CN107579286A - A kind of mixed poly- additive of lead accumulator and preparation method thereof - Google Patents
A kind of mixed poly- additive of lead accumulator and preparation method thereof Download PDFInfo
- Publication number
- CN107579286A CN107579286A CN201710754139.9A CN201710754139A CN107579286A CN 107579286 A CN107579286 A CN 107579286A CN 201710754139 A CN201710754139 A CN 201710754139A CN 107579286 A CN107579286 A CN 107579286A
- Authority
- CN
- China
- Prior art keywords
- additive
- parts
- volume
- mixed
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides mixed poly- additive of a kind of lead accumulator and preparation method thereof, described mixed poly- additive is based on 100 parts by volume, and component and content include：Main chain backbone is the parts by volume of organosiloxane 1~7 of (C Si O) structure and side base containing more than one unsaturated hydrophilic active groups；The parts by volume of organic silicon rubber 1~7；The parts by volume of industrial pure water 70.5~95.95；The parts by volume of aerosil 2~15；The parts by volume of emulsifying agent 0.05~0.5；Described mixed poly- additive is prepared by process of the present invention, it mixes conventional sulfuric acid liquid and added inside lead accumulator, the anti-softening ability of positive active material can be strengthened, there is the effect of helping softening positive active material to harden again, there is few, the cost-effective advantage of addition.
Description
Technical field
The present invention relates to the field of material technology of lead accumulator, the mixed poly- additive of more particularly to a kind of lead accumulator
Material, formula and preparation method thereof.
Background technology
Lead accumulator abbreviation battery, in high-power/Large Copacities such as electrically propelled traction vehicle, car and boat starting, communication equipment station, energy storage
Field occupies empery status；In recent years with photovoltaic generation industry, the development of wind power industry, market common requirements great Rong
The battery of amount makees energy storage with applying mechanically, but conventional battery shows short life in use out of doors, and it is higher to discard rate, constrains
The business application of photovoltaic energy storage system.Industry is generally accepted, and appropriate colloidal substance is added in the sulfuric acid liquid of lead accumulator, can
Effectively lift the life-span used out of doors.
The colloid that lead accumulator industry tradition uses is aerosil, passes through industrial pure water or other solvents during use
Method fully liquefies aerosil；In Chinese invention patent ZL01104182.X, disclose one kind and be known as by poly- member
The silicon composition of organic siloxane, organic silicon rubber and thinned water mixing, said composition store with the mixed poly- lead that is used as of sulfuric acid liquid
The electrolyte or forming liquid of battery.Applied by ten several years, industry generally believes aerosil colloid and organic polymer
Colloid is each has something to recommend him, and the former viscosity is high, manufacturability difference and lead accumulator decline without the income for reducing internal resistance, increasing capacity, but life-span
Subtract relatively steadily, the latter's viscosity is low, good manufacturability and lead accumulator can obtain the income for reducing internal resistance, increasing capacity, but stability
Not as the former.
In recent years since, lead accumulator industry is seeking to one kind can be by aerosil colloid and silicon composition glue
The technical scheme that body has complementary advantages, but some methods for being simply used in mixed way two class colloids and unsuccessful, technical reason is：
Conventional gas phase silicon dioxide colloid is a kind of aqueous-phase material, but described silicon composition is a kind of hydrophily oil phase thing, by two
The fine dispersion system that person is simply mixed is unstable, and it is unsatisfactory to be added into the performance of the lead accumulator electrochemistry after electrolyte.For
This, industry wishes to seek to one kind to be fully coupled aerosil and organic polymer composition, is added into sulfuric acid liquid
The mixed poly- colloidal additive of lead accumulator chemical property can be lifted afterwards, lead accumulator is effectively extended open air and used the longevity
Life, reduce the discarded rate of battery.
The content of the invention
It is an object of the invention to：For aerosil colloid and organosilicon group in current lead accumulator industry market
The technological deficiency of compound colloid, there is provided a kind of that aerosil and silicon composition are fully coupled, are added into sulfuric acid liquid
The colloidal additive of lead accumulator chemical property can be lifted by making electrolyte, lead accumulator is effectively extended discharge and recharge and used the longevity
Life, reaching reduces technology application target of the battery using discarded rate.
