CN1076011C - Porous carbon material producing process - Google Patents
Porous carbon material producing process Download PDFInfo
- Publication number
- CN1076011C CN1076011C CN98111117A CN98111117A CN1076011C CN 1076011 C CN1076011 C CN 1076011C CN 98111117 A CN98111117 A CN 98111117A CN 98111117 A CN98111117 A CN 98111117A CN 1076011 C CN1076011 C CN 1076011C
- Authority
- CN
- China
- Prior art keywords
- production method
- pore
- pitch
- roasting
- caking agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a production process of porous carbon materials, which comprises the steps of material selection, crushing, sieving, material mixture, the addition of an adhesive agent and a pore forming agent, forming, baking, etc. The production process has the advantages of simple technology and easy operation, the holes of the provided product are orderly arranged and are evenly distributed, and the product has the advantage of no desquamation, no delamination, large strength, high-temperature resistance, corrosion resistance, no pollution and no toxic or side effect.
Description
The present invention relates to a kind of production method of filtering material.
More as filtering porous material as pottery, porcelain, synthetic graphite, electrical carbon etc., but the arrangement of these material mesopores is state of disarray at random, closed pore and apparent boring ratio example, pore size generally belong to no control state, thereby be difficult to adapt to smart filtering technology needs usually, once occurred in the past with the plain polyporous materials of the charcoal of carbon fiber and organic polymer material, but easily layering, peeled off.
The object of the present invention is to provide a kind of hole ordered arrangement, and production method not stratified, adeciduate porous carbonaceous material.
Technical solution of the present invention is:
A kind of production method of porous carbonaceous material, the difference of itself and prior art is: comprise the following steps: successively
1) chooses raw material: get refinery coke and/or pitch coke;
2) broken and screening: with disintegrating apparatus with raw material crushing, and by sieving into 3～6 kinds of grain-size grades, maximum particle diameter≤4mm;
3) batch mixes: will be through 2) 3～6 grade raw materials that obtain mix, and the weight percent of various grades is 5～60%;
4) add people's caking agent and pore-forming material: the pitch that adding is equivalent to above-mentioned dosage 20～40% is as caking agent, and adding is equivalent to the pore-forming material of above-mentioned dosage 20～50%;
5) moulding and roasting: use the ordinary process forming processes, carry out roasting in 220～460 hours then, the roasting top temperature is between 800～1250 ℃.
Disintegrating apparatus is equipment such as pair roller or Raymond mill.
Adopting coal-tar pitch or petroleum pitch is caking agent.
Pore-forming material adopts sodium-chlor or materials such as Repone K or modified phenolic resins.Moulding process is extrusion molding or compression molding, vibratory compaction.
Arrange in order in product provided by the present invention hole, and cell size can artificially be controlled, and generally 35～70%, the aperture is controlled in 10～250 μ scopes, and the distribution in hole is quite even.The possibility that there is not layering in product or comes off; Enough intensity being arranged, can be because of assembling fastening force effect not damage, the pressure effect does not damage in the time of can be because of back flushing yet; The high temperature of ability ≯ 550 ℃, ability is removed the corrosion of acid with strong oxidizing property and concentration ≯ 10% sodium hydroxide lye; Pollution-free to medium, have no side effect; Both can be used for the essence filter of the solution of coarse filtration, also can be used for the filtering and the catalyzer absorption carrier of impurity in the metallic solution.Production technique is simple, and is easy to operate.
The invention will be further described below in conjunction with embodiment:
Embodiment 1:
A kind of production technique of porous carbon material comprises the following steps: successively
1) choose raw material: getting refinery coke is raw material;
2) broken and screening: with disintegrating apparatus such as pair roller or Raymond mills with raw material crushing, and with sieving into 3～6 grades, diameter≤4mm.
