-thermal process in a kind of aqueous dispersions, the slurry that hydro-thermal process is obtained
Shaping, obtains article shaped, the article shaped is dried and is optionally calcined, and the aqueous dispersions contain binding agent source,
The binding agent source is selected from the precursor of heat-resistant inorganic oxide and/or heat-resistant inorganic oxide.The binding agent source and this hair
The species in the bright 3rd aspect binding agent source is identical, is no longer described in detail herein.
According to the method described in the 5th aspect of the present invention, the nano-carbon material in various sources can be handled, can
Think not surface treated nano-carbon material, or surface treated nano-carbon material.The nano-carbon material tool
Body can be the nano-carbon material described in third aspect of the present invention methods described, no longer be described in detail herein.
According to the method described in the 5th aspect of the present invention, the aqueous dispersions preferably also contain at least one inorganic agent,
The inorganic agent is organic base and/or nitrogen-containing compound.It so can further improve the nano-carbon material formed body finally prepared
Crushing strength, while can also further improve catalysis of the nano-carbon material formed body finally prepared as hydrocarbon dehydrogenation reaction
Catalytic activity during agent.Particularly when the nano-carbon material is not surface treated nano-carbon material, it can significantly improve
The crushing strength and catalytic performance of the nano-carbon material formed body finally prepared.
The organic base can be more than one or both of amine and quaternary ammonium base (such as Formulas I, Formula II, formula III and formula
R12(NH2)2The material of expression), the organic base instantiation has been carried out in second aspect formed body of the present invention
Detailed description, is herein no longer described in detail.The organic base is preferably quaternary ammonium base (compound shown in formula I), particularly preferably
For synthesis of titanium silicon molecular sieve template.The nitrogen-containing compound can be selected from NH3, hydrazine and urea.
According to the present invention the 5th aspect described in method, in one embodiment, the inorganic agent be organic base or
Person's nitrogen-containing compound.
In a kind of embodiment being more highly preferred to, the inorganic agent is organic base and/or nitrogen-containing compound.At this more
In preferred embodiment, on the basis of the total amount of the inorganic agent, the content of the organic base can be 20-100 weight %,
Preferably 35-92 weight %.It is further preferred that the inorganic agent is organic base and nitrogen-containing compound, it is organic with individually using
Alkali is compared with nitrogen-containing compound as inorganic agent, using organic base and nitrogen-containing compound as inorganic agent by nano-carbon material
The nano-carbon material formed body that (particularly not surface treated nano-carbon material) carries out hydro-thermal process and prepared has higher
Crushing strength, in the catalyst as hydrocarbon dehydrogenation reaction in use, also showing that higher catalytic activity.Contain with first using
Not surface treated nano-carbon material is carried out hydro-thermal process by nitrogen compound, then in the presence of organic base with binding agent source
Hydro-thermal process aftershaping is carried out to compare, will not surface treated nano-carbon material and bonding in the presence of nitrogen-containing compound
Agent source and organic base are mixed into water-filling heat treatment aftershaping, can not only substantially reduce the dosage of nitrogen-containing compound, and prepare
Nano-carbon material formed body shows that the intensity of even more high suitable with the formed body for being first modified aftershaping and preparing and catalysis are lived
Property.On the basis of the total amount of the inorganic agent, the content of the organic base is preferably 50-95 weight %, and more preferably 65-92 is heavy
Measure %.It is further preferred that at least part organic base is quaternary ammonium base (compound shown in formula I), with the inorganic agent
On the basis of total amount, the content of the organic base is preferably 50-95 weight %, more preferably 65-92 weight %, with the organic base
Total amount on the basis of, the content of the quaternary ammonium base is preferably 40-100 weight %, more preferably 45-92 weight %.Partly having
When machine alkali is quaternary ammonium base, remainder organic base can be that (its instantiation may refer to the present invention second for hydramine and/or amine
Hydramine and amine described in the aspect formed body, no longer it is described in detail herein).
From the intensity of nano-carbon material formed body and the angle of catalytic performance that finally prepare further is improved, one
In kind preferred embodiment, the nitrogen-containing compound is ammonia, and part organic base is selected from the compound shown in formula III, preferably selected
From monoethanolamine, diethanol amine and triethanolamine, remainder organic base is preferably that (quaternary ammonium base is preferably 50-85 to quaternary ammonium base
Weight %)；In another preferred embodiment, the nitrogen-containing compound is hydrazine, and at least part organic base is selected from shown in Formulas I
Quaternary ammonium base (content of quaternary ammonium base is preferably more than 45 weight %)；In another preferred embodiment, the nitrogen
Compound is urea, and part organic base is selected from compound and general formula R shown in Formula II12(NH2)2The material of expression, is preferably selected from
Ethylenediamine, n-butylamine and diamines, remainder organic base are preferably that (quaternary ammonium base is preferably 75-95 weights to quaternary ammonium base
Measure %).
The dosage of the inorganic agent can carry out appropriate selection according to the amount in binding agent source.Preferably, the inorganic agent
Mol ratio with the binding agent source can be 0.05-15：1, preferably 0.1-12：1, more preferably 0.5-3.5：1, it is described viscous
Agent source is tied in terms of oxide.
According to the method described in the 5th aspect of the present invention, the dosage of water with can by nano-carbon material and binding agent source and
Optional alkali is well mixed to be defined.Usually, water and the mol ratio in the binding agent source can be 1-150：1, preferably 4-
120：1, the binding agent source is in terms of oxide.
According to the method described in the 5th aspect of the present invention, the dosage in the binding agent source can be according to formed body expection group
Into being selected.Usually, the dosage in the binding agent source make it that in the formed body that finally prepares that the content of nano-carbon material can
Think more than 5 weight % (such as more than 6 weight %), preferably more than 10 weight %, more preferably more than 50 weight %, further
It is still more preferably more than 70 weight % preferably more than 60 weight %, is still more preferably more than 75 weight %, especially
Preferably more than 80 weight %, the content of the nano-carbon material is generally below 95 weight %, preferably below 94 weight %,
More preferably below 90 weight %.In an example, on the basis of the total amount of the nano-carbon material formed body, the nanometer
The content of carbon material can be 5-95 weight % (such as 6-94 weight %), and preferably 8-92 weight %, more preferably 10-90 are heavy
%, more preferably 20-90 weight % are measured, is still more preferably 40-90 weight %, particularly preferably 70-90 weight %,
The content of the heat-resistant inorganic oxide can be 5-95 weight % (such as 6-94 weight %), preferably 8-92 weight %, more excellent
Elect 10-90 weight %, more preferably 10-80 weight % as, be still more preferably 10-60 weight %, particularly preferably
10-30 weight %.Nano-carbon material formed body prepared by method described according to the fifth aspect of the present invention, even in relatively low
Binder content under, can also obtain higher intensity.Usually, on the basis of the total amount of the formed body, the nano-sized carbon
The content of material is preferably 75-95 weight %, more preferably 85-95 weight %, and the content of the heat-resistant inorganic oxide is preferred
For 5-25 weight %, more preferably 5-15 weight %.
According to the method described in the 5th aspect of the present invention, the condition of hydro-thermal process is not particularly limited, as long as close
High-temperature process is carried out in closed loop border.Specifically, the temperature of the hydro-thermal process can be 100-200 DEG C, preferably 120-
180℃.The time of the hydro-thermal process can be selected according to the temperature for carrying out hydro-thermal process, typically can be that 0.5-24 is small
When, preferably 6-12 hours.The hydro-thermal process can be carried out (that is, in hydrothermal treatment process, not additionally at autogenous pressures
Apply pressure), it can also be carried out under conditions of pressure is additionally applied.Preferably, the hydro-thermal process is entered at autogenous pressures
OK.
