CN107619176A - A kind of preparation method of air strengthened glass - Google Patents
A kind of preparation method of air strengthened glass Download PDFInfo
- Publication number
- CN107619176A CN107619176A CN201610552826.8A CN201610552826A CN107619176A CN 107619176 A CN107619176 A CN 107619176A CN 201610552826 A CN201610552826 A CN 201610552826A CN 107619176 A CN107619176 A CN 107619176A
- Authority
- CN
- China
- Prior art keywords
- section
- glass
- bringing
- heating
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of air strengthened glass preparation method, its step are as follows:1)Plate glass load through roller-way be sent into heating chamber step, 2)Heating stepses, 3)Cooling step, 4)Unloading piece step;Its feature is:Heating chamber inner chamber is at least divided into 4 sections, and the hermatic door with control device is respectively mounted in the exit of the heating chamber porch and each bringing-up section;The overall heating-up temperature of heating chamber is 290-720 DEG C, is distributed in each bringing-up section;Temperature between previous bringing-up section and latter bringing-up section is trapezoidal incremental, and its temperature difference is 100-150 DEG C, and every section of heat time is respectively 100~300 seconds;Glass unidirectionally uninterruptedly moves forward with roller-way, and its translational speed is 20~100mm/ seconds;Cooling step uses cold wind blower, and cool time is 180~600 seconds.After the present invention integrates the glass heating after improvement, the mobile and type of cooling, suitable for the tempering of common and various coated glasses, eliminate roller print and reduce stress speckle, its technique is simple and convenient to operate, implementation easy to spread.
Description
Technical field
The present invention relates to the preparation method of air strengthened glass in glass post-processing field.
Background technology
Wind tempering technology refers to the glass strengthening technology that ordinary plate glass use intensity is improved by heat treatment process.
Air strengthened glass intensity is 2~3 times of simple glass intensity, and good impact resistance, heat endurance is good, is hit in external force
Hit down do not allow it is broken;Even if broken, internal tensile stress makes whole glass moment be broken into tiny particle, bearing stress
Then fine particle is pressed together, larger fragment will not be formed, avoid injury of the glass fragment to human body, therefore air hardening steel
Glass belongs to safety glass, in architectural extensive use.
The content of the invention
, can it is an object of the invention to provide one kind in order to solve defect present in above-mentioned existing wind tempering technology
Heating has the coated glass of heat reflection, reduces roller print and abrades, improves the flatness reduction table after flat glass tempering
The preparation method of the air strengthened glass of surface damage degree.
To achieve these goals, the technical solution adopted by the present invention is as follows:A kind of preparation method of air strengthened glass,
Realized by following steps:1) glass load through roller-way be sent into heating chamber step, 2) heating stepses, 3) cooling step, 4) unloading piece step
Suddenly;It is characterized in that:The heating chamber inner chamber is at least divided into 4 sections, the outlet of the heating chamber porch and each bringing-up section
Place is respectively mounted the hermatic door with control device;The heating-up temperature of the heating chamber inner chamber is arranged to 290-720 DEG C, by it is low to
Height is distributed in each bringing-up section, and the temperature between previous bringing-up section and latter bringing-up section is trapezoidal incremental, and its temperature difference is 100-
150 DEG C, every section of heat time is respectively set to 100~300 seconds;The glass unidirectionally uninterruptedly moves forward with the roller-way, its
Translational speed is 20~100mm/ seconds;The cooling step uses cold wind blower, and cool time is 180~600 seconds.
Setting up separately for above-mentioned bringing-up section can have various ways, one:4 bringing-up sections can be divided into, the 1st, 2,3 section is adopted
With electric furnace heating wire radiant heating;4th section is heated using convective air circulation;Its every section heating-up temperature is respectively set to:1st section
290-310℃;2nd section 440-460 DEG C;3rd section 540-560 DEG C;4th section 680 DEG C.
Secondly:4 bringing-up sections can be divided into, at least 1 section is heated using convective air circulation in the 1st, 2,3 section, and remaining is adopted
With electric furnace heating wire radiant heating;4th section is heated using convective air circulation;The heating-up temperature is respectively set to:1st section of 290-
310℃;2nd section 440-460 DEG C;3rd section 560 DEG C;4th section 680-720 DEG C.
Thirdly:4 bringing-up sections can be divided into, convective air circulation mode of heating is respectively adopted in 4 bringing-up sections;Every section
Heating-up temperature be respectively set to:1st section 290-310 DEG C;2nd section 440-460 DEG C;3rd section 540-560 DEG C;4th section is
680-700℃。
According to the specification size and quality requirement to safety glass, according to above-mentioned mode of heating, bringing-up section can also divide
Multistage is set to, heating-up temperature is scattered in multiple independent bringing-up sections, to ensure the safety glass surface quality processed not
It is damaged.
