CN107617813A - The welding method of cable wire and thin plate - Google Patents
The welding method of cable wire and thin plate Download PDFInfo
- Publication number
- CN107617813A CN107617813A CN201711026536.0A CN201711026536A CN107617813A CN 107617813 A CN107617813 A CN 107617813A CN 201711026536 A CN201711026536 A CN 201711026536A CN 107617813 A CN107617813 A CN 107617813A
- Authority
- CN
- China
- Prior art keywords
- cable wire
- thin plate
- plate
- pressing plate
- welding method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the welding method of a kind of cable wire and thin plate, in the fixed position of cable wire and thin plate, cable wire is set to be bonded with thin plate, the pressing plate adaptable with the face facial contour of thin plate on lid on cable wire, some place's resistance spot weldings are carried out to pressing plate and thin plate, pressing plate and thin plate is compressed cable wire, resistance spot welding at least two is carried out to pressing plate, thin plate and cable wire, is melted together pressing plate, thin plate and cable wire.This method deburring amount is few, and cable wire pulling-out force is high, and anti-corrosion capability is strong, high in machining efficiency.
Description
Technical field
The invention belongs to welding field, and in particular to a kind of welding method of cable wire and thin plate.
Background technology
Cable wire is as a kind of important flexible connection and stress conducting parts, it is necessary to be connected from different parts so as to realize
Different functions.As shown in figure 1, be existing several relatively common cable wire connected modes --- cable wire one end through joint,
Pressure is received by joint to fix；Cable wire both-end plug-in-sleeve, pressure fixation is received by sleeve pipe；Cable wire one end passes through steel ball, passes through steel ball
Pressure is received to fix.These are all the connections of cable wire and block part, and overall weight is larger, are not suitable for Aero-Space etc. to weight
It is required that strict occasion.
In order to mitigate weight, cable wire is connected by people by way of welding with thin plate, as shown in Fig. 2 being stitched for use
Thread cable wire draw ring support board structure on part, wherein, supporting plate is the thin plate of connection needed for cable wire, and thin plate is using 304 stainless steels, thickness
0.5mm, cable wire are inlayed on thin plate in R0.75 arc grooves using stainless steel wire braiding, diameter about φ 1.5, a cable wire part, due to
Electric arc welding is easily burnt, and the heat time is long when slab temperatures are more than 450~850 degrees Celsius of welding, under part decay resistance
, easily there is defect of getting rusty, is easily broken under corrosive environment in drop, therefore stainless steel cable wire is not suitable for using arc welding with thin plate
Connect or high temperature brazing, thus typically use manual flatiron tin-lead material soldering, using zinc chloride scaling powder, Sn-coupled SSBR temperature is less than
300 DEG C, all contact positions of cable wire and thin plate are welded.
Problems be present in the welding method of above-mentioned cable wire and thin plate：1) it is low using Sn-coupled SSBR weld strength, weld appearance
Difference, during use cable wire easily pull, it is discarded after pollute environment；2) easy brittle failure after cable wire surface treatment；3) manual iron soldering
It is low to connect efficiency；4) cable wire is exposed, and easily scratches material to be sewn, it is therefore desirable to carries out deburring processing to whole cable wire.
The content of the invention
It is an object of the invention to provide the welding method of a kind of cable wire and thin plate, this method deburring amount is few, and cable wire pulls
Power is high, and anti-corrosion capability is strong, high in machining efficiency.
The technical solution adopted in the present invention is：
A kind of welding method of cable wire and thin plate, in the fixed position of cable wire and thin plate, makes cable wire be bonded with thin plate,
The adaptable pressing plate of upper and thin plate face facial contour is covered on cable wire, some place's resistance spot weldings are carried out to pressing plate and thin plate, make pressure
Plate and thin plate compress cable wire, carry out resistance spot welding at least two to pressing plate, thin plate and cable wire, melt pressing plate, thin plate and cable wire
Together.
Further, thin plate is plane or curved surface.
Further, more than the fixed bit of cable wire and thin plate is equipped with one.
Further, cable wire is passed and worn back-shaped into cable wire draw ring on the pressing plate or thin plate of fixed position at one.
Further, cable wire forms cable wire draw ring between fixed position at adjacent two.
The beneficial effects of the invention are as follows：
Pressing plate is set up, covers cable wire opposite side, reduces cable wire and exposes area, deburring amount is less, for single cable wire
Pull ring structure, need to only polish the polishing of cable wire termination, be adapted to the occasion that material to be sewn be present；Flatiron is instead of with resistance spot welding to weld, weldering
It is good to stitch intensity, existing thrust, has again and is integrally fused at least two, obtained by contrast test, iron soldering pulling-out force exists
60kgf, between 120kgf-200kgf, cable wire pulling-out force is enhanced about more than once pulling-out force of the present invention, and security performance improves；Electricity
Hinder spot welding heating and cool time is short, stainless steel parts corrosion resistance is guaranteed, and is tested by salt spray test, and anti-corrosion capability obtains
Confirm；It can be processed using common alternating current-direct current spot-welding equipment, only need a few place's spot welding, process time is short, when at iron soldering one
Between 15-20 minutes, at resistance spot welding one time shorten within 1 minute, efficiency high.
