CN107599540A - A kind of insulating refractory composite metal plate - Google Patents
A kind of insulating refractory composite metal plate Download PDFInfo
- Publication number
- CN107599540A CN107599540A CN201710942027.6A CN201710942027A CN107599540A CN 107599540 A CN107599540 A CN 107599540A CN 201710942027 A CN201710942027 A CN 201710942027A CN 107599540 A CN107599540 A CN 107599540A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- metal
- insulating refractory
- metal plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of insulating refractory composite metal plate, including outer metal level, inner metal layer and the fire resisting packed layer being filled between the outer metal level and inner metal layer, one layer of coating is also coated with the outer metal level；The fire resisting packed layer is made up of the refractory material of following parts by weight：20 80 parts of ceramic particle, 5 40 parts of aluminum oxide, 2 15 parts of binding agent, 5 15 parts of metal and 14 parts of water.The composite plate of the present invention, it is ensured that it is preferably heat-insulated, and heat-insulated quality can be improved, composite plate of the invention is manufactured into the equipment such as safety cabinet.
Description
Technical field
The present invention relates to a kind of exotic material, and in particular to a kind of insulating refractory composite metal plate.
Background technology
Composite plate is practical and convenient and be widely used in furniture industry field because manufacturing cost is low, but existing multiple
Plywood and three-ply board do not have fire-proof function, are restricted when in use in the place that some have particular/special requirement to fire prevention, and now
Furniture etc. also requires there is fire protecting performance, such as safety box etc., the high temperature resistant sheet material poor-performing on existing market.
The content of the invention
The technical problems to be solved by the invention are in view of the shortcomings of the prior art, there is provided a kind of insulating refractory metal composite
Plate.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：A kind of insulating refractory composite metal plate, including outer gold
Belong to layer, inner metal layer and the fire resisting packed layer being filled between the outer metal level and inner metal layer, gone back on the outer metal level
Coated with one layer of coating；The fire resisting packed layer is made up of the refractory material of following parts by weight：The ceramic particle, 5- of 20-80 parts
40 parts of aluminum oxide, the binding agent of 2-15 parts, the metal of 5-15 parts and 1-4 part water.
The beneficial effects of the invention are as follows：The composite plate of the present invention, it is ensured that it is preferably heat-insulated, and heat-insulated matter can be improved
Amount, composite plate of the invention are manufactured into the equipment such as safety cabinet.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the fire resisting packed layer is made up of the refractory material of following parts by weight：60 parts of ceramic particle, 20 parts
Aluminum oxide, 7 parts of binding agent, 10 parts of metal and 3 parts of water.
Further, the metal is the hollow spherical particles of a diameter of 2mm-5mm made of aluminium.
Further, the outer metal level and inner metal layer are made by the raw metal of following parts by weight：50-62 parts molybdenum,
20-30 parts tungsten, 2-7 parts aluminium, 3-6 parts titanium, 2-4 parts manganese, 1-5 part silicon.
Further, the outer metal level and inner metal layer are made by the raw metal of following parts by weight：55 parts of molybdenums, 25 parts
Tungsten, 5 parts of aluminium, 5 parts of titaniums, 3 parts of manganese, 2 parts of silicon.
Further, the thickness of the outer metal level and inner metal layer is 2mm-10mm, the thickness of the fire resisting packed layer
For 5mm-20mm.
Further, the coating is included in aluminum oxide, lanthana, calcium oxide, magnesia, silica and titanium dioxide
The mixture of at least one or two or two or more oxide powders.
Embodiment
The principles and features of the present invention are described below, and the given examples are served only to explain the present invention, is not intended to limit
Determine the scope of the present invention.
Embodiment 1
A kind of insulating refractory composite metal plate of the present embodiment, including outer metal level, inner metal layer and be filled in described outer
Fire resisting packed layer between metal level and inner metal layer, one layer of coating is also coated with the outer metal level；The fire resisting filling
Layer is made up of the refractory material of following parts by weight：20 parts of ceramic particle, 5 parts of aluminum oxide, 2 parts of binding agent, 5 parts of metal
With 1 part of water.
Specifically, the metal is the hollow spherical particles of a diameter of 2mm made of aluminium.
Specifically, the outer metal level and inner metal layer are made by the raw metal of following parts by weight：50 parts of molybdenums, 20 parts
Tungsten, 2 parts of aluminium, 3 parts of titaniums, 2 parts of manganese, 1 part of silicon.
Specifically, the thickness of the outer metal level and inner metal layer is 2mmmm, the thickness of the fire resisting packed layer is
5mm。
Specifically, the coating is included in aluminum oxide, lanthana, calcium oxide, magnesia, silica and titanium dioxide
The mixture of at least one or two or two or more oxide powders.
The composite plate of the present embodiment, it is ensured that it is preferably heat-insulated, and heat-insulated quality can be improved, composite plate of the invention
It is manufactured into the equipment such as safety cabinet.
Embodiment 2
A kind of insulating refractory composite metal plate of the present embodiment, including outer metal level, inner metal layer and be filled in described outer
Fire resisting packed layer between metal level and inner metal layer, one layer of coating is also coated with the outer metal level；The fire resisting filling
Layer is made up of the refractory material of following parts by weight：60 parts of ceramic particle, 20 parts of aluminum oxide, 7 parts of binding agent, 10 parts of gold
Category and 3 parts of water.
