CN107573541A - A kind of pollution-free packaging material of Degradable environment protection and preparation method thereof - Google Patents
A kind of pollution-free packaging material of Degradable environment protection and preparation method thereof Download PDFInfo
- Publication number
- CN107573541A CN107573541A CN201710794297.7A CN201710794297A CN107573541A CN 107573541 A CN107573541 A CN 107573541A CN 201710794297 A CN201710794297 A CN 201710794297A CN 107573541 A CN107573541 A CN 107573541A
- Authority
- CN
- China
- Prior art keywords
- parts
- pollution
- packaging material
- environment protection
- degradable environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses pollution-free packaging material of a kind of Degradable environment protection and preparation method thereof, the pollution-free packaging material of Degradable environment protection includes the raw material of following parts by weight：15 25 parts of polystyrene, 10 20 parts of policapram, 25 40 parts of plant amylum, 8 13 parts of methyl-silicone oil, 6 12 parts of silica, 10 20 parts of calcium carbonate, 8 15 parts of makrolon, 13 parts of nano organic montmorillonite, 5 10 parts of cellulose, 13 parts of borax, 25 parts of foaming agent, 2.5 6 parts of talcum powder.Compared with prior art, the pollution-free packaging material of Degradable environment protection in the present invention will not cause any pollution in preparation process to environment, and preparation technology is simple, low raw-material cost.
Description
Technical field
The invention belongs to field of packaging material, more particularly to a kind of Degradable environment protection is pollution-free packaging material and its system
Preparation Method.
Background technology
As low-carbon economy and the theory of green package are progressively approved by people, Degradable environment protection is pollution-free packaging material is
It is used widely.At present, in amortizing packaging material field, existing several foamed plant fiber materials come out.Existing research is more
By the way that string is mixed with various auxiliary agents so that the mixed system of string and auxiliary agent turn into be easy to keep here gas and
The mixture of fast shaping, decompose foaming agent by hot conditions afterwards and produce gas.However, the ring of existing packaging material
Guaranteed cost is poor, and its degradation property is poor, and the later stage burns, burial can all pollute to environment.
The content of the invention
It is an object of the invention to provide pollution-free packaging material of a kind of Degradable environment protection and preparation method thereof, its degradation property
It is good, and preparation technology is simple, low raw-material cost.
To achieve the above object, the present invention provides following technical scheme：
A kind of pollution-free packaging material of Degradable environment protection, it includes the raw material of following parts by weight：Polystyrene 15-25 parts, gather
Acetamide 10-20 parts, plant amylum 25-40 parts, methyl-silicone oil 8-13 parts, silica 6-12 parts, calcium carbonate 10-20 parts, poly- carbon
Acid esters 8-15 parts, nano organic montmorillonite 1-3 parts, cellulose 5-10 parts, borax 1-3 parts, foaming agent 2-5 parts, talcum powder 2.5-6
Part.
Preferably, the pollution-free packaging material of the Degradable environment protection includes the raw material of following parts by weight：Polystyrene 18
Part, 14 parts of policapram, 32 parts of plant amylum, 10 parts of methyl-silicone oil, 8 parts of silica, 12 parts of calcium carbonate, 12 parts of makrolon,
1.6 parts of nano organic montmorillonite, 7 parts of cellulose, 1.5 parts of borax, 3.5 parts of foaming agent, 5 parts of talcum powder.
Preferably, the pollution-free packaging material of the Degradable environment protection includes the raw material of following parts by weight：Polystyrene 22
Part, 14 parts of policapram, 28 parts of plant amylum, 8 parts of methyl-silicone oil, 9 parts of silica, 12 parts of calcium carbonate, 11 parts of makrolon, receive
1.3 parts of organo montmorillonite of rice, 6 parts of cellulose, 1 part of borax, 3 parts of foaming agent, 4 parts of talcum powder.
