CN107513805A - Fusion proof metal splash fabric - Google Patents
Fusion proof metal splash fabric Download PDFInfo
- Publication number
- CN107513805A CN107513805A CN201710930078.7A CN201710930078A CN107513805A CN 107513805 A CN107513805 A CN 107513805A CN 201710930078 A CN201710930078 A CN 201710930078A CN 107513805 A CN107513805 A CN 107513805A
- Authority
- CN
- China
- Prior art keywords
- fabric
- modacrylic
- wool
- fibers
- kinds
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fusion proof metal splash fabric, forms as follows containing three kinds of wool, modacrylic, non-flame resistant cellulose fibre fibers, the quality relative scale of three kinds of fibers in the yarn of the fabric:Wool/modacrylic:40%~240%;Non-flame resistant cellulose fibre/modacrylic:50%~120%.The present invention adds non-flame resistant cellulose fibre in the mixed goods of deformation acrylic fibers and wool, the appropriate anti-flammability for reducing fabric, reduce the thermal loss of molten metal liquid, keep its mobile performance, so as to improve the performance of fusion proof metal splash fabric, and the cost of material of fabric is greatly lowered.
Description
Technical field
The present invention relates to fabric arts, more particularly to a kind of flame-retardant textile.
Background technology
Fusion proof metal splash mainly has fabric on the market, and one kind is cotton final finishing fabric, and grammes per square metre is very high, exceedes
400gsm, protection level is relatively low, reaches EN ISO 11612-2015 E1, D1 level reluctantly;Another kind is deformation acrylic fibers and wool
Mixed goods, 320~350gsm or so, protective capacities is not also high, can pass through EN ISO 11612-2015 E2 levels and aluminium
The D1 levels of water projection, the level of highest E3 and D3 rank is not reached.Such as continue to increase grammes per square metre, the cost of fabric can be very high, together
When wearability be also deteriorated;Also it is a kind of be wool and phosphorous flame-retardant viscose glue blend fabric, protection level can reach compared with Gao Shui
It is flat, but cost is too high.
The content of the invention
It is an object of the invention to provide a kind of inexpensive fabric of fusion proof metal splash.
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the quality relative scale of three kinds of fibers are as follows:
Wool/modacrylic:40%~240%;
Non-flame resistant cellulose fibre/modacrylic:50%~120%.
Further, the flame-retardant textile of fusion proof metal splash of the present invention, wherein, contain sheep in the fabric
Three kinds of hair, modacrylic, non-flame resistant cellulose fibre fibers, the quality relative scale of three kinds of fibers are as follows:
Wool/modacrylic:40%~240%
Non-flame resistant cellulose fibre/modacrylic:50%~120%.
The flame-retardant textile of fusion proof metal splash of the present invention, wherein, the non-flame resistant cellulose fibre does not include
Cotton fiber.
The flame-retardant textile of any fusion proof metal splash of the present invention, wherein, the fabric reaches EN ISO
11612-2015 D1, D2, D3, E1, E2 or E3 protection level.
The flame-retardant textile of any fusion proof metal splash of the present invention, wherein, the fabric passes through EN ISO
15025-2003 A1 flame retardant test.
The wool that embodiments of the invention and comparative example use is 64# australian wools, does not carry out anti-shrinking.Limit oxygen refers to
Number is 24~26%, is low fire resistance fibre, it is impossible to separately through EN ISO 15025-2003 A1 flame retardant test.
Modacrylic is typically copolymerized by vinyl chloride or vinylidene chloride with acrylonitrile monemer, or both simultaneously and acrylonitrile
Monomer is copolymerized, the copolymer of acrylonitrile content 35%~85%, the fiber obtained by spinning.The fiber has day in itself
Raw fire resistance, in order to further improve the fire resistance of the fiber, antimony of the total fiber mass than 1%~25% can be added
Oxide.Sb oxide can be trivalent antimony oxide, tetravalence antimony oxide or pentavalent antimony oxide or the wherein mixing of the two or three
Thing.The PROTEX-M fiber types of KANEKA companies are used in embodiment and comparative example.Specification is 3.3dt X V100, i.e. fineness
For 3.3dt, average length is 100mm fiber.
Non-flame resistant cellulose fibre, including Lyocell fibers, flaxen fiber, regenerated celulose fibre etc..The contrast of the present invention
Having been used beyond example 2 can be with wool blended wool type length fiber.Lyocell fibers are upper nautical mile bamboo 2.2dtX88 difficult to understand;Fiber crops
Fiber is flax, and length is 64~128mm;The specification of regenerated celulose fibre is 1.67X 76.Non-flame resistant cellulose fibre
Limited oxygen index is 20%~21%, is non-flame resistant fiber.
Fire-retardant principle:The heat of burning things which may cause a fire disaster will be absorbed when modacrylic is lighted by burning things which may cause a fire disaster, while discharge fire-retardant gas, the gas
Body is more heavy than the ratio of air, is covered in fabric face, fabric and oxygen are separated, so as to prevent the further burning of fabric.With
When cellulose fibre is mixed by certain ratio, the carbonization ability enhancing of fabric.
