CN107600004A - A kind of green energy conservation rod - Google Patents
A kind of green energy conservation rod Download PDFInfo
- Publication number
- CN107600004A CN107600004A CN201710697546.0A CN201710697546A CN107600004A CN 107600004 A CN107600004 A CN 107600004A CN 201710697546 A CN201710697546 A CN 201710697546A CN 107600004 A CN107600004 A CN 107600004A
- Authority
- CN
- China
- Prior art keywords
- energy conservation
- weight
- green energy
- rod
- rod according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of green energy conservation rod, the green energy conservation rod is bar-shaped, and its material includes following component：1~3 weight % germanium, 3~4 weight % iron, 1~3 weight % oxygen, 0.1~0.3 weight % manganese, 0.03~0.07 weight % zinc, the copper of 0.1~0.3 weight % selenium and surplus.The supposition principle of the green energy conservation rod of the present invention is as follows：On the one hand magnetic force can be produced under magnetic field caused by electric current, so as to which compartment of terrain produces far infrared, and send vibration after the process such as far infrared storage and release, so as to stabling current, in the case where not influenceing to load normal operation, voltage drop low current can be adjusted, so as to reduce watt-hour, reduces energy consumption.
Description
Technical field
The present invention relates to energy-saving material technical field, and in particular to a kind of green energy conservation rod.
Background technology
Energy-saving consumption-reducing is a big problem of current energy field, can reduce cost, reduces carbon emission.
Publication No. CN203410394U Chinese patent literature discloses a kind of conduction efficiency for being used to strengthen vehicle electrical,
So that the vehicle current balancing device that vehicle performance is not fully exerted, it includes housing and core component, and housing is by conduction
Material is made, generally the metallic copper of cylinder, and the centre of housing is arranged on accommodation space formed with accommodation space, core component
Interior, core component has a superconducting characteristic, head of the one end formed with taper of housing, clamping slot is provided with head, by taper
Head before be inserted in the cigar lighter of vehicle, or be assembled to vehicle power supply periphery, pass through core component superconducting characteristic and refine molecule
With the mode of free electron, improve the normal electrostrictive coefficient in electron stream telegram in reply road, the microwave oscillation superposition per second for producing hundreds thousand of times
Strength line of cut is produced, micel is reflected, cut, is separated, separates Van der Waals force between molecule, refines micel
For the individual molecule more preferably used, and greatly promote the efficiency and performance of the back-flow velocity of electric current, quality and electric system.
The core material of the patent document includes the materials such as calcium oxide, silica, aluminum oxide and rare earth, and generation can be to dividing
Son group is reflected, cut, being separated, separating Van der Waals force between molecule, make that micel is refined as more preferably using single point
Son, and greatly promote the efficiency and performance of the back-flow velocity of electric current, quality and electric system, but pass through actual measurement, effect but one
As, and engine ignition is simply possible to use in, can not large-scale promotion.
The content of the invention
It is an object of the invention to provide a kind of green energy conservation rod, green energy conservation rod provided by the invention can utilize remote red
Outside line is converted into useful electric energy to electric energy superfluous in circuit, so as to reduce energy waste.
To achieve the above object, the present invention provides a kind of green energy conservation rod, and the green energy conservation rod is bar-shaped, its material bag
Include following component：1~3 weight % germanium, 3~4 weight % iron, 1~3 weight % oxygen, 0.1~0.3 weight % manganese,
The copper of 0.03~0.07 weight % zinc, 0.1~0.3 weight % selenium and surplus.
Optionally, the material of the green energy conservation rod includes following component：2 weight % germanium, 3.6 weight % iron, 2.3
Weight % oxygen, 0.2 weight % manganese, 0.05 weight % zinc, the copper of 0.2 weight % selenium and surplus.
Optionally, the length of the green energy conservation rod is 3~15 centimetres, a diameter of 1~4 centimetre.
Optionally, the green energy conservation rod also includes electronic device fixed structure, the electronic device be electric wire, battery or
Storage battery.
Optionally, the electronic device fixed structure includes the first plastic coil being wrapped on green energy conservation rod and twined
The second plastic coil being wound on the outside of electronic device.
