CN107541143A - A kind of plating crystalline substance agent for automobile finish - Google Patents
A kind of plating crystalline substance agent for automobile finish Download PDFInfo
- Publication number
- CN107541143A CN107541143A CN201610488092.1A CN201610488092A CN107541143A CN 107541143 A CN107541143 A CN 107541143A CN 201610488092 A CN201610488092 A CN 201610488092A CN 107541143 A CN107541143 A CN 107541143A
- Authority
- CN
- China
- Prior art keywords
- plating
- agent
- base
- siloxanes
- crystalline substance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plating crystalline substance agent for automobile finish, it is characterised in that including：Base-material and auxiliary material；Wherein base-material is fluosilicic resin, and fluosilicic resin is to be made by 20%~60% alkyl fluoride trimethoxy silane, 30%~60% tetramethoxy silica alkane, 10%~20% monomethyl trimethoxy siloxane, 20%~50% dimethylformamide dimethyl epoxide siloxanes, 10%~30% water, 10%~20% ethanol, 20%~30% siloxanes by being copolymerized hydrolysis；Auxiliary material is made up of 1%~10% self-control auxiliary agent.The plating crystalline substance agent of automobile finish disclosed by the invention, not only improves the adhesive ability for plating brilliant agent, and the time for keeping plating crystal layer is longer, and adds the glossiness and slipping of lacquer painting, makes car lacquer painting more easy cleaning；Solve the problems, such as the easy floating oil of tradition plating crystal layer and dust suction simultaneously.
Description
Technical field
The present invention relates to automobile maintenance technical field, more particularly to a kind of plating crystalline substance agent for automobile finish.
Background technology
As environment is worsening, seriously polluted, the injury to surface of vehicle paint is also increasing, in order to allow car paint for a long time
Keep beautiful, increase the service life of genuine car paint, reduce the pollution to environment, it is brilliant that spy develops the plating of automobile nanometer；But mesh
, unavoidably there is the situation of lacquer painting deterioration, such as in preceding plating crystalline substance product plating crystal layer and car lacquer painting poor adhesive force, floating oil, dust suction：It is purple
Outside line irradiation lacquer painting aoxidizes, color is thin out, dimmed, gloss disappears；Acid rain, worm corpse, birds droppings, resin, other chemicals etc. are corroded
Lacquer painting is formed color spot, form oxide layer；Tiny hair cut weakens the mirror effect of lacquer painting.
Therefore, how to provide a kind of plating crystalline substance product that can effectively protect automobile finish gloss and color is this area skill
The problem of art personnel's urgent need to resolve.
The content of the invention
In view of this, the invention provides a kind of plating crystalline substance agent for automobile finish, the attachment for plating brilliant agent is not only improved
Power, the time for keeping plating crystal layer is longer, and solves the problems, such as the easy floating oil of tradition plating crystal layer and dust suction, while adds paint
The glossiness and slipping in face, make car lacquer painting more easy cleaning, save resource.
To achieve these goals, the present invention provides following technical scheme：
A kind of plating crystalline substance agent for automobile finish, including：Base-material and auxiliary material；Wherein base-material is fluosilicic resin, fluosilicic resin
It is by 20%~60% alkyl fluoride trimethoxy silane, 30%~60% tetramethoxy silica alkane, the one of 10%~20%
Methyl trimethoxy epoxide siloxanes, 20%~50% dimethylformamide dimethyl epoxide siloxanes, 10%~30% water, 10%~20%
Ethanol, 20%~30% siloxanes is made by being copolymerized hydrolysis；Auxiliary material is made up of 1%~10% self-control auxiliary agent
's.
Preferably, in a kind of above-mentioned plating crystalline substance agent for automobile finish, including：Base-material and auxiliary material；Wherein base-material is silicon
Fluororesin, fluosilicic resin be by 25%~55% alkyl fluoride trimethoxy silane, 35%~55% tetramethoxy silica alkane,
12%~18% monomethyl trimethoxy siloxane, 25%~45% dimethylformamide dimethyl epoxide siloxanes, 14%~25%
Water, 12%~18% ethanol, 22%~28% siloxanes be made by being copolymerized hydrolysis；Auxiliary material is by 4%~8%
Self-control auxiliary agent form.