Above-mentioned cold wind blower uses slit injector air grid type cold wind blower.
The present invention general principle be:
1. changing the mode of heating of a greenhouse heating in traditional safety glass technology, heated using the glass of a Room multi-temperature section
Technology, the thermal shock of the 290-720 DEG C of heating temperature difference is distributed in 4 or more bringing-up sections, glass is in previous heating
It is pre-heated in section and enters back into the latter bringing-up section after design temperature and continue to heat, thermal shock is small, and glass deformation is small, glass
Weight is undertaken by more rollers, can mitigate the scratch for even completely eliminating roller to glass back significantly.
2. the mode in rotary moving of glass in traditional safety glass technology with roller-way " positive-reversely-positive " is changed,
Using by glass in heating process unidirectional continual move mode, make glass keep a direction constant motion, the back side
The frictional force size and Orientation being subject to is constant, reduces glass deformation degree and surface damage degree;
3. heating glass by the way of hot-air convection heating, the glass of heating will not be by the shadow of glass surface membranous layer property
Ring, uniformly can quickly heat the various coated glasses such as Low-E, realize the tempering of coated glass.
4. using slit cooling air grid technology cooling glass, by the point cooling side of traditional circular hole formula air port
Formula makes the wire type type of cooling of slit type air spray line into, improves the uniformity to heating glass cooling, effectively reduces glass
The defects of glass surface stress difference, improve the flatness of glass surface.
The present invention is after adopting the above technical scheme, have the beneficial effect that:(1) add in improved wind steel process
Convective air circulation mode of heating is entered, has realized the air hardening steel to the various coated glasses such as Low-E, effectively increase Low-E
Etc. the intensity of various coated glasses;(2) heating chamber is divided into some bringing-up sections, is divided into 4 sections or more of section, by 290-720 DEG C
Temperature be divided into 4 or multiple temperature layers by the temperature difference, will piecewise elevated Temperature Distribution in each bringing-up section, enable glass
It is enough that another higher temperature range is steadily being entered by a temperature range, the heat acclimation power of glass is stepped up, it is real
The purpose that its existing air strengthened glass flatness is high, deformation is small;In the cladding glass of composition, image fault is small, and presentation quality shows
Write and improve;(3) cooling device uses slit injector air grid type cold wind blower, is dried by slit type air and sprays line
Wire type cools down, and improves the uniformity of glass surface cooling, makes its glass surface stress through air hardening steel uniform, stress speckle
Degree mitigates 50%, even completely eliminates;(4) as a result of improved glass mode of heating, move mode and new cooling
The integration technology of mode, solve safety glass unsolved problem always for a long time, be not only able to produce ordinary flat
Safety glass, and can also the various coated glasses of tempering, glass flatness, optical quality after tempering improve, roller print and should
Power speckle is reduced and even completely eliminated;Technique is simple and convenient to operate, implementation easy to spread.
Embodiment
The preparation method of air strengthened glass of the present invention, comprises the following steps:Glass is first positioned over load platform
On, heating chamber is entered by rollgang, after heating chamber, tempering cooling are sent out after preheated, then takes out and is molded through unloading piece process
For air strengthened glass;Above-mentioned heating chamber inner chamber is arranged with least four bringing-up section, and 6 bringing-up sections at most can be set;Each heating
The exit of section is respectively mounted the hermatic door with control device;Total heating-up temperature in heating chamber is 290 DEG C -720 DEG C, by preceding
It is laid in respectively in each bringing-up section to rear;Temperature between previous bringing-up section and latter bringing-up section is trapezoidal incremental, its temperature difference
For 100-150 DEG C;Every section of heat time is respectively 100~300 seconds;It is specifically configured to:1st bringing-up section is 290-310 DEG C;
2nd bringing-up section is 310-460 DEG C;3rd bringing-up section is 460-560 DEG C;4th section is 560-720 DEG C;Glass is with rollgang
Move forward, mobile is unidirectional uninterrupted reach, can also be by the way of moving back and forth;Translational speed is 20~100mm/
Second;Each bringing-up section forms separate space by the closing of hermatic door, individually heating, to the last a bringing-up section heating
To maximum temperature, heating chamber, then the colling end formed through the air grid provided with slit injector are removed, it is through drying that glass is cold
But to normal temperature, cool time is 180~600 seconds.
