CN107599726A - A kind of bionical compound insulating material of fluorine carbon and its production technology - Google Patents

A kind of bionical compound insulating material of fluorine carbon and its production technology Download PDF

Info

Publication number
CN107599726A
CN107599726A CN201711054492.2A CN201711054492A CN107599726A CN 107599726 A CN107599726 A CN 107599726A CN 201711054492 A CN201711054492 A CN 201711054492A CN 107599726 A CN107599726 A CN 107599726A
Authority
CN
China
Prior art keywords
fluorine carbon
time
plaque substrate
insulating material
dried
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711054492.2A
Other languages
Chinese (zh)
Inventor
李炳兴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Pulaite New Material Environmental Protection Co Ltd
Original Assignee
Suzhou Pulaite New Material Environmental Protection Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Pulaite New Material Environmental Protection Co Ltd filed Critical Suzhou Pulaite New Material Environmental Protection Co Ltd
Priority to CN201711054492.2A priority Critical patent/CN107599726A/en
Publication of CN107599726A publication Critical patent/CN107599726A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of bionical compound insulating material of fluorine carbon and its production technology, production technology comprise the following steps:S1., fluorine carbon plaque substrate Jing Guo primary coat is provided;S2. it is surface-treated;S3. first time roller coat is processed, and dry for the first time;S4. second of roller coat processing, and carry out second and dry;S5. third time roller coat is processed, and is carried out third time and dried;S6. after the fluorine carbon plaque substrate surface is dried completely, drying and processing is carried out to it;S7. surface coating is carried out to the fluorine carbon plaque substrate after drying;S8., warming plate is provided;S9. roller glue;S10. it is cold-pressed, after being firmly combined with, blanking obtains the bionical compound insulating material of fluorine carbon.The present invention can carry out effective working process to fluorine carbon plaque substrate, and can obtain surface texturing and meet the fluorine carbon plaque of actual demand, and can realize the strong bonded of fluorine carbon plaque substrate and warming plate.Meanwhile the present invention also has the advantages of continuity is good, high in machining efficiency.