Optionally, the preparation method of the green energy conservation rod includes：
Germanium, iron, manganese, zinc, selenium, copper and cupric oxide are mixed according to material mixture ratio, melted under inert gas atmosphere,
Then crushed after being quenched using inert gas；
Less than 100 nanometers of particle is taken after crushing to be kneaded under high pressure bar-shaped.
Optionally, the inert atmosphere is argon gas.
Optionally, the temperature of the melting is more than 2200 DEG C.
Optionally, the temperature of the quenching is -40~-80 DEG C.
Optionally, the pressure of the kneading is 50~100MPa.
The invention has the advantages that：
The supposition principle of the green energy conservation rod of the present invention is as follows：On the one hand magnetic can be produced under magnetic field caused by electric current
Power, so as to which compartment of terrain produces far infrared, and vibration is sent after the process such as far infrared storage and release, so as to stable electricity
Stream, in the case where not influenceing to load normal operation, voltage drop low current can be adjusted, so as to reduce watt-hour, reduce energy consumption.
Brief description of the drawings
Fig. 1 is the photo of green energy conservation rod provided by the invention.
Fig. 2 is the structural representation of green energy conservation rod provided by the invention.
Embodiment
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
The present invention provides a kind of green energy conservation rod, and the green energy conservation rod is bar-shaped, and its material includes following component：1~3
Weight % germanium, 3~4 weight % iron, 1~3 weight % oxygen, 0.1~0.3 weight % manganese, 0.03~0.07 weight %
Zinc, 0.1~0.3 weight % selenium and the copper of surplus, it is preferable that the material of the green energy conservation rod includes following component：2
Weight % germanium, 3.6 weight % iron, 2.3 weight % oxygen, 0.2 weight % manganese, 0.05 weight % zinc, 0.2 weight %
Selenium and surplus copper.Oxygen element in the present invention be present, because zinc-iron activity is high, the two is somebody's turn to do in alloy and is deposited in the form of an oxide
So that iron-oxygen species (particularly alternating current) in the case where being acted in current field produce magnetic field, and Ge element is being caused to produce far
Infrared ray, and manganese, zinc, selenium element can store and discharge infrared ray, so as to be launched as far-infrared source one by one, carry
High effect of the far infrared to circuit, stabling current, in the case where not influenceing to load normal operation, can adjust voltage drop
Low current, so as to reduce watt-hour, reduce energy consumption.Copper has good stability and containing to other elements due to it
Property, and matter is soft, is adapted to mediate, and is used as carrier.
Green energy conservation rod can have good effect on electric wire is bundled in, close to circuit, for example, the green energy conservation
The length of rod is 3~15 centimetres, a diameter of 1~4 centimetre.
In order to facilitate fixing on the electronic devices, the green energy conservation rod can also include electronic device fixed structure, institute
The first plastic coil for being wrapped on green energy conservation rod can be included and be wrapped in electronic device by stating electronic device fixed structure
Second plastic coil in outside, the electronic device can be electric wire, battery or storage battery.Certainly, those skilled in the art also may be used
To use other fixed structures, the present invention repeats no more.
The specific preparation method of green energy conservation rod of the present invention is provided below, the preparation method of the green energy conservation rod includes：
Germanium, iron, manganese, zinc, selenium, copper and cupric oxide are mixed according to material mixture ratio, melted under inert gas atmosphere, the inertia
Atmosphere can be argon gas, and the temperature of the melting is generally more than 2200 DEG C.Then crushed after being quenched using inert gas,
The temperature of the quenching can be -40~-80 DEG C；Less than 100 nanometers after crushing of particle is taken to be kneaded into bar-shaped, institute under high pressure
The pressure for stating kneading can be 50~100MPa.
The present invention will be further illustrated by embodiment below, but the present invention is not therefore subject to any restriction.