According to the method described in the 5th aspect of the present invention, the shaping, the drying of article shaped and optionally it is calcined
Method and condition are identical with the description in the method described in third aspect of the present invention, are no longer described in detail herein.
The sixth aspect of the invention, prepared the invention provides a kind of method as described in the 5th aspect of the present invention
Nano-carbon material formed body.
Nano-carbon material formed body according to the 6th aspect of the present invention has higher crushing strength.Typically
Ground, the radial direction crushing strength of the nano-carbon material formed body according to the 6th aspect of the present invention can be more than 7N/mm, excellent
More than 10N/mm is elected as, typically in the range of 12-25N/mm.According to the present invention the 6th aspect described in nano-carbon material into
Type body has higher porosity.Usually, the hole of the nano-carbon material formed body according to the 6th aspect of the present invention
Rate can be more than 5%, it might even be possible to it is more than 10%, such as can be in the range of 5-50%, the model preferably in 10-30%
In enclosing, more preferably in the range of 12-25%.
According to the seventh aspect of the present invention, the invention provides according to the present invention the on one side, second aspect, the
Application of the nano-carbon material formed body as the catalyst of hydrocarbon dehydrogenation reaction described in four aspects and the 6th aspect.It is described de-
Hydrogen reaction can be carried out in the presence of oxygen, can not also be carried out in the presence of oxygen.Preferably, the dehydrogenation reaction is in oxygen
In the presence of carry out, can so obtain more preferable catalytic effect.The species of the hydrocarbon and the actual conditions of dehydrogenation reaction will be under
Text is described in detail, and is no longer described in detail herein.
According to the eighth aspect of the present invention, the invention provides a kind of hydrocarbon dehydrogenation reaction method, this method, which is included in, deposits
Under conditions of oxygen, under hydrocarbon dehydrogenation reaction conditions, by hydrocarbon with the present invention the on one side, second aspect,
Nano-carbon material formed body contact described in 4th aspect and the 6th aspect.According to the nano-carbon material formed body of the present invention
It can use directly as catalyst, be used after can also crushing according to specific needs as catalyst.
Dehydrogenation can be carried out to polytype hydrocarbon according to the hydrocarbon dehydrogenation reaction method of the present invention, so as to obtain unsaturation
Hydrocarbon, such as alkene.The method according to the invention to alkane particularly suitable for carrying out dehydrogenation, so as to obtain alkene.The hydrocarbon is preferably alkane
Hydrocarbon, such as C2-C12Alkane.Specifically, the hydrocarbon can be but be not limited to ethane, propane, normal butane, iso-butane, pentane, different
Pentane, neopentane, pentamethylene, n-hexane, 2- methylpentanes, 3- methylpentanes, 2,3- dimethylbutanes, hexamethylene, methyl ring
Pentane, normal heptane, 2- methyl hexanes, 3- methyl hexanes, 2- ethylpentanes, 3- ethylpentanes, 2,3- dimethyl pentanes, 2,4- bis-
Methylpentane, normal octane, 2- methyl heptanes, 3- methyl heptanes, 4- methyl heptanes, 2,3- dimethylhexanes, 2,4- dimethyl oneself
Alkane, 2,5- dimethylhexanes, 3- ethyl hexanes, 2,2,3- trimethylpentanes, 2,3,3- trimethylpentanes, 2,4,4- trimethyls penta
Alkane, 2- methyl -3- ethylpentanes, n -nonane, 2- methyloctanes, 3- methyloctanes, 4- methyloctanes, 2,3- dimethyl heptanes,
2,4- dimethyl heptanes, 3- ethyl heptanes, 4- ethyl heptanes, 2,3,4- trimethyl cyclohexanes, 2,3,5- trimethyl cyclohexanes, 2,4,5-
Trimethyl cyclohexane, 2,2,3- trimethyl cyclohexanes, 2,2,4- trimethyl cyclohexanes, 2,2,5- trimethyl cyclohexanes, 2,3,3- trimethyls oneself
Alkane, 2,4,4- trimethyl cyclohexanes, 2- methyl -3- ethyl hexanes, 2- methyl -4- ethyl hexanes, 3- methyl -3- ethyl hexanes, 3-
Methyl -4- ethyl hexanes, 3,3- diethylpentanes, 1- methyl -2- ethyl cyclohexanes, 1- methyl -3- ethyl cyclohexanes, 1- first
(including trimethyl-cyclohexane is various for base -4- ethyl cyclohexanes, n-propyl hexamethylene, isopropyl cyclohexane, trimethyl-cyclohexane
Isomers, such as 1,2,3- trimethyl-cyclohexanes, 1,2,4- trimethyl-cyclohexanes, 1,2,5- trimethyl-cyclohexanes, 1,3,5- front threes
Butylcyclohexane), n-decane, 2- methylnonanes, 3- methylnonanes, 4- methylnonanes, 5- methylnonanes, 2,3- dimethyl octane,
2,4- dimethyl octane, 3- ethyls octane, 4- ethyls octane, 2,3,4- trimethylheptanes, 2,3,5- trimethylheptanes, 2,3,6-
Trimethylheptane, 2,4,5- trimethylheptanes, 2,4,6- trimethylheptanes, 2,2,3- trimethylheptanes, 2,2,4- trimethyls heptan
Alkane, 2,2,5- trimethylheptanes, 2,2,6- trimethylheptanes, 2,3,3- trimethylheptanes, 2,4,4- trimethylheptanes, 2- first
Base -3- ethyl heptanes, 2- methyl -4- ethyl heptanes, 2- methyl -5- ethyl heptanes, 3- methyl -3- ethyl heptanes, 4- methyl -3-
Ethyl heptane, 5- methyl -3- ethyl heptanes, 4- methyl -4- ethyl heptanes, 4- propyl group heptane, 3,3- diethylhexanes, 3,4- bis-
Ethyl hexane, 2- methyl -3,3- diethylpentanes, vinylbenzene, 1- phenyl-propanes, 2- phenyl-propanes, 1- phenyl butanes, 2- phenyl
Combination more than one or both of butane, 1- phenyl pentanes, 2- phenyl pentanes and 3- phenyl pentanes.
The hydrocarbon is more preferably more than one or both of propane, normal butane, iso-butane and vinylbenzene, further preferably
For normal butane.
According to the hydrocarbon dehydrogenation reaction method of the present invention, the reaction can be carried out under conditions of it oxygen be present, can also
Carried out under conditions of in the absence of oxygen.It is preferred that carried out under conditions of it oxygen be present.When being carried out under conditions of oxygen being present,
The dosage of oxygen can be conventional selection.Usually, the mol ratio of hydrocarbon and oxygen can be 0.01-100：1, preferably 0.1-
10：1, more preferably 0.2-5：1, most preferably 0.5-2：1.
According to the hydrocarbon dehydrogenation reaction method of the present invention, can by carrier gas by hydrocarbon and optional oxygen be sent into reactor with
The haptoreaction of nano-carbon material containing hetero atom.The carrier gas can be it is conventional at reaction conditions will not be with reactant and reaction
Chemical interaction and the gas that will not be decomposed occur for product, such as nitrogen, carbon dioxide, rare gas and vapor
One or both of more than combination.The dosage of the carrier gas can be conventional selection.Usually, the content of carrier gas can be with
30-99.5 volume %, preferably 50-99 volumes %, more preferably 70-98 volumes %.