To achieve the above object, the invention provides a kind of mixed poly- additive of lead accumulator, described mixed poly- addition
Agent is based on 100 parts by volume, including following components and content：
Component A：Main chain backbone is (- C-Si-O-) structure and side base contains more than one unsaturated hydrophilic active group R, divided
Organosiloxane of the son amount less than 3000,1~7 parts by volume；
B component：Viscosity is less than the organic silicon rubber of 1500 pas, 1~7 parts by volume；
Industrial pure water：Industrial pure water, 70.5~95.95 parts by volume；
Aerosil：2~15 parts by volume；
The parts by volume of emulsifying agent 0.05~0.5, described emulsifying agent include the one or more of following material：TWEEN Series breast
Agent, Span series emulsifying agent, triethanolamine, sodium carboxymethylcellulose, polyvinyl alcohol.
In the above-mentioned content for mixing poly- additive, the aerosil parts by volume is the scaled value of its weight/proportion.
In the above-mentioned component for mixing poly- additive, the R contained by the component A organosiloxane side base includes H, OH, SO2H、
NH2、CH3Or other unsaturated hydrophilic active groups.
In the above-mentioned component for mixing poly- additive, the organic silicon rubber of the B component includes methyl silicone rubber, ethyl silicon rubber
Glue, methyl phenyl silicone rubber, the organic silicon rubber containing nitrile silicone rubber or containing other organic groups.
In the above-mentioned component for mixing poly- additive, the alkalescence adjustment that preparation process is used to adjust mixture pH value is additionally included in
Agent.Described alkaline regulator includes but is not limited to use sodium hydroxide or potassium hydroxide.
The material and ratio range of mixed poly- additive based on above-mentioned lead accumulator, present invention also offers one kind by institute
The preparation method that stock is fabricated to the mixed poly- additive of the lead accumulator is stated, this method includes：
1) described industrial pure water is divided into two parts, described emulsifying agent is divided into 3 parts, standby；
2) described component A and described B component are thoroughly mixed uniformly；
3) HLB of a copy of it emulsifying agent is adjusted to 7~9, is added thereto a industrial pure water, added after well mixed
In the mixture that step 2) obtains, it is thoroughly mixed uniformly, then uses another described emulsifying agent will be mixed obtained by this step
The HLB of compound is adjusted to 10~14；
4) HLB of described another part emulsifying agent is adjusted to 10~14, adds another industrial pure water, be sufficiently mixed
After even, add described aerosil and stir more than 10 minutes；
5) mixture that step 3) obtains is well mixed with the mixture that step 4) obtains in being sufficiently stirred, that is, obtained
It is of the present invention to mix poly- additive.
In the above-mentioned preparation method for mixing poly- additive, described step 4) also includes：By adjusting the industry containing emulsifying agent
The material ratio of pure water and aerosil adjusts the clarity of this step mixture.
In the above-mentioned preparation method for mixing poly- additive, described step 4) also includes：To before adding aerosil
Mixture is adjusted its pH value to 8-10 with described alkaline regulator.
Present invention also offers a kind of lead storage battery electrolytic solution containing above-mentioned mixed poly- additive or repair liquid.The electrolysis
The sulfuric acid liquid of liquid or reparation liquid using density as 1.05-1.35 is key component, the body for mixing poly- additive in the electrolyte
Product content is not less than 0.2%, is not less than 2% in the volume content of the reparation liquid.
In the present invention, the viscosity for the mixed poly- additive produced with the material prescription and preparation technology is low, is added into sulphur
Gel is slow after acid solution, is typically added into sulfuric acid liquid a few hours and still meets technological requirement to lead accumulator routine liquid filling, and leads to
It is good with property, it can be used in mixed way with other conventional additives of lead storage battery electrolytic solution.
Before have described, aerosil colloid and silicon composition colloid have respective advantage and disadvantage, industrial gas
The spatial volume of aerosil belongs to non-type structure, and when its average grain diameter is more than tens nanometer, produced is inorganic
Colloid viscosity is big, gel is overrun, filling process is poor, and it is low that the lead accumulator of supporting making shows as initial capacity；And organosilicon
If composition can not be fabricated to the ball shape structure that particle diameter is less than 10 nanometers, although being added into the organic colloid that sulfuric acid liquid is produced
Viscosity is small, gel is slow, filling process is good, but the chemical property of supporting making lead accumulator is equally undesirable, such as lead stores
Battery latter stage capacity attenuation speed is relatively large.
