CN107541998A - A kind of environmentally-friendly decorative paper and preparation method thereof - Google Patents
A kind of environmentally-friendly decorative paper and preparation method thereof Download PDFInfo
- Publication number
- CN107541998A CN107541998A CN201710745437.1A CN201710745437A CN107541998A CN 107541998 A CN107541998 A CN 107541998A CN 201710745437 A CN201710745437 A CN 201710745437A CN 107541998 A CN107541998 A CN 107541998A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmentally
- decorative paper
- friendly decorative
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmentally-friendly decorative paper and preparation method thereof, include the raw material of following parts by weight：Needle starch 123 126 parts, broad-leaved starch 870 880 parts, 123 127 parts of titanium dioxide, 522 528 parts of kaolin, 87 88 parts of iron oxide yellow, 5 11 parts of rice skin powder, 58 parts of oyster shell powder, 28 parts of Nano-class zinc oxide, 27 parts of nano silicon, 15 25 parts of natural plant gum, 29 parts of ceramic, 25 parts of sodium carbonate, 35 parts of sodium alginate, 12 parts of methyl hydroxybenzoate and 22 30 parts of land plaster, 100 200 parts of distilled water.The decoration paper material of the present invention is easy to get, and cost is relatively low, and caused harmful substance is less in preparation process, more economical environmental protection, and should have good fungistatic effect, and use is safer.
Description
Technical field
The present invention relates to a kind of facing paper, specifically a kind of environmentally-friendly decorative paper and preparation method thereof.
Background technology
Facing paper is raw material essential in many building material products, such as low pressure plate, hardboard that furniture, cabinet are used,
Also fire-proof plate, floor etc..Facing paper is placed on below overlay paper in product structure, main to act the decoration for providing floral designs
Act on and prevent bottom glue from oozing existing covering effect.This layer requires that paper has good covering power, immersion and printing
Energy.Facing paper requires smooth surface, there is good absorption and adaptability, the requirement uniform hue for having background color, colored requirement face
Color is bright-coloured.Existing facing paper produces substantial amounts of harmful substance in preparation process, and product distributes poisonous chemical odor, uses
Security is low, and preparing raw material cost is high, not economic and environment-friendly enough.Therefore, the present invention provides a kind of new environment-friendly type decoration paper
And preparation method thereof.
The content of the invention
It is an object of the invention to provide a kind of environmentally-friendly decorative paper and preparation method thereof, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical scheme：
A kind of environmentally-friendly decorative paper, include the raw material of following parts by weight：Needle slurry 123-126 parts, broad-leaved slurry 870-880 parts, titanium
White powder 123-127 parts, kaolin 522-528 parts, iron oxide yellow 87-88 parts, rice skin powder 5-11 parts, oyster shell powder 5-8 parts, nanoscale oxygen
Change zinc 2-8 parts, nano silicon 2-7 parts, natural plant gum 15-25 parts, ceramic 2-9 parts, sodium carbonate 2-5 parts, sodium alginate
3-5 parts, methyl hydroxybenzoate 1-2 parts and land plaster 22-30 parts, distilled water 100-200 parts.
As the further scheme of the present invention：The natural plant gum includes the raw material of following parts by weight：Arabic gum 15-20
Part, aloe 5-11 parts, sesbania gum 3-5 parts, whey powder 8-12 parts.
As the further scheme of the present invention：The natural plant gum includes the raw material of following parts by weight：18 parts of Arabic gum,
7 parts of aloe, 4 parts of sesbania gum, 9 parts of whey powder.
As the further scheme of the present invention：Include the raw material of following parts by weight：Needle starches 125 parts, broad-leaved slurry 875
Part, 125 parts of titanium dioxide, 525 parts of kaolin, 87.5 parts of iron oxide yellow, 8 parts of rice skin powder, 6 parts of oyster shell powder, 4 parts of Nano-class zinc oxide,
5 parts of nano silicon, 18 parts of natural plant gum, 7 parts of ceramic, 4 parts of sodium carbonate, 4 parts of sodium alginate, 1.1 parts of methyl hydroxybenzoate and
25 parts of land plaster, 125 parts of distilled water.
