CN107650289A - A kind of equipment for preparing high performance nylon and preparation method thereof - Google Patents
A kind of equipment for preparing high performance nylon and preparation method thereof Download PDFInfo
- Publication number
- CN107650289A CN107650289A CN201610593530.0A CN201610593530A CN107650289A CN 107650289 A CN107650289 A CN 107650289A CN 201610593530 A CN201610593530 A CN 201610593530A CN 107650289 A CN107650289 A CN 107650289A
- Authority
- CN
- China
- Prior art keywords
- charge door
- conveyer belt
- mixer
- nylon
- screw rod
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of equipment for preparing high performance nylon and preparation method thereof, refers to technical field of polymer materials；The upper end that the glass fibre of its screw rod is sent into section is provided with charge door one, and the upper end of the filler entrance of screw rod is provided with charge door two, and the upper end of the polymer solids transportation section of screw rod is provided with charge door three；Its preparation method is that glass is divided into two sections and is added, and leading portion adds on conveyer belt three, and addition control is stirred pure in charge door one by mixer one 15 30%；Back segment is added on conveyer belt two, and addition control is stirred pure in charge door two by mixer two 25 40%；40% nylon is added on conveyer belt one, is delivered in charge door three, is finally processed into high glass fiber content nylon by screw rod；It can improve glass fiber content, prepare high glass fiber content nylon, reduce cost, improve product quality.
Description
Technical field
The present invention relates to technical field of polymer materials, specifically a kind of equipment for preparing high performance nylon and
Its preparation method.
Background technology
Nylon has excellent comprehensive such as good mechanical performance, preferable pliability, wearability, oil resistivity, self lubricity
Performance is closed, is widely used in the fields such as automobile industry, electronic apparatus industry, plant equipment, construction industry.Because it has processing
The advantages that cycle is short, production cost is low, service life is long and the product design free degree is high obtains more and more extensive application.In recent years
Come, the application in terms of heat-conductivity polymer composite is especially prominent.
Of the prior art to prepare high performance nylon equipment, cost is high, and glass addition is limited, it is also difficult to prepares high property
The nylon material of energy.
The content of the invention
Setting for high performance nylon is prepared in view of the defects and deficiencies of the prior art, the present invention intends to provide a kind of
It is standby and preparation method thereof, glass fiber content is improved, prepares high glass fiber content nylon, reduces cost, improves product quality.
To achieve the above object, the technical solution adopted by the present invention is：It include screw rod, charge door one, charge door two, plus
Material mouth three, mixer one, mixer two, conveyer belt one, conveyer belt two, conveyer belt three；The glass fibre of screw rod is sent into the upper of section
End is provided with charge door one, and the upper end of the filler entrance of screw rod is provided with charge door two, the polymer solids transportation section of screw rod it is upper
End is provided with charge door three, and mixer one is arranged on the top of charge door one, and mixer two is arranged on the top of charge door two, defeated
Band one is sent to be arranged on the top of charge door three, conveyer belt two is arranged on the top of mixer two, and conveyer belt three is arranged on mixer
One top.
A kind of preparation method of high performance nylon is：Glass is divided into two sections and is added, and leading portion adds on conveyer belt three,
Addition is controlled in 15-30%, is stirred by mixer one in essence to charge door one；Back segment adds on conveyer belt two, addition control
Make in 25-40%, stirred by mixer two in essence to charge door two；40% nylon is added on conveyer belt one, is delivered to charging
In mouth three, finally high glass fiber content nylon is processed into by screw rod.Leading portion adds small part glass, can be filled by mixer one
Divide plasticizing, back segment adds most of glass, avoids glass excessive shear, and mechanical performance reduces.Pass through two sections plus glass, Ji Nengti
High glass fiber content, high performance material can be prepared again.
This preparation method is applied to PA6, PA66, PA46, PA610, PA1010, PA1212, PA6T, PA9T, PPA and its group
The production of compound.