Bringing-up section set number with the production scale size of air strengthened glass determine when being divided into 4 sections, can there is three kinds
Mode, one is:First 3 sections use electric furnace heating wire radiant heating;4th section is heated using convective air circulation;It 2 is:In first 3 sections
At least 1 section is heated using convective air circulation, and remaining uses electric furnace heating wire radiant heating;4th section is added using convective air circulation
Heat;The third is:4 bringing-up sections are all using convective air circulation mode of heating.
Similarly, when heating chamber is divided into multistage, mode of heating is designed according to above-mentioned principle, heating-up temperature is distributed to respectively
In individual bringing-up section.
Technical scheme is described in detail by the following examples:
Embodiment 1:
It is 1000 × 1000 × 10mm ordinary plate glass to select a block specifications, and presentation quality checks no calculus, bubble, drawn
The defects of hindering, the milled processed periphery on linear edge grinder, clean dry it is standby.
Wind tempering apparatus is provided with load platform, heating chamber, cooling section and unloads fragment, and roller-way runs through load platform, heating
In room, refrigerating work procedure and unloading piece process;Above-mentioned ordinary plate glass is placed on the roller-way on load platform, starts motor, roller
Road is rotated, and the glass is sent into heating chamber under room temperature state and heated.The heating chamber is divided into 4 sections, the 1st, 2,3 section
Electric furnace heating wire radiant heating is respectively set to, i.e., is separately installed with electric furnace heating wire in the upper and lower sides of bringing-up section;4th section empty using convection current
Gas circulating-heating, i.e., closed box is set respectively in body of heater upper and lower sides, heater is set in case, upper and lower ends set inlet, outlet
Mouthful, air inlet is connected by pipeline with blower fan exhaust end, and gas outlet is jet orifice plate, and the gas of ejection heats glass surface, then
Fan air inlet is returned to, forms closed circulation.The porch of heating chamber and the exit of each bringing-up section are separately installed with band
There is the hermatic door of control device, hermatic door is turned on and off at any time by control device with movement of its glass in bringing-up section.
The cooling device that refrigerating work procedure is connected at heating chamber outlet by one is formed, and cooling device is mounted to the seam of roller-way upper and lower
Gap type nozzle air grid, outdoor air is compressed by the high-power blower of peripheral hardware caused by cold wind by air grid to after heating
Glass be uniformly blown, until glass is down to room temperature;Unloading piece process refers to the glass after cooling by being taken out on roller-way, folded to fall within
On glass frame.
Concrete technology:First above-mentioned glass horizontal is placed in the glass conveying roller way of wind tempering apparatus load platform, started
Motor, roller bed rotation, the hermatic door of heating chamber porch is opened, the plate glass is sent into the 1st bringing-up section and heated;
The temperature setting of 1st bringing-up section is 290 DEG C, and the heat time is 300 seconds;Glass unidirectionally uninterruptedly moves forward, translational speed 20mm/
Second;When moving to the 1st bringing-up section exit, the hermatic door in the exit is opened, and glass enters the 2nd bringing-up section, continues to heat;
After glass is completely into 2 bringing-up section, the hermatic door in the 1st bringing-up section exit is closed, and temperature is set in the 2nd bringing-up section
440 DEG C are set to, the heat time is 300 seconds;Glass continues uninterrupted reach, translational speed 20mm/ seconds, when glass is moved to the 2nd
During the outlet of bringing-up section, the hermatic door in the 2nd bringing-up section exit is opened, and now, glass moves to the 3rd bringing-up section, continues to heat;
After glass is completely into 3 bringing-up section, the hermatic door in the 2nd bringing-up section exit is closed, and temperature is set in the 3rd bringing-up section
540 DEG C are set to, the heat time is 300 seconds, and glass continues uninterrupted reach, translational speed 20mm/ seconds;When glass is moved to the 3rd
During the outlet of bringing-up section, the hermatic door in the 3rd bringing-up section exit is opened, and now, glass moves to the 4th bringing-up section, continues to heat;
After glass is completely into 4 bringing-up section, the hermatic door in the 3rd bringing-up section exit is closed, and is arranged in the 4th bringing-up section
Convective air circulation mode of heating, its heating-up temperature are arranged to 680 DEG C, and the heat time is 300 seconds, before glass continues uninterruptedly
Move, the translational speed 20mm/ seconds.When glass is moved to the outlet of the 4th bringing-up section, the hermatic door in the 4th bringing-up section exit is opened
Open, glass removes heating chamber and enters refrigerating work procedure, and the air grid through being set in refrigerating work procedure is blown a cold wind over steel to the glass after heating
Change, the air grid uses the air outlet slit of slit, wind can be made to blow to glass surface with narrow line shape, to ensure glass surface
What is cooled down is uniform;After safety glass is cooled down 180 seconds, then through roller-way immigration unloading piece process, glass is removed, folded completion case is complete
Into whole tempering preparation process.
