CN107602828A - The synthesis technique of short oil aqueous alkide resin - Google Patents
The synthesis technique of short oil aqueous alkide resin Download PDFInfo
- Publication number
- CN107602828A CN107602828A CN201710724573.2A CN201710724573A CN107602828A CN 107602828 A CN107602828 A CN 107602828A CN 201710724573 A CN201710724573 A CN 201710724573A CN 107602828 A CN107602828 A CN 107602828A
- Authority
- CN
- China
- Prior art keywords
- alkide resin
- aqueous alkide
- short oil
- synthesis technique
- cooled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
High the invention discloses a kind of quality, the synthesis technique of the simple short oil aqueous alkide resin of preparation technology, the technique prepares convenient and simple, it is environment friendly and pollution-free, raw material is easy to get, and equipment investment is few, and quality is pure, it is easy to operation, the aqueous alkide resin using effect of preparation is good, safe and non-toxic, storage time length, manufacturing cost is low, securely and reliably.
Description
Technical field
The present invention relates to chemical technology field, particularly a kind of synthesis technique of short oil aqueous alkide resin.
Background technology
Phthalic resin coating has that paint film combination property is preferable, raw material is cheap and easy to get, technical maturity is stable and independent of stone
The advantages that oily resource, but traditional solvent-borne alkyd resins contain a large amount of organic solvents in the production and use process, these
Organic solvent can be discharged into air in construction stage and drying process, cause high risks, and caused volatile organic matter is
The main reason for indoor pollution.With the limitation of environmental regulation and the increasingly enhancing of people's environmental consciousness, environmentally friendly water
The developmental research of property alkyd resin receives the attention of people.
Therefore water paint, introduces the water into coating because water is nontoxic, tasteless, non-ignitable and cheap, can both reduce production
Cost, VOC content is substantially reduced again, so water paint is just able to fast development.But exactly because the introducing of water is brought again
A series of new problem, such as the evaporation latent heat of water are very big, and accelerating to dry needs to improve temperature, and the evaporation rate of water is by phase
Influence to humidity is very big, and the surface tension of water is very big, and scattered and coating the coating to pigment all adversely affects, and works as water
When property coating is applied to metallic matrix, because the high conductivity of water may cause matrix corrosion etc..It is past in order to solve the above problems
Toward the method using the auxiliary agent such as addition cosolvent, surfactant and reducing agent in coating, and the addition of these auxiliary agents is not
Bring certain negative effect with can avoiding.In a word, the preparation of water paint is complicated far beyond solvent based coating, there is also some not
Foot part, but because it can greatly reduce VOC content, environmentally friendly trend is complied with, and disclosure satisfy that the performance under many occasions
It is required that still there are very big market prospects.
The content of the invention
Goal of the invention:The invention aims to solve the deficiencies in the prior art, there is provided a kind of quality is high, preparation technology
The synthesis technique of simple short oil aqueous alkide resin.
Technical scheme:A kind of in order to realize the above object synthesis work of short oil aqueous alkide resin of the present invention
Skill, the technique comprise the following steps that:
Step 1:By 20g~25g phthalic anhydride, 5g~5.8g M-phthalic acid, 35g~40g laurate, 30g~
Pour into carry respectively after the antioxidant of 32g trimethylolpropane, 9g~12g dimethylbenzene and 0.1g~0.2g is well mixed and stir
In the four-hole bottle for mixing the 250ml of device, thermometer, water knockout drum and nitrogen conduit;
Step 2:Agitator is adjusted to slow shelves and mixed slowly to 140 DEG C~150 DEG C by electricity consumption heating mantle heats,
60min is warming up to 180 DEG C~190 DEG C, is incubated 90min~120min;
Step 3:When water outlet is slack-off, continues electricity consumption heating mantle heats to 200 DEG C~210 DEG C, acid number is surveyed after 60min;
Step 4:When acid number is less than 10mgKOH/g, solvent is evaporated off, is cooled to 160 DEG C~170 DEG C, adds 8g~10g
Trimellitic anhydride, it is 45mgKOH/g~50mgKOH/g to control acid number, is then cooled to 80 DEG C~85 DEG C, adds ethylene glycol list
Butyl ether, continue to be cooled to 60 DEG C~65 DEG C, the dimethylethanolamine for adding 6g~8g neutralizes and stirs 30min~40min;
Step 5:Distilled water is added by 50% solid content, filtering, obtains aqueous alkide resin base-material.