Preferably, in a kind of above-mentioned plating crystalline substance agent for automobile finish, including：Base-material and auxiliary material；Wherein base-material is silicon
Fluororesin, fluosilicic resin are by 25% alkyl fluoride trimethoxy silane, 35%% tetramethoxy silica alkane, 15% first
Base trimethoxy siloxane, 30% dimethylformamide dimethyl epoxide siloxanes, 20% water, 15% ethanol, 23% siloxanes
It is made by being copolymerized hydrolysis；Auxiliary material is made up of 5% self-control auxiliary agent.
Preferably, in a kind of above-mentioned plating crystalline substance agent for automobile finish, the alkyl fluoride trimethoxy silane can be by
Alkyl fluoride triethoxysilane is replaced, and the tetramethoxy silica alkane can be replaced by tetraethoxy silica alkane, the monomethyl
Trimethoxy siloxane can be replaced by monomethyl triethoxy silica alkane, and the dimethylformamide dimethyl epoxide siloxanes can be by two
Methyl diethoxy siloxanes is replaced.
Preferably, in a kind of above-mentioned plating crystalline substance agent for automobile finish, auxiliary material is that base-material is added in a manner of addition
In.
Understood via above-mentioned technical scheme, compared with prior art, the present disclosure provides one kind to be used for automobile coating
The plating crystalline substance agent in face, on the one hand improves the adhesive ability for plating brilliant agent, so that the time that plating crystal layer is kept is longer, and solves
The problem of easy floating oil of tradition plating crystal layer and dust suction；The brilliant agent of plating that simultaneously prepared by the present invention has superpower lotus leaf effect, easy cleaning
Maintenance, various dusts and all kinds of dirts directly with clear water and are not added with after any detergent rinses, car body surface can recover and
Keep sparkling and crystal-clear bright, even if body surface speckles with greasy dirt or winged insect slurries, it is only necessary to which wet towel is directly wiped to car paint table
Face can easily removes, and can save more than 90% car washing water；On the other hand the present invention has superpower hydrophobic self-cleaning function,
So as to reduce the waste to resource and the pollution of environment.Therefore, the present invention has wide market application space, can be extensive
Promoted.
Embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
The embodiment of the invention discloses a kind of plating crystalline substance agent for automobile finish, not only improves the brilliant agent adhesive force of plating and asks
Topic, so that the time that plating crystal layer is kept is longer, and solves the problems, such as the easy floating oil of tradition plating crystal layer and dust suction, increase simultaneously
The glossiness and slipping of lacquer painting, make car lacquer painting more easy cleaning, cleaning does not need detergent, and water consumption do not plate brilliant car paint only
/ 10th of flushing dose, save resource.
A kind of plating crystalline substance agent for automobile finish, including：Base-material and auxiliary material；Wherein base-material is fluosilicic resin, fluosilicic resin
It is by 20%~60% alkyl fluoride trimethoxy silane, 30%~60% tetramethoxy silica alkane, the one of 10%~20%
Methyl trimethoxy epoxide siloxanes, 20%~50% dimethylformamide dimethyl epoxide siloxanes, 10%~30% water, 10%~20%
Ethanol, 20%~30% siloxanes is made by being copolymerized hydrolysis；Auxiliary material is made up of 1%~10% self-control auxiliary agent
's.
In order to further optimize above-mentioned technical proposal, including：Base-material and auxiliary material；Wherein base-material is fluosilicic resin, fluosilicic tree
Fat is by 25%~55% alkyl fluoride trimethoxy silane, 35%~55% tetramethoxy silica alkane, 12%~18%
Monomethyl trimethoxy siloxane, 25%~45% dimethylformamide dimethyl epoxide siloxanes, 14%~25% water, 12%~
18% ethanol, 22%~28% siloxanes are made by being copolymerized hydrolysis；Auxiliary material is by 4%~8% self-control auxiliary agent
Form.