Preferably, the pollution-free packaging material of the Degradable environment protection includes the raw material of following parts by weight：Polystyrene 23
Part, 10 parts of policapram, 30 parts of plant amylum, 12 parts of methyl-silicone oil, 12 parts of silica, 18 parts of calcium carbonate, 15 parts of makrolon,
2 parts of nano organic montmorillonite, 9 parts of cellulose, 2.3 parts of borax, 3.8 parts of foaming agent, 5.5 parts of talcum powder.
The preparation method of described Degradable environment protection is pollution-free packaging material, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.
Compared with prior art, the beneficial effects of the invention are as follows：
Packaging material in the present invention has been especially added with the raw materials such as plant amylum, methyl-silicone oil, silica and calcium carbonate, not only makes
It has a good degradation effect, and preparation technology is simple, low raw-material cost, will not be produced in early stage production process or
Volatile pollutants, later stage bury or burned and be also beneficial to reduce environmental pollution.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one：
A kind of pollution-free packaging material of Degradable environment protection, it includes the raw material of following parts by weight：22 parts of polystyrene, poly- acetyl
15 parts of amine, 32 parts of plant amylum, 11 parts of methyl-silicone oil, 7 parts of silica, 13 parts of calcium carbonate, 12 parts of makrolon, the organic illiteracy of nanometer
De- 1.2 parts of soil, 7 parts of cellulose, 2.8 parts of borax, 4 parts of foaming agent, 4.5 parts of talcum powder.
The preparation method of described Degradable environment protection is pollution-free packaging material, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.
Embodiment two：
A kind of pollution-free packaging material of Degradable environment protection, it includes the raw material of following parts by weight：17 parts of polystyrene, poly- acetyl
13 parts of amine, 32 parts of plant amylum, 8 parts of methyl-silicone oil, 8 parts of silica, 13 parts of calcium carbonate, 13 parts of makrolon, the organic illiteracy of nanometer
De- 3 parts of soil, 8.5 parts of cellulose, 1 part of borax, 3 parts of foaming agent, 4.2 parts of talcum powder.
The preparation method of described Degradable environment protection is pollution-free packaging material, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.
Embodiment three：
A kind of pollution-free packaging material of Degradable environment protection, it includes the raw material of following parts by weight：18 parts of polystyrene, poly- acetyl
14 parts of amine, 32 parts of plant amylum, 10 parts of methyl-silicone oil, 8 parts of silica, 12 parts of calcium carbonate, 12 parts of makrolon, the organic illiteracy of nanometer
De- 1.6 parts of soil, 7 parts of cellulose, 1.5 parts of borax, 3.5 parts of foaming agent, 5 parts of talcum powder.
The preparation method of described Degradable environment protection is pollution-free packaging material, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.
Example IV：
A kind of pollution-free packaging material of Degradable environment protection, it includes the raw material of following parts by weight：22 parts of polystyrene, poly- acetyl
14 parts of amine, 28 parts of plant amylum, 8 parts of methyl-silicone oil, 9 parts of silica, 12 parts of calcium carbonate, 11 parts of makrolon, the organic illiteracy of nanometer
De- 1.3 parts of soil, 6 parts of cellulose, 1 part of borax, 3 parts of foaming agent, 4 parts of talcum powder.
The preparation method of described Degradable environment protection is pollution-free packaging material, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.
Embodiment five：
A kind of pollution-free packaging material of Degradable environment protection, it includes the raw material of following parts by weight：23 parts of polystyrene, poly- acetyl
10 parts of amine, 30 parts of plant amylum, 12 parts of methyl-silicone oil, 12 parts of silica, 18 parts of calcium carbonate, 15 parts of makrolon, nanometer is organic
2 parts of montmorillonite, 9 parts of cellulose, 2.3 parts of borax, 3.8 parts of foaming agent, 5.5 parts of talcum powder.
The preparation method of described Degradable environment protection is pollution-free packaging material, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.
