CN107555858A - A kind of high-strength slope protection brick composition of raw materials - Google Patents
A kind of high-strength slope protection brick composition of raw materials Download PDFInfo
- Publication number
- CN107555858A CN107555858A CN201710718986.XA CN201710718986A CN107555858A CN 107555858 A CN107555858 A CN 107555858A CN 201710718986 A CN201710718986 A CN 201710718986A CN 107555858 A CN107555858 A CN 107555858A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw materials
- slope protection
- silica
- protection brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of high-strength slope protection brick composition of raw materials, is made from the following raw materials in parts by weight：30~40 parts of gangue, 10~20 parts of lime stone, 00~200 part of silica 1,10~12 parts of calcium oxide particle, 9~15 parts of modifying agent, 2~4 parts of gypsum, 6~9 parts of clay, 2~4 parts of iron powder.Instant invention overcomes the deficiencies in the prior art, and traditional cement is transformed, and silica, calcium oxide particle and modifying agent are added in cement original formulation, make to contain substantial amounts of silica in the cement of processing in body, add water to can be used directly, it is easy to use, and stability is good, cost is low.
Description
Technical field
The present invention relates to revetment brick technical field, particularly belongs to a kind of high-strength slope protection brick composition of raw materials.
Background technology
The mankind cause different degrees of destruction to natural environment while nature remodeling carries out infrastructure construction, special
It is not the implementation with the development continuously and healthily of China's economy and the strategy of sustainable development over nearly more than 20 years, country is special to various regions
It is the input that west area increases the builds to foundation engineering such as water conservancy, highway, railway, the implementation of these builds to foundation engineering, companion
With there is substantial amounts of construction and excavation, substantial amounts of exposed soil-slope and rock slope are caused, original landforms is changed and answers
Power state so that the stability of some side slopes is changed, and original ecosystem is destroyed, and result in serious water and soil
It is lost in and environmental ecology unbalance.In order to ensure the stabilization of side slope and protecting ecology bad border, people employ various
Method, generally speaking, side slope protection experienced the process from pure project post-evaluation to ecological revetment.
The sustainable development of ecological environmental protection relation economic society, the development of relation people's lives and descendants, close
Based environment protects the development of cause.
Wherein existing ecological revetment brick also still mixes territory using original reinforcing bar mostly and is made, simply in structure and shape
A further improvement is done on shape, but reinforcing bar mixes ecological revetment brick washing away with current made of territory, surface occurs
Breakage, internal reinforcing bar, which exposes, to be come, and is then got rusty, and final total collapse, now, the ecological revetment brick of collapse can be to slope
Vegetation on bank and sloping bank causes very big secondary injury.
The content of the invention
It is an object of the invention to provide a kind of high-strength slope protection brick composition of raw materials, the deficiencies in the prior art are overcome, it is right
Traditional cement is transformed, and silica, calcium oxide particle and modifying agent are added in cement original formulation, makes the cement of processing
Contain substantial amounts of silica in middle body, add water to can be used directly, it is easy to use, and stability is good, cost is low.
To solve the above problems, the technical solution used in the present invention is as follows：
A kind of high-strength slope protection brick composition of raw materials, is made from the following raw materials in parts by weight：30~40 parts of gangue, lime
It is 10~20 parts of stone, 00~200 part of silica 1,10~12 parts of calcium oxide particle, 9~15 parts of modifying agent, 2~4 parts of gypsum, viscous
Native 6~9 parts, 2~4 parts of iron powder.
Further, described high-strength slope protection brick composition of raw materials is made from the following raw materials in parts by weight：35 parts of gangue, stone
15 parts of lime stone, 75 parts of silica 1,11 parts of calcium oxide particle, 13 parts of modifying agent, 3 parts of gypsum, 7 parts of clay, 3 parts of iron powder.
Further, described calcium oxide particle size is 100 mesh.
Further, described silica dioxide granule size is 20 mesh.
Compared with prior art, implementation result of the invention is as follows by the present invention：
A kind of high-strength slope protection brick composition of raw materials of the present invention, is transformed traditional cement, in cement original formulation
Middle addition silica, calcium oxide particle and modifying agent, make to contain substantial amounts of silica in the cement of processing in body, add
Water can be used directly, easy to use, and stability is good, and cost is low.
Embodiment
With reference to embodiment, the invention will be further described, but the present invention is not limited only to these examples, to be de-
On the premise of from present inventive concept, carried out by it is any improvement be within the scope of the present invention.
Embodiment 1
A kind of high-strength slope protection brick composition of raw materials of the present invention, is made from the following raw materials in parts by weight：Gangue 30
~40 parts, 10~20 parts of lime stone, 00~200 part of silica 1,10~12 parts of calcium oxide particle, 9~15 parts of modifying agent, stone
2~4 parts of cream, 6~9 parts of clay, 2~4 parts of iron powder.
Further, described calcium oxide particle size is 100 mesh.
Further, described silica dioxide granule size is 20 mesh.
Embodiment 2
A kind of high-strength slope protection brick composition of raw materials of the present invention, is made from the following raw materials in parts by weight：Gangue 35
Part, 15 parts of lime stone, 75 parts of silica 1,11 parts of calcium oxide particle, 13 parts of modifying agent, 3 parts of gypsum, 7 parts of clay, iron powder 3
Part.
Claims (4)
- A kind of 1. high-strength slope protection brick composition of raw materials, it is characterised in that：It is made from the following raw materials in parts by weight：Gangue 30~40 Part, 10~20 parts of lime stone, 00~200 part of silica 1,10~12 parts of calcium oxide particle, 9~15 parts of modifying agent, gypsum 2~ 4 parts, 6~9 parts of clay, 2~4 parts of iron powder.
- A kind of 2. high-strength slope protection brick composition of raw materials according to claim 1, it is characterised in that：Described high-strength slope protection Brick composition of raw materials is made from the following raw materials in parts by weight：35 parts of gangue, 15 parts of lime stone, 75 parts of silica 1, calcium oxide 11 parts of grain, 13 parts of modifying agent, 3 parts of gypsum, 7 parts of clay, 3 parts of iron powder.
- A kind of 3. high-strength slope protection brick composition of raw materials according to claim 1, it is characterised in that：Described calcium oxide particle Size is 100 mesh.
- A kind of 4. high-strength slope protection brick composition of raw materials according to claim 1, it is characterised in that：Described silica Grain size is 20 mesh.