The present invention has the beneficial effect that：
1st, equipment provided by the invention can improve glass fiber content, prepare high glass fiber content nylon, reduce cost, improve product
Quality.
2nd, high glass fiber content nylon advantage provided by the invention is product size temperature, high-impact, top load.
Brief description of the drawings
Fig. 1 is the structural representation of the present invention；
1. screw rods, 2. charge doors one, 3. charge doors two, 4. charge doors three, 5. mixers one, the conveying of 6. mixers two, 7. in figure
Band one, 8. conveyer belts two, 9. conveyer belts three.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with accompanying drawing and specific implementation
Mode, the present invention will be described in further detail.It should be appreciated that embodiment described herein is only explaining this
Invention, is not intended to limit the present invention.
Referring to Fig. 1, present embodiment uses following technical scheme：It includes screw rod 1, charge door 1, charge door two
3rd, charge door 34, mixer 1, mixer 26, conveyer belt 1, conveyer belt 28, conveyer belt 39；The glass fibre of screw rod 1
The upper end for being sent into section a is provided with charge door 1, and the filler entrance b of screw rod 1 upper end is provided with charge door 23, the polymerization of screw rod 1
Thing solid conveying section c upper end is provided with charge door 34, and mixer 1 is arranged on the top of charge door 1, and mixer 26 is set
Put on the top of charge door 23, conveyer belt 1 is arranged on the top of charge door 34, and conveyer belt 28 is arranged on mixer 26
Top, conveyer belt 39 are arranged on the top of mixer 1.
A kind of preparation method of high performance nylon is：Glass is divided into two sections and is added, and leading portion adds on conveyer belt 39
Add, addition control is stirred pure in charge door 1 by mixer 1 20%；Back segment adds on conveyer belt 28, adds
Amount control is stirred pure in charge door 23 by mixer 26 40%；40% nylon is added on conveyer belt 1, is delivered to
In charge door 34, finally high glass fiber content nylon is processed into by screw rod 1.Leading portion adds small part glass, passes through mixer one
5 can fully plastify, and back segment adds most of glass, avoid glass excessive shear, and mechanical performance reduces.Pass through two sections plus glass
Fibre, glass fiber content can be improved, high performance material can be prepared again.
This preparation method is applied to PA6, PA66, PA46, PA610, PA1010, PA1212, PA6T, PA9T, PPA and its group
The production of compound.
The advantages of present embodiment：
1st, the equipment that present embodiment provides can improve glass fiber content, prepare high glass fiber content nylon, reduce cost,
Improve product quality.
2nd, the high glass fiber content nylon advantage that present embodiment provides is product size temperature, high-impact, top load.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.Any reference in claim should not be considered as to the involved claim of limitation.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It is appreciated that other embodiment.
Claims (2)
- A kind of 1. equipment for preparing high performance nylon, it is characterised in that：It includes screw rod, charge door one, charge door two, charge door 3rd, mixer one, mixer two, conveyer belt one, conveyer belt two, conveyer belt three；The upper end that the glass fibre of screw rod is sent into section is set There is charge door one, the upper end of the filler entrance of screw rod is provided with charge door two, and the upper end of the polymer solids transportation section of screw rod is set Charge door three is equipped with, mixer one is arranged on the top of charge door one, and mixer two is arranged on the top of charge door two, conveyer belt One is arranged on the top of charge door three, and conveyer belt two is arranged on the top of mixer two, and conveyer belt three is arranged on mixer one Top.
- A kind of 2. preparation method of high performance nylon, it is characterised in that：Glass is divided into two sections and is added, and leading portion is in conveyer belt three Upper addition, addition are controlled in 15-30%, stirred by mixer one in essence to charge door one；Back segment adds on conveyer belt two, Addition is controlled in 25-40%, is stirred by mixer two in essence to charge door two；40% nylon is added on conveyer belt one, it is defeated Deliver in charge door three, be finally processed into high glass fiber content nylon by screw rod.