CN107599556A - A kind of environmentally friendly cloth cover color steel and its manufacture method - Google Patents
A kind of environmentally friendly cloth cover color steel and its manufacture method Download PDFInfo
- Publication number
- CN107599556A CN107599556A CN201710918638.7A CN201710918638A CN107599556A CN 107599556 A CN107599556 A CN 107599556A CN 201710918638 A CN201710918638 A CN 201710918638A CN 107599556 A CN107599556 A CN 107599556A
- Authority
- CN
- China
- Prior art keywords
- metal substrate
- color steel
- environmentally friendly
- cloth
- cloth cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmentally friendly cloth cover color steel, including metal substrate, metal substrate front is covered with bed of cloth, and metal substrate passes through adhesive bond with bed of cloth.The present invention also provides a kind of environmentally friendly cloth cover color steel manufacture method, including step：Metallic substrate surfaces carry out cleaning by degreasing processing, remove surface oil stain and foreign matter, then dry；Chemical surface treatment is carried out to metal substrate, passivation layer is formed and dries；The anti-backpiece paint of roller coat and solidify at the metal substrate back side；In metal substrate face-side roll coating adhesive, after activated, cloth is pasted.This color steel is the metal decorative material that surface pastes cloth; overturn innovation; cloth cover new material is introduced, the elegant style of cloth material is brought to metal material, this color steel is transboundary innovated; manufacturing process is simple; it is very environmentally friendly, and antibacterial is resistance to goes mouldy, and not only meets the individual demand of consumer; and broken original material, the limitation of technique, create more possibilities for color coating board industry.
Description
Technical field
The present invention relates to color steel field, more particularly to a kind of environmentally friendly cloth cover color steel.
Background technology
Color steel is widely used, and the field such as household electrical appliance, culture, education and public health, communications and transportation, construction and decoration is seen everywhere.Mesh
Before, color steel is by coating organic coating in surface of steel plate or to paste decoration thin still based on precoating plate and film coated plate
The mode of film is required with realizing that decorative appearance, function selection etc. are different.Current consumption market is quickly grown, and consumer demand layer goes out
Not poor, existing color steel product can not meet the more individual demands of consumer, e.g., cloth be realized in sheet metal surface
The elegant style of material.So developing the novel color steel plate of different function requirements, become urgent demand.
The content of the invention
In order to overcome the above-mentioned deficiencies of the prior art, the invention provides a kind of environmentally friendly cloth cover color steel and its manufacturer
Method, it is environmentally friendly, antibacterial is resistance to goes mouldy, and has the elegant style of cloth material.
The technical solution adopted for the present invention to solve the technical problems is：
A kind of environmentally friendly cloth cover color steel, including metal substrate, the metal substrate front are covered with bed of cloth, the metal
Substrate passes through adhesive bond with bed of cloth.
As the improvement of above-mentioned technical proposal, metal substrate back side roller coat has back of the body enamelled coating.
As the improvement of above-mentioned technical proposal, the metal substrate front and back adheres to passivation layer.
As the improvement of above-mentioned technical proposal, the passivation layer is chromium-free deactivation layer.
As the improvement of above-mentioned technical proposal, diaphragm is covered with the bed of cloth.
As the improvement of above-mentioned technical proposal, the bed of cloth uses cowboy's cloth material.
As the improvement of above-mentioned technical proposal, the metal substrate is cold-reduced sheet, heat zinc coating plate, electrolytic galvanized sheet, aluminum-zinc alloy
Plate, aluminium sheet, chromium plating iron plate or stainless steel plate.
A kind of environmentally friendly cloth cover color steel manufacture method, the described method comprises the following steps：
Step 1: metallic substrate surfaces carry out cleaning by degreasing processing, surface oil stain and foreign matter are removed, then dry；
Step 2: carrying out chemical surface treatment to metal substrate, form passivation layer and dry；
Step 3: in the anti-backpiece paint of metal substrate back side roller coat and solidify；
Step 4: in metal substrate face-side roll coating adhesive, after activated, cloth is pasted.
As the improvement of above-mentioned technical proposal, in addition to step 5, PE diaphragms are pasted on cloth.
As the improvement of above-mentioned technical proposal, the drying temperature in step 1 and step 2 is 60 DEG C, consolidating in step 3
It is 216 DEG C to change temperature, and the activation temperature in step 4 is 120-150 DEG C.
Beneficial effects of the present invention have：
This color steel is the metal decorative material that surface pastes cloth, overturns innovation, introduces cloth cover new material, color with tradition
Steel plate is compared to there is obvious difference, and the precoating plate for either coating organic coating still pastes the film coated plate of decorating film,
The elegant style of cloth material can not be brought to metal material, this color steel is transboundary innovated, and manufacturing process is simple, very environmentally friendly,
And antibacterial is resistance to goes mouldy, not only meet the individual demand of consumer, and broken original material, the limitation of technique, for coloured silk
Apply board industry and create more possibilities, actively promote Industry Innovation development.
Brief description of the drawings
Below in conjunction with the accompanying drawings and specific embodiment the invention will be further described, wherein：
Fig. 1 is the diagrammatic cross-section of the embodiment of the present invention.