According to the hydrocarbon dehydrogenation reaction method of the present invention, the temperature of the contact can be conventional selection, to be enough to send out hydrocarbon
Raw dehydrogenation reaction is defined.Usually, the contact can be carried out at a temperature of 200-650 DEG C, preferably in 300-600 DEG C of temperature
Degree is lower to be carried out, and is carried out more preferably at a temperature of 350-550 DEG C, further preferably in 400-450 DEG C of temperature when such as hydrocarbon being butane
Degree is lower to be carried out.
According to the hydrocarbon dehydrogenation reaction method of the present invention, the contact is carried out preferably in fixed bed reactors.
According to the hydrocarbon dehydrogenation reaction method of the present invention, the duration of the contact can be selected according to the temperature of contact
Select, when such as described contact is carried out in fixed bed reactors, the duration of contact can be represented with the weight (hourly) space velocity (WHSV) of charging.
Usually, the weight (hourly) space velocity (WHSV) of feed gas can be 1-50000h-1, preferably 10-20000h-1, more preferably 50-10000h-1, more preferably 100-8000h-1, such as 1000-3000h-1。
Describe the present invention in detail with reference to embodiments, but and be not so limited the scope of the present invention.
In following preparation example, X-ray photoelectron spectroscopic analysis are in Thermo Scientific companies equipped with Thermo
Tested on the ESCALab250 type x-ray photoelectron spectroscopies of Avantage V5.926 softwares, excitaton source is monochromatization Al
K α X ray, energy 1486.6eV, power 150W, the penetrating base vacuum that can be 30eV, analyze during test used in narrow scan
For 6.5 × 10-10Mbar, C1s peaks (284.0eV) correction of electron binding energy simple substance carbon, in Thermo Avantage softwares
Upper carry out data processing, quantitative analysis is carried out using sensitivity factor method in analysis module.Sample is before testing at 150 DEG C
Temperature and 1 normal atmosphere are depressed to be dried 3 hours in helium atmosphere.
In following preparation example, thermogravimetric analysis is carried out on TA5000 thermal analyzers, and test condition is air atmosphere, heating speed
It is room temperature (25 DEG C) to 1000 DEG C to spend for 10 DEG C/min, temperature range.Sample is big in 150 DEG C of temperature and 1 standard before testing
Dried 3 hours in helium atmosphere under air pressure.Using the ASAP2000 types N of Micromertrics companies of the U.S.2Physical adsorption appearance
Measurement the specific area.
The property of multi-walled carbon nanotube in following preparation example as raw material nano carbon material is listed in table 1 below.
Table 1
In following examples and comparative example, the content of silicon, titanium and aluminium element in crystallization mother liquor and rearrangement solution and alkali
Content is using Perkin-Elmer 3300DV types sensing coupled plasma (ICP) spectroanalysis instrument measure.
In following examples and comparative example, radial direction crushing strength according to《Petrochemical Engineering Analysis method》(Science Press,
The nineteen ninety first edition, Yang Cui surely wait compile) described in RIPP 25-90 specified in method measure；Porosity refers to nano-carbon material
The ratio of all interstitial space volume sums and the volume of the nano-carbon material formed body, is referred to as the nanometer in formed body
The porosity of carbon material formed body, is expressed as a percentage, using mercury injection method (reference literature《Graphite porosity of porous material determines
Technique study》,《Lubrication and sealing》, 2010,35 (10)：99-101) method determines.
Preparation example 1-40 is used to prepare nano-carbon material containing hetero atom.
Preparation example 1
(1) (it is purchased from Chinese Academy of Sciences's Chengdu organic chemistry using 20g as the multi-walled carbon nanotube A of raw material nano carbon material
Co., Ltd) it is scattered in deionized water, be dispersed under the conditions of sonic oscillation and carry out, sonic oscillation condition includes：Frequency is
14kHz, time are 0.5 hour.Then, NH is added3It is well mixed with triethanolamine, so as to obtain aqueous dispersions, wherein, by original
Expect nano-carbon material：NH3：Triethanolamine：H2O weight ratio is 1：0.05：0.25：50 ratio feeds intake.
(2) by obtained aqueous dispersions in the autoclave with polytetrafluoroethyllining lining, in 140 DEG C of temperature
Under, react 36 hours at autogenous pressures.After reaction terminates, after the temperature in autoclave is down to room temperature, reaction is opened
Kettle, reactant mixture is filtered and washed, and collect solid matter.By the solid matter being collected into, in normal pressure, (1 standard is big
Air pressure, similarly hereinafter), after drying 12 hours at a temperature of 120 DEG C, obtain nano-carbon material containing hetero atom, its composition, specific surface area with
And w500/w800Listed in table 2.
Preparation example 2
It is equipped with being placed in the identical aqueous dispersions of preparation example 1 in the three-necked flask of condenser pipe, the three-necked flask is placed in
Temperature is back flow reaction 36 hours under normal pressure in 140 DEG C of oil bath.After reaction terminates, treat that the temperature in three-necked flask is down to
After room temperature, reactant mixture is filtered and washed, and collects solid matter.By the solid matter being collected into normal pressure, 120
After being dried 12 hours at a temperature of DEG C, nano-carbon material containing hetero atom is obtained.
Preparation example 3
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 1, unlike, in step (1), as
Raw material nano carbon material is multi-walled carbon nanotube B.
Preparation example 4
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 1, unlike, in step (2), will
To aqueous dispersions be placed in the autoclave with polytetrafluoroethyllining lining, at a temperature of 90 DEG C, at autogenous pressures
Reaction 36 hours.
Preparation example 5
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 1, unlike, in step (1), NH3
With the integral molar quantity of triethanolamine with preparation example 1 under the same conditions, make NH3Mol ratio with triethanolamine is 1：1.
Preparation example 6
(1) (it is purchased from Chinese Academy of Sciences's Chengdu organic chemistry using 20g as the multi-walled carbon nanotube C of raw material nano carbon material
Co., Ltd) it is scattered in deionized water, be dispersed under the conditions of sonic oscillation and carry out, sonic oscillation condition includes：Frequency is
90kHz, time are 2 hours.Then, NH is added3It is well mixed with diethanol amine, so as to obtain aqueous dispersions, wherein, by raw material
Nano-carbon material：NH3：Diethanol amine：H2O weight ratio is 1：2：5：80 ratio feeds intake.
(2) by obtained aqueous dispersions in the autoclave with polytetrafluoroethyllining lining, in 180 DEG C of temperature
Under, react 24 hours at autogenous pressures.After reaction terminates, after the temperature in autoclave is down to room temperature, reaction is opened
Kettle, reactant mixture is filtered and washed, and collect solid matter.By the solid matter being collected into normal pressure, 150 DEG C
At a temperature of dry 6 hours after, obtain nano-carbon material containing hetero atom, its structural parameters is listed in table 2.
Preparation example 7
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), as
Raw material nano carbon material is multi-walled carbon nanotube D.
Preparation example 8
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (2), will
To aqueous dispersions in the autoclave with polytetrafluoroethyllining lining, at a temperature of 230 DEG C, at autogenous pressures instead
Answer 24 hours.
Preparation example 9
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), NH3
With the integral molar quantity of diethanol amine with preparation example 5 under the same conditions, make NH3：The mol ratio of diethanol amine is 1：0.1.
Preparation example 10
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), diethyl
Hydramine is replaced with the n-propylamine of equimolar amounts.
Preparation example 11
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), diethyl
Hydramine is replaced with the pyridine of equimolar amounts.