As present invention further optimization, the amount of the ethylene glycol monobutyl ether in described step four is 16g~18g.
As present invention further optimization, the amount of the dimethylethanolamine in described step four is 6g~8g.
As present invention further optimization, the amount of the distilled water added in described step five is 80g~85g.
Beneficial effect:A kind of synthesis technique of short oil aqueous alkide resin provided by the invention, the technique prepare convenient
Simply, environment friendly and pollution-free, raw material is easy to get, and equipment investment is few, and quality is pure, easy to operation, and the aqueous alkide resin of preparation uses
Effect is good, safe and non-toxic, storage time length, manufacturing cost bottom, securely and reliably.
Embodiment
With reference to embodiment, the present invention is furture elucidated.
Embodiment 1
A kind of synthesis technique of short oil aqueous alkide resin, the technique comprise the following steps that:
Step 1:By 20g phthalic anhydride, 5g M-phthalic acid, 35g laurate, 30g trimethylolpropane, 9g
Poured into respectively with agitator, thermometer, water knockout drum and nitrogen conduit after dimethylbenzene and 0.1g antioxidant are well mixed
In 250ml four-hole bottle;
Step 2:Agitator is adjusted to slow shelves and mixed slowly to 140 DEG C by electricity consumption heating mantle heats, 60min heatings
To 180 DEG C, 90min is incubated;
Step 3:When water outlet is slack-off, continues electricity consumption heating mantle heats to 200 DEG C, acid number is surveyed after 60min;
Step 4:When acid number is less than 10mgKOH/g, solvent is evaporated off, is cooled to 160 DEG C, adds 8g trimellitic anhydride,
It is 45mgKOH/g to control acid number, is then cooled to 80 DEG C, adds 16g ethylene glycol monobutyl ether, continues to be cooled to 60 DEG C, adds
6g dimethylethanolamine neutralizes and stirs 30min;
Step 5:80g distilled water is added by 50% solid content, filtering, obtains aqueous alkide resin base-material.
Embodiment 2
A kind of synthesis technique of short oil aqueous alkide resin, the technique comprise the following steps that:
Step 1:By 21g phthalic anhydride, 5.1g M-phthalic acid, 36g laurate, 31g trimethylolpropane, 10g
Dimethylbenzene and 0.15g antioxidant it is well mixed after pour into respectively with agitator, thermometer, water knockout drum and nitrogen conduit
In 250ml four-hole bottle;
Step 2:Agitator is adjusted to slow shelves and mixed slowly to 141 DEG C by electricity consumption heating mantle heats, 60min heatings
To 182 DEG C, 100min is incubated;
Step 3:When water outlet is slack-off, continues electricity consumption heating mantle heats to 205 DEG C, acid number is surveyed after 60min;
Step 4:When acid number is less than 10mgKOH/g, solvent is evaporated off, is cooled to 162 DEG C, adds 8.5g trimellitic acid
Acid anhydride, it is 46mgKOH/g to control acid number, is then cooled to 82 DEG C, adds 17g ethylene glycol monobutyl ether, continues to be cooled to 62 DEG C, adds
The dimethylethanolamine for entering 6.5g neutralizes and stirs 35min;
Step 5:82g distilled water is added by 50% solid content, filtering, obtains aqueous alkide resin base-material.
Embodiment 3
A kind of synthesis technique of short oil aqueous alkide resin, the technique comprise the following steps that:
Step 1:By 24g phthalic anhydride, 5.6g M-phthalic acid, 38g laurate, 31.5g trimethylolpropane,
Pour into after 11g dimethylbenzene and 0.18g antioxidant are well mixed and led with agitator, thermometer, water knockout drum and nitrogen respectively
In the 250ml of pipe four-hole bottle;
Step 2:Agitator is adjusted to slow shelves and mixed slowly to 148 DEG C by electricity consumption heating mantle heats, 60min heatings
To 188 DEG C, 115min is incubated;
Step 3:When water outlet is slack-off, continues electricity consumption heating mantle heats to 208 DEG C, acid number is surveyed after 60min;
Step 4:When acid number is less than 10mgKOH/g, solvent is evaporated off, is cooled to 168 DEG C, adds 9.5g trimellitic acid
Acid anhydride, it is 48mgKOH/g to control acid number, is then cooled to 83 DEG C, adds 17g ethylene glycol monobutyl ether, continues to be cooled to 64 DEG C, adds
The dimethylethanolamine for entering 7.5g neutralizes and stirs 38min;
Step 5:84g distilled water is added by 50% solid content, filtering, obtains aqueous alkide resin base-material.