The principle of fusion proof metal splash:First ensure that 1400 degrees Celsius of molten iron or 780 degrees Celsius of aluminium instant water connect
When touching fabric, fabric can not be ignited, next to that molten metal liquid without being adhered on fabric, otherwise molten metal and fabric
It is changed into contacting for a long time, causes fabric to be ignited or scald to wear, so that the personnel of wearing are burned.The effect of wool is exactly in melting gold
Belong to the moment of solution contact fabric, open wool scale ejects the molten metal liquid initially contacted, does not allow molten metal
Liquid wraps up fiber.Otherwise wool scale is carbonized and is attached to fabric face by molten metal, causes protection to fail.Modacrylic
The fire-retardant gas discharged is advantageous to slow down the consumption of wool scale, but the combustion process of flame-retardant acrylic fibre and wool is that heat absorption is anti-
Should, the skin temperature of the molten metal liquid of contact fabric reduces, if not reaching metal freezing temperature and consuming heat of solidification,
The viscosity on contact surface of the molten metal liquid with fabric will increase considerably, elongated with the time of contact of fabric face, glide
Slow, protection may finally be allowed to fail.Can quick carbon after the non-flame resistant cellulose fibre contacting molten metal liquid added
Change, and discharge heat, the viscosity on contact surface of the molten metal liquid with fabric will not be increased considerably, reduction and fabric
The time of contact on surface, accelerate the gliding speed of molten metal, reach the ability for improving fusion proof metal splash.It is but if fine
Cellulose fiber is excessive, and the heat of release is excessive, and beyond the control range of modacrylic, the overall flame of fabric disappears, as a result
It can run counter to desire.So interfibrous quality compare it is critically important.
Fusion proof metal splash experimental method normative reference EN ISO 9185-2008 of the present invention.Such as Fig. 1 institutes
Show.Standard specification PVC film, if any more than 5mm cavities, is determined as protection failure after casting metal melt liquid 30 seconds.Not lose
Premised on losing, the quality (g) of the most metal melting liquid poured into a mould judges the protective capacities of tested fabric.
EN ISO 11612-2015 judgment standard is shown in Table 1.
Table 1
The present invention has summed up the proportion of each fiber proposed in technical scheme by largely testing.
Compared with the existing technology, it protrudes effect and is the present invention:
The present invention adds non-flame resistant cellulose fibre in the mixed goods of deformation acrylic fibers and wool, suitably reduces fabric
Anti-flammability, reduce molten metal liquid thermal loss, its mobile performance is kept, so as to improve fusion proof metal splash fabric
Performance, and the cost of material of fabric is greatly lowered.
Explanation and specific embodiment are made further to fusion proof metal splash fabric of the present invention below in conjunction with the accompanying drawings
Explanation.
Brief description of the drawings
Fig. 1 is splash test schematic diagram.Wherein, 1- point molten metals;Fabric or clothes tested 2-;3- standard gauges
Lattice PVC film.
Fig. 2 is the fabric organization chart of embodiment and comparative example.
Embodiment
Embodiment 1
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:60%;
Modacrylic:25%;
Lyocell fibers:15%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:240%;
Non-flame resistant cellulose fibre/modacrylic:60%.
Embodiment 2
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:55%;
Modacrylic:25%;
Lyocell fibers:20%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:220%;
Non-flame resistant cellulose fibre/modacrylic:80%.
Embodiment 3
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:50%;
Modacrylic:25%;
Lyocell fibers:25%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:200%;
Non-flame resistant cellulose fibre/modacrylic:100%.
Embodiment 4
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:45%;
Modacrylic:30%;
Lyocell fibers:25%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:150%;
Non-flame resistant cellulose fibre/modacrylic:83.33%.
Embodiment 5
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:45%;
Modacrylic:30%;
Flax:25%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:150%;
Non-flame resistant cellulose fibre/modacrylic:83.33%.
Embodiment 6
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:45%;
Modacrylic:30%;
Common regenerated cellulose:25%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:150%;
Non-flame resistant cellulose fibre/modacrylic:83.33%.
Embodiment 7
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:45%;
Modacrylic:25%;
Lyocell fibers:30%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:180%;
Non-flame resistant cellulose fibre/modacrylic:120%.
Embodiment 8
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:40%;
Modacrylic:30%;
Lyocell fibers:30%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:133.33%;
Non-flame resistant cellulose fibre/modacrylic:100%.
Embodiment 9
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:40%;
Modacrylic:40%;
Lyocell fibers:20%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:100%;
Non-flame resistant cellulose fibre/modacrylic:50%.
Embodiment 10
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:30%;
Modacrylic:40%;
Lyocell fibers:30%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:75%;
Non-flame resistant cellulose fibre/modacrylic:75%.
Embodiment 11
A kind of fusion proof metal splash fabric, form in the yarn of the fabric containing wool, modacrylic, non-flame resistant fibre
Three kinds of fibers of cellulose fiber, the mass ratio of three kinds of fibers are as follows:
Wool:20%;
Modacrylic:50%;
Lyocell fibers:30%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:40%;
Non-flame resistant cellulose fibre/modacrylic:60%.
