CN107556625A - A kind of durable fire prevention fire-fighting rubber and preparation method thereof - Google Patents
A kind of durable fire prevention fire-fighting rubber and preparation method thereof Download PDFInfo
- Publication number
- CN107556625A CN107556625A CN201610524934.4A CN201610524934A CN107556625A CN 107556625 A CN107556625 A CN 107556625A CN 201610524934 A CN201610524934 A CN 201610524934A CN 107556625 A CN107556625 A CN 107556625A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- fire
- durable
- fire prevention
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of durable fire prevention fire-fighting rubber and preparation method thereof, it is related to fire-fighting equipment technical field.It is prepared from the following raw materials in parts by weight：5 10 parts of forsterite powder, 20 40 parts of EP rubbers, 10 20 parts of graphite powder, 5 15 parts of sulphur powder, 5 20 parts of Cab-O-sil, 10 30 parts of filler, 20 40 parts of diatomite in powder, 5 20 parts of high molecular weight fatty acid fat, 20 30 parts of carbon black, 5 20 parts of age resistor, 15 35 parts of high temperature adhesive, 15 25 parts of preservative, 10 30 parts of curing agent.The present invention has good heat-insulating flame-retardant, and anti-scald effect is good, in light weight, and good permeability is durable.
Description
Technical field
The present invention relates to a kind of durable fire prevention fire-fighting rubber and preparation method thereof, it is related to fire-fighting equipment technical field.
Background technology
Rubber is widely used in fire-fighting footwear because it has good elasticity, heat resistance and wearability, once hair
During raw the condition of a disaster, fireman is often punched in First Line, and the situation at fire-fighting scene is typically intricate, easily has object to pound fire-fighting
It is to remove only with personal strength if some heavy dropped objects on the instep of member, under this emergency situation, fire-fighting
The consciousness of member is weak, it is difficult to be got in touch with other team members, misses optimal rescue time, if some light-duty dropped objects,
The instep of fireman can also be injured by a crashing object by falling from above, and have a strong impact on the flexibility of its action..
Lack a kind of durable fire prevention fire-fighting rubber in the market, to be protected well to fireman.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of durable fire prevention fire-fighting rubber and preparation method thereof, have good
Good heat-insulating flame-retardant, anti-scald effect is good, in light weight, good permeability, durable.
In order to solve the above technical problems, present invention institute is using technical scheme：A kind of durable fire prevention fire-fighting rubber, its by
The raw material of following parts by weight is made：Forsterite powder 5-10 parts, EP rubbers 20-40 parts, graphite powder 10-20 parts, Cosan
Last 5-15 parts, Cab-O-sil 5-20 parts, filler 10-30 parts, diatomite in powder 20-40 parts, high molecular weight fatty acid fat 5-20 parts, charcoal
Black 20-30 parts, age resistor 5-20 parts, high temperature adhesive 15-35 parts, preservative 15-25 parts, curing agent 10-30 parts.
Preferably, it is prepared from the following raw materials in parts by weight：5 parts of forsterite powder, 20 parts of EP rubbers, graphite powder 10
Part, 5 parts of sulphur powder, 5 parts of Cab-O-sil, 10 parts of filler, 20 parts of diatomite in powder, 5 parts of high molecular weight fatty acid fat, carbon black 20
Part, 5 parts of age resistor, 15 parts of high temperature adhesive, 15 parts of preservative, 10 parts of curing agent.
Preferably, it is prepared from the following raw materials in parts by weight：10 parts of forsterite powder, 40 parts of EP rubbers, graphite powder
20 parts, 15 parts of sulphur powder, 20 parts of Cab-O-sil, 30 parts of filler, 40 parts of diatomite in powder, 20 parts of high molecular weight fatty acid fat, charcoal
Black 30 parts, 20 parts of age resistor, 35 parts of high temperature adhesive, 25 parts of preservative, 30 parts of curing agent.
Preferably, it is prepared from the following raw materials in parts by weight：8 parts of forsterite powder, 30 parts of EP rubbers, graphite powder 15
Part, 10 parts of sulphur powder, 12 parts of Cab-O-sil, 20 parts of filler, 30 parts of diatomite in powder, 12 parts of high molecular weight fatty acid fat, carbon black
25 parts, 12 parts of age resistor, 25 parts of high temperature adhesive, 20 parts of preservative, 20 parts of curing agent.
The preparation method of described durable fire prevention fire-fighting rubber, its step are as follows：First various raw materials by weight
Weigh, mixing is carried out after attrition grinding and is heated, when whipping temp is crossed to 130 DEG C, release feed powder and pour into
Die worker has, pressurized cooling, after normal temperature stands 2 hours, form removal, and packaging and storage after inspection.
Beneficial effects of the present invention：With good heat-insulating flame-retardant, anti-scald effect is good, in light weight, and good permeability is resistance to
With.
Embodiment
The present invention is further illustrated with reference to embodiments, but the present invention is not limited only to these embodiments, not
On the premise of departing from present inventive concept, any improvement made is within the scope of the present invention.
