CN107521134A - A kind of preparation method of polarized lenses - Google Patents
A kind of preparation method of polarized lenses Download PDFInfo
- Publication number
- CN107521134A CN107521134A CN201710725191.1A CN201710725191A CN107521134A CN 107521134 A CN107521134 A CN 107521134A CN 201710725191 A CN201710725191 A CN 201710725191A CN 107521134 A CN107521134 A CN 107521134A
- Authority
- CN
- China
- Prior art keywords
- polarized
- plexiglas
- base
- resin
- polarized lenses
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of polarized lenses, comprise the following steps:(1)Early-stage preparations;(2)The making of front glass thin slice;(3)The making of resin polarized light eyeglass:Fixation will be detained under a lateral edges of polarisation diaphragm by manufacturing die insert, then another lateral edges of light polarizing film will be fixed, by the upper mould for manufacturing mould and lower mould matched moulds;The thermoplastic resin of melting is projected in perfusion to manufacture mold cavity by injecting glue road, and shaping to be cooled, remove upper mould, manufacture die insert successively, and from the resin polarized light eyeglass base of the ejecting injection molded shaping of lower mould;(4)The making of plexiglas polarized lenses;(5)Solidification cleaning;(6)Plated film;Weight saving of the plexiglas polarized lenses compared to existing safety glass light polarizing film at least 30% is made, improves comfortableness greatly, while is improved compared to the polarizing coefficient of existing resin light polarizing film, improves polarization effect.
Description
Technical field
The present invention relates to optical composite material technical field, more particularly to a kind of preparation method of polarized lenses.
Background technology
With scientific and technical high speed development, light pollution is increasingly severe, and various dazzling dazzling light give people to bring discomfort.
Polarized lenses can alleviate light pollution, and polarized lenses are made of the polarization theories according to light, have unique preferentially elimination dizzy
The function of light, the scattering light in light beam is effectively excluded and filtered out, light is put into ocular vision in the light transmission shaft of the right path
Image, make vision apparent naturally, with shutter principle, light is adjusted to light in the same direction and injects interior, has seen scenery
Come softer without dazzling.Existing polarized lenses mainly have:The gluing light polarizing film piece of interlayer and pad pasting polarized lenses.Both polarisations
Eyeglass is all the eyeglass with deep base coat colour, can not solve people in night, rainy days and the round-the-clock requirement used, at present
It can only be confined to use under the conditions of fine day is out of doors etc. bright and clear, can not popularize and push away in daily life, work, academic environment
Wide application.
Polarized lenses be according to the polarization theory of light manufacture it is a kind of can be the scatter reflections light in natural light, dizzy
Light and object random scatters photoresistance fall absolutely, to avoid the eyeglass of ophthalmic uncomfortable sense and potential safety hazard generation, are adapted to people to exist
Under extremely hot sunlight, or play with water in the strong lake surface of the glistening light of waves, or stay among glass architecture, or drive to wear when smooth road surface
Wear, to filter emergency light reflex, avoid the life to people, tourism, particularly summer from driving to make troubles.
Currently used is glass polarized lens and resin polarized light eyeglass, and wherein glass polarized lens will in manufacturing process
It is more loaded down with trivial details than resin polarisation, and the polarized lenses weight of glass is relatively more heavy, the comfort level that people wear is not high, but glass polarisation
The high polarization effect of polarizing coefficient of eyeglass is good, and Wear-resistant scratch-resistant;Resin polarized light eyeglass is although in light weight, but polarization effect is not so good as glass
Glass is good, and easily mill flower;Therefore, it is necessary to develop, a kind of technique is simple, operability is high, Wear-resistant scratch-resistant and polarizing coefficient in light weight
The preparation method of high plexiglas polarized lenses.
The content of the invention
The technical problem to be solved in the present invention is to provide that a kind of technique is simple, operability is high, Wear-resistant scratch-resistant and in light weight
The preparation method of the high plexiglas polarized lenses of polarizing coefficient.