The shortcomings that mixed poly- additive of the present invention can overcome aerosil colloid and silicon composition colloid, passes through
Above-mentioned material prescription and preparation method, inorganic aerosil can be obtained and mix poly- add with what silicon composition was fully coupled
Add agent, the additive, which adds sulfuric acid liquid, has percdation ability to chloride plate, can slow down positive active material because of sulphur
Lattice avalanche speed caused by lead plumbate oxidationreduction, cycle life is set to give extension (the main reason for lead accumulator end-of-life
Caused by positive material(PAM) softening, to account for end-of-life probability 80%), now described mixed poly- additive can be considered a kind of
The reinforcing agent used for positive pole.Similarly, the capacity attenuation lead accumulator of confirmation positive material(PAM) softening, the additive are added
Enter sulfuric acid liquid and can be considered a kind of reparation liquid.
A kind of mixed poly- additive of lead accumulator of the present invention and preparation method thereof advantage is：
The material prescription and preparation method of poly- additive are mixed with the present invention, can produce a kind of has work(to lead accumulator
The mixed poly- additive of effect, the mixed poly- additive, which is added into sulfuric acid liquid, which makees electrolyte, can effectively lift the electrochemistry of lead accumulator
Can, the especially anti-softening and recovery hardening to lifting positive active material has original effect, while can be with other hydrophilic lead
Battery additive, which mixes, to be used, and purposes is wide, and using effect is good.
Embodiment
With reference to embodiment further the material to the mixed poly- additive of lead accumulator of the present invention a kind of, match somebody with somebody
Side and its and its prepare process be described in detail.
Component A organosiloxane of the present invention is a species in organosilicon material, and its architectural feature is main chain
Skeleton has m (- C-Si-O-) segments, the positive integer of described m Wei≤1, and its side base (side chain) has more than one unsaturation
Hydrophilic active group R, wherein described R includes but is not limited to H, OH, SO2H、NH2、CH3Deng or other unsaturated parents
Water active group；In numerous main chain backbones in the organosiloxane of (- C-Si-O-) segmented structure, all side bases (side chain) are contained
The poly- element siloxanes of unsaturated hydrophilic active group can select with B component organic silicon rubber be coupled, for ensure component A and
B component is easier to be coupled under normal conditions, and is easily diluted after being copolymerized with B component, the A that molecular weight should be selected to be less than 3000
Component.
Another species in the organic silicon rubber category organosilicon material of the B component, its product line include methyl silicon
Rubber, ethyl silicon rubber, methyl phenyl silicone rubber or the organic silicon rubber containing other active groups, there is the chain of different polymerization degree
Structure, with chain hop count n increases, molecular weight increases, and viscosity increases, and viscosity should be selected during application to be less than the organosilicon of 1500 pas
Rubber product, such flowable organic silicon rubber are commonly called as liquid silastic；One of important function of B component, it is as component A
Molecular structure segment end-capping reagent, a kind of two-phase interface theory of electrochemistry thinks, the special Composite Bone that (A+B) copolymerization is formed
Bone adds the set directed movement that sulfate liquid system is more beneficial for ion cluster, the ability of increase ion transition in the channel, has
Beneficial to the absorption electric double layer that dynamic equilibrium is formed in electrode and electrolyte two-phase interface, strengthen the work that ion reacts in electrode surface
Change energy, accelerate the speed of electrode reaction, so as to strengthen the high current respond of electrode.
Described industrial pure water is also known as industrial water, deionized water etc., because common source water salt content and pH value not
Together, these trace impurities can influence the production effect for mixing poly- additive；Industrial pure water be routinely by electric dialyzator method, from
Sub- exchanger method, hyperfiltration and be made, industrial pure water of the present invention, the ion removed include cation and it is cloudy from
Son, technical requirements resistivity is more than 10 megohms.