Embodiment six：
A kind of pollution-free packaging material of Degradable environment protection, it includes the raw material of following parts by weight：25 parts of polystyrene, poly- acetyl
17 parts of amine, 32 parts of plant amylum, 10 parts of methyl-silicone oil, 10 parts of silica, 11 parts of calcium carbonate, 10 parts of makrolon, nanometer is organic
1.6 parts of montmorillonite, 6.5 parts of cellulose, 2.2 parts of borax, 2.8 parts of foaming agent, 4 parts of talcum powder.
The preparation method of described Degradable environment protection is pollution-free packaging material, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.
Embodiment seven：
A kind of pollution-free packaging material of Degradable environment protection, it includes the raw material of following parts by weight：24 parts of polystyrene, poly- acetyl
15 parts of amine, 35 parts of plant amylum, 9 parts of methyl-silicone oil, 11 parts of silica, 17 parts of calcium carbonate, 12 parts of makrolon, the organic illiteracy of nanometer
De- 2 parts of soil, 5 parts of cellulose, 1.3 parts of borax, 3.6 parts of foaming agent, 5 parts of talcum powder.
The preparation method of described Degradable environment protection is pollution-free packaging material, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (5)
1. a kind of pollution-free packaging material of Degradable environment protection, it is characterised in that include the raw material of following parts by weight：Polystyrene
15-25 parts, policapram 10-20 parts, plant amylum 25-40 parts, methyl-silicone oil 8-13 parts, silica 6-12 parts, calcium carbonate 10-
20 parts, makrolon 8-15 parts, nano organic montmorillonite 1-3 parts, cellulose 5-10 parts, borax 1-3 parts, foaming agent 2-5 parts, slide
Stone flour 2.5-6 parts.
2. the pollution-free packaging material of Degradable environment protection according to claim 1, it is characterised in that including following parts by weight
Raw material：18 parts of polystyrene, 14 parts of policapram, 32 parts of plant amylum, 10 parts of methyl-silicone oil, 8 parts of silica, calcium carbonate 12
Part, 12 parts of makrolon, 1.6 parts of nano organic montmorillonite, 7 parts of cellulose, 1.5 parts of borax, 3.5 parts of foaming agent, talcum powder 5
Part.
3. the pollution-free packaging material of Degradable environment protection according to claim 1, it is characterised in that including following parts by weight
Raw material：22 parts of polystyrene, 14 parts of policapram, 28 parts of plant amylum, 8 parts of methyl-silicone oil, 9 parts of silica, calcium carbonate 12
Part, 11 parts of makrolon, 1.3 parts of nano organic montmorillonite, 6 parts of cellulose, 1 part of borax, 3 parts of foaming agent, 4 parts of talcum powder.
4. the pollution-free packaging material of Degradable environment protection according to claim 1, it is characterised in that including following parts by weight
Raw material：23 parts of polystyrene, 10 parts of policapram, 30 parts of plant amylum, 12 parts of methyl-silicone oil, 12 parts of silica, calcium carbonate
18 parts, 15 parts of makrolon, 2 parts of nano organic montmorillonite, 9 parts of cellulose, 2.3 parts of borax, 3.8 parts of foaming agent, talcum powder 5.5
Part.
5. the preparation method of the pollution-free packaging material of Degradable environment protection according to any one of claim 1-4, its feature
It is, comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) polystyrene, policapram are mixed with water, dissolving gelatinization 20-25 minutes, are gelatinized under the conditions of 85-95 DEG C
Liquid I；
(3) plant amylum is mixed with water, dissolving gelatinization 30-40 minutes, obtain dextrin II under the conditions of 65-75 DEG C；
(4) dextrin I is well mixed with dextrin II, adds methyl-silicone oil, silica, calcium carbonate, makrolon, nanometer
Organo montmorillonite, cellulose, borax, foaming agent and talcum powder, after being sufficiently stirred 10-15 minutes, it is put into circular die sizing hair
Bubble.