Embodiment
Referring to Fig. 1, a kind of environmentally friendly cloth cover color steel of the invention, including metal substrate 1, the front of metal substrate 1 and
Passivation layer 2 is adhered at the back side, and the back side roller coat of metal substrate 1 has back of the body enamelled coating 3, and the face-side roll of metal substrate 1 scribbles gluing
Agent, and gluing oxidant layer 4 is formed, bed of cloth 5 is covered with gluing oxidant layer 4, diaphragm 6 is covered with the bed of cloth 5, at other
In embodiment, it is convenient to omit the one or more in passivation layer 2, back of the body enamelled coating 3 and diaphragm 6, also can production and application.
Wherein, the passivation layer 2 is chromium-free deactivation layer, by increasing capacitance it is possible to increase adhesive force between metal substrate 1 and adhesive with
And the adhesive force between metal substrate 1 and back of the body enamelled coating 3, the metal substrate 1 are cold-reduced sheet, heat zinc coating plate, electrolytic galvanized sheet, aluminized
Zine plate, aluminium sheet, chromium plating iron plate or stainless steel plate, can specifically be selected according to customer demand, and in the present embodiment, bed of cloth 5 uses
Cowboy's cloth material, metal substrate 1 are heat zinc coating plate.
The present invention also provides a kind of environmentally friendly cloth cover color steel manufacture method, including step in detail below：
Step 1: metal substrate from heat zinc coating plate thick 0.5mm, carries out cleaning by degreasing processing, remove surface oil stain and
Foreign matter, then with 60 DEG C of drying；
Step 2: carrying out chemical surface treatment to metal substrate, roller coat chrome-free tanning agent, passivation layer is formed and with 60 DEG C of bakings
It is dry；
Step 3: in the anti-backpiece paint of metal substrate back side roller coat, solidification temperature is 216 DEG C, and the thickness of dry film after solidification is 6
μm；
Step 4: it is in metal substrate face-side roll coating adhesive, 120-150 DEG C of activation temperature, the thickness of dry film after activation
6-8 μm, after activated, paste the denim that thickness is 0.3mm；
Step 5, the PE diaphragms that thickness is 0.05mm are pasted on denim, obtain color steel.
This color steel is transboundary innovated, and manufacturing process is simple, very environmentally friendly, and antibacterial is resistance to goes mouldy, and is brought to metal material
The elegant style of cloth material, not only meets the individual demand of consumer, and has broken original material, the limitation of technique,
More possibilities are created for color coating board industry, actively promote Industry Innovation development.
It is described above, the simply better embodiment of the present invention, but the present invention is not limited to above-described embodiment, due to
The selection of the material of metal substrate 1 and bed of cloth 5 is abundant, and color steel can also omit one in passivation layer 2, back of the body enamelled coating 3 and diaphragm 6
Kind is a variety of, can do a variety of matched combineds, not enumerate here, as long as it reaches this hair with any same or similar means
Bright technique effect, it should all belong to protection scope of the present invention.
Claims (10)
1. a kind of environmentally friendly cloth cover color steel, including metal substrate, it is characterised in that the metal substrate front is covered with cloth
Layer, the metal substrate pass through adhesive bond with bed of cloth.
2. a kind of environmentally friendly cloth cover color steel according to claim 1, it is characterised in that metal substrate back side roller coat has
Carry on the back enamelled coating.
A kind of 3. environmentally friendly cloth cover color steel according to claim 1 or 2, it is characterised in that metal substrate front and
Passivation layer is adhered at the back side.
4. a kind of environmentally friendly cloth cover color steel according to claim 3, it is characterised in that the passivation layer is chromium-free deactivation
Layer.
5. a kind of environmentally friendly cloth cover color steel according to claim 1, it is characterised in that protection is covered with the bed of cloth
Film.
6. a kind of environmentally friendly cloth cover color steel according to claim 1, it is characterised in that the bed of cloth uses denim material
Material.
A kind of 7. environmentally friendly cloth cover color steel according to claim 1, it is characterised in that the metal substrate be cold-reduced sheet,
Heat zinc coating plate, electrolytic galvanized sheet, aluminium plating zinc plate, aluminium sheet, chromium plating iron plate or stainless steel plate.
8. a kind of environmentally friendly cloth cover color steel manufacture method, it is characterised in that the described method comprises the following steps：
Step 1: metallic substrate surfaces carry out cleaning by degreasing processing, surface oil stain and foreign matter are removed, then dry；
Step 2: carrying out chemical surface treatment to metal substrate, form passivation layer and dry；
Step 3: in the anti-backpiece paint of metal substrate back side roller coat and solidify；
Step 4: in metal substrate face-side roll coating adhesive, after activated, cloth is pasted.
A kind of 9. environmentally friendly cloth cover color steel manufacture method according to claim 8, it is characterised in that also including step 5,
PE diaphragms are pasted on cloth.
10. a kind of environmentally friendly cloth cover color steel manufacture method according to claim 8, it is characterised in that step 1 and step
Drying temperature in two is 60 DEG C, and the solidification temperature in step 3 is 216 DEG C, and the activation temperature in step 4 is 120-150 DEG C.