CN107604221A - A kind of high-strength, antioxidant aluminum alloy materials and preparation method thereof - Google Patents
A kind of high-strength, antioxidant aluminum alloy materials and preparation method thereof Download PDFInfo
- Publication number
- CN107604221A CN107604221A CN201710999472.6A CN201710999472A CN107604221A CN 107604221 A CN107604221 A CN 107604221A CN 201710999472 A CN201710999472 A CN 201710999472A CN 107604221 A CN107604221 A CN 107604221A
- Authority
- CN
- China
- Prior art keywords
- temperature
- aluminum alloy
- alloy materials
- magnesium
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-strength, antioxidant aluminum alloy materials and preparation method thereof, the material is formed by following percentage by weight:0.5 1 copper, 1 1.5 titanium, 35 silicon, 23 iron, 1 1.4 magnesium, 0.02 0.04 vanadium, 0.5 0.7 zinc, 0.3 0.7 boron, remaining is aluminium and inevitable impurity.Specific preparation method is as follows:Molten state is heated to Step 1: fine aluminium ingot is put into boiler, heating-up temperature is 420 440 DEG C, and the heat time is 35 45 minutes;Step 2: carry out removing impurities matter and deoxidation treatment;Step 3: being sequentially placed into copper, titanium, silicon, iron, magnesium, vanadium, zinc, boron, heating-up temperature is 550 600 DEG C, is incubated 1 1.5 hours;Step 4: being again heated to 650 680 DEG C, insulation 23 is small;Step 5: cooling, then carries out hot rolling twice at 450 500 DEG C of temperature, carries out cold rolling sizing again when temperature naturally cools to room temperature.Gained aluminum alloy materials of the invention have the characteristics of inoxidizability, corrosion resistance, can extend the service life of aluminum alloy materials.
Description
Technical field
The present invention relates to a kind of high-strength, antioxidant aluminum alloy materials and preparation method thereof, belong to aluminium alloy technology of preparing neck
Domain.
Background technology
Aluminium alloy is widely used conventional non-ferrous metal, has the characteristics that very high plasticity, in light weight, easy to process,
Extensively using in the industrial production.It is easily oxidized and dimmed in humid air but because pure aluminium is very soft, intensity is little,
The gloss of metal is lost, not only influences service life, and has an effect on attractive in appearance, therefore one need to be entered to the anti-oxidant treatment of aluminium alloy
Step is improved.
The content of the invention
The present invention is to solve the above problems, provide a kind of high-strength, antioxidant aluminum alloy materials and preparation method thereof.
The purpose of the present invention is achieved through the following technical solutions:
A kind of high-strength, antioxidant aluminum alloy materials and preparation method thereof, the material are formed by following percentage by weight:
0.5-1 copper, 1-1.5 titanium, 3-5 silicon, 2-3 iron, 1-1.4 magnesium, 0.02-0.04 vanadium, 0.5-0.7 zinc, 0.3-
0.7 boron, remaining is aluminium and inevitable impurity.
Specific preparation method is as follows:
Molten state is heated to Step 1: fine aluminium ingot is put into boiler, heating-up temperature is 420-440 DEG C, the heat time
For 35-45 minutes;
Step 2: carry out removing impurities matter and deoxidation treatment;
Step 3: being sequentially placed into copper, titanium, silicon, iron, magnesium, vanadium, zinc, boron, heating-up temperature is 550-600 DEG C, is incubated 1-1.5
Hour;
Step 4: being again heated to 650-680 DEG C, insulation 2-3 is small;
Step 5: cooling, then carries out hot rolling twice, when temperature naturally cools to room temperature at 450-500 DEG C of temperature
Cold rolling sizing is carried out again.
The beneficial effects of the invention are as follows:Gained aluminum alloy materials of the invention have the characteristics of inoxidizability, corrosion resistance, can
Extend the service life of aluminum alloy materials.
Embodiment
Embodiment one
A kind of high-strength, antioxidant aluminum alloy materials of the present invention and preparation method thereof, the material press following weight
Percentage forms:0.5 copper, 1 titanium, 3 silicon, 2 iron, 1 magnesium, 0.02 vanadium, 0.5 zinc, 0.3 boron, remaining is aluminium
With inevitable impurity.