Described emulsifying agent is used to prepare the hydrophilic lipophilic balance (HLB) of mixed poly- additive procedure regulation intermediate.
Such as the experiences that are about worth of HLB are estimated according to water-soluble method, the HLB of (A+B) copolymer being typically prepared works as use 7~9
, it is necessary to which the HLB of two intermediates is adjusted to oil respectively when industrial pure water is scattered, operation need to mix poly- with aqueous-phase material again in next step
Phase/aqueous phase adaptation value.Described emulsifying agent is the common articles for use of pharmacy/chemical industry, such as tween (polyoxyethylene sorbitan mountain
Pears alcohol fatty acid ester) it is a kind of nonionic surface active agent, it is widely used as oil-in-water (O/W) type emulsifying agent and oil phase substance
Solubilizer, the stabilization that can increase emulsifying agent is shared with other emulsifying agents such as sapn (sorbitan fatty acid ester) class emulsifying agent
Property, and spans is widely used as Water-In-Oil (W/O) type emulsifying agent and the solubilizer of aqueous phase substance.The HLB of various emulsifying agents
It is each variant, even same component emulsifying agent also can influence its HLB because of content, purity difference, according to right when specifically used
HLB requirements different and it is preferred that compound regulation, it is such as required with tween emulsifier type and the compounding regulation of spans emulsifying agent
HLB。
Described aerosil (white carbon) is that a kind of colloid known to lead accumulator manufacturing prepares material, its
Chemical formula is SiO2, the concentrated phosphoric acid of hydrofluoric acid and heat is soluble in, bases and can be melted and worked；Aerosil because of particle diameter very
Small, specific surface area is big, and superficial attractive forces are strong, and surface energy is big, and chemical purity is high, and dispersive property is good, has in thermal resistance, resistance etc.
There is specific performance, be always lead accumulator manufacturing colloidal electrolyte with its superior stability, reinforcing and thixotropy
Traditional material.Due to aerosil impalpable structure and in foam-like is accumulated, easily floated by moving air, true volume
Difficult accurate measuring, therefore aerosil parts by volume of the present invention, recommend to use volume instead and with proportion multiply in practical operation
Long-pending parts by weight metering.
Described alkaline regulator, effect be adjust mixture preparation process intermediate pH value, it include it is all can
Adjustment mixture pH value will not produce the alkaline regulator of sediment again, and alkaline regulator mixes poly- additive of the present invention
Content in belong to micro, select face wider, but consider preferred sodium hydroxide or potassium hydroxide from cost performance.Such as sodium hydroxide is
A kind of highly basic, it is a kind of the most frequently used alkaline regulator of lead accumulator industry.
The above-described raw material for mixing poly- additive can be purchased commercially, and the purity of the aerosil will
Ask and reach 99.99%, the purity requirement of the component A, B component and emulsifying agent is at least technical pure, and SILVER REAGENT more preferably, works as synthesis
During the contaminant overstandard of raw material, the synthetic effect for mixing poly- additive is influenced whether, the mixed poly- additive of contaminant overstandard is added
Enter to the electrolyte for being added into lead accumulator, lead accumulator increase self discharge can be caused or even produce other side effects, meeting simultaneously
Influence the storage period for mixing poly- additive.
The mixed poly- additive of lead accumulator of the present invention can not use one kettle way to mix, and be followed after need to stocking up certain
Prepared by process, the preparation method includes：
1) described industrial pure water is divided into two parts, described emulsifying agent is divided into 3 parts, standby；
2) described component A and described B component are thoroughly mixed uniformly；
3) HLB of a copy of it emulsifying agent is adjusted to 7~9, is added thereto a industrial pure water, added after well mixed
In the mixture that step 2) obtains, it is thoroughly mixed uniformly, then uses another described emulsifying agent will be mixed obtained by this step
The HLB of compound is adjusted to 10~14；
4) HLB of described another part emulsifying agent is adjusted to 10~14, adds another industrial pure water, be sufficiently mixed
After even, add described aerosil and stir more than 10 minutes；
5) mixture that step 3) obtains is well mixed with the mixture that step 4) obtains in being sufficiently stirred, that is, obtained
It is of the present invention to mix poly- additive.