In order to further optimize above-mentioned technical proposal, including：Base-material and auxiliary material；Wherein base-material is fluosilicic resin, fluosilicic tree
Fat is by 25% alkyl fluoride trimethoxy silane, 35%% tetramethoxy silica alkane, 15% monomethyl trimethoxy silicon
Oxygen alkane, 30% dimethylformamide dimethyl epoxide siloxanes, 20% water, 15% ethanol, 23% siloxanes are hydrolyzed by being copolymerized
It is made；Auxiliary material is made up of 5% self-control auxiliary agent.
In order to further optimize above-mentioned technical proposal, alkyl fluoride trimethoxy silane can be by alkyl fluoride triethoxysilane
Replace, tetramethoxy silica alkane can be replaced by tetraethoxy silica alkane, and monomethyl trimethoxy siloxane can be by monomethyl
Triethoxy silica alkane is replaced, and dimethylformamide dimethyl epoxide siloxanes can be replaced by dimethyl diethoxy siloxanes.
In order to further optimize above-mentioned technical proposal, auxiliary material is to be added in a manner of addition in base-material.
In order to further optimize above-mentioned technical proposal, self-control auxiliary agent can be base-material.
Each embodiment is described by the way of progressive in this specification, what each embodiment stressed be and other
The difference of embodiment, between each embodiment identical similar portion mutually referring to.For device disclosed in embodiment
For, because it is corresponded to the method disclosed in Example, so description is fairly simple, related part is said referring to method part
It is bright.
The foregoing description of the disclosed embodiments, professional and technical personnel in the field are enable to realize or using the present invention.
A variety of modifications to these embodiments will be apparent for those skilled in the art, as defined herein
General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.Therefore, it is of the invention
The embodiments shown herein is not intended to be limited to, and is to fit to and principles disclosed herein and features of novelty phase one
The most wide scope caused.
Claims (5)
- A kind of 1. plating crystalline substance agent for automobile finish, it is characterised in that including：Base-material and auxiliary material；Wherein base-material is fluosilicic resin, Fluosilicic resin be by 20%~60% alkyl fluoride trimethoxy silane, 30%~60% tetramethoxy silica alkane, 10%~ 20% monomethyl trimethoxy siloxane, 20%~50% dimethylformamide dimethyl epoxide siloxanes, 10%~30% water, 10%~20% ethanol, 20%~30% siloxanes are made by being copolymerized hydrolysis；Auxiliary material be by 1%~10% from What auxiliary agent processed was formed.
- A kind of 2. plating crystalline substance agent for automobile finish according to claim 1, it is characterised in that including：Base-material and auxiliary material； Wherein base-material is fluosilicic resin, fluosilicic resin be by 25%~55% alkyl fluoride trimethoxy silane, the four of 35%~55% Methoxy radical siloxane, 12%~18% monomethyl trimethoxy siloxane, 25%~45% dimethylformamide dimethyl epoxide silica Alkane, 14%~25% water, 12%~18% ethanol, 22%~28% siloxanes are made by being copolymerized hydrolysis；It is auxiliary Material is made up of 4%~8% self-control auxiliary agent.
- A kind of 3. plating crystalline substance agent for automobile finish according to claim 1, it is characterised in that including：Base-material and auxiliary material； Wherein base-material is fluosilicic resin, and fluosilicic resin is alkyl fluoride trimethoxy silane, the 35%% tetramethoxy silica by 25% Alkane, 15% monomethyl trimethoxy siloxane, 30% dimethylformamide dimethyl epoxide siloxanes, 20% water, 15% ethanol, 23% siloxanes is made by being copolymerized hydrolysis；Auxiliary material is made up of 5% self-control auxiliary agent.
- A kind of 4. plating crystalline substance agent for automobile finish according to any claim 1~3, it is characterised in that the alkyl Fluorine trimethoxy silane can be replaced by alkyl fluoride triethoxysilane, and the tetramethoxy silica alkane can be by tetraethoxy-silicane Oxygen alkane is replaced, and the monomethyl trimethoxy siloxane can be replaced by monomethyl triethoxy silica alkane, the dimethyl two Methoxy radical siloxane can be replaced by dimethyl diethoxy siloxanes.
- 5. a kind of plating crystalline substance agent for automobile finish according to claim 1, it is characterised in that auxiliary material is the side with addition Formula is added in base-material.