CN107629322A - A kind of high-strength polypropylene film - Google Patents
A kind of high-strength polypropylene film Download PDFInfo
- Publication number
- CN107629322A CN107629322A CN201711009333.0A CN201711009333A CN107629322A CN 107629322 A CN107629322 A CN 107629322A CN 201711009333 A CN201711009333 A CN 201711009333A CN 107629322 A CN107629322 A CN 107629322A
- Authority
- CN
- China
- Prior art keywords
- parts
- polypropylene film
- nano
- pelopon
- zeolite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of high-strength polypropylene film, include the raw material of following parts by weight：80 90 parts of polypropylene, 10 15 parts of fourth etherified resin, 48 parts of triallyl isocyanate, 10 15 parts of ethyl cellulose, 6 12 parts of pulullan polysaccharide, 36 parts of pelopon A, 30 40 parts of propane diols, 24 parts of nm-class boron nitride, 13 parts of nano silicon oxide, 0.5 1 parts of nanometer antimony oxide, 0.5 1 parts of flax fiber, 13 parts of carbon fiber, 0.1 0.5 parts of wormwood essential oil, 0.3 0.8 parts of attapulgite, 0.1 0.5 parts of zeolite with carrying silver, 13 parts of chitosan, 13 parts of magnesium hydroxide, 0.3 0.8 parts of nano barium sulfate.The polypropylene film combination property of the present invention is superior, and tear-resistant intensity is high, improves the stability of film, greatly strengthen the service life of film；It is economic and practical meanwhile raw material sources are extensive.
Description
Technical field
The present invention relates to film applications, and in particular to a kind of high-strength polypropylene film.
Background technology
As the continuous development of industry, high polymer material extensive use, requirement of the every field to material property constantly carry
Rise.In order to meet the needs of application, material made of simple pure resin seems unable to do what one wishes, so, polymeric material field must
It must weed out the old and bring forth the new, the research of modifying plastics is also just more and more important, such as it is expected polymeric material high temperature resistant, is easily processed into
Type, there is good toughness, be higher intensity, functional and cheap etc..Single homopolymer material is often difficult
To meet above-mentioned requirements, therefore existing polymeric material can be modified by nanometer composite technology, synthesis can be made
The novel high polymer material of excellent performance, it has also become the important research direction of new material development field, there is wide market to open
Send out application prospect.
Polypropylene film has good gloss and good transparency, heat-resisting soda acid, solvent resistant, rub resistance, tear-resistant, energy
The advantages that ventilative；It is widely used in the packaging of food, candy, cigarette, tealeaves, fruit juice, milk, textile etc., there is " packaging emperor
Laudatory title afterwards ".But there is the problem of tear-resistant intensity is not high in existing polypropylene film.
The content of the invention
It is an object of the invention to：A kind of high-strength polypropylene film is provided.
To achieve the above object, the present invention provides following technical scheme：
A kind of high-strength polypropylene film, include the raw material of following parts by weight：
Polypropylene 80-90 parts, fourth etherified resin 10-15 parts, triallyl isocyanate 4-8 parts, ethyl cellulose 10-15
Part, pulullan polysaccharide 6-12 parts, pelopon A 3-6 parts, propane diols 30-40 parts, nm-class boron nitride 2-4 parts, receive
Rice silica 1-3 parts, nanometer antimony oxide 0.5-1 parts, flax fiber 0.5-1 parts, carbon fiber 1-3 parts, wormwood essential oil 0.1-0.5
Part, attapulgite 0.3-0.8 parts, zeolite with carrying silver 0.1-0.5 parts, chitosan 1-3 parts, magnesium hydroxide 1-3 parts, nano barium sulfate
0.3-0.8 parts.
Preferably, a kind of high-strength polypropylene film, the raw material of following parts by weight is included：
85 parts of polypropylene, 12 parts of fourth etherified resin, 5 parts of triallyl isocyanate, 12 parts of ethyl cellulose, Propiram are more
8 parts of sugar, 4 parts of pelopon A, 35 parts of propane diols, 3 parts of nm-class boron nitride, 2 parts of nano silicon oxide, nanometer antimony oxide
0.7 part, 0.7 part of flax fiber, 2 parts of carbon fiber, 0.2 part of wormwood essential oil, 0.5 part of attapulgite, 0.2 part of zeolite with carrying silver, shell gather
2 parts of sugar, 2 parts of magnesium hydroxide, 0.5 part of nano barium sulfate.
Preferably, a kind of high-strength polypropylene film, the raw material of following parts by weight is included：
88 parts of polypropylene, 14 parts of fourth etherified resin, 6 parts of triallyl isocyanate, 14 parts of ethyl cellulose, Propiram are more
11 parts of sugar, 5 parts of pelopon A, 36 parts of propane diols, 2.5 parts of nm-class boron nitride, nano silicon oxide 1.5 part, nanometer
0.8 part of antimony oxide, 0.9 part of flax fiber, 1.5 parts of carbon fiber, 0.4 part of wormwood essential oil, 0.7 part of attapulgite, zeolite with carrying silver 0.4
Part, 1.5 parts of chitosan, 1.5 parts of magnesium hydroxide, 0.6 part of nano barium sulfate.
The beneficial effects of the present invention are:
The polypropylene film combination property of the present invention is superior, and tear-resistant intensity is high, improves the stability of film, increases
The strong service life of film；It is economic and practical meanwhile raw material sources are extensive.