A kind of preparation method of environmentally-friendly decorative paper, comprises the following steps：
First, natural plant gum, ceramic, oyster shell powder, Nano-class zinc oxide, sodium alginate and land plaster are weighed by weight ratio
In distilled water, mixture A is uniformly mixing to obtain；
2nd, rice skin powder, needle slurry, broad-leaved slurry are weighed by weight ratio carries out molten slurry；
3rd, titanium dioxide, kaolin, sodium carbonate and methyl hydroxybenzoate are slowly added in the molten slurry being molded in upper step, mixing is stirred
0.3-1h is mixed, obtains mixture B；
4th, mixture A obtained by step 1 and mixture B obtained by upper step are mixed, and adds iron oxide yellow in stirring, receives
Rice silica；
5th, sodium hydroxide is added in upper step gains and adjusts pH value to 5.5-7.5；
6th, by after upper step gains drying forming, then it is coiled by shape-moulding wand crimped, rewinding, it is now package facing paper.
As the further scheme of the present invention：Step 3: be slowly added in the molten slurry being molded in upper step titanium dioxide,
Kaolin, sodium carbonate and methyl hydroxybenzoate, 0.5h is mixed, obtains mixture B.
As the further scheme of the present invention：Step 5: in upper step gains add sodium hydroxide adjust pH value to
6.8。
Compared with prior art, the beneficial effects of the invention are as follows：
The decoration paper material of the present invention is easy to get, and cost is relatively low, and caused harmful substance is less in preparation process, more economical ring
Protect, poisonous chemical odor will not be distributed, and there should be good fungistatic effect, use is safer；The product color of preparation
Glossy, intensity meets use demand, market popularization value height；Preparation method is simple, is advantageous to industrialized production.
Embodiment
The technical scheme of this patent is described in more detail with reference to embodiment.
Embodiment 1
A kind of environmentally-friendly decorative paper, include the raw material of following parts by weight：Needle starches 123 parts, broad-leaved slurry 870 parts, titanium dioxide 123
Part, 522 parts of kaolin, 87 parts of iron oxide yellow, 5 parts of rice skin powder, 5 parts of oyster shell powder, 2 parts of Nano-class zinc oxide, nano silicon 2
Part, 15 parts of natural plant gum, 2 parts of ceramic, 2 parts of sodium carbonate, 3 parts of sodium alginate, 1 part of methyl hydroxybenzoate and 22 parts of land plaster, distillation
100 parts of water.The natural plant gum includes the raw material of following parts by weight：15 parts of Arabic gum, 5 parts of aloe, 3 parts of sesbania gum, whey
8 parts of powder.
A kind of preparation method of environmentally-friendly decorative paper, comprises the following steps：First, natural plant gum, ceramics are weighed by weight ratio
Micro mist, oyster shell powder, Nano-class zinc oxide, sodium alginate and land plaster are uniformly mixing to obtain mixture A in distilled water；2nd,
Rice skin powder, needle slurry, broad-leaved slurry are weighed by weight ratio carries out molten slurry；3rd, in the molten slurry being molded in upper step slowly
Titanium dioxide, kaolin, sodium carbonate and methyl hydroxybenzoate are added, 0.3h is mixed, obtains mixture B；4th, will be mixed obtained by step 1
Compound A is mixed with mixture B obtained by upper step, and iron oxide yellow, nano silicon are added in stirring；5th, in upper step
Sodium hydroxide is added in gains and adjusts pH value to 5.5；6th, by after upper step gains drying forming, then by shape-moulding wand crimped,
Rewinding is coiled, is now package facing paper.
Embodiment 2
A kind of environmentally-friendly decorative paper, include the raw material of following parts by weight：Needle starches 126 parts, broad-leaved slurry 880 parts, titanium dioxide 127
Part, 528 parts of kaolin, 88 parts of iron oxide yellow, 11 parts of rice skin powder, 8 parts of oyster shell powder, 8 parts of Nano-class zinc oxide, nano silicon 7
Part, 25 parts of natural plant gum, 9 parts of ceramic, 5 parts of sodium carbonate, 5 parts of sodium alginate, 2 parts of methyl hydroxybenzoate and 30 parts of land plaster, distillation
200 parts of water.The natural plant gum includes the raw material of following parts by weight：20 parts of Arabic gum, 11 parts of aloe, 5 parts of sesbania gum, whey
12 parts of powder.
