CN107619217A - A kind of high durable fire-retardant heat-insulation material - Google Patents
A kind of high durable fire-retardant heat-insulation material Download PDFInfo
- Publication number
- CN107619217A CN107619217A CN201710967813.1A CN201710967813A CN107619217A CN 107619217 A CN107619217 A CN 107619217A CN 201710967813 A CN201710967813 A CN 201710967813A CN 107619217 A CN107619217 A CN 107619217A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- insulation material
- retardant heat
- high durable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high durable fire-retardant heat-insulation material, including inorganic raw material, Organic Ingredients and fiber mixture, the inorganic raw material includes following components by weight percent：18 55 parts of metal aggregate, 15 44 parts of filler-silicon dioxide powder, 10 36 parts of powdered whiting powder, 25 79 parts of sulfate compound, 25 66 parts of silicate compound, 10 48 parts of adhesive special, 31 56 parts of foaming agent；The Organic Ingredients includes following composition by weight：15 26 parts of acrylic resin powder, 13 26 parts of polyurethane powder；The fiber mixture includes following composition by weight：25 62 parts of asbestos fibre, 11 17 parts of metallic fiber.The reasonable raw material proportioning of the present invention, in the case of proof strength and heat-insulating property, density ratio Conventional insulation is smaller, therefore lighter, makes the use range of the present invention wider.
Description
Technical field
The present invention relates to field of heat insulating materials, specially a kind of high durable fire-retardant heat-insulation material.
Background technology
Existing most of insulation materials, heat-insulating property is poor, and thermal conductivity factor is higher, can not in the occasion for needing to be incubated
Preferable insulation effect is played, traditional insulation material does not have fireproof effect, and burning-point is relatively low, therefore in the mistake used
Cheng Zhong, once there is fire, caused by loss the density of huge, traditional insulation material will be made larger, inadequate lightweight is overall
The caking property of material is poor, causes product strength made of Conventional insulation inadequate, easily comes off, use range has larger
Limitation.
The content of the invention
It is an object of the invention to provide a kind of high durable fire-retardant heat-insulation material, to solve what is proposed in above-mentioned background technology
Problem.
To achieve the above object, the present invention provides following technical scheme：A kind of fire-retardant heat-insulation material, including inorganic raw material,
Organic Ingredients and fiber mixture, the inorganic raw material include following components by weight percent：Metal aggregate 18-55 parts, filler titanium dioxide
Si powder 15-44 parts, powdered whiting powder 10-36 parts, sulfate compound 25-79 parts, silicate compound 25-66 parts,
Adhesive special 10-48 parts, foaming agent 31-56 parts；The Organic Ingredients includes following composition by weight：Acrylic resin powder
15-26 parts, polyurethane powder 13-26 parts；The fiber mixture includes following composition by weight：Asbestos fibre 25-62 parts, metal
Fiber 11-17 parts.
Preferably, the metal aggregate includes following composition by weight：Alundum (Al2O3) 12-27 parts, iron oxide 16-24 parts,
Calcium oxide 2-10 parts, magnesia 4-12 parts, potassium oxide 0.1-0.8 parts, sodium oxide molybdena 0.1-1.3 parts.
Preferably, the sulfate compound includes following composition by weight：Magnesium sulfate 15-46 parts, calcium sulfate 17-47 parts,
Alum 5-34 parts, barium sulfate 2-27 parts.
Preferably, the silicate compound includes following composition by weight：Alumina silicate 8-13 parts, magnesium silicate 6-24 parts, silicon
Sour calcium 7-16 parts.
Preferably, the particle diameter of the acrylic resin powder and polyurethane powder is respectively less than 90 microns.
Preferably, the asbestos fibre includes chrysotile 3-16 parts, amphibole asbestos 2-17 parts, actinolite asbestos 3-
17 parts, antophyllite 9-25 parts, amosite 5-13 parts.
Preferably, the metallic fiber is to include stainless steel fibre 1-17 parts, silver fiber 5-9 parts.
Preferably, the fibre length of the fiber mixture is 2-6 millimeters.