Specific embodiment
Embodiment 1
A kind of high-strength polypropylene film, include the raw material of following parts by weight：
80 parts of polypropylene, 10 parts of fourth etherified resin, 4 parts of triallyl isocyanate, 10 parts of ethyl cellulose, Propiram are more
6 parts of sugar, 3 parts of pelopon A, 30 parts of propane diols, 2 parts of nm-class boron nitride, 1 part of nano silicon oxide, nanometer antimony oxide
0.5 part, 0.5 part of flax fiber, 1 part of carbon fiber, 0.1 part of wormwood essential oil, 0.3 part of attapulgite, 0.1 part of zeolite with carrying silver, shell gather
1 part of sugar, 1 part of magnesium hydroxide, 0.3 part of nano barium sulfate.
Embodiment 2
A kind of high-strength polypropylene film, include the raw material of following parts by weight：
85 parts of polypropylene, 12 parts of fourth etherified resin, 5 parts of triallyl isocyanate, 12 parts of ethyl cellulose, Propiram are more
8 parts of sugar, 4 parts of pelopon A, 35 parts of propane diols, 3 parts of nm-class boron nitride, 2 parts of nano silicon oxide, nanometer antimony oxide
0.7 part, 0.7 part of flax fiber, 2 parts of carbon fiber, 0.2 part of wormwood essential oil, 0.5 part of attapulgite, 0.2 part of zeolite with carrying silver, shell gather
2 parts of sugar, 2 parts of magnesium hydroxide, 0.5 part of nano barium sulfate.
Embodiment 3
A kind of high-strength polypropylene film, include the raw material of following parts by weight：
88 parts of polypropylene, 14 parts of fourth etherified resin, 6 parts of triallyl isocyanate, 14 parts of ethyl cellulose, Propiram are more
11 parts of sugar, 5 parts of pelopon A, 36 parts of propane diols, 2.5 parts of nm-class boron nitride, nano silicon oxide 1.5 part, nanometer
0.8 part of antimony oxide, 0.9 part of flax fiber, 1.5 parts of carbon fiber, 0.4 part of wormwood essential oil, 0.7 part of attapulgite, zeolite with carrying silver 0.4
Part, 1.5 parts of chitosan, 1.5 parts of magnesium hydroxide, 0.6 part of nano barium sulfate.
Embodiment 4
A kind of high-strength polypropylene film, include the raw material of following parts by weight：
90 parts of polypropylene, 15 parts of fourth etherified resin, 8 parts of triallyl isocyanate, 15 parts of ethyl cellulose, Propiram are more
It is 12 parts of sugar, 6 parts of pelopon A, 40 parts of propane diols, 4 parts of nm-class boron nitride, 3 parts of nano silicon oxide, nano oxidized
1 part of antimony, 1 part of flax fiber, 3 parts of carbon fiber, 0.5 part of wormwood essential oil, 0.8 part of attapulgite, 0.5 part of zeolite with carrying silver, chitosan 3
Part, 3 parts of magnesium hydroxide, 0.8 part of nano barium sulfate.
Claims (3)
- A kind of 1. high-strength polypropylene film, it is characterised in that：Include the raw material of following parts by weight：Polypropylene 80-90 parts, fourth etherified resin 10-15 parts, triallyl isocyanate 4-8 parts, ethyl cellulose 10-15 parts, Pulullan polysaccharide 6-12 parts, pelopon A 3-6 parts, propane diols 30-40 parts, nm-class boron nitride 2-4 parts, nano oxygen It is SiClx 1-3 parts, nanometer antimony oxide 0.5-1 parts, flax fiber 0.5-1 parts, carbon fiber 1-3 parts, wormwood essential oil 0.1-0.5 parts, recessed Convex rod soil 0.3-0.8 parts, zeolite with carrying silver 0.1-0.5 parts, chitosan 1-3 parts, magnesium hydroxide 1-3 parts, nano barium sulfate 0.3-0.8 Part.
- A kind of 2. high-strength polypropylene film according to claim 1, it is characterised in that：Include the original of following parts by weight Material：85 parts of polypropylene, 12 parts of fourth etherified resin, 5 parts of triallyl isocyanate, 12 parts of ethyl cellulose, pulullan polysaccharide 8 Part, 4 parts of pelopon A, 35 parts of propane diols, 3 parts of nm-class boron nitride, 2 parts of nano silicon oxide, nanometer antimony oxide 0.7 Part, 0.7 part of flax fiber, 2 parts of carbon fiber, 0.2 part of wormwood essential oil, 0.5 part of attapulgite, 0.2 part of zeolite with carrying silver, chitosan 2 Part, 2 parts of magnesium hydroxide, 0.5 part of nano barium sulfate.
- A kind of 3. high-strength polypropylene film according to claim 1, it is characterised in that：Include the original of following parts by weight Material：88 parts of polypropylene, 14 parts of fourth etherified resin, 6 parts of triallyl isocyanate, 14 parts of ethyl cellulose, pulullan polysaccharide 11 It is part, 5 parts of pelopon A, 36 parts of propane diols, 2.5 parts of nm-class boron nitride, 1.5 parts of nano silicon oxide, nano oxidized 0.8 part of antimony, 0.9 part of flax fiber, 1.5 parts of carbon fiber, 0.4 part of wormwood essential oil, 0.7 part of attapulgite, 0.4 part of zeolite with carrying silver, 1.5 parts of chitosan, 1.5 parts of magnesium hydroxide, 0.6 part of nano barium sulfate.