A kind of preparation method of environmentally-friendly decorative paper, comprises the following steps：First, natural plant gum, ceramics are weighed by weight ratio
Micro mist, oyster shell powder, Nano-class zinc oxide, sodium alginate and land plaster are uniformly mixing to obtain mixture A in distilled water；2nd,
Rice skin powder, needle slurry, broad-leaved slurry are weighed by weight ratio carries out molten slurry；3rd, in the molten slurry being molded in upper step slowly
Titanium dioxide, kaolin, sodium carbonate and methyl hydroxybenzoate are added, 1h is mixed, obtains mixture B；4th, will be mixed obtained by step 1
Thing A is mixed with mixture B obtained by upper step, and iron oxide yellow, nano silicon are added in stirring；5th, in upper step institute
Obtain and sodium hydroxide regulation pH value is added in thing to 7.5；6th, by after upper step gains drying forming, then by shape-moulding wand crimped, receive
Material is coiled, is now package facing paper.
Embodiment 3
A kind of environmentally-friendly decorative paper, include the raw material of following parts by weight：Needle starches 125 parts, broad-leaved slurry 875 parts, titanium dioxide 125
Part, 525 parts of kaolin, 87.5 parts of iron oxide yellow, 8 parts of rice skin powder, 6 parts of oyster shell powder, 4 parts of Nano-class zinc oxide, nano silicon 5
Part, 18 parts of natural plant gum, 7 parts of ceramic, 4 parts of sodium carbonate, 4 parts of sodium alginate, 1.1 parts of methyl hydroxybenzoate and 25 parts of land plaster, steam
125 parts of distilled water.The natural plant gum includes the raw material of following parts by weight：18 parts of Arabic gum, 7 parts of aloe, 4 parts of sesbania gum, breast
Clear 9 parts of powder.
A kind of preparation method of environmentally-friendly decorative paper, comprises the following steps：First, natural plant gum, ceramics are weighed by weight ratio
Micro mist, oyster shell powder, Nano-class zinc oxide, sodium alginate and land plaster are uniformly mixing to obtain mixture A in distilled water；2nd,
Rice skin powder, needle slurry, broad-leaved slurry are weighed by weight ratio carries out molten slurry；3rd, in the molten slurry being molded in upper step slowly
Titanium dioxide, kaolin, sodium carbonate and methyl hydroxybenzoate are added, 0.5h is mixed, obtains mixture B；4th, will be mixed obtained by step 1
Compound A is mixed with mixture B obtained by upper step, and iron oxide yellow, nano silicon are added in stirring；5th, in upper step
Sodium hydroxide is added in gains and adjusts pH value to 6.8；6th, by after upper step gains drying forming, then by shape-moulding wand crimped,
Rewinding is coiled, is now package facing paper.
Embodiment 4
A kind of environmentally-friendly decorative paper, include the raw material of following parts by weight：Needle starches 124 parts, broad-leaved slurry 878 parts, titanium dioxide 124
Part, 527 parts of kaolin, 87.2 parts of iron oxide yellow, 10 parts of rice skin powder, 6 parts of oyster shell powder, 7 parts of Nano-class zinc oxide, nano silicon
3 parts, 22 parts of natural plant gum, 3 parts of ceramic, 4.5 parts of sodium carbonate, 3.2 parts of sodium alginate, 1.8 parts of methyl hydroxybenzoate and land plaster 24
Part, 158 parts of distilled water.The natural plant gum includes the raw material of following parts by weight：16 parts of Arabic gum, 10 parts of aloe, sesbania gum 4
Part, 11 parts of whey powder.
A kind of preparation method of environmentally-friendly decorative paper, comprises the following steps：First, natural plant gum, ceramics are weighed by weight ratio
Micro mist, oyster shell powder, Nano-class zinc oxide, sodium alginate and land plaster are uniformly mixing to obtain mixture A in distilled water；2nd,
Rice skin powder, needle slurry, broad-leaved slurry are weighed by weight ratio carries out molten slurry；3rd, in the molten slurry being molded in upper step slowly
Titanium dioxide, kaolin, sodium carbonate and methyl hydroxybenzoate are added, 0.4h is mixed, obtains mixture B；4th, will be mixed obtained by step 1
Compound A is mixed with mixture B obtained by upper step, and iron oxide yellow, nano silicon are added in stirring；5th, in upper step
Sodium hydroxide regulation pH value 7.2 is added in gains；6th, by after upper step gains drying forming, then by shape-moulding wand crimped, receive
Material is coiled, is now package facing paper.