Description

A kind of bionical compound insulating material of fluorine carbon and its production technology
Technical field
The present invention relates to fluorine carbon plaque production technical field, more particularly to a kind of bionical compound insulating material of fluorine carbon and its life Production. art.
Background technology
Fluorine carbon plaque is a kind of dalle, and it has good incubation and thermal insulation function, and plate body is light and handy.Existing fluorine carbon In plaque production process, it is desirable to provide the fluorine carbon plaque substrate handled by primary coat, then the fluorine carbon plaque substrate of primary coat is entered The a series of working process of row, to form it into satisfactory surface texturing.However, the production technology of existing fluorine carbon plaque In, each production stage continuity is bad, and the surface texturing effect of obtained fluorine carbon plaque is not ideal enough.
Therefore, in view of the above-mentioned problems, the present invention proposes further solution.
The content of the invention
The present invention is intended to provide a kind of bionical compound insulating material of fluorine carbon and its production technology, are deposited in the prior art with overcoming Deficiency.
In order to solve the above technical problems, the technical scheme is that:
A kind of production technology of the bionical compound insulating material of fluorine carbon, it comprises the following steps:
S1., fluorine carbon plaque substrate Jing Guo primary coat is provided;
S2. the fluorine carbon plaque substrate is surface-treated;
S3. first time roller coat processing is carried out to the fluorine carbon plaque substrate after surface treatment, and first time roller coat is processed Fluorine carbon plaque substrate afterwards dry for the first time;
S4. after the fluorine carbon plaque substrate surface is dried completely, second of roller coat is carried out to the fluorine carbon plaque substrate Processing, and second is carried out to the fluorine carbon plaque substrate after second of roller coat processing and is dried;
S5. after the fluorine carbon plaque substrate surface is dried completely, third time roller coat is carried out to the fluorine carbon plaque substrate Processing, and third time is carried out to the fluorine carbon plaque substrate after the processing of third time roller coat and dried;
S6. after the fluorine carbon plaque substrate surface is dried completely, drying and processing is carried out to it;
S7. surface coating is carried out to the fluorine carbon plaque substrate after drying;
S8., warming plate is provided;
S9. some grooves are opened up to the surface of the warming plate, and the one side that some grooves are offered to warming plate is carried out Roller glue;
S10., the one side that fluorine carbon plaque substrate after drying is offered to some grooves with the warming plate is stacked, and Fluorine carbon plaque substrate and warming plate are cold-pressed, after the two is firmly combined with, blanking obtains the bionical complex heat-preservation of fluorine carbon Material.
As the improvement of the production technology of the bionical compound insulating material of fluorine carbon of the present invention, in the step S1 and S8, lead to Cross the feeding that feeder completes the fluorine carbon plaque substrate and warming plate.
As the improvement of the production technology of the bionical compound insulating material of fluorine carbon of the present invention, in the step S2, to described The surface treatment that fluorine carbon plaque substrate is carried out includes successively:For the first time mend greasy, first time uv drying, first time washed ore, for the second time Mend greasy, second uv dryings, second of washed ore.
As the improvement of the production technology of the bionical compound insulating material of fluorine carbon of the present invention, the first time uv is dried and the The drying energy that secondary uv is dried is that emittance is 985-995J, the first time washed ore and second of washed ore using 315 mesh- The washed ore machine of 325 mesh.
As the improvement of the production technology of the bionical compound insulating material of fluorine carbon of the present invention, in the step S3, pass through roller Painting machine carries out first time roller coat processing to the fluorine carbon plaque substrate, and by levelling drying to the institute after the processing of first time roller coat State fluorine carbon plaque substrate dry for the first time, the temperature that the levelling is dried is 60-70 DEG C.
As the improvement of the production technology of the bionical compound insulating material of fluorine carbon of the present invention, in the step S4, pass through roller Painting machine carries out second of roller coat processing to the fluorine carbon plaque substrate, and by levelling drying to the institute after second of roller coat processing State fluorine carbon plaque substrate dry for the second time, the temperature that the levelling is dried is 60-70 DEG C.
As the improvement of the production technology of the bionical compound insulating material of fluorine carbon of the present invention, in the step S5, pass through roller Painting machine carries out third time roller coat processing to the fluorine carbon plaque substrate, and by levelling drying to the institute after the processing of third time roller coat State fluorine carbon plaque substrate dry for the third time, the temperature that the levelling is dried is 60-70 DEG C.
As the improvement of the production technology of the bionical compound insulating material of fluorine carbon of the present invention, in the step S6, pass through baking Room is dried to the fluorine carbon plaque substrate, and the drying temperature of the drying room is 55-65 DEG C.
It is described cold in the step S10 as the improvement of the production technology of the bionical compound insulating material of fluorine carbon of the present invention The pressure of pressure is maintained at 6-10mpa, and the cold pressing time is 4.0-4.5H.
In order to solve the above technical problems, another technical scheme of the present invention is:
A kind of bionical compound insulating material of fluorine carbon, it is obtained by production technology as described above.
Compared with prior art, the beneficial effects of the invention are as follows:The present invention can carry out effective to fluorine carbon plaque substrate Working process, and surface texturing can be obtained and meet the fluorine carbon plaque of actual demand, and fluorine carbon plaque substrate can be realized with protecting The strong bonded of warm plate.Meanwhile the present invention also has the advantages of continuity is good, high in machining efficiency.
Embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below in conjunction with the embodiment of the present invention, Obviously, described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.Based in the present invention Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all Belong to the scope of protection of the invention.
The production technology of the bionical compound insulating material of fluorine carbon of the present invention comprises the following steps:
S1., fluorine carbon plaque substrate Jing Guo primary coat is provided.
Wherein, it is possible to provide the feeder suitable for fluorine carbon plaque substrate feeding completes the feeding of fluorine carbon plaque substrate.
S2. the fluorine carbon plaque substrate is surface-treated.
Wherein, the purpose being surface-treated to the fluorine carbon plaque substrate of offer is, after meeting fluorine carbon plaque substrate Continuous roller coat process requirements.Specifically, the surface treatment carried out to the fluorine carbon plaque substrate includes successively:For the first time mend it is greasy, First time uv dryings, first time washed ore, greasy, second uv dryings, second of washed ore are mended for the second time.In one embodiment, The drying energy that the first time uv is dried and second of uv is dried is that emittance is 985-995J, it is preferable that drying energy It is 990J for emittance.The first time washed ore and second of washed ore use the washed ore machine of the mesh of 315 mesh -325, it is preferable that adopt With the washed ore machine of 320 mesh.
S3. first time roller coat processing is carried out to the fluorine carbon plaque substrate after surface treatment, and first time roller coat is processed Fluorine carbon plaque substrate afterwards dry for the first time.
Wherein, first time roller coat processing is carried out to the fluorine carbon plaque substrate by roll coater, and passes through levelling drying pair The fluorine carbon plaque substrate after the processing of first time roller coat dry for the first time, is advantageous to maintain first time roller by drying Apply the decorative pattern formed.The temperature that the levelling is dried is 60-70 DEG C, it is preferable that the drying temperature of the levelling drying machine is 65 ℃。
S4. after the fluorine carbon plaque substrate surface is dried completely, second of roller coat is carried out to the fluorine carbon plaque substrate Processing, and second is carried out to the fluorine carbon plaque substrate after second of roller coat processing and is dried.
Wherein, second of roller coat processing is carried out to the fluorine carbon plaque substrate by roll coater, and passes through levelling drying pair The fluorine carbon plaque substrate after second of roller coat processing carries out second and dried, and is advantageous to maintain second of roller by drying Apply the decorative pattern formed.The temperature that the levelling is dried is 60-70 DEG C, it is preferable that the drying temperature of the levelling drying machine is 65 ℃。
S5. after the fluorine carbon plaque substrate surface is dried completely, third time roller coat is carried out to the fluorine carbon plaque substrate Processing, and third time is carried out to the fluorine carbon plaque substrate after the processing of third time roller coat and dried.
Wherein, third time roller coat processing is carried out to the fluorine carbon plaque substrate by roll coater, and passes through levelling drying pair The fluorine carbon plaque substrate after the processing of third time roller coat carries out third time and dried, and is advantageous to maintain third time roller by drying Apply the decorative pattern formed.The temperature that the levelling is dried is 60-70 DEG C, it is preferable that the drying temperature of the levelling drying machine is 65 ℃。
S6. after the fluorine carbon plaque substrate surface is dried completely, drying and processing is carried out to it.
Wherein, the fluorine carbon plaque substrate is dried by drying room, the drying temperature of the drying room is 55-65 DEG C. Preferably, the drying temperature of the drying room is 60 DEG C.
S7. surface coating is carried out to the fluorine carbon plaque substrate after drying.
Wherein, by surface coating, be advantageous to protect the surface of fluorine carbon plaque, avoid the scuffing of fluorine carbon decorative pattern, Influence the attractive in appearance of fluorine carbon plaque.
S8., warming plate is provided.
Wherein, it is possible to provide the feeder suitable for warming plate feeding completes the feeding of warming plate.
S9. some grooves are opened up to the surface of the warming plate, and the one side that some grooves are offered to warming plate is carried out Roller glue.
Wherein, the passage for being incubated plate surface by opening up above-mentioned some grooves and forming ventilation, so as to avoid warming plate Deformed with the compound rear drum that occurred of fluorine carbon plaque.Meanwhile the attachment of some grooves opened up glue when also helping follow-up roller glue, It is easy to the pressing between fluorine carbon plaque substrate and warming plate to fix.
S10., the one side that fluorine carbon plaque substrate after drying is offered to some grooves with the warming plate is stacked, and Fluorine carbon plaque substrate and warming plate are cold-pressed, after the two is firmly combined with, blanking obtains the bionical complex heat-preservation of fluorine carbon Material.
Wherein, in order to ensure that fluorine carbon plaque substrate is sufficiently combined with warming plate, the pressure of the cold pressing is maintained at 6-10mpa, cold pressing time are 4.0-4.5H.
Based on production technology as described above, it is bionical compound that the present invention also provides a kind of fluorine carbon obtained by the production technology Insulation material.
In summary, the present invention can carry out effective working process to fluorine carbon plaque substrate, and can obtain surface line Decorations meet the fluorine carbon plaque of actual demand, and can realize the strong bonded of fluorine carbon plaque substrate and warming plate.Meanwhile the present invention Also there is the advantages of continuity is good, high in machining efficiency.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power Profit requires rather than described above limits, it is intended that all in the implication and scope of the equivalency of claim by falling Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped Containing an independent technical scheme, this narrating mode of specification is only that those skilled in the art should for clarity Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art It is appreciated that other embodiment.