During the entire process of above-mentioned operation operation, the hermatic door of heating chamber porch and each bringing-up section exit
The control device of hermatic door is arranged on the operating desk used by this patent on the outside of firing equipment, and control device is to heating chamber
The hermatic door of porch and the hermatic door in each bringing-up section exit carry out Synchronization Control, and glass adds by each bringing-up section
The speed of hot time and reach is identical.
Embodiment 2:
In the glass size of selection and used tempering apparatus and operating process to heating glass in each section of heating
Between with the speed that glass unidirectionally moves forward with embodiment 1, will not be repeated here.
Its difference is:The heating chamber is divided into 4 sections, and the 1st, 3 section is respectively set to electric furnace heating wire radiant heating, that is, exists
The upper and lower sides of bringing-up section are separately installed with electric furnace heating wire;2nd, 4 section is heated using convective air circulation, i.e., in body of heater upper and lower sides point
Closed box is not set, heater is set in case, upper and lower ends set inlet, outlet, and air inlet is vented by pipeline and blower fan
End is connected, and gas outlet is jet orifice plate, and the gas of ejection returns to fan air inlet, forms closed circulation.
Concrete technology:First above-mentioned glass horizontal is placed in the glass conveying roller way of wind tempering apparatus load platform, started
Motor, roller bed rotation, the hermatic door of heating chamber porch is opened, the plate glass is sent into the 1st bringing-up section and heated;
The temperature setting of 1st bringing-up section is 310 DEG C, and the heat time is 200 seconds;Glass unidirectionally uninterruptedly moves forward, translational speed 50mm/
Second;When moving to the 1st bringing-up section exit, the hermatic door in the exit is opened, and glass enters the 2nd bringing-up section, continues to heat;
After glass is completely into 2 bringing-up section, the hermatic door in the 1st bringing-up section exit is closed, and temperature is set in the 2nd bringing-up section
460 DEG C are set to, the heat time is 200 seconds;Glass continues uninterrupted reach, translational speed 50mm/ seconds, when glass is moved to the 2nd
During the outlet of bringing-up section, the hermatic door in the 2nd bringing-up section exit is opened, and now, glass moves to the 3rd bringing-up section, continues to heat;
After glass is completely into 3 bringing-up section, the hermatic door in the 2nd bringing-up section exit is closed, and temperature is set in the 3rd bringing-up section
560 DEG C are set to, the heat time is 200 seconds, and glass continues uninterrupted reach, translational speed 50mm/ seconds;When glass is moved to the 3rd
During the outlet of bringing-up section, the hermatic door in the 3rd bringing-up section exit is opened, and now, glass moves to the 4th bringing-up section, and convection current continues to add
Heat;
After glass is completely into 4 bringing-up section, the hermatic door in the 3rd bringing-up section exit is closed, the 4th bringing-up section heating-up temperature
720 DEG C are arranged to, the heat time is 200 seconds, and glass continues uninterrupted reach, translational speed 50mm/ seconds.When glass is moved to
During the outlet of the 4th bringing-up section, the hermatic door in the 4th bringing-up section exit is opened, and now, glass moves to refrigerating work procedure, through bosher
The air grid blowing tempering set in sequence, after cooling down 600 seconds, cooling fan is exported using slit type air, can be polygonal
Degree, multiple duct by wind to glass surface, ensure that glass surface cools down uniform;By the safety glass after cooling through roller
Road is moved into unloading piece process, and glass is removed, and folds completion case, completes whole tempering preparation process.
Embodiment 3
In the glass size of selection and used tempering apparatus and operating process to heating glass in each section of heating
Between with the speed that glass unidirectionally moves forward with embodiment 1, will not be repeated here.
Its difference is:Heating chamber inner chamber is divided into 4 bringing-up sections, and 4 bringing-up sections are all using convective air circulation
Mode of heating.