Above-mentioned steps 1) in, the quantitative ratio for industrial pure water being divided into two parts requires looser, also with being stirred
The operating condition of step is related (such as the environment temperature and environmental stress being stirred), and in general, the step 3) is to step
The industrial pure water that rapid 2) gained mixture adds, can make mixture obtained by step 2) form the preferable liquid of mobility,
More industrial pure water remains step 4) operation.
Above-mentioned steps 3) in, before this using w/o type emulsifying agent, O/W type emulsifying agents are used afterwards, the emulsifying agent of one-component is not
This pair of HLB regulation requirement can be met, the two or more compoundings of foregoing emulsifying agent can be used.
The optimization operation of step 4), in addition to pass through industrial pure water of the regulation containing emulsifying agent and the material of aerosil
Ratio adjusts the clarity of mixture, when obtained mixture clarity deficiency (big generally with apparent viscosity), can pass through
Described material ratio adjusts the clarity of mixture, makes the quality of mixture more preferably.
Described alkalescence is used to adjust in the optimization operation of step 4), in addition to the mixture before addition aerosil
Whole dose adjusts its pH value to 8-10, and the pH value adjustment of the intermediate blend, is to make two kinds of step 5) in the basic conditions
The mixed effect of mixture is more preferable.
Above-mentioned steps 5) in, recommend mixture obtained by step 3) being slowly injected into the mixture that step 4) obtains, and
Persistently stirred in being slowly injected into.In order that the quality for mixing poly- additive is more preferable, routine can also be increased afterwards in step 5)
Filtering technique.Described mixed poly- additive, if desired for long-term storage or as commodity selling, can continue to fit after completing to prepare
Amount adds alkaline regulator and adjusts its pH value to more than 10.
Being stirred in the preparation method can be carried out at normal temperatures and pressures, and described is stirred including rotatably stirring
Mix, the shearing stirring that periodicity or corner cut are random, can also heat, help reaction using compressive reaction kettle, such as in mixture
Be stirred during keep mixture temperature be 75 DEG C ± 15 DEG C；When adding reaction pressure to mix using reactor, kettle
Pressure is no more than 25MPa.
The mixed poly- additive of lead accumulator of the present invention is a kind of typical micro- dispersoid, is successful journey
Degree associates larger with preparation method, and its production effect can be tested by Tyndall (Tyndall) phenomenon to colloidal dispersion；
It is known in industry, wavelength be 400-700mm light by microdispersed colloidal dispersion when, if dispersed colloidal particle is straight
Footpath, which is less than lambda1-wavelength, to be scattered, and current general experiment conclusion is：When colloidal dispersion system particle diameter≤
During 94nm, luminous intensity is hit in scattering and the biquadratic of wavelength is inversely proportional.The Tyndall phenomenon of prepared mixed poly- additive is obvious, says
The bright making for mixing poly- additive reaches Technology design target；Conversely, can verify made mixed poly- additive system not into
Work(.
More deep personnel are studied for this area, and above-mentioned preparation method can be carried out etc. by adjusting mixed process completely
With replacement；Such as first operating procedure 4) operating procedure 2 afterwards) and step 3) sheerly process stock sequential replacement；In another example when step
When the mobility of rapid 2) gained mixture is good enough, step 3) is merged into step 4) operation, the preparation side of this kind of equivalent substitution
Though method is operable, isomers is easily produced, influences electrochemistry effect.
In the specific implementation of the present invention, different selections and the married operation that feeds intake, as final mixture Stabilized
Under the premise of, it is possible that the contradiction of clarity and electrochemistry effect, the latter are often related to the aobvious state degree of Tyndall phenomenon.
When can'tting eat one's cake and have it, electrochemistry effect is recommended preferably to refine formula and technique.
The technical advantage that this mixes poly- additive is obvious, when mixed with other conventional additives, it is necessary first to attention and its
Whether his additive occurs precipitating when mixed or viscosity increases to and is difficult to be filled into inside lead accumulator, meanwhile, set as one kind
Count additive of the target for lifting performance of lead-acid battery, it is necessary to which the performance of lead-acid battery for using other additives with is examined comprehensively
Test, the mixtures' ratio with other additives is determined with cost performance.
