CN107573617A - A kind of PVC plastic pipe - Google Patents
A kind of PVC plastic pipe Download PDFInfo
- Publication number
- CN107573617A CN107573617A CN201710894609.1A CN201710894609A CN107573617A CN 107573617 A CN107573617 A CN 107573617A CN 201710894609 A CN201710894609 A CN 201710894609A CN 107573617 A CN107573617 A CN 107573617A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic pipe
- pvc plastic
- stabilizer
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of PVC plastic pipe, it is prepared from the following raw materials in parts by weight：20 30 parts of DOP, 10 20 parts of modified xylanase, 10 20 parts of attapulgite, 10 15 parts of bentonite, 10 15 parts of nano-calcium carbonate, 5 15 parts of silicon carbide whisker, 10 16 parts of TPUE, 6 12 parts of di-iron trioxide, 25 45 parts of Corvic, 10 20 parts of crosslinked starch, 5 10 parts of antimony oxide, 35 parts of stabilizer, 24 parts of lubricant, 13 parts of colouring agent, 13 parts of filler.The features such as PVC plastic pipe of the present invention, improves the anti-wear performance of tubing, reduces abrasion, extends the service life of tubing, and good flame resistance, intensity is high, resistant to chemical etching, ageing-resistant, high temperature resistant, simple easy processing, and cost is low, has a extensive future.
Description
Technical field
The present invention relates to the production technology of wall material, specifically a kind of PVC plastic pipe.
Background technology
Plastic tube is usually to be raw material, added stabilizer, lubricant, plasticizer etc. with synthetic resin, that is, polyester, with
The method of " modeling " forms in tuber through extrusion process.Due to it have light, corrosion-resistant, good appearance, without bad smell,
Handling ease, it is easy for construction the features such as, more and more extensive application is obtained in architectural engineering.It is mainly used as building construction
Tap water supply system pipe arrangement, draining, exhaust and blowdown sanitary pipe, subsoil drain system, rain pipe and electric wire installation are matched somebody with somebody
Penetration pipe applied mechanically etc..
With the continuous propulsion of Chinese Urbanization construction, the demand of plumbing tubing is expanded therewith, and to the performance of pipe
It is required that improve therewith, especially impact strength.It is inadequate ring stiffness to be present in common extrusion type polyvinyl chloride pipe, typically can only achieve
S1 levels, and internal pressure-resistant degree is poor, only reaches 0.25MPa, therefore easily ftractureed during normal use, especially apply
There is the fluid of interior pressure medium in conveying.Often result in unnecessary economic loss.
The content of the invention
The invention provides a kind of PVC plastic pipe, to solve above-mentioned technical problem.
A kind of PVC plastic pipe, is prepared from the following raw materials in parts by weight：
DOP 20-30 parts, modified xylanase 10-20 parts, attapulgite 10-20 parts, bentonite 10-15 parts, nano-calcium carbonate
10-15 parts, silicon carbide whisker 5-15 parts, TPUE 10-16 parts, di-iron trioxide 6-12 parts, polyvinyl chloride
Resin 25-45 parts, crosslinked starch 10-20 parts, antimony oxide 5-10 parts, stabilizer 3-5 parts, lubricant 2-4 parts, colouring agent 1-
3 parts, filler 1-3 parts.
Preferably, the stabilizer is calcium zinc stabilizer.
Preferably, the lubricant is microcrystalline wax.
Preferably, the colouring agent is titanium dioxide.
Beneficial effects of the present invention：
PVC plastic pipe of the present invention, the anti-wear performance of tubing is improved, reduce abrasion, extend the service life of tubing, resistance
The features such as combustion property is good, and intensity is high, resistant to chemical etching, ageing-resistant, high temperature resistant, simple easy processing, and cost is low, has a extensive future.
Embodiment
Embodiments of the invention are described in detail below, but what the present invention can be defined by the claims and cover
Multitude of different ways is implemented.
Below by way of specific embodiment, the present invention will be described in detail.
Embodiment 1
A kind of PVC plastic pipe, is prepared from the following raw materials in parts by weight：
20 parts of DOP, 10 parts of modified xylanase, 10 parts of attapulgite, 10 parts of bentonite, 10 parts of nano-calcium carbonate, silicon carbide whisker
5 parts of palpus, 10 parts of TPUE, 6 parts of di-iron trioxide, 25 parts of Corvic, 10 parts of crosslinked starch, three oxygen
Change 5 parts of two antimony, 3 parts of stabilizer, 2 parts of lubricant, 1 part of colouring agent, 1 part of filler.
Aforementioned stable agent is calcium zinc stabilizer.
Above-mentioned lubricant is microcrystalline wax.
Above-mentioned colouring agent is titanium dioxide.
Embodiment 2
A kind of PVC plastic pipe, is prepared from the following raw materials in parts by weight：
25 parts of DOP, 15 parts of modified xylanase, 15 parts of attapulgite, 12.5 parts of bentonite, 12.5 parts of nano-calcium carbonate, carbonization
10 parts of silicon wafer palpus, 13 parts of TPUE, 10 parts of di-iron trioxide, 35 parts of Corvic, crosslinked starch 15
Part, 8 parts of antimony oxide, 4 parts of stabilizer, 3 parts of lubricant, 2 parts of colouring agent, 2 parts of filler.
Aforementioned stable agent is calcium zinc stabilizer.
Above-mentioned lubricant is microcrystalline wax.
Above-mentioned colouring agent is titanium dioxide.
Embodiment 3
A kind of PVC plastic pipe, is prepared from the following raw materials in parts by weight：
30 parts of DOP, 20 parts of modified xylanase, 20 parts of attapulgite, 15 parts of bentonite, 15 parts of nano-calcium carbonate, silicon carbide whisker
15 parts of palpus, 16 parts of TPUE, 12 parts of di-iron trioxide, 45 parts of Corvic, 20 parts of crosslinked starch, three
Aoxidize 10 parts of two antimony, 5 parts of stabilizer, 4 parts of lubricant, 3 parts of colouring agent, 3 parts of filler.
Aforementioned stable agent is calcium zinc stabilizer.
Above-mentioned lubricant is microcrystalline wax.
Above-mentioned colouring agent is titanium dioxide.
The embodiments of the present invention described above are not intended to limit the scope of the present invention, any in the present invention
Spirit and principle within the modifications, equivalent substitutions and improvements made etc., should be included in the claim protection model of the present invention
Within enclosing.
Claims (4)
1. a kind of PVC plastic pipe, it is characterised in that be prepared from the following raw materials in parts by weight：
DOP 20-30 parts, modified xylanase 10-20 parts, attapulgite 10-20 parts, bentonite 10-15 parts, nano-calcium carbonate 10-15
Part, silicon carbide whisker 5-15 parts, TPUE 10-16 parts, di-iron trioxide 6-12 parts, Corvic
25-45 parts, crosslinked starch 10-20 parts, antimony oxide 5-10 parts, stabilizer 3-5 parts, lubricant 2-4 parts, colouring agent 1-3 parts,
Filler 1-3 parts.
2. according to the PVC plastic pipe described in claims 1, it is characterised in that the stabilizer is calcium zinc stabilizer.
3. according to the PVC plastic pipe described in claims 1, it is characterised in that the lubricant is microcrystalline wax.
4. according to the PVC plastic pipe described in claims 1, it is characterised in that the colouring agent is titanium dioxide.