Preparation example 12
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), diethyl
Hydramine is replaced with the cyclohexylamine of equimolar amounts.
Preparation example 13
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), diethyl
Hydramine is replaced with ethylenediamine, and the mole of ethylenediamine is 0.5 times of the mole of diethanol amine in preparation example 6.
Preparation example 14
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), diethyl
Hydramine is replaced with the tetraethyl ammonium hydroxide of equimolar amounts.
Preparation example 15
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), diethyl
Hydramine is replaced with hexamethylenetetramine, and the mole of hexamethylenetetramine is 0.25 of the mole of diethanol amine in preparation example 6
Times.
Preparation example 16
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, unlike, in step (1), diethyl
Hydramine is replaced with diethylenetriamine, and the mole of diethylenetriamine is 0.3 times of the mole of diethanol amine in preparation example 6.
Preparation example 17
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 1, difference is as follows：
It is in step (1), raw material nano carbon material is scattered in deionized water, then add hydrazine and TMAH
It is well mixed, wherein, by raw material nano carbon material：Hydrazine：TMAH：H2O weight ratio is 1：0.02：4.5：40
Ratio feeds intake；In step (2), by obtained aqueous dispersions in the autoclave with polytetrafluoroethyllining lining, in 120 DEG C
At a temperature of, react 48 hours at autogenous pressures, obtain nano-carbon material containing hetero atom, its structural parameters is listed in table 3.
Preparation example 18
It is equipped with being placed in the identical aqueous dispersions of preparation example 17 in the three-necked flask of condenser pipe, the three-necked flask is placed in
Temperature is back flow reaction 48 hours under normal pressure in 120 DEG C of oil bath.After reaction terminates, treat that the temperature in three-necked flask is down to
After room temperature, reactant mixture is filtered and washed, and collects solid matter.By the solid matter being collected into normal pressure, 120
After being dried 12 hours at a temperature of DEG C, nano-carbon material containing hetero atom is obtained.
Preparation example 19
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 17, unlike, will in step (2)
Obtained aqueous dispersions are in the autoclave with polytetrafluoroethyllining lining, at a temperature of 80 DEG C, at autogenous pressures
Reaction 48 hours.
Preparation example 20
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 17, unlike, as raw material nano
Carbon material is multi-walled carbon nanotube B preparation examples.
Preparation example 21
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 17, unlike, in step (1), hydrazine
With the integral molar quantity of TMAH with preparation example 17 under the same conditions, make hydrazine：The mol ratio of TMAH
For 1：85.
Preparation example 22
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, difference is as follows：
It is in step (1), raw material nano carbon material is scattered in deionized water, then add hydrazine and TPAOH
It is well mixed, so as to obtain aqueous dispersions, wherein, raw material nano carbon material：Hydrazine：TPAOH：H2O weight ratio is
1：1：8：200；In step (2), obtained aqueous dispersions are placed in the autoclave with polytetrafluoroethyllining lining, in
At a temperature of 170 DEG C, react 24 hours at autogenous pressures.
Preparation example 23
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 22, unlike, in step (1), make
What it is for raw material nano carbon material is multi-walled carbon nanotube D preparation examples.
Preparation example 24
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 22, unlike, in step (1), hydrazine
With the integral molar quantity of TPAOH with preparation example 22 under the same conditions, make hydrazine：The mol ratio of TPAOH
For 1：1.
Preparation example 25
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 22, unlike, will in step (2)
Obtained aqueous dispersions are in the autoclave with polytetrafluoroethyllining lining, at a temperature of 200 DEG C, at autogenous pressures
Reaction 24 hours.
Preparation example 26
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 22, unlike, in step (1), four
Propyl group ammonium hydroxide is replaced with the diethanol amine of equimolar amounts.
Preparation example 27
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 22, unlike, in step (1), four
Propyl group ammonium hydroxide is replaced with the n-propylamine of equimolar amounts.
Preparation example 28
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 22, unlike, in step (1), four
Propyl group ammonium hydroxide is replaced with hexamethylene diamine, and the mole of hexamethylene diamine is the mole of TPAOH in preparation example 22
0.5 times.
Preparation example 29
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 1, difference is as follows：In step (1),
Raw material nano carbon material is scattered in deionized water, urea is added and hexamethylene diamine is well mixed, so as to obtain aqueous dispersions, its
In, raw material nano carbon material：Urea：Hexamethylene diamine：H2O weight ratio is 1：1：1：20；In step (2), obtained moisture is dissipated
Liquid is placed in the autoclave with polytetrafluoroethyllining lining, and at a temperature of 110 DEG C, it is small to react 36 at autogenous pressures
When.
Preparation example 30
It is equipped with being placed in the identical aqueous dispersions of preparation example 29 in the three-necked flask of condenser pipe, the three-necked flask is placed in
Temperature is back flow reaction 36 hours under normal pressure in 110 DEG C of oil bath.After reaction terminates, treat that the temperature in three-necked flask is down to
After room temperature, reactant mixture is filtered and washed, and collects solid matter.By the solid matter being collected into normal pressure, 120
After being dried 6 hours at a temperature of DEG C, nano-carbon material containing hetero atom is obtained.
Preparation example 31
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 29, unlike, will in step (2)
Obtained aqueous dispersions are in the autoclave with polytetrafluoroethyllining lining, at a temperature of 80 DEG C, at autogenous pressures
Reaction 36 hours.
Preparation example 32
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 29, unlike, as raw material nano
Carbon material is multi-walled carbon nanotube B preparation examples.
Preparation example 33
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 29, unlike, in step (1),
The integral molar quantity of urea and hexamethylene diamine and preparation example 29 are under the same conditions so that urea：The mol ratio of hexamethylene diamine is 1：0.1.
Preparation example 34
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 6, difference is as follows：
It is in step (1), raw material nano carbon material is scattered in deionized water, then add urea and n-butylamine mixing is equal
It is even, so as to obtain aqueous dispersions, wherein, by raw material nano carbon material：Urea：N-butylamine：H2O weight ratio is 1：4：8：150
Ratio feed intake；In step (2), obtained aqueous dispersions are placed in the autoclave with polytetrafluoroethyllining lining, in
At a temperature of 160 DEG C, react 24 hours at autogenous pressures.
Preparation example 35
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 34, unlike, in step (1), make
What it is for raw material nano carbon material is multi-walled carbon nanotube D preparation examples.
Preparation example 36
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 34, unlike, in step (1),
The integral molar quantity of urea and n-butylamine and preparation example 34 are under the same conditions so that urea：The mol ratio of n-butylamine is 1：2.5.
Preparation example 37
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 34, unlike, will in step (2)
Obtained aqueous dispersions are in the autoclave with polytetrafluoroethyllining lining, at a temperature of 190 DEG C, at autogenous pressures
Reaction 24 hours.
Preparation example 38
Using with the identical method of preparation example 34 prepare nano-carbon material containing hetero atom, the difference is that, n-butylamine with etc. rub
The diethanol amine of your amount replaces.
Preparation example 39
Using with the identical method of preparation example 34 prepare nano-carbon material containing hetero atom, the difference is that, n-butylamine with etc. rub
The TMAH of your amount replaces.
Preparation example 40
Nano-carbon material containing hetero atom is prepared using with the identical method of preparation example 34, unlike, n-butylamine second two
Amine replaces, and the mole of ethylenediamine is 0.5 times of the mole of n-butylamine in preparation example 34.
Embodiment 1-95 is used to illustrate according to nano-carbon material formed body of the present invention and preparation method thereof.
It is related to following binding agent source in embodiment 1-95.