Compared with prior art, the beneficial effects of the invention are as follows：This fire-retardant heat-insulation material formula is simple, and heat-insulating property is more
Good, the caking property of material in itself is preferable, and manufactured insulating product is more sturdy and durable, is less prone to the phenomenon to come off, and this
The fire protecting performance of invention is more preferable, and flammable raw material is few, therefore this material closes without combustibility, raw material proportioning of the invention
Reason, in the case of proof strength and heat-insulating property, density ratio Conventional insulation is smaller, therefore lighter, makes the present invention's
Use range is wider.
Embodiment
The technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described implementation
Example only part of the embodiment of the present invention, rather than whole embodiments.It is common based on the embodiment in the present invention, this area
The every other embodiment that technical staff is obtained under the premise of creative work is not made, belong to the model that the present invention protects
Enclose.
Embodiment one
The present invention provides a kind of technical scheme：A kind of high durable fire-retardant heat-insulation material, including inorganic raw material, Organic Ingredients and
Fiber mixture, inorganic raw material include following components by weight percent：25 parts of metal aggregate, 15 parts of filler-silicon dioxide powder, heavy carbon
Sour 16 parts of calcium powder, 53 parts of sulfate compound, 27 parts of silicate compound, 25 parts of adhesive special, 26 parts of foaming agent；It is organic
Raw material includes following composition by weight：24 parts of acrylic resin powder, 13 parts of polyurethane powder；Fiber mixture includes following weight
Component：35 parts of asbestos fibre, 12 parts of metallic fiber.
Metal aggregate includes following composition by weight：18 parts of alundum (Al2O3), 16 parts of iron oxide, 12 parts of calcium oxide, magnesia
14 parts, 0.2 part of potassium oxide, 0.8 part of sodium oxide molybdena.
Sulfate compound includes following composition by weight：12 parts of magnesium sulfate, 14 parts of calcium sulfate, 16 parts of alum, sulfuric acid
13 parts of barium.
Silicate compound includes following composition by weight：14 parts of alumina silicate, 15 parts of magnesium silicate, 11 parts of calcium silicates.
The particle diameter of Phenolic resin powder and polyurethane powder is respectively less than 90 microns.
Asbestos fibre includes 8 parts of chrysotile, 4 parts of amphibole asbestos, 10 parts of actinolite asbestos, antophyllite 12
Part, 6 parts of amosite.
Metallic fiber is to include 12 parts of stainless steel fibre, 2 parts of silver fiber.
The fibre length of fiber mixture is 6 millimeters.
Embodiment two
The present invention provides a kind of technical scheme：A kind of high durable fire-retardant heat-insulation material, including inorganic raw material, Organic Ingredients and
Fiber mixture, inorganic raw material include following components by weight percent：38 parts of metal aggregate, 21 parts of filler-silicon dioxide powder, heavy carbon
Sour 26 parts of calcium powder, 48 parts of sulfate compound, 55 parts of silicate compound, 36 parts of adhesive special, 35 parts of foaming agent；It is organic
Raw material includes following composition by weight：21 parts of acrylic resin powder, 18 parts of polyurethane powder；Fiber mixture includes following weight
Component：32 parts of asbestos fibre, 36 parts of metallic fiber.
Metal aggregate includes following composition by weight：13 parts of alundum (Al2O3), 19 parts of iron oxide, 22 parts of calcium oxide, magnesia
15 parts, 0.6 part of potassium oxide, 0.5 part of sodium oxide molybdena.
Sulfate compound includes following composition by weight：26 parts of magnesium sulfate, 10 parts of calcium sulfate, 15 parts of alum, sulfuric acid
12 parts of barium.
Silicate compound includes following composition by weight：17 parts of alumina silicate, 13 parts of magnesium silicate, 12 parts of calcium silicates.
The particle diameter of Phenolic resin powder and polyurethane powder is respectively less than 90 microns.
Asbestos fibre includes 15 parts of chrysotile, 12 parts of amphibole asbestos, 19 parts of actinolite asbestos, antophyllite 15
Part, 7 parts of amosite.
Metallic fiber is to include 12 parts of stainless steel fibre, 4 parts of silver fiber.
The fibre length of fiber mixture is 5 millimeters.