Specifically, the metal is the hollow spherical particles of a diameter of 3mm made of aluminium.
Specifically, the outer metal level and inner metal layer are made by the raw metal of following parts by weight：55 parts of molybdenums, 25 parts
Tungsten, 5 parts of aluminium, 5 parts of titaniums, 3 parts of manganese, 2 parts of silicon.
Specifically, the thickness of the outer metal level and inner metal layer is 6mm, the thickness of the fire resisting packed layer is
10mm。
Specifically, the coating is included in aluminum oxide, lanthana, calcium oxide, magnesia, silica and titanium dioxide
The mixture of at least one or two or two or more oxide powders.
The composite plate of the present embodiment, it is ensured that it is preferably heat-insulated, and heat-insulated quality can be improved, composite plate of the invention
It is manufactured into the equipment such as safety cabinet.
Embodiment 3
A kind of insulating refractory composite metal plate of the present embodiment, including outer metal level, inner metal layer and be filled in described outer
Fire resisting packed layer between metal level and inner metal layer, one layer of coating is also coated with the outer metal level；The fire resisting filling
Layer is made up of the refractory material of following parts by weight：80 parts of ceramic particle, 40 parts of aluminum oxide, 15 parts of binding agent, 15 parts
Metal and 4 parts of water.
Specifically, the metal is the hollow spherical particles of a diameter of 5mm made of aluminium.
Specifically, the outer metal level and inner metal layer are made by the raw metal of following parts by weight：62 parts of molybdenums, 30 parts
Tungsten, 7 parts of aluminium, 6 parts of titaniums, 4 parts of manganese, 5 parts of silicon.
Specifically, the thickness of the outer metal level and inner metal layer is 10mm, the thickness of the fire resisting packed layer is
20mm。
Specifically, the coating is included in aluminum oxide, lanthana, calcium oxide, magnesia, silica and titanium dioxide
The mixture of at least one or two or two or more oxide powders.
The composite plate of the present embodiment, it is ensured that it is preferably heat-insulated, and heat-insulated quality can be improved, composite plate of the invention
It is manufactured into the equipment such as safety cabinet.
The fire resistance that composite plate is carried out to the fire resisting in embodiment 1, embodiment 2 and embodiment 3 detects, and takes identical
The composite plate of the embodiment 1 of size, embodiment 2 and embodiment 3, respectively A, B, C.Take again and be not added with the compound of ceramic particle
Plate；Take additive identical with the present embodiment again, but the composite plate E that addition is few.Respectively to composite plate A, B, C, D, E
One side carries out fire and baked, and the temperature of its another side is detected, testing result is as shown in table 1.
The fire resistance of the different composite plate of table 1
| Composite plate | A | B | C | D | E |
| Temperature DEG C | 25 | 28 | 24 | 45 | 55 |
As shown in Table 1, the fire resistance of the present embodiment 1-3 composite plate is far superior to composite plate D and E fire resistance.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (7)
1. a kind of insulating refractory composite metal plate, it is characterised in that including outer metal level, inner metal layer and be filled in the outer gold
Belong to the fire resisting packed layer between layer and inner metal layer, one layer of coating is also coated with the outer metal level；The fire resisting packed layer
It is made up of the refractory material of following parts by weight：The ceramic particle of 20-80 parts, the aluminum oxide of 5-40 parts, the binding agent, 5- of 2-15 parts
15 parts of metal and 1-4 part water.
2. a kind of insulating refractory composite metal plate according to claim 1, it is characterised in that the fire resisting packed layer is by following
The refractory material of parts by weight is made：60 parts of ceramic particle, 20 parts of aluminum oxide, 7 parts of binding agent, 10 parts of metal and 3 parts
Water.
3. a kind of insulating refractory composite metal plate according to claim 1, it is characterised in that the metal is straight made of aluminium
Footpath is 2mm-5mm hollow spherical particles.
4. a kind of insulating refractory composite metal plate according to claim 1, it is characterised in that the outer metal level and interior metal
Layer is made by the raw metal of following parts by weight：50-62 parts molybdenum, 20-30 parts tungsten, 2-7 parts aluminium, 3-6 parts titanium, 2-4 parts manganese, 1-
5 parts of silicon.
5. a kind of insulating refractory composite metal plate according to claim 4, it is characterised in that the outer metal level and interior metal
Layer is made by the raw metal of following parts by weight：55 parts of molybdenums, 25 parts of tungsten, 5 parts of aluminium, 5 parts of titaniums, 3 parts of manganese, 2 parts of silicon.
6. according to a kind of any one of claim 1 to 5 insulating refractory composite metal plate, it is characterised in that the outer metal
The thickness of layer and inner metal layer is 2mm-10mm, and the thickness of the fire resisting packed layer is 5mm-20mm.
7. according to a kind of any one of claim 1 to 5 insulating refractory composite metal plate, it is characterised in that the coating bag
Include at least one of aluminum oxide, lanthana, calcium oxide, magnesia, silica and titanium dioxide or two or more
The mixture of oxide powder.