Brief description of the drawings
Fig. 1 is three kinds of common connected mode schematic diagrams of cable wire that pressure fixing tightwire is received by block part.
Fig. 2 is used in cable wire draw ring support board structure on material to be sewn.
Fig. 3 is the schematic diagram that cable wire draw ring connection on material to be sewn is carried out using the present invention.
Fig. 4 is that the present invention applies the schematic diagram on curved sheets.
In figure：1- cable wires；2- is received at pressure；3- joints；4- sleeve pipes；5- steel balls；6- supporting plates；7- thin plates (plane)；8- pressing plates；
9- nuggets；10- resistance spot welds；11- thin plates (arc surface)；12- thin plates (circular conical surface).
Embodiment
The present invention is further illustrated with reference to the accompanying drawings and examples.
As shown in figure 3, the welding method of a kind of cable wire and thin plate, in the present embodiment, thin plate 7 is circular flat, cable wire 1
Only have with the fixed position of thin plate 7 at one, in the fixed position of cable wire 1 and thin plate 7, cable wire 1 is bonded with thin plate 7, in steel
The adaptable pressing plate 8 of upper and thin plate 7 face facial contour is covered on rope 1, some place's resistance spot weldings are carried out to pressing plate 8 and thin plate 7, made
Pressing plate 8 and thin plate 7 compress cable wire 1, carry out resistance spot welding at least two to pressing plate 8, thin plate 7 and cable wire 1, make pressing plate 8, thin plate
7 and cable wire 1 be melted together, cable wire 1 is passed on thin plate 7 (or pressing plate 8) and worn back-shaped into cable wire draw ring.As shown in figure 4, thin plate
(11,12) can also be curved surface, and the fixed position of cable wire 1 and thin plate (7,11,12) is more than at one, and cable wire 1 is consolidated at adjacent two
Positioning forms cable wire draw ring between putting.The present invention possesses fine autgmentability, is adapted to plane and curved surface bond pattern, can be widely used for
Ejector seat umbrella case closes up and other flexible sealing environment, can be widely used for needing Aero-Space etc. to the strict field of weight demands
Close, can be widely used for the occasion for being adapted to the flexible connections such as material to be sewn package.
The present invention sets up pressing plate 8, covers the opposite side of cable wire 1, reduces cable wire 1 and exposes area, and deburring amount is less, for
Single cable wire pull ring structure, need to only polish the polishing of the termination of cable wire 1, be adapted to the occasion that material to be sewn be present；It instead of with resistance spot welding
Flatiron is welded, and weld strength is good, existing thrust, has again and is integrally fused at least two, is obtained by contrast test, and iron soldering is drawn
De- power is in 60kgf, and pulling-out force of the present invention is between 120kgf-200kgf, and cable wire pulling-out force is enhanced about more than once, and security performance carries
It is high；Resistance spot welding is heated and cool time is short, and stainless steel parts corrosion resistance is guaranteed, and is tested by salt spray test, anti-corrosion energy
Power is confirmed；It can be processed using common alternating current-direct current spot-welding equipment, only need a few place's spot welding, process time is short, iron soldering one
Minute time 15-20 at part, at resistance spot welding one time shorten within 1 minute, efficiency high.
It should be appreciated that for those of ordinary skills, can according to the above description be improved or converted,
And all these modifications and variations should all belong to the protection domain of appended claims of the present invention.
Claims (5)
- A kind of 1. welding method of cable wire and thin plate, it is characterised in that：In the fixed position of cable wire and thin plate, make cable wire with it is thin Plate is bonded, and the pressing plate adaptable with the face facial contour of thin plate on lid on cable wire, some place's resistance is carried out to pressing plate and thin plate Spot welding, pressing plate and thin plate is compressed cable wire, resistance spot welding at least two is carried out to pressing plate, thin plate and cable wire, makes pressing plate, thin plate It is melted together with cable wire.
- 2. the welding method of cable wire as claimed in claim 1 and thin plate, it is characterised in that：Thin plate is plane or curved surface.
- 3. the welding method of cable wire as claimed in claim 1 and thin plate, it is characterised in that：The fixed bit of cable wire and thin plate is equipped with More than at one.
- 4. the welding method of cable wire as claimed in claim 3 and thin plate, it is characterised in that：The pressure of cable wire fixed position at one Pass and wear back-shaped into cable wire draw ring on plate or thin plate.
- 5. the welding method of cable wire as claimed in claim 3 and thin plate, it is characterised in that：Cable wire fixed position at adjacent two Between formed cable wire draw ring.