Specific preparation method is as follows:
Molten state is heated to Step 1: fine aluminium ingot is put into boiler, heating-up temperature is 420 DEG C, the heat time 35
Minute;
Step 2: carry out removing impurities matter and deoxidation treatment;
Step 3: being sequentially placed into copper, titanium, silicon, iron, magnesium, vanadium, zinc, boron, heating-up temperature is 550-600 DEG C, is incubated 1 hour;
Step 4: being again heated to 650 DEG C, insulation 2 is small;
Step 5: cooling, then carries out hot rolling twice at 450 DEG C of temperature, enters again when temperature naturally cools to room temperature
Row cold rolling is shaped.
Embodiment 2
A kind of high-strength, antioxidant aluminum alloy materials of the present invention and preparation method thereof, the material press following weight
Percentage forms:1 copper, 1.5 titanium, 5 silicon, 3 iron, 1.4 magnesium, 0.04 vanadium, 0.7 zinc, 0.7 boron, remaining is
Aluminium and inevitable impurity.
Specific preparation method is as follows:
Molten state is heated to Step 1: fine aluminium ingot is put into boiler, heating-up temperature is 440 DEG C, the heat time 45
Minute;
Step 2: carry out removing impurities matter and deoxidation treatment;
Step 3: being sequentially placed into copper, titanium, silicon, iron, magnesium, vanadium, zinc, boron, heating-up temperature is 600 DEG C, is incubated 1.5 hours;
Step 4: being again heated to 680 DEG C, insulation 3 is small;
Step 5: cooling, then carries out hot rolling twice at 500 DEG C of temperature, enters again when temperature naturally cools to room temperature
Row cold rolling is shaped.
Embodiment 3
A kind of high-strength, antioxidant aluminum alloy materials of the present invention and preparation method thereof, the material press following weight
Percentage forms:0.8 copper, 1.2 titanium, 4 silicon, 2.5 iron, 1.2 magnesium, 0.03 vanadium, 0.6 zinc, 0.5 boron, its
Remaining is aluminium and inevitable impurity.
Specific preparation method is as follows:
Molten state is heated to Step 1: fine aluminium ingot is put into boiler, heating-up temperature is 430 DEG C, the heat time 40
Minute;
Step 2: carry out removing impurities matter and deoxidation treatment;
Step 3: being sequentially placed into copper, titanium, silicon, iron, magnesium, vanadium, zinc, boron, heating-up temperature is 575 DEG C, is incubated 1.3 hours;
Step 4: being again heated to 665 DEG C, insulation 2.5 is small;
Step 5: cooling, then carries out hot rolling twice at 475 DEG C of temperature, enters again when temperature naturally cools to room temperature
Row cold rolling is shaped.
Claims (2)
1. a kind of high-strength, antioxidant aluminum alloy materials and preparation method thereof, it is characterised in that the material presses following weight hundred
Divide than composition:0.5-1 copper, 1-1.5 titanium, 3-5 silicon, 2-3 iron, 1-1.4 magnesium, 0.02-0.04 vanadium, 0.5-0.7
Zinc, 0.3-0.7 boron, remaining is aluminium and inevitable impurity.Specific preparation method is as follows:Step 1: fine aluminium ingot is put
Enter and molten state is heated in boiler, heating-up temperature is 420-440 DEG C, and the heat time is 35-45 minutes;Step 2: taken off
Impurity and deoxidation treatment;Step 3: being sequentially placed into copper, titanium, silicon, iron, magnesium, vanadium, zinc, boron, heating-up temperature is 550-600 DEG C, is protected
Warm 1-1.5 hours;Step 4: being again heated to 650-680 DEG C, insulation 2-3 is small;Step 5: cooling, then in temperature 450-
Hot rolling twice is carried out at 500 DEG C, carries out cold rolling sizing again when temperature naturally cools to room temperature.
A kind of 2. high-strength, antioxidant aluminum alloy materials according to claim 1 and preparation method thereof, it is characterised in that institute
Magnesium, vanadium, the zinc stated are added in a manner of magnesium alloy, vananum, allumen respectively.