3) batch mixes: will be through 2) 3～6 grade raw materials that obtain mix, and the weight proportion of various grades is 5～60%;
4) add caking agent and pore-forming material: add the coal-tar pitch that is equivalent to above-mentioned dosage 22% or petroleum pitch as caking agent, and add the pore-forming material that is equivalent to above-mentioned dosage 30%, pore-forming material adopts sodium-chlor or materials such as Repone K or modified phenolic resins
5) moulding and roasting: with extrusion molding or compression molding, vibro-moulding process forming processes, carry out roasting then, roasting time is between 220～460 hours, and the roasting top temperature is between 800～1250 ℃.
On the basis of the above, can on demand blank be processed as needed geometrical shape and size.
Embodiment 2: a kind of production technique of porous carbon material comprises the following steps: successively
1) choose raw material: getting pitch coke is raw material;
2) broken and screening: with disintegrating apparatus such as pair roller or Raymond mills with raw material crushing, and with sieving into 3～6 grades, diameter≤4mm.
3) batch mixes: will be through 2) 3～6 grade raw materials that obtain mix, and the weight proportion of various grades is 5～60%;
4) add caking agent and pore-forming material: add the coal-tar pitch that is equivalent to above-mentioned dosage 30% or petroleum pitch as caking agent, and add the pore-forming material that is equivalent to above-mentioned dosage 40%, pore-forming material adopts sodium-chlor or materials such as Repone K or modified phenolic resins;
5) moulding and roasting: with extrusion molding or compression molding, vibro-moulding process forming processes, carry out roasting then, roasting time is between 220～460 hours, and the roasting top temperature is between 800～1250 ℃.
On the basis of the above, can on demand blank be processed as needed geometrical shape and size.
Embodiment 3:
A kind of production technique of porous carbon material comprises the following steps: successively
1) chooses raw material: get refinery coke 10～30% and pitch coke 70～90% or get refinery coke 70～90% and pitch coke 10～30% is raw material;
2) broken and screening: with disintegrating apparatus such as pair roller or Raymond mills with raw material crushing, and with sieving into 3～6 grades, diameter≤4mm.
3) batch mixes: will be through 2) 3～6 grade raw materials that obtain mix, and the proportioning of various grades is 5～60%;
4) add caking agent and pore-forming material: add the coal-tar pitch that is equivalent to above-mentioned dosage 40% or petroleum pitch as caking agent, and add the pore-forming material that is equivalent to above-mentioned dosage 50%, pore-forming material adopts sodium-chlor or materials such as Repone K or modified phenolic resins;
5) moulding and roasting: with extrusion molding or compression molding, vibro-moulding process forming processes, carry out roasting then, roasting time is between 220～460 hours, and the roasting top temperature is between 800～1250 ℃.
On the basis of the above, can on demand blank be processed as needed geometrical shape and size.
Claims (5)
1, a kind of production method of porous carbon material is characterized in that: comprise the following steps: successively
1) chooses raw material: get refinery coke and/or pitch coke;
2) broken and screening: with disintegrating apparatus with raw material crushing, and by sieving into 3～6 kinds of grain-size grades, maximum particle diameter≤4mm;
3) batch mixes: will be through 2) 3～6 grade raw materials that obtain mix, and the weight percent of various grades is 5～60%;
4) add caking agent and pore-forming material: the pitch that adding is equivalent to above-mentioned dosage 20～40% is as caking agent, and adding is equivalent to the pore-forming material of above-mentioned dosage 20～50%;
5) moulding and roasting: use the ordinary process forming processes, carry out roasting in 220～460 hours then, the roasting top temperature is between 800～1250 ℃.
2, the production method of porous carbon material according to claim 1 is characterized in that: disintegrating apparatus is pair roller or Raymond mill.
3, the production method of porous material according to claim 1 and 2 is characterized in that: adopting coal-tar pitch or petroleum pitch is caking agent.
4, the production method of porous material according to claim 1 and 2 is characterized in that: pore-forming material adopts sodium-chlor or Repone K or modified phenolic resins.
5, the production method of porous material according to claim 1 and 2 is characterized in that: moulding process is extrusion molding or compression molding, vibratory compaction.