Claims (10)

1. a kind of production technology of the bionical compound insulating material of fluorine carbon, it is characterised in that the production technology comprises the following steps:
S1., fluorine carbon plaque substrate Jing Guo primary coat is provided;
S2. the fluorine carbon plaque substrate is surface-treated;
S3. to after surface treatment fluorine carbon plaque substrate carry out first time roller coat processing, and to first time roller coat process after Fluorine carbon plaque substrate dry for the first time;
S4. after the fluorine carbon plaque substrate surface is dried completely, second of roller coat processing is carried out to the fluorine carbon plaque substrate, And the fluorine carbon plaque substrate after being processed to second of roller coat carries out second and dried;
S5. after the fluorine carbon plaque substrate surface is dried completely, third time roller coat processing is carried out to the fluorine carbon plaque substrate, And the fluorine carbon plaque substrate after being processed to third time roller coat carries out third time and dried;
S6. after the fluorine carbon plaque substrate surface is dried completely, drying and processing is carried out to it;
S7. surface coating is carried out to the fluorine carbon plaque substrate after drying;
S8., warming plate is provided;
S9. some grooves are opened up to the surface of the warming plate, and the one side that some grooves are offered to warming plate carries out roller glue;
S10., the one side that fluorine carbon plaque substrate after drying is offered to some grooves with the warming plate is stacked, and to fluorine Carbon plaque substrate and warming plate are cold-pressed, and after the two is firmly combined with, blanking obtains the bionical compound insulating material of fluorine carbon.
2. the production technology of the bionical compound insulating material of fluorine carbon according to claim 1, it is characterised in that the step S1 In S8, the feeding of the fluorine carbon plaque substrate and warming plate is completed by feeder.
3. the production technology of the bionical compound insulating material of fluorine carbon according to claim 1, it is characterised in that the step S2 In, the surface treatment carried out to the fluorine carbon plaque substrate includes successively:For the first time mend greasy, first time uv is dry, for the first time essence Sand, greasy, second uv dryings, second of washed ore are mended for the second time.
4. the production technology of the bionical compound insulating material of fluorine carbon according to claim 3, it is characterised in that the first time The drying energy that uv is dried and second of uv is dried is that emittance is 985-995J, the first time washed ore and second of washed ore Using the washed ore machine of the mesh of 315 mesh -325.
5. the production technology of the bionical compound insulating material of fluorine carbon according to claim 1, it is characterised in that the step S3 In, first time roller coat processing is carried out to the fluorine carbon plaque substrate by roll coater, and by levelling drying to first time roller coat The fluorine carbon plaque substrate after processing dry for the first time, and the temperature that the levelling is dried is 60-70 DEG C.
6. the production technology of the bionical compound insulating material of fluorine carbon according to claim 1, it is characterised in that the step S4 In, second of roller coat processing is carried out to the fluorine carbon plaque substrate by roll coater, and by levelling drying to second of roller coat The fluorine carbon plaque substrate after processing carries out second and dried, and the temperature that the levelling is dried is 60-70 DEG C.
7. the production technology of the bionical compound insulating material of fluorine carbon according to claim 1, it is characterised in that the step S5 In, third time roller coat processing is carried out to the fluorine carbon plaque substrate by roll coater, and by levelling drying to third time roller coat The fluorine carbon plaque substrate after processing carries out third time and dried, and the temperature that the levelling is dried is 60-70 DEG C.
8. the production technology of the bionical compound insulating material of fluorine carbon according to claim 1, it is characterised in that the step S6 In, the fluorine carbon plaque substrate is dried by drying room, the drying temperature of the drying room is 55-65 DEG C.
9. the production technology of the bionical compound insulating material of fluorine carbon according to claim 1, it is characterised in that the step In S10, the pressure of the cold pressing is maintained at 6-10mpa, and the cold pressing time is 4.0-4.5H.
10. a kind of bionical compound insulating material of fluorine carbon, it is characterised in that have, the bionical compound insulating material of fluorine carbon will by right Seek the production technology described in any one of 1-9 and obtain.
CN201711054492.2A 2017-11-01 2017-11-01 A kind of bionical compound insulating material of fluorine carbon and its production technology Pending CN107599726A (en)