In order to solve the above technical problems, the technical solution adopted by the present invention is, the plexiglas polarized lenses include preceding glass
Glass thin slice, rear resin flake and light polarizing film plain film, the light polarizing film plain film is bonded in the back concave surface of front glass thin slice and rear tree
Between the convex front surface of fat thin slice, plexiglas polarized lenses are formed;The preparation method of the plexiglas polarized lenses includes following
Step:
(1)Early-stage preparations:The heated press-bending of light polarizing film, sizing, surface treatment, shearing after the assay was approved, and light polarizing film are put
Put and positioned in the Cavity surface of the lower mould of manufacture mould, it is stand-by;
(2)The making of front glass thin slice:The blank sheet of front glass thin slice is ground through optics and reaches defined radian and thickness, then
It is stand-by after immersion forced fluid progress is chemical enhanced;
(3)The making of resin polarized light eyeglass:Fixation will be detained under a lateral edges of polarisation diaphragm by manufacturing die insert, then will be inclined
Another lateral edges of light film are fixed, by the upper mould for manufacturing mould and lower mould matched moulds;By the thermoplastic resin of melting by noting
Jiao Dao is projected in perfusion to manufacture mold cavity, and shaping to be cooled, removes upper mould, manufacture die insert successively, and from lower mould
The resin polarized light eyeglass base of ejecting injection molded shaping;
(4)The making of plexiglas polarized lenses:Again by the back concave surface of front glass thin slice and the light polarizing film of resin polarized light eyeglass base
It is bonding, and the bubble formation binder resin glass polarized lens base between light polarizing film and front glass thin slice is discharged simultaneously;
(5)Solidification cleaning:Binder resin glass polarized lens base is sent into isothermal curing stove and carries out one-step solidification, circle is made
Lens blank;Circular eyeglass blank is subjected to edging cutting, edging and polishing are carried out on automatic edging machine, is reused clear
Lotion and solvent clean in supersonic wave cleaning machine, then keep flat again in feeding isothermal curing stove and carry out secondary solidification, secondary solid
After internal stress, finishing surface are eliminated after change, plexiglas polarized lenses base is obtained, and cleaned, examined;
(6)Plated film:Using electron-beam vapor deposition method prepared by antiultraviolet film to plexiglas polarized lenses base;Specifically include following
Step:Comprise the following steps:
1)The Chemical cleaning of plexiglas polarized lenses base:1. in order to remove the organic matter on plexiglas polarized lenses base surface,
First with hydrogen peroxide and the mixed solution of the concentrated sulfuric acid, volume ratio 3:1,20 ~ 30min of immersion ultrasound after cleaned with deionized water;
2. plexiglas polarized lenses base is successively put into 25 ~ 35min of ultrasound in acetone soln, ethanol solution and deionized water, to carry
High resin glass polarized lens base surface-active, so as to increase the adhesion of film and plexiglas polarized lenses blank material material;③
Clean after terminating and plexiglas polarized lenses base is placed in oven drying, be fixed on after drying on chip bench, then by chip bench
It is tightened on the rotating disk of vacuum chamber;
2)The acquisition of equipment vacuum:Start mechanical pump, open side and take out valve II, vacuum chamber is vacuumized;When vacuum reaches 1 ~
During 8Pa, close side and take out valve II, open side and takes out valve I, and start molecular pump, open slide valve, vacuum chamber is entered using molecular pump
One step vacuumizes;Stable operation after molecular pump accelerates is until vacuum reaches 1 ~ 5 × 10-3Pa;
3)Ion beam cleaning:Argon plasma cleans;Argon gas valve is opened, argon gas is passed through, plexiglas polarized lenses base is entered
Row ion beam cleaning, scavenging period are 3 ~ 8 min;Argon gas valve is closed after the completion of cleaning;
4)The preparation of antiultraviolet film:Start electron beam gun when vacuum reaches 1 ~ 3 × 10-7 Pa in coating machine, adjust
The position of line and adjustment electron beam, is located among target, then successively in the front glass of plexiglas polarized lenses base
Plated on thin slice and carry out argon oxygen plasma etch after last layer after surface stiffened scratch resistant layer and rear surface antireflection film layer, during etching
Between be 1 ~ 2 min;The super membrane waterproofing in surface and argon oxygen plasma etch is carried out after plating one layer on rear surface antireflection film layer,
Etch period is 2 ~ 4 min;Surface metal oxidization film layer after plating one layer on the super membrane waterproofing in rear surface, then in rear surface metal
Surface fluorination thing film layer and argon oxygen plasma etch is carried out after plating one layer on oxidation film layer, etch period is 2 ~ 4 min;
5)Release vacuum:Molecular pump is closed, intake valve is opened, is passed through air;Take out eyeglass;
6)Eyeglass post-processes:By step 5)The eyeglass of taking-up is put into Muffle furnace and made annealing treatment, and annealing temperature is 60 ~ 80 DEG C,
Annealing time is 30min, obtains antiultraviolet plexiglas polarized lenses.