Ludox：Purchased from Zhejiang Province Yuda Chemical Co., Ltd, dioxide-containing silica is 25 weight %
Tetraethyl orthosilicate：Purchased from Zhangjiagang new Asia Chemical Co., Ltd. (numbering TES)
Alumina gel：Purchased from Shandong, Chile reaches chemical inc, and alumina content is 12 weight %
Aluminium isopropoxide：Purchased from Beijing Deco Dao Jin Science and Technology Ltd.s (numbering IPOA)
Titanium oxide：Purchased from Shandong Origine Nanomaterial Engineering Co., Ltd., particle diameter 5-10nm
Tetraethyl titanate：Purchased from Jin Yu chemical industry Co., Ltd of Shouguang City (numbering TET)
(1) crystallization mother liquor of HTS
Method according to US4410501 embodiments 1 prepares titanium-silicon molecular sieve TS-1, and collects crystallization mother liquor.Concrete operations
Process is：
455g tetraethyl orthosilicates are placed in equipped with agitating device and for without CO2In the reactor of atmosphere, Ran Houxian
The TPAOH aqueous solution of 15g tetraethyl titanates and 800g concentration for 25 weight % is added afterwards., will after stirring 1 hour
Temperature is increased to 80~90 DEG C, continues stirring 5 hours.Then deionized water is added into reaction solution, until the totality of reaction solution
Product is 1.5L.Then, reaction solution is transferred to and be equipped with the autoclave of agitating device, the hydro-thermal under 175 DEG C, self-generated pressure
After crystallization 10 days, obtained reactant mixture is filtered, crystallization mother liquor is collected, by the solid being filtrated to get in 550 DEG C of air gas
It is calcined 6 hours in atmosphere, so as to obtain titanium-silicon molecular sieve TS-1.
After testing, on the basis of the total amount of crystallization mother liquor, with SiO2The content of the element silicon of meter is 1.2 weight %, with TiO2
The content of the titanium elements of meter is 0.04 weight %, and the content of TPAOH is 3.1 weight %.The crystallization mother liquor is concentrated
(concentrate numbering be TS-A) on the basis of the total amount of concentrate, with SiO2The content of the element silicon of meter is 3.6 weight %, with
TiO2The content of the titanium elements of meter is 0.12 weight %, and the content of TPAOH is 9.3 weight %.
(2) crystallization mother liquor of HTS
Method according to US4410501 embodiments 2 prepares titanium-silicon molecular sieve TS-1, and collects crystallization mother liquor.Concrete operations
Process is：
150g tetraethyl titanates are slowly added dropwise in 2.5L distilled water and hydrolyzed under agitation, obtain a white gum
Suspension, this suspension is then cooled to 5 DEG C；Then it is 30% by the 1.8L mass concentrations for having cooled to 5 DEG C in advance
Aqueous hydrogen peroxide solution is incorporated in wherein, and is kept for 2 hours at 5 DEG C under conditions of intermittent stirring, and it is molten to obtain an orange clarification
Liquid；Then the TPAOH aqueous solution that the 2.4L mass concentrations for having cooled to 5 DEG C in advance are 25% is added to orange
In settled solution, after 1 hour, 500g SiO are added2The Ludox that content is 40% carefully mixes, and obtained mixture is in normal temperature
Left overnight；Most after 70-80 DEG C of heating stirring 6 hours.Obtained mixture is transferred to the high pressure for being equipped with agitating device
In reactor, hydrothermal crystallizing filtered obtained reactant mixture after 10 days under 175 DEG C, self-generated pressure, and it is female to collect crystallization
Liquid, the solid phase being filtrated to get is calcined 6 hours in 550 DEG C of air atmospheres, confirmed through X-ray diffraction analysis, obtain titanium silicon point
Son sieve TS-1.
After testing, on the basis of the total amount of crystallization mother liquor, with SiO2The content of the element silicon of meter is 2.8 weight %, with TiO2
The content of the titanium elements of meter is 0.04 weight %, and the content of TPAOH is 1.6 weight %.The crystallization mother liquor is concentrated
(concentrate numbering be TS-B) on the basis of the total amount of concentrate, with SiO2The content of the element silicon of meter is 7 weight %, with
TiO2The content of the titanium elements of meter is 0.1 weight %, and the content of TPAOH is 4 weight %.
(3) crystallization mother liquor of HTS
According to J.Chem.Soc.Chem.Commun., the method described in 1992,589-590 prepares HTS
Ti-Beta, crystallization mother liquor is collected during separation of solid and liquid.Specifically preparation process is：
At room temperature, tetraethyl titanate and amorphous silica gel Aerosil 200 are added to tetraethyl hydrogen-oxygen under agitation
Change in ammonium (TEAOH) aqueous solution, then add appropriate aluminum nitrate, the glue mole composition now formed is A12O3：TiO2：
SiO2：H2O：TEAOH=1：12：388：6000：108, the glue of formation is transferred to the autoclave with polytetrafluoroethyllining lining
Middle carry out dynamic crystallization, crystallization temperature are 130 DEG C, mixing speed 60rpm, crystallization time 3d.After cooling, consolidate what is obtained
Liquid mixture is centrifuged, and obtains solid and crystallization mother liquor (numbering TS-C).The solid isolated is washed with water to pH=9
Left and right, 80 DEG C of dry 5h, the lower 580 DEG C of roastings 5h of air atmosphere, so as to obtain HTS Ti-Beta.
After testing, on the basis of the total amount of crystallization mother liquor (numbering TS-C), with SiO2The content of the element silicon of meter is 3.4
Weight %, with TiO2The content of the titanium elements of meter is 0.3 weight %, and the content of tetraethyl ammonium hydroxide is 13.1 weight %.
(4) rearrangement solution of HTS
Method according to the embodiment 9 of China's application 99126289.1 obtains the rearrangement solution of HTS, specific to prepare
Process is：
According to TS-1 molecular sieves (gram)：Tetraethyl ammonium hydroxide (mole)：Water (mole)=100：0.25：60 ratio is mixed
Close uniformly, mixture is placed in stainless steel sealing reactor, constant temperature is placed 3 days under 175 DEG C and self-generated pressure.Cool down release
Afterwards, filtered, gained filtrate is the rearrangement solution of HTS.
After testing, on the basis of the total amount of rearrangement solution, with SiO2The content of the element silicon of meter is 1.1 weight %, with TiO2Meter
The contents of titanium elements be 0.02 weight %, the content of TPAOH is 3.6 weight %.Rearrangement solution is concentrated into (concentration
Liquid numbering is TS-D) extremely on the basis of the total amount of rearrangement solution, with SiO2The content of the element silicon of meter is 4.4 weight %, with TiO2Meter
The contents of titanium elements be 0.08 weight %, the content of TPAOH is 14.4 weight %.
(5) crystallization mother liquor of Si-Al molecular sieve
With reference to the method for US4410501 embodiments 1 sial is prepared using silicon source aluminium isopropoxide replacement titanium source tetraethyl titanate
Molecular sieve, and collect crystallization mother liquor.Specific operation process is：
Without CO2Atmosphere under, 455g tetraethyl orthosilicates are positioned in heatproof glass container, with stirring add 15g
Aluminium isopropoxide, be subsequently added into by 800g mass concentrations be 25% the TPAOH aqueous solution, mix 4h after, in 80-90
DEG C heating stirring drives ethanol out of after 5 hours completely.Then 1.5L is added water to, obtained mixture is transferred to outfit stirring
In the autoclave of device, hydrothermal crystallizing 10 days under 175 DEG C, self-generated pressure, obtained reactant mixture is filtered, collected
Crystallization mother liquor.