According to 2 weight % germanium, 3.6 weight % iron, 2.3 weight % oxygen, 0.2 weight % manganese, 0.05 weight %
Zinc, 0.2 weight % selenium and the proportioning of copper of surplus germanium, iron, manganese, zinc, selenium, copper and cupric oxide are mixed, and stirring
Under be warming up to 2300 DEG C in Muffle furnace in tungsten crucible and carry out insulation 1 hour, be during which passed through in Muffle furnace argon gas carry out every
Exhausted air, then tungsten crucible is taken out in the case where completely cutting off air, is put into the container of room temperature, -58 DEG C of argon gas is passed through and is quenched,
The alloy of fragmentation is obtained, the alloy is subjected to flotation screening, less than 100 nanometers of particle is obtained, is then pinched in 60MPa high pressure
Carry out being kneaded into 2.2 centimetres of diameter, the alloy bar that 10 centimetres of length, as green energy conservation rod, by the green energy conservation rod under conjunction machine
Detection Science and Technology Co., Ltd. of AsiaINFO and juridical person's industrial science foundation of improving oneself is entrusted to be detected as follows respectively：
1st, far infrared average radiation rate is determined：
Far infrared (25 DEG C of wavelength 2~22 μm), test result 0.75, test mode：From constant temperature radioactive source, by red
Outside line is irradiated, and does inspection/calculation mode of reflected energy, test condition：Completed under hot 2hr per positive, record numerical value.Emissivity
0.00-1.00, measure area, 15mm2, measurement distance 13mm, measuring instrument, far infrared irradiation rate detector is TSS-5X.
2nd, watt-hour measures：
A watt-hours measure (plus before green energy conservation rod)
B watt-hours measure (plus after green energy conservation rod)
A 322KWH, B 274KWH, (A-B)/A percentage 15%, experimental period are respectively one week, are compiled using watt-hour meter instrument
Number it is D35G10, measured power device is motor.
Illustrate green energy conservation rod can steady wire current, reduce magnetic hystersis loss, so as to increase energy efficiency, have to power saving
Excellent effect, and usage time is elongated, with respect to its effect percentage, more because electric current can steadily increase appliance life, such as household electrical appliances
Electrical equipment, factory's electromechanical etc., and accessory loss is reduced, reduce disbursement.
Although above with general explanation and specific embodiment, the present invention is described in detail, at this
On the basis of invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Therefore,
These modifications or improvements without departing from theon the basis of the spirit of the present invention, belong to the scope of protection of present invention.
Claims (10)
1. a kind of green energy conservation rod, it is characterised in that the green energy conservation rod is bar-shaped, and its material includes following component：1~3
Weight % germanium, 3~4 weight % iron, 1~3 weight % oxygen, 0.1~0.3 weight % manganese, 0.03~0.07 weight %
Zinc, 0.1~0.3 weight % selenium and the copper of surplus.
2. green energy conservation rod according to claim 1, it is characterised in that the material of the green energy conservation rod includes such as the following group
Point：2 weight % germanium, 3.6 weight % iron, 2.3 weight % oxygen, 0.2 weight % manganese, 0.05 weight % zinc, 0.2 weight
Measure % selenium and the copper of surplus.
3. green energy conservation rod according to claim 1, it is characterised in that the length of the green energy conservation rod is 3~15 lis
Rice, a diameter of 1~4 centimetre.
4. green energy conservation rod according to claim 1, it is characterised in that the green energy conservation rod is also consolidated including electronic device
Determine structure, the electronic device is electric wire, battery or storage battery.
5. green energy conservation rod according to claim 4, it is characterised in that the electronic device fixed structure includes being wrapped in
The first plastic coil on green energy conservation rod and the second plastic coil being wrapped on the outside of electronic device.
6. green energy conservation rod according to claim 1, it is characterised in that the preparation method of the green energy conservation rod includes：
Germanium, iron, manganese, zinc, selenium, copper and cupric oxide are mixed according to material mixture ratio, melted under inert gas atmosphere, then
Crushed after being quenched using inert gas；
Less than 100 nanometers of particle is taken after crushing to be kneaded under high pressure bar-shaped.
7. green energy conservation rod according to claim 6, it is characterised in that the inert atmosphere is argon gas.
8. green energy conservation rod according to claim 6, it is characterised in that the temperature of the melting is more than 2200 DEG C.
9. green energy conservation rod according to claim 6, it is characterised in that the temperature of the quenching is -40~-80 DEG C.
10. green energy conservation rod according to claim 6, it is characterised in that the pressure of the kneading is 50~100MPa.