The decoration paper material of the present invention is easy to get, and cost is relatively low, and caused harmful substance is less in preparation process, more economically
Environmental protection, poisonous chemical odor will not be distributed, and there should be good fungistatic effect, use is safer；The product color of preparation
Pool is glossy, and intensity meets use demand, market popularization value height；Preparation method is simple, is advantageous to industrialized production.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, can also be on the premise of this patent objective not be departed from one skilled in the relevant art's possessed knowledge
Make a variety of changes.
Claims (7)
1. a kind of environmentally-friendly decorative paper, it is characterised in that include the raw material of following parts by weight：Needle slurry 123-126 parts, broad-leaved slurry
870-880 parts, titanium dioxide 123-127 parts, kaolin 522-528 parts, iron oxide yellow 87-88 parts, rice skin powder 5-11 parts, oyster shell powder 5-
8 parts, Nano-class zinc oxide 2-8 parts, nano silicon 2-7 parts, natural plant gum 15-25 parts, ceramic 2-9 parts, sodium carbonate 2-5
Part, sodium alginate 3-5 parts, methyl hydroxybenzoate 1-2 parts and land plaster 22-30 parts, distilled water 100-200 parts.
2. environmentally-friendly decorative paper according to claim 1, it is characterised in that the natural plant gum includes the original of following parts by weight
Material：Arabic gum 15-20 parts, aloe 5-11 parts, sesbania gum 3-5 parts, whey powder 8-12 parts.
3. environmentally-friendly decorative paper according to claim 1, it is characterised in that the natural plant gum includes the original of following parts by weight
Material：18 parts of Arabic gum, 7 parts of aloe, 4 parts of sesbania gum, 9 parts of whey powder.
4. environmentally-friendly decorative paper according to claim 1, it is characterised in that include the raw material of following parts by weight：Needle is starched
125 parts, broad-leaved starches 875 parts, 125 parts of titanium dioxide, 525 parts of kaolin, 87.5 parts of iron oxide yellow, 8 parts of rice skin powder, 6 parts of oyster shell powder, receives
4 parts of nanoscale zinc oxide, 5 parts of nano silicon, 18 parts of natural plant gum, 7 parts of ceramic, 4 parts of sodium carbonate, 4 parts of sodium alginate, hydroxyl
1.1 parts of benzene methyl and 25 parts of land plaster, 125 parts of distilled water.
5. the preparation method of a kind of environmentally-friendly decorative paper as described in claim 1-4 is any, it is characterised in that including following step
Suddenly：
First, natural plant gum, ceramic, oyster shell powder, Nano-class zinc oxide, sodium alginate and land plaster are weighed by weight ratio
In distilled water, mixture A is uniformly mixing to obtain；
2nd, rice skin powder, needle slurry, broad-leaved slurry are weighed by weight ratio carries out molten slurry；
3rd, titanium dioxide, kaolin, sodium carbonate and methyl hydroxybenzoate are slowly added in the molten slurry being molded in upper step, mixing is stirred
0.3-1h is mixed, obtains mixture B；
4th, mixture A obtained by step 1 and mixture B obtained by upper step are mixed, and adds iron oxide yellow in stirring, receives
Rice silica；
5th, sodium hydroxide is added in upper step gains and adjusts pH value to 5.5-7.5；
6th, by after upper step gains drying forming, then it is coiled by shape-moulding wand crimped, rewinding, it is now package facing paper.
6. the preparation method of environmentally-friendly decorative paper according to claim 5, it is characterised in that Step 3: in upper step
Titanium dioxide, kaolin, sodium carbonate and methyl hydroxybenzoate are slowly added in the molten slurry of shaping, 0.5h is mixed, obtains mixture B.
7. the preparation method of environmentally-friendly decorative paper according to claim 5, it is characterised in that Step 5: in upper step gains
Middle addition sodium hydroxide adjusts pH value to 6.8.