After testing, on the basis of the total amount of crystallization mother liquor (being AS-F by crystallization mother liquor numbering), with SiO2The element silicon of meter
Content be 2.3 weight %, with Al2O3The content of the aluminium element of meter is 0.14 weight %, and the content of TPAOH is
12.5 weight %.By crystallization mother liquor concentration (concentrate numbering is AS-E) extremely on the basis of the total amount of concentrate, with concentrate
Total amount on the basis of, with SiO2The content of the element silicon of meter is 8.28 weight %, with Al2O3The content of the aluminium element of meter is 0.50
Weight %, the content of TPAOH is 45 weight %.
Embodiment 1-48
The condition provided according to table 4, nano-carbon material is molded respectively using following methods.
Nano-carbon material is well mixed with binding agent source under environment temperature (25 DEG C) respectively, mixture feeding will be obtained
After being dried and be optionally calcined in strip mould, obtain nano-carbon material formed body and (randomly select part formed body to enter
Row polishing, obtain the batten that length is 3-5mm and be used to determine crushing strength and porosity, as a result listed in table 4), will be surplus
Sieved after remaining formed body is broken, obtain graininess formed body, its mean particle size (abbreviation particle diameter) is listed in table 4.
Table 4
1：The dosage of nano-carbon material is 10g2：TPAOH3：Tetraethyl ammonium hydroxide4：Dosage is to aoxidize
Thing meter5：The species and dosage of the inorganic agent additionally added outside contained inorganic agent in binding agent source
Embodiment 49-91
Using following methods, nano-carbon material is molded by the condition provided according to table 5 respectively：
Nano-carbon material is mixed with binding agent source and optional inorganic agent respectively, is then placed in obtained mixture
In sealing autoclave with polytetrafluoroethyllining lining, hydro-thermal process is carried out under self-generated pressure.Treat in autoclave
Temperature be down to environment temperature after, open reactor, obtained slurries be sent into strip mould and are dried and optionally
After roasting, obtain nano-carbon material formed body and (randomly select part formed body to be polished, obtain the batten that length is 3-5mm
For determining crushing strength and porosity, as a result listed in table 5), by remaining formed body it is broken after sieved, obtain
Granular formed body, its mean particle size are listed in table 5.
Embodiment 92
Difference with embodiment 49 is, nano-carbon material is well mixed with binding agent source in environment temperature (25 DEG C)
Afterwards, without hydro-thermal process, but directly it is molded.
Embodiment 93
Difference with embodiment 49 is, the mixture in nano-carbon material and binding agent source is placed in three-necked flask,
With carrying out back flow reaction, time and the water in embodiment 49 of back flow reaction at a temperature of the hydro-thermal process temperature identical of embodiment 49
Heat treatment time is identical, and the mixture that back flow reaction is obtained is sent into mould.
Embodiment 94
Difference with embodiment 54 is, nano-carbon material is well mixed with binding agent source in environment temperature (25 DEG C)
Afterwards, without hydro-thermal process, but directly it is molded.
Embodiment 95
Difference with embodiment 54 is, the mixture in nano-carbon material and binding agent source is placed in three-necked flask,
With carrying out back flow reaction, time and the water in embodiment 54 of back flow reaction at a temperature of the hydro-thermal process temperature identical of embodiment 54
Heat treatment time is identical, and the mixture that back flow reaction is obtained is sent into mould.
Table 5
1：The dosage of nano-carbon material is 10g2：TPAOH3：Tetraethyl ammonium hydroxide4：Dosage is with oxide
Meter5：The species and dosage of the inorganic agent additionally added outside contained inorganic agent in binding agent source
Testing example 1-95
The catalytic performance of the catalyst prepared using following methods successively testing example 1-95.
The graininess formed body respectively prepared by 0.25g embodiments 1-95 is micro- in universal fixed bed as Catalyst packing
In type quartz tube reactor, the end seal of miniature quartz pipe reactor two has quartz sand, will under the conditions of 0MPa (gauge pressure) and 425 DEG C
(concentration of normal butane is 2.08 volume %, normal butane and oxygen molar ratio 0.5 to gas containing normal butane and oxygen：1, surplus
For the nitrogen as carrier gas) with 2000h-1Weight (hourly) space velocity (WHSV) be passed through in reactor and reacted, continuous monitoring is defeated from reactor
The composition of the reactant mixture gone out, and calculate n-butane conversion and total olefin selectivity, the result of reaction 3 hours and 24 hours
Listed in table 6.
Test comparison example 1-4
Using the catalytic performance for testing multi-walled carbon nanotube A, B, C and D successively with testing example 1-95 identicals method.
Table 6
The preferred embodiment of the present invention described in detail above, still, the present invention are not limited in above-mentioned embodiment
Detail, in the range of the technology design of the present invention, a variety of simple variants can be carried out to technical scheme, this
A little simple variants belong to protection scope of the present invention.It is further to note that described in above-mentioned embodiment
Each particular technique feature, in the case of reconcilable, can be combined by any suitable means, in order to avoid not
Necessary repetition, the present invention no longer separately illustrate to various combinations of possible ways.In addition, a variety of implementations of the present invention
It can also be combined between mode, as long as it without prejudice to the thought of the present invention, it is public that it should equally be considered as institute of the invention
The content opened.
Claims (37)
1. a kind of nano-carbon material formed body, the formed body contains nano-carbon material and for the nano-carbon material to be bonded
The heat-resistant inorganic oxide of shaping, the nano-carbon material contain O elements and N element.
2. formed body according to claim 1, on the basis of the total amount of the nano-carbon material and in terms of element, O elements
Content be 1-8 weight %, more preferably preferably 2.5-7.5 weight %, 3-7 weight %, more preferably 4.5-7 weights
Measure %；The content of N element is 1-8 weight %, more preferably preferably 2-6 weight %, 3-5 weight %, is more preferably
3.5-4.5 weight %；The content of C element is 84-98 weight %, and preferably 86.5-95.5 weight %, more preferably 88-94 are heavy
Measure %, more preferably 88.5-92 weight %.
3. formed body according to claim 2, wherein, in the range of 531.0-532.5eV in x-ray photoelectron power spectrum
The amount for the O elements that peak determines is IO c, the O elements that are determined by the peak in the range of 532.6-533.5eV in x-ray photoelectron power spectrum
Measure as IO e, IO c/IO eIn the range of 1.2-2.5, preferably in the range of 1.3-2.2, more preferably in the range of 1.4-2；
In the nano-carbon material, the total amount of the N element in the nano-carbon material containing hetero atom is determined by x-ray photoelectron power spectrum
For IN t, the amount of the N element determined by the peak in the range of 398.5-400.1eV in x-ray photoelectron power spectrum is IN c, IN c/IN t
In the range of 0.7-1, preferably in the range of 0.75-0.98, more preferably in the range of 0.8-0.95.
4. according to the formed body described in any one in claim 1-3, wherein, in the nano-carbon material, by X ray photoelectricity
The amount for the C element that peak in sub- power spectrum in the range of 288.6-288.8eV determines is IC c, by 286.0- in x-ray photoelectron power spectrum
The amount for the C element that peak in the range of 286.2eV determines is IC e, IC c/IC eIn the range of 1.5-4, the model preferably in 1.5-3.5
In enclosing, more preferably in the range of 1.55-3.