Using above-mentioned technical proposal, by by resin material and light polarizing film carry out injection molding can with reinforced resin material with
The adhesion of light polarizing film, reduce pollution when both combine;Plexiglas polarized lenses, which are made, compares existing tempering glass simultaneously
The weight saving of glass polaroid at least 30%, comfortableness is improved greatly, while carried compared to the polarizing coefficient of existing resin polaroid
Gao Liao, improve polarization effect;And preparation method technique is simple, controllability is strong, is produced suitable for pipeline system, improve life
Efficiency and product qualified rate are produced, is widely used in popularization and application.
The present invention further improvement is that, the step(2)In forced fluid by nano-metal-oxide and organosilan
Monomer is formed, add during use nitric acid Glass optical thin slice is carried out it is chemical enhanced.Using the forced fluid under the catalysis of acid
To the hardness and abrasion resistant effect of organic/inorganic nano-hybrid materials, both organic/inorganic substance, there is the adhesive force of organic polymer and soft again
Toughness, at the same also have up to more than 93% light transmittance, therefore, can especially suitable for the surface abrasion resistance of transparent optical plastics,
Hardening, anti-scratch processing.
The present invention further improvement is that, the step(4)The middle back concave surface by front glass thin slice and light polarizing film bonding
Process is to carry out compressing fitting in vacuum environment, is concretely comprised the following steps:Front glass thin slice, resin polarized light eyeglass base are pressed respectively
Order is sequentially inserted into die sample space and the margin location of front glass thin slice, resin polarized light eyeglass base is fixed with fixing device
Put, and the back concave surface in front glass thin slice, the resin polarized light eyeglass respectively before front glass thin slice is inserted into die sample space
Uniformly applied in the convex front surface of base and spread resin glue, by die sample space sealing and vacuumized, vacuum is 0.1 ~ 1MPa, so
Control the pressing element in die sample space to move down again afterwards and front glass thin slice, resin polarized light eyeglass base are compressed into fitting, formed
Binder resin glass polarized lens, then die sample inflated spatial is given, binder resin glass polarized lens are taken out, it is thick by coating
The scraping blade of film cloth discharges the bubble between light polarizing film and front glass thin slice and rear glass flake.Before being incited somebody to action in vacuum environment
Glass flake, resin polarized light eyeglass base are bonded, and bubble caused by bonding can be effectively reduced, when greatling save technique
Between and human cost, while can prevent bonding when be mixed into the impurity such as dust, if any a small amount of bubble after bonding be present, then pass through bag
The scraping blade for covering thick film cloth discharges bubble, so simple and easy for bubble clear operation, and operating efficiency and accuracy rate are high.
The present invention further improvement is that, the step(5)Middle one-step solidification and the temperature of secondary solidification be 50 DEG C~
80 DEG C, hardening time is 90~150min.
Further improve and be, the step(2)With the step(3)In using nitrogen jet gun to being set after removing
The dust of fat thin slice and the curved membrane surface of polarisation.Resin flake and the curved film of polarisation after can effectively being removed by nitrogen jet gun
The dust on piece surface.
Further improve and be, the step(4)Middle one-step solidification and the temperature of secondary solidification are 50 DEG C~80 DEG C,
Hardening time is 90~150min.
Compared with prior art, the beneficial effects of the invention are as follows:Plexiglas polarized lenses are made and compare existing tempering
The weight saving of glass light polarizing film at least 30%, comfortableness is improved greatly, while compared to the polarizing coefficient of existing resin light polarizing film
Improve, improve polarization effect;And preparation method technique is simple, controllability is strong, produces, improve suitable for pipeline system
Production efficiency and product qualified rate, are widely used in popularization and application.
