CN107619638A - A kind of special-purpose nanometer coating of material for carving on it - Google Patents
A kind of special-purpose nanometer coating of material for carving on it Download PDFInfo
- Publication number
- CN107619638A CN107619638A CN201711056252.6A CN201711056252A CN107619638A CN 107619638 A CN107619638 A CN 107619638A CN 201711056252 A CN201711056252 A CN 201711056252A CN 107619638 A CN107619638 A CN 107619638A
- Authority
- CN
- China
- Prior art keywords
- nano
- carving
- special
- coating
- oxide liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of special-purpose nanometer coating of material for carving on it, it is processed into by following steps：By 10% 15% nano zine oxide liquid, after 5% 10% nano-titanium oxide liquid, 5% 15% nano silicon oxide liquid and 30% 50% polyurethane resin mixing, uniformly filtered again with gauze with mechanical agitation, dilute damp agent is added during use, and uses and is sprayed in air compressor machine.It is an advantage of the current invention that preparation method is simple, suitable multimedium surface treatment, acid and alkali-resistance, the engraving machine that anti-oxidant, Clear ＆ Transparent, cost is low are for the special nano coating of carving material.
Description
Technical field
The present invention relates to a kind of nano coating, the special-purpose nanometer coating of especially a kind of material for carving on it.
Background technology
Engraving machine is for the special multimedium coating of carving material, due to using epoxy resin powder, ethyl acetate as primary raw material,
Its composition is more active, oxidizable, and machine spraying normal temperature cure, such a technique high processing costs, technique must be carried out during production
Complexity, product is easy to aging, discoloration, is easily stained with oil smoke, not resistant to chemical etching, and coating easy peeling, change under high temperature, freezing environment
Color, loss of gloss, there is the difficult control of technique, quality is difficult to ensure card, the difficult weak point reduced of cost.
The content of the invention
It is an object of the invention to provide a kind of preparation method is simple, suitable multimedium surface treatment, acid and alkali-resistance, it is anti-oxidant,
A kind of special-purpose nanometer coating of material for carving on it Clear ＆ Transparent, cost is low.
The purpose of the present invention is achieved through the following technical solutions, and its preparation method comprises the following steps：
By 10%-15% nano zine oxide liquid, 5%-10% nano-titanium oxide liquid, 5%-15% nano oxygen
It is uniform with mechanical agitation after the mixing of SiClx liquid and 30%-50% polyurethane resin, then contained after being filtered with 200 mesh gauzes
In plastic barrel, because nanometer particle size of the present invention is quite tiny, admittedly it is all Clear ＆ Transparent shape after adding polyurethane resin equal solvent.
The nano coating of the present invention in 5-5 ratio in use, add dilute damp agent, and precipitation 30 minutes, is adopted after rocking uniformly
Sprayed with air compressor machine.
Dosage：The hardness needed according to user is voluntarily measured addition and used.
Storage：This product is stable in 5 DEG C -35 DEG C long-term indoor retention.
The present invention compared with prior art, has following outstanding advantages and beneficial effect：
1st, it is acidproof, alkaline-resisting, resistant to chemical etching, non-sticky lampblack dirty, the strong of inoxidizability
2nd, place after 5h without peeling loss of gloss phenomenon, and can be kept intact in the environment of ' C-150 ' C respectively 1.
3rd, nano coating of the invention is in the presence of 60kg/c expands power, and coating is without that comes off
4th, nano coating color clarification of the invention is transparent, bright, non-discolouring, colour-fast.
5th, technique cost of manufacture is cheap, environmental.
Embodiment
The technical scheme in inventive embodiments will be clearly and completely described below, it is clear that described embodiment
Only part of the embodiment of the present invention, rather than whole embodiments.Based on embodiments of the invention, ordinary skill
The every other embodiment that personnel are obtained on the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
Embodiment：
By 10%-15% nano zine oxide liquid, 5%-10% nano-titanium oxide liquid, 5%-15% nano oxygen
It is uniform with mechanical agitation after the mixing of SiClx liquid and 30%-50% polyurethane resin, then contained after being filtered with 200 mesh gauzes
In plastic barrel, because nanometer particle size of the present invention is quite tiny, admittedly it is all Clear ＆ Transparent shape after adding polyurethane resin equal solvent.
The nano coating of the present invention in 5-5 ratio in use, add dilute damp agent, and precipitation 30 minutes, is adopted after rocking uniformly
Sprayed with air compressor machine.
Dosage：The hardness needed according to user is voluntarily measured addition and used.
Storage：This product is stable in 5 DEG C -35 DEG C long-term indoor retention.
The present invention compared with prior art, has following outstanding advantages and beneficial effect：
1st, it is acidproof, alkaline-resisting, resistant to chemical etching, non-sticky lampblack dirty, the strong of inoxidizability
2nd, place after 5h without peeling loss of gloss phenomenon, and can be kept intact in the environment of ' C-150 ' C respectively 1.
3rd, nano coating of the invention is in the presence of 60kg/c expands power, and coating is without that comes off
4th, nano coating color clarification of the invention is transparent, bright, non-discolouring, colour-fast.
5th, technique cost of manufacture is cheap, environmental.
Above disclosed is only several preferred embodiments of the present invention, can not limit the present invention's with this certainly
Interest field, therefore the equivalent variations made according to the claims in the present invention, still belong to the scope that the present invention is covered.
Claims (4)
1. the special-purpose nanometer coating of a kind of material for carving on it, it is characterised in that be processed into by following steps：By 10%-15%
Nano zine oxide liquid, 5%-10% nano-titanium oxide liquid, 5%-15% nano silicon oxide liquid and 30%-50%
Polyurethane resin mixing after, uniformly filtered again with gauze with mechanical agitation, dilute damp agent added during use, and in use air compressor machine
Spraying.
A kind of 2. special-purpose nanometer coating of material for carving on it according to claim 1, it is characterised in that：Described nano coating
It is to add dilute damp agent in 5-5 ratio during use.
A kind of 3. special-purpose nanometer coating of material for carving on it according to claim 1, it is characterised in that：Described gauze filtering
It is the gauze with 200.
A kind of 4. special-purpose nanometer coating of material for carving on it according to claim 2, it is characterised in that：The dilute pool of described addition
The nano coating of agent need to be precipitated 30 minutes and could used.