CN107640897A - refractory metal enamel glaze - Google Patents
refractory metal enamel glaze Download PDFInfo
- Publication number
- CN107640897A CN107640897A CN201711088304.8A CN201711088304A CN107640897A CN 107640897 A CN107640897 A CN 107640897A CN 201711088304 A CN201711088304 A CN 201711088304A CN 107640897 A CN107640897 A CN 107640897A
- Authority
- CN
- China
- Prior art keywords
- parts
- refractory metal
- enamel glaze
- aluminium
- metal enamel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is composed of the following components by weight the invention discloses a kind of refractory metal enamel glaze:Amorphous silicon di-oxide, zinc oxide, aluminium triphosphate, cobalt naphthenate, 3 diethylaminopropylamines; micaceous iron oxide, modified Nano clay, feldspar in powder, vinyl three (β methoxy ethoxies) silane; the double (phosphonomethyl) aspartic acids of N, N, aluminium polychloride, vinylidene chloride.Refractory metal enamel glaze of the present invention, it has corrosion-resistant, resistance to elevated temperatures, and the acute degeneration of resistance to the temperature difference is excellent, service life length.
Description
Technical field
The present invention relates to refractory metal enamel glaze.
Background technology
Metal enamel glaze is widely used in chemical industry equipment, but existing ceramic glaze performance is single, has much room for improvement.
The content of the invention
It is an object of the invention to provide a kind of refractory metal enamel glaze, and it has corrosion-resistant, resistance to elevated temperatures, and
The acute degeneration of resistance to the temperature difference is excellent, service life length.
To achieve the above object, the technical scheme is that designing a kind of refractory metal enamel glaze, by weight
Count composed of the following components:Amorphous silicon di-oxide, zinc oxide, aluminium triphosphate, cobalt naphthenate, 3 diethyl aminopropylamine, cloud
Female iron oxide, modified Nano clay, feldspar in powder, vinyl three ('beta '-methoxy ethyoxyl) silane, the double (phosphonomethyl)s of N, N-
Aspartic acid, aluminium polychloride, vinylidene chloride.
Preferably, described refractory metal enamel glaze, it is composed of the following components by weight:
35 parts of amorphous silicon di-oxides,
3~8 parts of zinc oxide,
1~2 part of aluminium triphosphate,
2~5 parts of cobalt naphthenates,
1~3 part of 3 diethyl aminopropylamine,
1~2 part of micaceous iron oxide,
2~3 parts of modified Nano clay,
1~2 part of feldspar in powder,
5~8 parts of vinyl three ('beta '-methoxy ethyoxyl) silane,
The double (phosphonomethyl) aspartic acids of 3~6 parts of N, N-,
1~2 part of aluminium polychloride,
4~7 parts of vinylidene chlorides.
Preferably, described refractory metal enamel glaze, it is composed of the following components by weight:
35 parts of amorphous silicon di-oxides,
3.8 parts of zinc oxide,
1.2 parts of aluminium triphosphates,
2.5 parts of cobalt naphthenates,
1.3 parts of 3 diethyl aminopropylamines,
1.2 parts of micaceous iron oxides,
2.3 parts of modified Nano clay,
1.2 part feldspar in powder,
5.8 parts of vinyl three ('beta '-methoxy ethyoxyl) silane,
The double (phosphonomethyl) aspartic acids of 3.6 parts of N, N-,
1.2 parts of aluminium polychlorides,
4.7 parts of vinylidene chlorides.
The advantages of the present invention are:A kind of refractory metal enamel glaze is provided, it has corrosion-resistant, resistance to
High-temperature behavior, and the acute degeneration of resistance to the temperature difference is excellent, service life length.
Embodiment
With reference to embodiment, the embodiment of the present invention is further described.Following examples are only used for more
Add and clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied is:
A kind of refractory metal enamel glaze, it is composed of the following components by weight:Amorphous silicon di-oxide, zinc oxide, three
Poly aluminium phosphate, cobalt naphthenate, 3 diethyl aminopropylamine, micaceous iron oxide, modified Nano clay, feldspar in powder, vinyl three (β-
Methoxy ethoxy) silane, the double (phosphonomethyl) aspartic acids of N, N-, aluminium polychloride, vinylidene chloride.
Preferably, described refractory metal enamel glaze, it is composed of the following components by weight:
35 parts of amorphous silicon di-oxides,
3~8 parts of zinc oxide,
1~2 part of aluminium triphosphate,
2~5 parts of cobalt naphthenates,
1~3 part of 3 diethyl aminopropylamine,
1~2 part of micaceous iron oxide,
2~3 parts of modified Nano clay,
1~2 part of feldspar in powder,
5~8 parts of vinyl three ('beta '-methoxy ethyoxyl) silane,
The double (phosphonomethyl) aspartic acids of 3~6 parts of N, N-,
1~2 part of aluminium polychloride,
4~7 parts of vinylidene chlorides.
Preferably, described refractory metal enamel glaze, it is composed of the following components by weight:
35 parts of amorphous silicon di-oxides,
3.8 parts of zinc oxide,
1.2 parts of aluminium triphosphates,
2.5 parts of cobalt naphthenates,
1.3 parts of 3 diethyl aminopropylamines,
1.2 parts of micaceous iron oxides,
2.3 parts of modified Nano clay,
1.2 parts of feldspars in powder,
5.8 parts of vinyl three ('beta '-methoxy ethyoxyl) silane,
The double (phosphonomethyl) aspartic acids of 3.6 parts of N, N-,
1.2 parts of aluminium polychlorides,
4.7 parts of vinylidene chlorides.
Refractory metal enamel glaze of the present invention, it has corrosion-resistant, resistance to elevated temperatures, and the acute degeneration of resistance to the temperature difference is excellent,
Service life is grown.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (3)
1. refractory metal enamel glaze, it is characterised in that composed of the following components by weight:Amorphous silicon di-oxide,
Zinc oxide, aluminium triphosphate, cobalt naphthenate, 3 diethyl aminopropylamine, micaceous iron oxide, modified Nano clay, feldspar in powder, second
Alkenyl three ('beta '-methoxy ethyoxyl) silane, the double (phosphonomethyl) aspartic acids of N, N-, aluminium polychloride, vinylidene chloride.
2. refractory metal enamel glaze according to claim 1, it is characterised in that by weight by following components group
Into:
35 parts of amorphous silicon di-oxides,
3~8 parts of zinc oxide,
1~2 part of aluminium triphosphate,
2~5 parts of cobalt naphthenates,
1~3 part of 3 diethyl aminopropylamine,
1~2 part of micaceous iron oxide,
2~3 parts of modified Nano clay,
1~2 part of feldspar in powder,
5~8 parts of vinyl three ('beta '-methoxy ethyoxyl) silane,
The double (phosphonomethyl) aspartic acids of 3~6 parts of N, N-,
1~2 part of aluminium polychloride,
4~7 parts of vinylidene chlorides.
3. refractory metal enamel glaze according to claim 2, it is characterised in that by weight by following components group
Into:
35 parts of amorphous silicon di-oxides,
3.8 parts of zinc oxide,
1.2 parts of aluminium triphosphates,
2.5 parts of cobalt naphthenates,
1.3 parts of 3 diethyl aminopropylamines,
1.2 parts of micaceous iron oxides,
2.3 parts of modified Nano clay,
1.2 parts of feldspars in powder,
5.8 parts of vinyl three ('beta '-methoxy ethyoxyl) silane,
The double (phosphonomethyl) aspartic acids of 3.6 parts of N, N-,
1.2 parts of aluminium polychlorides,
4.7 parts of vinylidene chlorides.