Embodiment
Embodiment:The preparation method of the plexiglas polarized lenses, comprises the following steps:
(1)Early-stage preparations:The heated press-bending of light polarizing film, sizing, surface treatment, shearing after the assay was approved, and light polarizing film are put
Put and positioned in the Cavity surface of the lower mould of manufacture mould, it is stand-by;
(2)The making of front glass thin slice:The blank sheet of front glass thin slice is ground through optics and reaches defined radian and thickness, then
It is stand-by after immersion forced fluid progress is chemical enhanced;
(3)The making of resin polarized light eyeglass:Fixation will be detained under a lateral edges of polarisation diaphragm by manufacturing die insert, then will be inclined
Another lateral edges of light film are fixed, by the upper mould for manufacturing mould and lower mould matched moulds;By the thermoplastic resin of melting by noting
Jiao Dao is projected in perfusion to manufacture mold cavity, and shaping to be cooled, removes upper mould, manufacture die insert successively, and from lower mould
The resin polarized light eyeglass base of ejecting injection molded shaping;
(4)The making of plexiglas polarized lenses:Again by the back concave surface of front glass thin slice and the light polarizing film of resin polarized light eyeglass base
It is bonding, and the bubble formation binder resin glass polarized lens base between light polarizing film and front glass thin slice is discharged simultaneously;
(5)Solidification cleaning:Binder resin glass polarized lens base is sent into isothermal curing stove and carries out one-step solidification, circle is made
Lens blank;Circular eyeglass blank is subjected to edging cutting, edging and polishing are carried out on automatic edging machine, is reused clear
Lotion and solvent clean in supersonic wave cleaning machine, then keep flat again in feeding isothermal curing stove and carry out secondary solidification, secondary solid
After internal stress, finishing surface are eliminated after change, plexiglas polarized lenses base is obtained, and cleaned, examined;
(6)Plated film:Using electron-beam vapor deposition method prepared by antiultraviolet film to plexiglas polarized lenses base;Specifically include following
Step:Comprise the following steps:
1)The Chemical cleaning of plexiglas polarized lenses base:1. in order to remove the organic matter on plexiglas polarized lenses base surface,
First with hydrogen peroxide and the mixed solution of the concentrated sulfuric acid, volume ratio 3:1,20 ~ 30min of immersion ultrasound after cleaned with deionized water;
2. plexiglas polarized lenses base is successively put into 25 ~ 35min of ultrasound in acetone soln, ethanol solution and deionized water, to carry
High resin glass polarized lens base surface-active, so as to increase the adhesion of film and plexiglas polarized lenses blank material material;③
Clean after terminating and plexiglas polarized lenses base is placed in oven drying, be fixed on after drying on chip bench, then by chip bench
It is tightened on the rotating disk of vacuum chamber;
2)The acquisition of equipment vacuum:Start mechanical pump, open side and take out valve II, vacuum chamber is vacuumized;When vacuum reaches 1 ~
During 8Pa, close side and take out valve II, open side and takes out valve I, and start molecular pump, open slide valve, vacuum chamber is entered using molecular pump
One step vacuumizes;Stable operation after molecular pump accelerates is until vacuum reaches 1 ~ 5 × 10-3Pa;
3)Ion beam cleaning:Argon plasma cleans;Argon gas valve is opened, argon gas is passed through, plexiglas polarized lenses base is entered
Row ion beam cleaning, scavenging period are 3 ~ 8 min;Argon gas valve is closed after the completion of cleaning;
4)The preparation of antiultraviolet film:Start electron beam gun when vacuum reaches 1 ~ 3 × 10-7 Pa in coating machine, adjust
The position of line and adjustment electron beam, is located among target, then successively in the front glass of plexiglas polarized lenses base
Plated on thin slice and carry out argon oxygen plasma etch after last layer after surface stiffened scratch resistant layer and rear surface antireflection film layer, during etching
Between be 1 ~ 2 min;The super membrane waterproofing in surface and argon oxygen plasma etch is carried out after plating one layer on rear surface antireflection film layer,
Etch period is 2 ~ 4 min;Surface metal oxidization film layer after plating one layer on the super membrane waterproofing in rear surface, then in rear surface metal
Surface fluorination thing film layer and argon oxygen plasma etch is carried out after plating one layer on oxidation film layer, etch period is 2 ~ 4 min;