5. according to the formed body described in any one in claim 1-4, wherein, with nano-carbon material by x-ray photoelectron
On the basis of the total amount for the C element that power spectrum determines, the C that is determined by the peak in the range of 284.7-284.9eV in x-ray photoelectron power spectrum
The content of element is 60-98 weight %, preferably 65-95 weight %, more preferably 70-90 weight %, by x-ray photoelectron energy
The content for the C element that peak in the range of 286.0-288.8eV determines is 2-40 weight %, preferably 5-35 weight % in spectrum, more
Preferably 10-30 weight %.
6. according to the formed body described in any one in claim 1-5, wherein, nano-sized carbon is determined by x-ray photoelectron power spectrum
The total amount of N element in material is IN t, the N element that is determined by the peak in the range of 400.6-401.5eV in x-ray photoelectron power spectrum
Amount be IN g, IN g/IN tFor not higher than 0.3, typically in the range of 0.02-0.25, preferably in the range of 0.05-0.2.
7. according to the formed body described in any one in claim 1-6, wherein, the nano-carbon material is CNT；It is excellent
Selection of land, the nano-carbon material are multi-walled carbon nanotube；
Preferably, the specific surface area of the multi-walled carbon nanotube is 50-500m2/ g, preferably 80-300m2/ g, more preferably 90-
150m2/ g, more preferably 95-140m2/g；
Preferably, total weight loss rate of the multi-walled carbon nanotube in 400-800 DEG C of temperature range is w800, at 400-500 DEG C
Temperature range in total weight loss rate be w500, w500/w800In the range of 0.01-0.5, preferably in the range of 0.02-0.2,
The weight-loss ratio determines in air atmosphere.
8. a kind of nano-carbon material formed body, the formed body contains nano-carbon material and for the nano-carbon material to be bonded
The heat-resistant inorganic oxide of shaping；
The nano-carbon material is made using the method comprised the following steps：One kind is dispersed with raw material nano carbon material, at least
The aqueous dispersions of a kind of nitrogen-containing compound and at least one organic base are reacted in closed container, the nitrogen-containing compound
Selected from NH3, hydrazine and urea, the organic base is selected from amine and quaternary ammonium base, and in course of reaction, the temperature of the aqueous dispersions is maintained at
In the range of 80-250 DEG C.
9. formed body according to claim 8, wherein, raw material nano carbon material：Nitrogen-containing compound：The weight ratio of organic base
For 1：0.01-20：0.01-20, preferably 1：0.02-10：0.02-15.
10. formed body according to claim 8 or claim 9, wherein, raw material nano carbon material：H2O weight ratio is 1：2-1000,
Preferably 1：5-500, more preferably 1：10-300, more preferably 1：20-200.
11. according to the formed body described in any one in claim 8-10, wherein, nitrogen-containing compound：The mol ratio of organic base
For 1：
0.05-100, preferably 1：0.1-90, more preferably 1：0.4-80.
12. according to the formed body described in any one in claim 8-11, wherein, the organic base is the chemical combination shown in Formulas I
The compound and general formula R shown in compound, formula III shown in thing, Formula II12(NH2)2One or both of material of expression
More than, R12For C1-C6Alkylidene,
In Formulas I, R1、R2、R3And R4Respectively C1-C20Alkyl or C6-C12Aryl；
In Formula II, R5、R6And R7Respectively H or C1-C6Alkyl, and R5、R6And R7It is asynchronously H；
In formula III, R8、R9And R10Respectively-R11OH, hydrogen or C1-C6Alkyl, and R8、R9And R10In it is at least one for-
R11OH, R11For C1-C4Alkylidene.
13. according to the formed body described in any one in claim 8-12, wherein, the nitrogen-containing compound is ammonia, described to have
Machine alkali is selected from the compound shown in formula III, is preferably selected from monoethanolamine, diethanol amine and triethanolamine, raw material nano carbon material：Contain
Nitrogen compound：The weight ratio of organic base is 1：0.02-10：0.05-8, preferably 1：0.03-5：0.1-6, more preferably 1：
0.05-2：0.2-5, nitrogen-containing compound：The mol ratio of organic base is 1：0.05-5, preferably 1：0.1-2.5, more preferably 1：
0.4-0.8；Or
The nitrogen-containing compound is hydrazine, and the organic base is selected from the compound shown in Formulas I, raw material nano carbon material：Nitrogenous chemical combination
Thing：The weight ratio of organic base is 1：0.01-5：0.02-10, preferably 1：0.02-2.5：1-9, more preferably 1：0.02-1.5：
4.5-8, nitrogen-containing compound：The mol ratio of organic base is 1：0.5-100, preferably 1：1-90, more preferably 1：1.1-80；Or
The nitrogen-containing compound is urea, and the organic base is selected from compound and general formula R shown in Formula II12(NH2)2Represent
Material, it is preferably selected from ethylenediamine, n-butylamine and diamines, raw material nano carbon material：Nitrogen-containing compound：The weight ratio of organic base is
1：0.02-10：0.05-20, preferably 1：0.1-8：0.5-15, more preferably 1：1-5：1-10, nitrogen-containing compound：Organic base
Mol ratio is 1：0.1-5, preferably 1：0.5-2.
14. according to the formed body described in any one in claim 8-13, wherein, in course of reaction, the aqueous dispersions
In the range of temperature is kept for 80-250 DEG C, preferably remain in the range of 100-180 DEG C；
Preferably, the duration of the reaction is more excellent preferably in the range of 2-72 hours in the range of 0.5-96 hours
It is selected in the range of 10-40 hours.
15. according to the formed body described in any one in claim 8-14, wherein, in the raw material nano carbon material, N element
Content be not higher than 0.2 weight %, preferably not higher than 0.02 weight %；The content of O elements be not higher than 1.5 weight %,
Preferably not higher than 0.3 weight %；The total amount of metallic element is below 2.5 weight %, preferably below 0.5 weight %.
16. according to the formed body described in any one in claim 8-15, wherein, the raw material nano carbon material is carbon nanometer
Pipe；Preferably, the raw material nano carbon material is multi-walled carbon nanotube；
Preferably, the specific surface area of the multi-walled carbon nanotube is 50-500m2/ g, preferably 100-260m2/ g, more preferably
120-190m2/g；
Preferably, total weight loss rate of the multi-walled carbon nanotube in 400-800 DEG C of temperature range is w800, at 400-500 DEG C
Temperature range in total weight loss rate be w500, w500/w800In the range of 0.01-0.5, preferably in the range of 0.02-0.4,
The weight-loss ratio determines in air atmosphere.
17. according to the formed body described in any one in claim 8-16, wherein, methods described also includes what is obtained from reaction
Solid matter is isolated in mixture, and the solid matter isolated is dried；
Preferably, the drying is carried out at a temperature of 50-400 DEG C, is carried out preferably at a temperature of 80-180 DEG C；The drying
Duration be preferably 4-24 hours, more preferably 6-12 hours no more than 48 hours.
18. according to the formed body described in any one in claim 1-17, wherein, on the basis of the total amount of the formed body,
The content of the nano-carbon material is 6-94 weight %, more preferably preferably 10-90 weight %, 40-90 weight %, further
Preferably 70-90 weight %, the content of the heat-resistant inorganic oxide are 6-94 weight %, preferably 10-90 weight %, more excellent
Elect 10-60 weight %, more preferably 10-30 weight % as.
19. according to the formed body described in any one in claim 1-18, wherein, the heat-resistant inorganic oxide is oxidation
It is more than one or both of aluminium, silica and titanium oxide；
Preferably, the heat-resistant inorganic oxide contains silica；
It is highly preferred that on the basis of the total amount of the heat-resistant inorganic oxide, the content of the silica is 10-100 weight %,
Preferably 20-99 weight %, more preferably 50-99 weight %.