Embodiment 4
A kind of synthesis technique of short oil aqueous alkide resin, the technique comprise the following steps that:
Step 1:By 25g phthalic anhydride, 5.8g M-phthalic acid, 40g laurate, 32g trimethylolpropane, 12g
Dimethylbenzene and 0.2g antioxidant it is well mixed after pour into respectively with agitator, thermometer, water knockout drum and nitrogen conduit
In 250ml four-hole bottle;
Step 2:Agitator is adjusted to slow shelves and mixed slowly to 150 DEG C by electricity consumption heating mantle heats, 60min heatings
To 190 DEG C, 120min is incubated;
Step 3:When water outlet is slack-off, continues electricity consumption heating mantle heats to 210 DEG C, acid number is surveyed after 60min;
Step 4:When acid number is less than 10mgKOH/g, solvent is evaporated off, is cooled to 170 DEG C, adds 10g trimellitic acid
Acid anhydride, it is 50mgKOH/g to control acid number, is then cooled to 85 DEG C, adds 18g ethylene glycol monobutyl ether, continues to be cooled to 65 DEG C, adds
The dimethylethanolamine for entering 8g neutralizes and stirs 40min;
Step 5:85g distilled water is added by 50% solid content, filtering, obtains aqueous alkide resin base-material.
The technical concepts and features of above-mentioned embodiment only to illustrate the invention, the purpose is to allow be familiar with technology neck
The technical staff in domain can understand present disclosure and implement according to this, can not be limited the scope of the invention with this.
All equivalent changes or modificationss made according to spirit of the invention, should all be included within the scope of the present invention.
Claims (4)
- A kind of 1. synthesis technique of short oil aqueous alkide resin, it is characterised in that:The technique comprises the following steps that:Step 1:By 20g~25g phthalic anhydride, 5g~5.8g M-phthalic acid, 35g~40g laurate, 30g~32g Poured into respectively after the antioxidant of trimethylolpropane, 9g~12g dimethylbenzene and 0.1g~0.2g is well mixed with agitator, In the 250ml of thermometer, water knockout drum and nitrogen conduit four-hole bottle;Step 2:Agitator is adjusted to slow shelves and mixed slowly to 140 DEG C~150 DEG C by electricity consumption heating mantle heats, 60min 180 DEG C~190 DEG C are warming up to, is incubated 90min~120min;Step 3:When water outlet is slack-off, continues electricity consumption heating mantle heats to 200 DEG C~210 DEG C, acid number is surveyed after 60min;Step 4:When acid number is less than 10mgKOH/g, solvent is evaporated off, is cooled to 160 DEG C~170 DEG C, adds the inclined of 8g~10g Benzenetricarboxylic anhydride, it is 45mgKOH/g~50mgKOH/g to control acid number, is then cooled to 80 DEG C~85 DEG C, adds ethylene glycol only son Ether, continue to be cooled to 60 DEG C~65 DEG C, the dimethylethanolamine for adding 6g~8g neutralizes and stirs 30min~40min;Step 5:Distilled water is added by 50% solid content, filtering, obtains aqueous alkide resin base-material.
- A kind of 2. synthesis technique of short oil aqueous alkide resin according to claim 1, it is characterised in that:Described step The amount of ethylene glycol monobutyl ether in rapid four is 16g~18g.
- A kind of 3. synthesis technique of short oil aqueous alkide resin according to claim 1, it is characterised in that:Described step The amount of dimethylethanolamine in rapid four is 6g~8g.
- A kind of 4. synthesis technique of short oil aqueous alkide resin according to claim 1, it is characterised in that:Described step The amount of the distilled water added in rapid five is 80g~85g.