The electrolyte of lead accumulator sulfuric acid liquid, filling lead accumulator are prepared with mixed poly- additive of the present invention
With the obvious technical advantage of following items：
1st, the stable coupling of inorganic aerosil and silicon composition is realized, is reached aerosil glue
The technical advantage of body and silicon composition colloid is complementary, and the mixed poly- additive made is added into the sulfuric acid of lead accumulator
Liquid possesses the double technique advantage of aerosil colloid and silicon composition colloid；
2nd, after the mixed poly- colloidal additive is added to conventional sulfuric acid liquid, the life time decay of lead accumulator performance is more steady,
And lead accumulator can obtain increase capacity, reduce the income of internal resistance；
3rd, preferable anti-softening and capacity repairs effect to positive electode of lead battery active material.
4th, versatility is good：It can be used in mixed way with other conventional additives of lead accumulator；
5th, stability is good, adapts to storage, transports and sell the commodity turnaround time needed for each link.
Following examples are only used for further illustrating technical scheme, and these technical schemes can be used alone,
It can add or combine and use other mature technologies.
Embodiment 1
A kind of target is designed to add in lead accumulator sulfuric acid liquid, the mixed of the anti-softening ability of positive active material can be increased
Poly- additive, stocks up first, and this mixes poly- additive in terms of 100 parts by volume, and component and content are：
Component A：There is the organosiloxane of some (- C-Si-O-) segmented structures using a kind of main chain backbone, its side base contains
H, molecular weight 1200, addition are 7 parts by volume；
B component：Viscosity be 1000 pas methyl silicone rubber, 7 parts by volume；
Industrial pure water：83.5 parts by volume；
Aerosil：2 parts by volume (scaled value of weight/proportion)；
The parts by volume of emulsifying agent 0.5：From span 20 and Tween 80, wherein span 20 is for 0.2 parts by volume, and Tween 80 is for 0.3
Parts by volume, actual amount can adjust, to realize that the HLB of intermediate is adjusted to design object.
Wherein, for selecting sodium hydroxide, hydroxide in the alkaline regulator of preparation process adjustment intermediate blend pH value
Sodium is used by the dosage of actual adjustment pH value, is prepared after completing stock using following process：
1) industrial pure water is divided into two parts first, respectively 60 parts by volume and 23.5 parts by volume：Two kinds of described emulsifications
Agent is respectively divided into 3 parts, and a copy of it compounds Tween 80 based on span 20, and HLB is adjusted to 8；Another is multiple based on Tween 80
With span 20, HLB is adjusted to 12；A Tween 80 is stayed for adjusting HLB.
2) component A of 7 parts by volume and the B component of 7 parts by volume are thoroughly mixed uniformly；
3) a copy of it emulsifying agent that HLB is 8 is added to the industrial pure water of 60 parts by volume, step is added after being well mixed
In the rapid mixture 2) obtained, it is sufficiently stirred, then using described Tween 80 emulsifying agent by the HLB of mixture obtained by this step
Adjust to 12；
4) another emulsifying agent that HLB is 12 is added to the industrial pure water of 23.5 parts by volume, added after being sufficiently mixed uniformly
The 2 parts by volume aerosil, stirring 30 minutes, then, the described sodium hydroxide of appropriate addition will mix obtained by this step
The pH value of compound is adjusted to 8；
5) mixture for obtaining step 3) is slowly injected into the mixture that step 4) obtains, and is filled during being slowly injected into
Divide and be uniformly mixed, gained mixture is mixed poly- additive of the present invention.
Above-mentioned preparation method is stirred at normal temperatures and pressures, and the mixed poly- additive of gained need to such as be deposited for a long time, can be appropriate
The described sodium hydroxide of addition adjusts its pH value to 12.The mixed poly- additive that the present embodiment obtains can be used as a kind of lead accumulator
The wide spectrum additive of sulfuric acid liquid, different proportion is added according to different purposes.
Embodiment 2
The gained of embodiment 1 is mixed into the sulfuric acid liquid of poly- additive and density 1.245 by volume 1：100 is well mixed, turns into
A kind of silicon composition of lead accumulator, silica and sulfuric acid liquid mix poly- colloidal electrolyte.