5)Release vacuum:Molecular pump is closed, intake valve is opened, is passed through air;Take out eyeglass;
6)Eyeglass post-processes:By step 5)The eyeglass of taking-up is put into Muffle furnace and made annealing treatment, and annealing temperature is 60 ~ 80 DEG C,
Annealing time is 30min, obtains antiultraviolet plexiglas polarized lenses;The step(2)In forced fluid by nano metal
Oxide and organosilane monomers are formed, add during use nitric acid Glass optical thin slice is carried out it is chemical enhanced;The step(4)
The middle back concave surface by front glass thin slice is carried out compressing in vacuum environment and is bonded with the process that light polarizing film bonds, specific steps
For:Front glass thin slice, resin polarized light eyeglass base are sequentially inserted into die sample space in order respectively and consolidated with fixing device
Determine front glass thin slice, the marginal position of resin polarized light eyeglass base, and divide before front glass thin slice is inserted into die sample space
Back concave surface not in front glass thin slice, uniformly applied in the convex front surface of resin polarized light eyeglass base and spread resin glue, by die sample
Space sealing simultaneously vacuumizes, and vacuum is 0.1 ~ 1MPa, and then controlling the pressing element in die sample space to move down again will be preceding
Glass flake, resin polarized light eyeglass base compress fitting, form binder resin glass polarized lens, then fill to die sample space
Gas, binder resin glass polarized lens are taken out, by coating the scraping blade of thick film cloth by light polarizing film and front glass thin slice and rear glass
Bubble discharge between thin slice;The step(5)Middle one-step solidification and the temperature of secondary solidification are 50 DEG C~80 DEG C, during solidification
Between be 90~150min.
The front glass thin slice of the plexiglas polarized lenses plays wear-resisting anti-scratch effect, and rear resin flake then mitigates weight
Amount;The weight of the product is lighter than safety glass light polarizing film by 30%, greatly improves comfortableness.
General principle, the main features and advantages of the present invention have been shown and described above.The technical staff of the industry should
Understand, the present invention is not limited to the above embodiments, the original for simply illustrating the present invention described in above-described embodiment and specification
Reason, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes and improvements
It all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appended claims and its equivalent circle
It is fixed.
Claims (4)
1. a kind of preparation method of polarized lenses, it is characterised in that comprise the following steps:
(1)Early-stage preparations:The heated press-bending of light polarizing film, sizing, surface treatment, shearing after the assay was approved, and light polarizing film are put
Put and positioned in the Cavity surface of the lower mould of manufacture mould, it is stand-by;
(2)The making of front glass thin slice:The blank sheet of front glass thin slice is ground through optics and reaches defined radian and thickness, then
It is stand-by after immersion forced fluid progress is chemical enhanced;
(3)The making of resin polarized light eyeglass:Fixation will be detained under a lateral edges of polarisation diaphragm by manufacturing die insert, then will be inclined
Another lateral edges of light film are fixed, by the upper mould for manufacturing mould and lower mould matched moulds;By the thermoplastic resin of melting by noting
Jiao Dao is projected in perfusion to manufacture mold cavity, and shaping to be cooled, removes upper mould, manufacture die insert successively, and from lower mould
The resin polarized light eyeglass base of ejecting injection molded shaping;
(4)The making of plexiglas polarized lenses:Again by the back concave surface of front glass thin slice and the light polarizing film of resin polarized light eyeglass base
It is bonding, and the bubble formation binder resin glass polarized lens base between light polarizing film and front glass thin slice is discharged simultaneously;
(5)Solidification cleaning:Binder resin glass polarized lens base is sent into isothermal curing stove and carries out one-step solidification, circle is made
Lens blank;Circular eyeglass blank is subjected to edging cutting, edging and polishing are carried out on automatic edging machine, is reused clear
Lotion and solvent clean in supersonic wave cleaning machine, then keep flat again in feeding isothermal curing stove and carry out secondary solidification, secondary solid
After internal stress, finishing surface are eliminated after change, plexiglas polarized lenses base is obtained, and cleaned, examined;
