CN107641440A - Anti-corrosion automobile coating - Google Patents
Anti-corrosion automobile coating Download PDFInfo
- Publication number
- CN107641440A CN107641440A CN201711098521.5A CN201711098521A CN107641440A CN 107641440 A CN107641440 A CN 107641440A CN 201711098521 A CN201711098521 A CN 201711098521A CN 107641440 A CN107641440 A CN 107641440A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- resin
- automobile coating
- levelling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Anti-corrosion automobile coating, is prepared from the following raw materials in parts by weight：0.1~4.5 part of drier, 0.1~0.3 part of organosilicon levelling agent, 0.5~1 part of non-organic silicon levelling agent, 35~45 parts of chlorinated rubber compound resin liquid, 22~26 parts of modified alkyd resin, modified rosin resin 3~9,7~14 parts of anti-settling agent, 7~11 parts of high-carbon black pigment, 1~2 part of aluminium triphosphate；It is an advantage of the invention that：Practicality and good endurance.
Description
Technical field
The present invention relates to anti-corrosion automobile coating, belongs to paint technology field.
Background technology
Paint is seen everywhere in schedule life, and it mainly plays a part of to protect and decorated, and according to different uses
Environment, the species of paint is also varied, traditional paint generally existing smell weight, easily comes off, be perishable, not enough environmental protection etc.
Problem, requirement of the consumer to paint can not be met, therefore, it is necessary to improve the formula of original paint, increase is painted
Practicality and durability, reduce its harm to environment and human body, and various use environment conditions can be adapted to.
The content of the invention
It is an object of the invention to provide anti-corrosion automobile coating.
The problem to be solved in the present invention is traditional paint generally existing smell weight, easily comes off, be perishable, not environmentally friendly enough
The problems such as.
To realize the purpose of the present invention, the technical solution adopted by the present invention is：
Anti-corrosion automobile coating, is prepared from the following raw materials in parts by weight：
0.1~4.5 part of drier, 0.1~0.3 part of organosilicon levelling agent, 0.5~1 part of non-organic silicon levelling agent, chlorination rubber
35~45 parts of glue compound resin liquid, 22~26 parts of modified alkyd resin, modified rosin resin 3~9,7~14 parts of anti-settling agent, high color
Plain 7~11 parts of carbon black, 1~2 part of aluminium triphosphate, 4~6 parts of trbasic zinc phosphate, more 2~5 parts of metal composite phosphate, clay 0.2~
0.5 part, 5~8 parts of styrene, 11~14 parts of aramid fiber short fibre, styrene series thermoplastic elastomer 3~5, polyester varnish 43~51
Part, 13~18 parts of paint naphtha, 7~12 parts of curing agent, 1~100 part of deionized water.
Above-mentioned anti-corrosion automobile coating, is prepared from the following raw materials in parts by weight：2 parts of drier, organosilicon levelling agent 0.2
Part, 0.7 part of non-organic silicon levelling agent, 38 parts of chlorinated rubber compound resin liquid, 23 parts of modified alkyd resin, modified rosin resin 5,
11 parts of anti-settling agent, 8 parts of high-carbon black pigment, 1 part of aluminium triphosphate, trbasic zinc phosphate 5, more 3 parts of metal composite phosphate, 0.4 part of clay,
6 parts of styrene, 12 parts of aramid fiber short fibre, styrene series thermoplastic elastomer 4,48 parts of polyester varnish, 15 parts of paint naphtha, Gu
9 parts of agent, 55 parts of deionized water.
Anti-corrosion automobile coating advantage of the present invention is：Crosslink density is good, and coating late hardness is high, mechanical performance, and ageing properties are excellent
It is different, and be not easy peeling after drying and do not break；Add aramid fiber short fibre so that paint has certain pressure resistance after drying
Degree；Add epoxy resin so that paint sticky moderate performance；Rosin has the moistening dispersiveness of resin and pigment to change greatly very much
Kind, manufactured paint film film forming is fast, drying property is good, and brightness and hardness are high.
Embodiment
With reference to embodiment, the present invention is further illustrated.
Embodiment 1, anti-corrosion automobile coating of the present invention, is prepared from the following raw materials in parts by weight：2.3 parts of drier, organosilicon
0.3 part of levelling agent, 0.6 part of non-organic silicon levelling agent, 39 parts of chlorinated rubber compound resin liquid, 26 parts of modified alkyd resin, rosin
Modified resin 7,10 parts of anti-settling agent, 8 parts of high-carbon black pigment, 1 part of aluminium triphosphate, 4~6 parts of trbasic zinc phosphate, more metal composite phosphoric acid
3 parts of salt, 0.5 part of clay, 7 parts of styrene, 12 parts of aramid fiber short fibre, styrene series thermoplastic elastomer 4,47 parts of polyester varnish,
16 parts of paint naphtha, 10 parts of curing agent, 49 parts of deionized water.
Embodiment 2, anti-corrosion automobile coating of the present invention, is prepared from the following raw materials in parts by weight：2 parts of drier, organosilicon stream
Flat 0.2 part of agent, 0.7 part of non-organic silicon levelling agent, 38 parts of chlorinated rubber compound resin liquid, 23 parts of modified alkyd resin, rosin change
Property resin 5,11 parts of anti-settling agent, 8 parts of high-carbon black pigment, 1 part of aluminium triphosphate, trbasic zinc phosphate 5, more 3 parts of metal composite phosphate, stick
0.4 part of soil, 6 parts of styrene, 12 parts of aramid fiber short fibre, styrene series thermoplastic elastomer 4,48 parts of polyester varnish, paint solvent
15 parts of oil, 9 parts of curing agent, 55 parts of deionized water.
Claims (2)
1. anti-corrosion automobile coating, it is characterized in that：0.1~4.5 part of drier, 0.1~0.3 part of organosilicon levelling agent, non-organic silicon stream
Flat 0.5~1 part of agent, 35~45 parts of chlorinated rubber compound resin liquid, 22~26 parts of modified alkyd resin, modified rosin resin 3~
9th, 7~14 parts of anti-settling agent, 7~11 parts of high-carbon black pigment, 1~2 part of aluminium triphosphate, 4~6 parts of trbasic zinc phosphate, more metal composite phosphorus
2~5 parts of hydrochlorate, 0.2~0.5 part of clay, 5~8 parts of styrene, 11~14 parts of aramid fiber short fibre, polystyrene thermoplastic elastic
Body 3~5,43~51 parts of polyester varnish, 13~18 parts of paint naphtha, 7~12 parts of curing agent, 1~100 part of deionized water.
2. anti-corrosion automobile coating according to claim 1, it is characterized in that：It is prepared from the following raw materials in parts by weight：Drier 2
Part, 0.2 part of organosilicon levelling agent, 0.7 part of non-organic silicon levelling agent, 38 parts of chlorinated rubber compound resin liquid, modified alkyd resin
23 parts, modified rosin resin 5,11 parts of anti-settling agent, 8 parts of high-carbon black pigment, 1 part of aluminium triphosphate, trbasic zinc phosphate 5, more metal composites
3 parts of phosphate, 0.4 part of clay, 6 parts of styrene, 12 parts of aramid fiber short fibre, styrene series thermoplastic elastomer 4, polyester varnish 48
Part, 15 parts of paint naphtha, 9 parts of curing agent, 55 parts of deionized water.