The colloidal electrolyte is filled into inside lead accumulator of the 2V500Ah energy storage with valve-regulated AGM diaphragm structures, passed through
After conventional dipping, formation charging, turning into one has the extraordinary colloid plumbic storage battery of resistant to elevated temperatures outdoor energy storage.The present embodiment
Poly- additive is mixed with volume ratio 1：The filling lead accumulator of 100 mix sulphur acid solutions uses, and under the liquid-tight degree same case of sulfuric acid, can make
The effect that lead accumulator substantially obtains and reduces internal resistance, increases capacity.
In the present embodiment, the conventional anhydrous sodium sulfate of lead accumulator industry can be also added in described colloidal electrolyte,
Anhydrous sodium sulfate accounts for the 0.5% of the extraordinary colloidal electrolyte volume total amount, and industry is generally accepted, and one is added in colloidal electrolyte
Determine the anhydrous sodium sulfate of content, electrolyte electrochemical activity can be lifted, reduce the internal resistance of colloid plumbic storage battery, lift leaching colloidal
The charge acceptance of battery.
Embodiment 3
In embodiment 1, aerosil is 2 parts by volume in the content for mixing poly- additive, and the present embodiment is by gas
Aerosil increase be 6 parts by volume, that is, it is 104 parts by volume to mix the total amount of poly- additive by 100 parts by volume to be increased, remaining component
Constant with content, preparation method is same as Example 1.
Typically contrast effect test result on probation is：The proportioning of organic polymer composition and aerosil is not
Together, different electrochemical properties can be shown by mixing poly- additive, when mixed poly- additive is using organic polymer composition to be main, lead
The income that battery can obtain and reduce internal resistance, increase capacity；And when increasing the mixed proportion of aerosil, lead accumulator
The cycle charge-discharge life time decay shown is more steady.
The mixed poly- additive of the present embodiment is with volume ratio 1：The filling lead accumulator of 100 mix sulphur acid solutions uses, cycle charge discharge
The life-span effect of electricity is better than embodiment 2；The mixed poly- additive of the present embodiment is with volume ratio 1：10 mix sulphur acid solutions, by 1ml/
Quantifying for 10Ah is added into through being judged as inside the lead accumulator of positive material(PAM) softening and capacity attenuation, through known to industry
Add negative pressure technique after the inner panel group of lead accumulator is evenly distributed, by secondary formation charging technique, the positive pole of softening can be made
Plate active material hardens again, lead accumulator is recovered capacity.
Embodiment 4
Design a kind of electrolysis additive for adapting to the lead accumulator that long-term floating charge system uses, its organic polymer composition
Component and content in terms of 100 parts by volume：
Component A：Used organosiloxane is that main chain backbone has some (- C-Si-O-) segmented structures, and molecular weight is
1500, its side base contains SO2H, the parts by volume of addition 1；
B component：Viscosity be 1100 pas ethyl silicon rubber, 1 parts by volume；
Industrial pure water：82.95 parts by volume；
Aerosil：15 parts by volume；
The parts by volume of emulsifying agent 0.05：It is standby for 0.01 parts by volume, Tween 80 from span 40 and Tween 80, wherein span 40
0.04 parts by volume, actual amount can adjust, to realize that the HLB of intermediate is adjusted to design object.
Prepared after completing stock using following process：
1) industrial pure water is divided into two parts first, respectively 7.95 parts by volume and 75 parts by volume：Two kinds of described emulsifications
Agent is respectively divided into 3 parts, and a copy of it compounds Tween 80 based on span 40, and HLB is adjusted to 7；Another is multiple based on Tween 80
With span 40, HLB is adjusted to 13；A Tween 80 is stayed for adjusting HLB.
2) component A of 1 parts by volume and the B component of 1 parts by volume are thoroughly mixed uniformly；
3) a copy of it emulsifying agent that HLB is 7 is added to the industrial pure water of 7.95 parts by volume, added after well mixed
In the mixture that step 2) obtains, it is sufficiently stirred, then using described Tween 80 emulsifying agent by mixture obtained by this step
HLB is adjusted to 12；
4) another emulsifying agent that HLB is 13 is added to the industrial pure water of 75 parts by volume, institute is added after being sufficiently mixed uniformly
The aerosil of 15 parts by volume is stated, is persistently stirred 25 minutes, is pressurizeed being persistently stirred process using reactor
And heat and help reaction, kettle pressure be 20MPa, the mixture temperature in the mixed process using reactor in holding kettle is 75 DEG C ±
10℃；If mixture clarity deficiency or viscosity are bigger than normal, by adjusting industrial pure water and aerosil containing emulsifying agent
Material ratio adjust the clarity of this step mixture.
