CN107541089A - A kind of good modified engineered plastic of anti-wear performance - Google Patents
A kind of good modified engineered plastic of anti-wear performance Download PDFInfo
- Publication number
- CN107541089A CN107541089A CN201610524141.2A CN201610524141A CN107541089A CN 107541089 A CN107541089 A CN 107541089A CN 201610524141 A CN201610524141 A CN 201610524141A CN 107541089 A CN107541089 A CN 107541089A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- wear
- plastic
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of good modified engineered plastic of anti-wear performance, and by adding raw material extruding pelletization, then injection molding forms, and described raw material includes following ingredients：The parts by weight of thermoplastic resin masterbatch 94 98, the parts by weight of modifying agent 12, the parts by weight of silicone plasties anti-wear agent 0.5 1.5, the parts by weight of tetrafluoroethene Ultramicro-powder 0.5 1.5 and the parts by weight of toughener 0.5 1.5.The present invention has the following technical effect that：The anti-wear performance of plastic products can be improved, coefficient of friction and wear extent can be reduced, is mainly used in automotive plastic, plastic gear, high-grade footwear material, the manufacture of EVA shoe bottom and other modified engineered plastics, there is super-high wear-resistant and adhesion strength.
Description
Technical field
The present invention relates to a kind of good modified engineered plastic of anti-wear performance, belong to modified engineered plastic technical field.
Background technology
Modified engineered plastic, refer on the basis of general-purpose plastics and engineering plastics, by filling, being blended, the side such as strengthening
Method is processed, and improves the plastic products of the performance of anti-flammability, intensity, impact resistance, toughness etc..Common plastics are often
There are the characteristic and defect of its own, modified plastics is exactly to change property to plastics, and basic technology includes：1st, strengthen：Will
Glass fibre etc. is with plastic blend to increase the mechanical strength of plastics.2nd, fill：By the fillers such as mineral and plastic blend, make modeling
The properties such as the shrinkage factor of material, hardness, intensity are changed.3rd, toughness reinforcing：By adding toughener blending to common plasticses to improve
The toughness of plastics, the product after toughening modifying：Rail pad.4th, it is fire-retardant：To addition fire retardant inside common plasticses resin, you can
Make plastics that there is flame-retarding characteristic, fire retardant can be the compound system of a kind of or several fire retardants, such as bromine+antimony system, phosphorus system,
Nitrogen system, silicon systems, and other inorganic fire-retarded systems.5th, resist cold：Increase the intensity and toughness of plastics at low temperature, general plastics exist
Intrinsic black brittleness under low temperature so that using limited, it is necessary to which adding some low temperature resistant toughener changes modeling in low temperature environment
The fragility of material at low temperature, such as the plastic such as bumper are general to require cold-resistant.
With flourishing for domestic automobile electric and electronic communication mechanical industry, the demand of modified engineered plastic will significantly on
Rise, the high temperature resistant, wear-resisting, conductive, electro-magnetic screen function to modified engineered plastic require more and more higher.
The content of the invention
The purpose of the present invention is overcome the deficiencies in the prior art part, there is provided a kind of good modification engineering plastic of anti-wear performance
Material.
The modified engineered plastic with anti-wear performance of the present invention, by adding raw material extruding pelletization, then injection molding
Form, described raw material includes following ingredients：Thermoplastic resin masterbatch 94-98 parts by weight, modifying agent 1-2 parts by weight, organosilicon
Plastic wear-resisting agent 0.5-1.5 parts by weight, tetrafluoroethene Ultramicro-powder 0.5-1.5 parts by weight and toughener 0.5-1.5 parts by weight.
Preferably,
Described raw material includes following ingredients：The parts by weight of thermoplastic resin masterbatch 96, the parts by weight of modifying agent 1.5, organosilicon
The parts by weight of plastic wear-resisting agent 1, the parts by weight of tetrafluoroethene Ultramicro-powder 1 and the parts by weight of toughener 1.
The present invention has the following technical effect that：The anti-wear performance of plastic products can be improved, coefficient of friction and abrasion can be reduced
Amount, it is mainly used in automotive plastic, plastic gear, high-grade footwear material, the manufacture of EVA shoe bottom and other modified engineered plastics, has super
High-wearing feature and adhesion strength.
Embodiment
Embodiment 1
The modified engineered plastic with anti-wear performance of the present embodiment, by adding raw material extruding pelletization, is then molded into
Type forms, and described raw material includes following ingredients：The parts by weight of thermoplastic resin masterbatch 98, the parts by weight of modifying agent 2, silicone plasties
The parts by weight of anti-wear agent 1.5, the parts by weight of tetrafluoroethene Ultramicro-powder 1.5 and the parts by weight of toughener 0.5.
Embodiment 2
The modified engineered plastic with anti-wear performance of the present embodiment, by adding raw material extruding pelletization, is then molded into
Type forms, and described raw material includes following ingredients：The parts by weight of thermoplastic resin masterbatch 94, the parts by weight of modifying agent 1, silicone plasties
The parts by weight of anti-wear agent 0.5, the parts by weight of tetrafluoroethene Ultramicro-powder 0.5 and the parts by weight of toughener 1.5.
Embodiment 3
The modified engineered plastic with anti-wear performance of the present embodiment, by adding raw material extruding pelletization, is then molded into
Type forms, and described raw material includes following ingredients：The parts by weight of thermoplastic resin masterbatch 96, the parts by weight of modifying agent 1.5, organosilicon modeling
Expect the parts by weight of anti-wear agent 1, the parts by weight of tetrafluoroethene Ultramicro-powder 1 and the parts by weight of toughener 1.
Claims (2)
1. a kind of good modified engineered plastic of anti-wear performance, by adding raw material extruding pelletization, then injection molding forms, it is special
Sign is that described raw material includes following ingredients：It is thermoplastic resin masterbatch 94-98 parts by weight, modifying agent 1-2 parts by weight, organic
Silastomer anti-wear agent 0.5-1.5 parts by weight, tetrafluoroethene Ultramicro-powder 0.5-1.5 parts by weight and toughener 0.5-1.5 parts by weight.
2. the modified engineered plastic according to claim 1 with anti-wear performance, it is characterised in that described raw material includes
Following ingredients：The parts by weight of thermoplastic resin masterbatch 96, the parts by weight of modifying agent 1.5, the parts by weight of silicone plasties anti-wear agent 1, tetrafluoro
The parts by weight of ethene Ultramicro-powder 1 and the parts by weight of toughener 1.