20. a kind of preparation method of nano-carbon material formed body, this method includes mixing nano-carbon material with binding agent source, will
Obtained mixture is molded, and obtains article shaped, and the article shaped is dried and is optionally calcined, the binding agent
Source is selected from the precursor of heat-resistant inorganic oxide and/or heat-resistant inorganic oxide, and the nano-carbon material is non-surface treated
Nano-carbon material and/or surface treated nano-carbon material, through x-ray photoelectron power spectrum determine, the surface treated
Nano-carbon material contain O elements and N element.
21. according to the method for claim 20, wherein, the mixture also contains at least one alkali；
Preferably, alkali, urea, hydrazine, amine and the season that the alkali is ammonia, cation is the alkali of alkali metal, cation is alkaline-earth metal
More than one or both of ammonium alkali, quaternary ammonium base is preferably selected from, is more preferably selected from synthesis of titanium silicon molecular sieve template, further
It is preferably selected from the compound shown in Formulas I：
In Formulas I, R1、R2、R3And R4Respectively C1-C20Alkyl, preferably respectively C1-C6Alkyl；
The alkali and the mol ratio in the binding agent source are preferably 0.05-15：1, preferably 0.1-12：1, the binding agent source with
Oxide meter.
22. the method according to claim 20 or 21, wherein, before the mixture is molded, this method also includes will
The mixture carries out hydro-thermal process.
23. according to the method for claim 22, wherein, the hydro-thermal process is at 100-200 DEG C, preferably 120-180 DEG C
At a temperature of carry out, the duration of the hydro-thermal process is 0.5-24 hours, preferably 6-12 hours.
24. according to the method described in any one in claim 20-23, wherein, at least part binding agent source, at least partly may be used
The alkali and at least part water of choosing come from molecular sieve preparation solution, and the molecular sieve preparation solution is the crystallization mother liquor of siliceous molecular sieve
With the mixed liquor reset more than one or both of modified mother liquor of siliceous molecular sieve；
Preferably, the molecular sieve preparation solution is the crystallization mother liquor of silica zeolite and/or resets modification liquid, HTS
One or both of crystallization mother liquor and/or rearrangement modification liquid of crystallization mother liquor and/or rearrangement modification liquid and Si-Al molecular sieve
Mixed liquor above.
25. a kind of forming method of nano-carbon material, this method includes nano-carbon material entering water-filling in a kind of aqueous dispersions
Heat treatment, the sizing material forming that hydro-thermal process is obtained, obtains article shaped, the article shaped is dried and optionally roasted
Burn, the aqueous dispersions contain binding agent source, and the binding agent source is selected from heat-resistant inorganic oxide and/or heat-resistant inorganic oxide
Precursor, the nano-carbon material is not surface treated nano-carbon material and/or surface treated nano-carbon material,
Determined through x-ray photoelectron power spectrum, the surface treated nano-carbon material contains O elements and N element.
26. forming method according to claim 25, wherein, the aqueous dispersions also contain at least one inorganic agent, institute
It is organic base and/or nitrogen-containing compound to state inorganic agent, and the nitrogen-containing compound is selected from NH3, hydrazine and urea；
Preferably, the organic base is selected from quaternary ammonium base and amine, is more preferably selected from synthesis of titanium silicon molecular sieve template, further excellent
Choosing is selected from further preferably selected from the compound shown in Formulas I：
In Formulas I, R1、R2、R3And R4Respectively C1-C20Alkyl, preferably respectively C1-C6Alkyl；
Preferably, the inorganic agent is organic base and/or nitrogen-containing compound, described to have on the basis of the total amount of the inorganic agent
The content of machine alkali is preferably 20-100 weight %, more preferably 35-92 weight %；
It is highly preferred that the inorganic agent is organic base and/or nitrogen-containing compound, and at least part organic base is quaternary ammonium base, with institute
On the basis of the total amount for stating inorganic agent, the content of the organic base is preferably 50-100 weight %, more preferably 65-92 weight %,
The content of the quaternary ammonium base is preferably 40-100 weight %, more preferably 45-92 weight %.
27. according to the method for claim 26, wherein, the inorganic agent and the mol ratio in the binding agent source are 0.05-
15：1, preferably 0.1-12：1, more preferably 0.5-3.5：1, the binding agent source is in terms of oxide.
28. according to the method described in any one in claim 25-27, wherein, at least part binding agent source, at least partly may be used
The organic base and at least part water of choosing come from molecular sieve preparation solution, and the molecular sieve preparation solution is the crystallization of siliceous molecular sieve
Mixed liquor more than one or both of rearrangement modified mother liquor of mother liquor and siliceous molecular sieve；
Preferably, the molecular sieve preparation solution is the crystallization mother liquor of silica zeolite and/or resets modification liquid, HTS
One or both of crystallization mother liquor and/or rearrangement modification liquid of crystallization mother liquor and/or rearrangement modification liquid and Si-Al molecular sieve
Mixed liquor above.
29. according to the method described in any one in claim 25-28, wherein, the hydro-thermal process 100-200 DEG C, it is excellent
Carried out at a temperature of selecting 120-180 DEG C, the duration of the hydro-thermal process is 0.5-24 hours, preferably 6-12 hours.
30. according to the method described in any one in claim 20-29, wherein, the heat-resistant inorganic oxide be aluminum oxide,
It is more than one or both of silica and titanium oxide；
Preferably, the heat-resistant inorganic oxide contains silica；
It is highly preferred that on the basis of the total amount of the heat-resistant inorganic oxide, the content of the silica is 10-100 weight %,
Preferably 20-99 weight %, more preferably 50-99 weight %.
31. according to the method described in any one in claim 20-30, wherein, the dosage in the binding agent source causes finally
In the formed body of preparation, the content of nano-carbon material is 5-95 weight %, and preferably 6-94 weight %, more preferably 75-95 are heavy
% is measured, more preferably 85-95 weight %, the content of the heat-resistant inorganic oxide is 5-95 weight %, preferably 6-94
Weight %, more preferably 5-25 weight %, more preferably 5-15 weight %.
32. according to the method described in any one in claim 20-31, wherein, the surface treated nano-carbon material
For the nano-carbon material described in any one in claim 2-7 and 8-17.
33. according to the method described in any one in claim 20-32, wherein, the drying is at a temperature of 50-200 DEG C
Carry out, carried out preferably at a temperature of 120-180 DEG C；The duration of the drying is no more than 48 hours, preferably 3-24
Hour, more preferably 5-15 hours；
The roasting is carried out at a temperature of 300-800 DEG C, is carried out preferably at a temperature of 350-650 DEG C, the roasting is held
The continuous time is 1-12 hours, preferably 2-4 hours.
34. nano-carbon material formed body prepared by a kind of method in 20-33 as claim described in any one.
35. catalyst of the nano-carbon material formed body as hydrocarbon dehydrogenation reaction in claim 1-19 and 34 described in any one
Application, the hydrocarbon is preferably alkane, more preferably C2-C12Alkane, more preferably normal butane.
36. a kind of hydrocarbon dehydrogenation reaction method, this method is included under conditions of existence or non-existence oxygen, in hydrocarbon dehydrogenation reaction bar
Under part, hydrocarbon is contacted with the nano-carbon material formed body described in any one in claim 1-19 and 34.
37. according to the method for claim 36, wherein, the hydrocarbon is alkane, preferably C2-C12Alkane, more preferably
Normal butane.