Embodiment three
The present invention provides a kind of technical scheme：A kind of high durable fire-retardant heat-insulation material, including inorganic raw material, Organic Ingredients and
Fiber mixture, inorganic raw material include following components by weight percent：45 parts of metal aggregate, 33 parts of filler-silicon dioxide powder, heavy carbon
Sour 34 parts of calcium powder, 67 parts of sulfate compound, 55 parts of silicate compound, 54 parts of binding agent, 65 parts of foaming agent；Organic Ingredients
Including following composition by weight：16 parts of acrylic resin powder, 5 parts of polyurethane powder；Fiber mixture includes following composition by weight：
39 parts of asbestos fibre, 26 parts of metallic fiber.
Metal oxide includes following composition by weight：8 parts of alundum (Al2O3), 12 parts of iron oxide, 11 parts of calcium oxide, magnesia
7 parts, 0.6 part of potassium oxide, 0.3 part of sodium oxide molybdena.
Sulfate compound includes following composition by weight：18 parts of magnesium sulfate, 16 parts of calcium sulfate, 14 parts of alum, sulfuric acid
21 parts of barium.
Silicate compound includes following composition by weight：12 parts of alumina silicate, 13 parts of magnesium silicate, 17 parts of calcium silicates.
The particle diameter of Phenolic resin powder and polyurethane powder is respectively less than 90 microns.
Asbestos fibre includes 16 parts of chrysotile, 13 parts of amphibole asbestos, 9 parts of actinolite asbestos, antophyllite 7
Part, 3 parts of amosite.
Metallic fiber is to include 11 parts of stainless steel fibre, 14 parts of silver fiber.
The fibre length of fiber mixture is 5 millimeters.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. a kind of high durable fire-retardant heat-insulation material, including inorganic raw material, Organic Ingredients and fiber mixture, it is characterised in that institute
Stating inorganic raw material includes following components by weight percent：Metal aggregate 18-55 parts, filler-silicon dioxide powder 15-44 parts, powdered whiting
Powder 10-36 parts, sulfate compound 25-79 parts, silicate compound 25-66 parts, adhesive special 10-48 parts, foaming agent
31-56 parts；The Organic Ingredients includes following composition by weight：Acrylic resin powder 15-26 parts, polyurethane powder 13-26 parts；
The fiber mixture includes following composition by weight：Asbestos fibre 25-62 parts, metallic fiber 11-17 parts.
A kind of 2. high durable fire-retardant heat-insulation material according to claim 1, it is characterised in that the metal aggregate include with
Lower composition by weight：Alundum (Al2O3) 12-27 parts, iron oxide 16-24 parts, calcium oxide 2-10 parts, magnesia 4-12 parts, potassium oxide
0.1-0.8 parts, sodium oxide molybdena 0.1-1.3 parts.
A kind of 3. high durable fire-retardant heat-insulation material according to claim 1, it is characterised in that the sulfate salt and spice
Include following composition by weight：Magnesium sulfate 15-46 parts, calcium sulfate 17-47 parts, alum 5-34 parts, barium sulfate 2-27 parts.
A kind of 4. high durable fire-retardant heat-insulation material according to claim 1, it is characterised in that the silicate salt and spice
Include following composition by weight：Alumina silicate 8-13 parts, magnesium silicate 6-24 parts, calcium silicates 7-16 parts.
A kind of 5. high durable fire-retardant heat-insulation material according to claim 1, it is characterised in that the acrylic resin powder
90 microns are respectively less than with the particle diameter of polyurethane powder.
6. a kind of high durable fire-retardant heat-insulation material according to claim 1, it is characterised in that the asbestos fibre includes snake
Line stone asbestos 3-16 parts, amphibole asbestos 2-17 parts, actinolite asbestos 3-17 parts, antophyllite 9-25 parts, amosite 5-13
Part.
7. a kind of high durable fire-retardant heat-insulation material according to claim 1, it is characterised in that the metallic fiber is to include
Stainless steel fibre 1-17 parts, silver fiber 5-9 parts.
A kind of 8. high durable fire-retardant heat-insulation material according to claim 1, it is characterised in that the fibre of the fiber mixture
Dimension length is 2-6 millimeters.