Embodiment one
A kind of durable fire prevention fire-fighting rubber, it is prepared from the following raw materials in parts by weight：Forsterite powder 5-10 parts, second
Third rubber 20-40 parts, graphite powder 10-20 parts, sulphur powder 5-15 parts, Cab-O-sil 5-20 parts, filler 10-30 parts, diatomite
Powder 20-40 parts, high molecular weight fatty acid fat 5-20 parts, carbon black 20-30 parts, age resistor 5-20 parts, high temperature adhesive 15-35 parts,
Preservative 15-25 parts, curing agent 10-30 parts.
Embodiment two
Preferably, it is prepared from the following raw materials in parts by weight：5 parts of forsterite powder, 20 parts of EP rubbers, graphite powder 10
Part, 5 parts of sulphur powder, 5 parts of Cab-O-sil, 10 parts of filler, 20 parts of diatomite in powder, 5 parts of high molecular weight fatty acid fat, carbon black 20
Part, 5 parts of age resistor, 15 parts of high temperature adhesive, 15 parts of preservative, 10 parts of curing agent.
Embodiment three
Preferably, it is prepared from the following raw materials in parts by weight：10 parts of forsterite powder, 40 parts of EP rubbers, graphite powder
20 parts, 15 parts of sulphur powder, 20 parts of Cab-O-sil, 30 parts of filler, 40 parts of diatomite in powder, 20 parts of high molecular weight fatty acid fat, charcoal
Black 30 parts, 20 parts of age resistor, 35 parts of high temperature adhesive, 25 parts of preservative, 30 parts of curing agent.
Example IV
Preferably, it is prepared from the following raw materials in parts by weight：8 parts of forsterite powder, 30 parts of EP rubbers, graphite powder 15
Part, 10 parts of sulphur powder, 12 parts of Cab-O-sil, 20 parts of filler, 30 parts of diatomite in powder, 12 parts of high molecular weight fatty acid fat, carbon black
25 parts, 12 parts of age resistor, 25 parts of high temperature adhesive, 20 parts of preservative, 20 parts of curing agent.
The preparation method of described durable fire prevention fire-fighting rubber, its step are as follows：First various raw materials by weight
Weigh, mixing is carried out after attrition grinding and is heated, when whipping temp is crossed to 130 DEG C, release feed powder and pour into
Die worker has, pressurized cooling, after normal temperature stands 2 hours, form removal, and packaging and storage after inspection.
Claims (5)
- A kind of 1. durable fire prevention fire-fighting rubber, it is characterised in that：It is prepared from the following raw materials in parts by weight：Forsterite powder 5-10 parts, EP rubbers 20-40 parts, graphite powder 10-20 parts, sulphur powder 5-15 parts, Cab-O-sil 5-20 parts, filler 10-30 Part, diatomite in powder 20-40 parts, high molecular weight fatty acid fat 5-20 parts, carbon black 20-30 parts, age resistor 5-20 parts, high temperature adhesive 15-35 parts, preservative 15-25 parts, curing agent 10-30 parts.
- 2. the durable fire prevention fire-fighting rubber of one kind according to claim 1, it is characterised in that：It is by following parts by weight Raw material is made：5 parts of forsterite powder, 20 parts of EP rubbers, 10 parts of graphite powder, 5 parts of sulphur powder, 5 parts of Cab-O-sil, filler 10 Part, 20 parts of diatomite in powder, 5 parts of high molecular weight fatty acid fat, 20 parts of carbon black, 5 parts of age resistor, 15 parts of high temperature adhesive, preservative 15 parts, 10 parts of curing agent.
- A kind of 3. durable fire prevention fire-fighting rubber, it is characterised in that：It is prepared from the following raw materials in parts by weight：Forsterite powder 10 parts, 40 parts of EP rubbers, 20 parts of graphite powder, 15 parts of sulphur powder, 20 parts of Cab-O-sil, 30 parts of filler, 40 parts of diatomite in powder, 20 parts of high molecular weight fatty acid fat, 30 parts of carbon black, 20 parts of age resistor, 35 parts of high temperature adhesive, 25 parts of preservative, curing agent 30 Part.
- A kind of 4. durable fire prevention fire-fighting rubber, it is characterised in that：It is prepared from the following raw materials in parts by weight：Forsterite powder 8 parts, 30 parts of EP rubbers, 15 parts of graphite powder, 10 parts of sulphur powder, 12 parts of Cab-O-sil, 20 parts of filler, 30 parts of diatomite in powder, 12 parts of high molecular weight fatty acid fat, 25 parts of carbon black, 12 parts of age resistor, 25 parts of high temperature adhesive, 20 parts of preservative, curing agent 20 Part.
- 5. the preparation method of durable fire prevention fire-fighting rubber according to claim 1, it is characterised in that：First various originals Material is weighed by weight, and mixing is carried out after attrition grinding and is heated, and when whipping temp is crossed to 130 DEG C, is released Feed powder pours into die worker's tool, and pressurized cooling, normal temperature standing is after 2 hours, form removal, packaging and storage after inspection.