(6)Plated film:Using electron-beam vapor deposition method prepared by antiultraviolet film to plexiglas polarized lenses base;Specifically include following
Step:Comprise the following steps:
1)The Chemical cleaning of plexiglas polarized lenses base:1. in order to remove the organic matter on plexiglas polarized lenses base surface,
First with hydrogen peroxide and the mixed solution of the concentrated sulfuric acid, volume ratio 3:1,20 ~ 30min of immersion ultrasound after cleaned with deionized water;
2. plexiglas polarized lenses base is successively put into 25 ~ 35min of ultrasound in acetone soln, ethanol solution and deionized water, to carry
High resin glass polarized lens base surface-active, so as to increase the adhesion of film and plexiglas polarized lenses blank material material;③
Clean after terminating and plexiglas polarized lenses base is placed in oven drying, be fixed on after drying on chip bench, then by chip bench
It is tightened on the rotating disk of vacuum chamber;
2)The acquisition of equipment vacuum:Start mechanical pump, open side and take out valve II, vacuum chamber is vacuumized;When vacuum reaches 1 ~
During 8Pa, close side and take out valve II, open side and takes out valve I, and start molecular pump, open slide valve, vacuum chamber is entered using molecular pump
One step vacuumizes;Stable operation after molecular pump accelerates is until vacuum reaches 1 ~ 5 × 10-3Pa;
3)Ion beam cleaning:Argon plasma cleans;Argon gas valve is opened, argon gas is passed through, plexiglas polarized lenses base is entered
Row ion beam cleaning, scavenging period are 3 ~ 8 min;Argon gas valve is closed after the completion of cleaning;
4)The preparation of antiultraviolet film:When vacuum reaches 1 ~ 3 × 10 in coating machine-7Start electron beam gun during Pa, adjust beam
The position of stream and adjustment electron beam, is located among target, then thin in the front glass of plexiglas polarized lenses base successively
On piece argon oxygen plasma etch, etch period are carried out after plating last layer after surface stiffened scratch resistant layer and rear surface antireflection film layer
For 1 ~ 2 min;The super membrane waterproofing in surface and argon oxygen plasma etch is carried out after plating one layer on rear surface antireflection film layer, quarter
The erosion time is 2 ~ 4 min;Surface metal oxidization film layer after plating one layer on the super membrane waterproofing in rear surface, then in rear surface metal oxygen
Change surface fluorination thing film layer after plating one layer in film layer and carry out argon oxygen plasma etch, etch period is 2 ~ 4 min;
5)Release vacuum:Molecular pump is closed, intake valve is opened, is passed through air;Take out eyeglass;
6)Eyeglass post-processes:By step 5)The eyeglass of taking-up is put into Muffle furnace and made annealing treatment, and annealing temperature is 60 ~ 80 DEG C,
Annealing time is 30min, obtains antiultraviolet plexiglas polarized lenses.
2. the preparation method of polarized lenses according to claim 1, it is characterised in that the step(2)In forced fluid
Be made up of nano-metal-oxide and organosilane monomers, add during use nitric acid Glass optical thin slice is carried out it is chemical enhanced.
3. the preparation method of polarized lenses according to claim 1, it is characterised in that the step(4)It is middle by front glass
The back concave surface of thin slice is carried out compressing in vacuum environment and is bonded with the process that light polarizing film bonds, and is concretely comprised the following steps:By preceding glass
Glass thin slice, resin polarized light eyeglass base are sequentially inserted into die sample space in order respectively and to fix front glass with fixing device thin
The marginal position of piece, resin polarized light eyeglass base, and respectively in front glass before front glass thin slice is inserted into die sample space
Uniformly applied in the back concave surface of thin slice, the convex front surface of resin polarized light eyeglass base and spread resin glue, by die sample space sealing simultaneously
Vacuumize, vacuum is 0.1 ~ 1MPa, then controls the pressing element in die sample space to move down front glass thin slice, tree again
Fat polarized lenses base compresses fitting, forms binder resin glass polarized lens, then gives die sample inflated spatial, takes out bonding tree
Fat glass polarized lens, by coating the scraping blade of thick film cloth by the bubble between light polarizing film and front glass thin slice and rear glass flake
Discharge.
4. the preparation method of polarized lenses according to claim 1, it is characterised in that the step(5)Middle one-step solidification
Temperature with secondary solidification is 50 DEG C~80 DEG C, and hardening time is 90~150min.