Concrete technology:First above-mentioned glass horizontal is placed in the glass conveying roller way of wind tempering apparatus load platform, started
Motor, roller bed rotation, the hermatic door of heating chamber porch is opened, the plate glass is sent into the 1st bringing-up section and heated;
The temperature setting of 1st bringing-up section is 300 DEG C, and the heat time is 100 seconds;Glass unidirectionally uninterruptedly moves forward, translational speed 100mm/
Second;When moving to the 1st bringing-up section exit, the hermatic door in the exit is opened, and glass enters the 2nd bringing-up section, continues to heat;
After glass is completely into 2 bringing-up section, the hermatic door in the 1st bringing-up section exit is closed, and temperature is set in the 2nd bringing-up section
450 DEG C are set to, the heat time is 100 seconds;Glass continues uninterrupted reach, the translational speed 100mm/ seconds, when glass is moved to the
During the outlet of 2 bringing-up sections, the hermatic door in the 2nd bringing-up section exit is opened, and now, glass moves to the 3rd bringing-up section, continues to heat;
After glass is completely into 3 bringing-up section, the hermatic door in the 2nd bringing-up section exit is closed, and temperature is set in the 3rd bringing-up section
550 DEG C are set to, the heat time is 100 seconds, and glass continues uninterrupted reach, translational speed 100mm/ seconds;When glass is moved to
During the outlet of 3 bringing-up sections, the hermatic door in the 3rd bringing-up section exit is opened, and now, glass moves to the 4th bringing-up section, and convection current continues
Heating;
After glass is completely into 4 bringing-up section, the hermatic door in the 3rd bringing-up section exit is closed, and the 4th bringing-up section is arranged to pair
Air circulation mode of heating is flowed, its heating-up temperature is arranged at 700 DEG C, and glass continues uninterrupted reach, translational speed 100mm/
Second.When glass is moved to the outlet of the 4th bringing-up section, the hermatic door in the 4th bringing-up section exit is opened, and now, glass moves to cold
But process, the air grid blowing tempering through being set in refrigerating work procedure, after cooling down 360 seconds, cooling fan is gone out using slit type air
Mouthful, can multi-angle, multiple duct by wind to glass surface, ensure that glass surface cools down uniform;After cooling down
Safety glass through roller-way be moved into unloading piece process, glass is removed, fold completion case, complete whole tempering preparation process.
The air strengthened glass prepared using the present invention, detected according to standard GB/T/T 9963-1998 of safety glass,
The mass parameters such as its transmittance, impact resistance, fragmentation status, canister shot bag impact property, resisting wind press capacity comply fully with national mark
Accurate regulation, and flatness is then much smaller than Bow 0.5% in standard, the regulation of sinusoidal degree 0.3%.Although mark
Stress speckle is not provided in standard, but adverse effect has caused use caused by the presence of stress speckle
The attention of person, therefore in safety glass standard revision declaration version, add the illustrative annex of data to stress speckle.This
Air strengthened glass prepared by invention is hardly visible the presence of stress speckle.
In addition, present invention employs the heating technique that radiation-convection current combines, with the microwave heating technique in United States Patent (USP)
Compare, cost reduces, and technology maturation, device structure is simple, easy to operate, application easy to spread.
Claims (4)
1. a kind of preparation method of air strengthened glass, is realized by following steps:1) glass load is sent into heating chamber step through roller-way
Suddenly, 2) heating stepses, 3) cooling step, 4) unloading piece step;It is characterized in that:The heating chamber inner chamber is at least divided into 4 sections,
The heating chamber porch and the exit of each bringing-up section are respectively mounted the hermatic door with control device;In the heating chamber
The heating-up temperature of chamber is arranged to 290-720 DEG C, is distributed in from low to high in each bringing-up section, previous bringing-up section and latter heating
Temperature between section is trapezoidal incremental, and its temperature difference is 100-150 DEG C, and every section of heat time is respectively set to 100~300 seconds;
The glass unidirectionally uninterruptedly moves forward with the roller-way, and its translational speed is 20~100mm/ seconds;The cooling step, which uses, to be blown
Air-cooling device, cool time are 180~600 seconds.
2. the preparation method of air strengthened glass as claimed in claim 1, it is characterised in that:The bringing-up section is divided into 4 sections, and
1st, 2,3 sections use electric furnace heating wire radiant heating;4th section is heated using convective air circulation;The heating-up temperature is respectively set to:
1st section 290-310 DEG C;2nd section 440-460 DEG C;3rd section 540-560 DEG C;4th section 680 DEG C.
3. the preparation method of air strengthened glass as claimed in claim 1, it is characterised in that:The bringing-up section is divided into 4 sections, point
Cai Yong not convective air circulation mode of heating;The heating-up temperature is respectively set to:1st section 290-310 DEG C;2nd section of 440-
460℃;3rd section 540-560 DEG C;4th section is 680-700 DEG C.
4. the preparation method of air strengthened glass as described in claim 1 or 2 or 3, it is characterised in that:The cold wind blower
For slit injector air grid type cold wind blower.