5) mixture for obtaining step 3) is slowly injected into the mixture that step 4) obtains, and is filled during being slowly injected into
Divide and be uniformly mixed, gained mixture is filtered, filtrate is described mixed poly- additive.
Content of the present embodiment because of aerosil in poly- additive is mixed is higher, and great Rong is made with suitable after sulfuric acid liquid
Lead accumulator is measured, is especially suitable for the outdoor Large Copacity energy storage lead accumulator for making long-term floating charge.
It should be noted last that the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted.Although ginseng
The present invention is described in detail according to embodiment, it will be understood by those within the art that, to the technical side of the present invention
Case is modified or equivalent substitution, and without departure from the spirit and scope of technical solution of the present invention, it all should cover in the present invention
Right among.
Claims (8)
1. the mixed poly- additive of a kind of lead accumulator, it is characterised in that based on the mixed poly- additive described in 100 parts by volume, bag
Include following components and content：
Component A：Main chain backbone is (- C-Si-O-) structure and side base contains more than one unsaturated hydrophilic active group R, molecular weight
Organosiloxane less than 3000,1~7 parts by volume；
B component：Viscosity is less than the organic silicon rubber of 1500 pas, 1~7 parts by volume；
Industrial pure water：70.5~95.95 parts by volume；
Aerosil：2~15 parts by volume；
The parts by volume of emulsifying agent 0.05~0.5, described emulsifying agent include the one or more of following material：TWEEN Series emulsify
Agent, Span series emulsifying agent, triethanolamine, sodium carboxymethylcellulose, polyvinyl alcohol.
2. the mixed poly- additive of lead accumulator according to claim 1, it is characterised in that the component A organosiloxane
R contained by side base includes H, OH, SO2H、NH2、CH3Or other unsaturated hydrophilic active groups.
3. the mixed poly- additive of lead accumulator according to claim 1, it is characterised in that the organosilicon rubber of the B component
Glue includes methyl silicone rubber, ethyl silicon rubber, methyl phenyl silicone rubber, the organosilicon containing nitrile silicone rubber or containing other organic groups
Rubber.
4. the mixed poly- additive of lead accumulator according to claim 1, it is characterised in that described mixed poly- additive also wraps
Include in alkaline regulator of the preparation process for adjusting mixture pH value.
5. a kind of preparation method of the mixed poly- additive based on any lead accumulator of Claims 1 to 4, including：
1) described industrial pure water is divided into two parts, described emulsifying agent is divided into 3 parts, standby；
2) described component A and described B component are thoroughly mixed uniformly；
3) HLB of a copy of it emulsifying agent is adjusted to 7~9, is added thereto a industrial pure water, step is added after well mixed
2) in the mixture obtained, it is thoroughly mixed uniformly, then with another described emulsifying agent by mixture obtained by this step
HLB adjust to 10~14；
4) HLB of described another part emulsifying agent is adjusted to 10~14, adds another industrial pure water, be sufficiently mixed uniformly
Afterwards, described aerosil is added to stir more than 10 minutes；
5) mixture that step 3) obtains is well mixed with the mixture that step 4) obtains in being sufficiently stirred, that is, obtains this hair
Bright described mixed poly- additive.
6. according to the method for claim 5, it is characterised in that described step 4) also includes：Emulsifying agent is contained by adjustment
Industrial pure water and the material ratio of aerosil adjust the clarity of this step mixture.
7. according to the method for claim 5, it is characterised in that described step 4) also includes：To addition gas phase titanium dioxide
Mixture before silicon is adjusted its pH value to 8-10 with described alkaline regulator.
8. containing any lead storage battery electrolytic solution for mixing poly- additive of Claims 1 to 4 or repair liquid.