For the effect of the prominent present invention, following comparative example experiment has also been carried out.
Comparative example 1
A kind of fabric, form in the yarn of the fabric containing two kinds of wool, modacrylic fibers, the quality of two kinds of fibers
Than as follows:
Wool:50%;
Modacrylic:50%.
The quality relative scale of two kinds of fibers is as follows:
Wool/modacrylic:100%.
Comparative example 2
A kind of fabric, form in the yarn of the fabric containing two kinds of modacrylic, cellulose fibre fibers, two kinds of fibers
Mass ratio it is as follows:
Modacrylic:55%;
Cotton:45%.
The quality relative scale of two kinds of fibers is as follows:
Cellulose fibre/modacrylic:81.82%.
Comparative example 3
A kind of fabric, form and contain three kinds of wool, modacrylic, cellulose fibre fibers in the yarn of the fabric, three
The mass ratio of kind fiber is as follows:
Wool:65%;
Modacrylic:20%;
Lyocell fibers:15%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:325%;
Cellulose fibre/modacrylic:75%.
Comparative example 4
A kind of fabric, form and contain three kinds of wool, modacrylic, cellulose fibre fibers in the yarn of the fabric, three
The mass ratio of kind fiber is as follows:
Wool:15%;
Modacrylic:50%;
Lyocell fibers:35%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:30%;
Cellulose fibre/modacrylic:70%.
Comparative example 5
A kind of fabric, form and contain three kinds of wool, modacrylic, cellulose fibre fibers in the yarn of the fabric, three
The mass ratio of kind fiber is as follows:
Wool:45%;
Modacrylic:20%;
Lyocell fibers:35%.
The quality relative scale of three kinds of fibers is as follows:
Wool/modacrylic:225%;
Cellulose fibre/modacrylic:175%.
Comparative example 6
A kind of fabric, form in the yarn of the fabric containing two kinds of wool, phosphorous flame-retardant viscose glue fibers, two kinds of fibers
Mass ratio is as follows:
Wool:45%;
Phosphorous flame-retardant viscose glue:55%.
The fabric organization chart that embodiment and comparative example use is as shown in Figure 2.1 time twill left to right on 2, dash area represent warp thread
1st, 2,3 above weft yarn, and non-shaded portion represents warp thread below weft yarn.
Weft density:1 inch is represented, i.e., the radical of warp thread or weft yarn in 25.4mm.
Through close:92/1 inch.
Filling density:72/1 inch.
Yarn:Nm 40.5/2, i.e., the 40.5 public double yarns of branch, the yarn doubling twisting of two 40.5 public branch form.40.5 public affairs branch
The thickness of yarn is referred to, data are bigger, and yarn is thinner.Just 40500 meters of 1Kg yarns, i.e. 40.5 kms, the branch of the yarn
Number is just 40.5.
The fabric weight of embodiment and comparative example is 350gsm, and deviation range is ± 3%.350gsm represents that every square metre is knitted
The weight of official regain under the standard atmosphere of thing is 350g.
Fabric in embodiment 1-11 and comparative example 1-6, fusion proof metal splash experimental result are as shown in table 2.
The substantially price of listed fiber is as shown in table 3 in table 2.
Table 3
The cost of material of fabric in embodiment 1-11 and comparative example 1-6 is adjusted as shown in table 4.
Pass through table 2-4 result, it can be deduced that to draw a conclusion:
(1) protection effect of fusion proof metal splash not exclusively closes with the percentage of any fiber into positive correlation
System.
(2) embodiment 1~11 is all qualified, is arranged from high to low by the composition of wool successively.Embodiment 3~5 is best, its
He takes second place.
(3) for comparative example 1 compared with embodiment 3, wool content is identical, but changes fiber quality because adding cellulose fibre
Relative scale, test result is from E2 levels bring up to E3 levels, D1 levels bring up to D3 levels.The barrier propterty of embodiment 3 substantially improves,
Cost of material declines 15%.
(4) comparative example 3, the quality relative scale of wool/modacrylic is too high, causes fabrics flame resistance to decline, protective
Can be bad.
(5) comparative example 4, the quality of wool/modacrylic compare too low, the obvious step-down of barrier propterty.
(6) comparative example 2, without wool, anti-aluminium water projection ability does not reach D1 levels.
(7) for embodiment 4 compared with embodiment 7, wool content is identical, changes the content of modacrylic and cellulose, fiber
Between quality relative scale change, the anti-aluminium of embodiment 4 is water-based to be substantially eager to excel than embodiment 7.
(8) embodiment 4~6, the species change of cellulose have substantially no effect on the test result of fusion proof metal splash.
(9) embodiment 1~11, form in the yarn of the fabric containing three kinds of wool, modacrylic, cellulose fibre fibres
Dimension, the quality relative scale of three kinds of fibers are:Wool/modacrylic:40%~240%;Cellulose fibre/modacrylic:
50%~120%.At least E1, more than D1 protection effect can be obtained.Fabric passes through flame retardant test.
(10) embodiment 1~9, test result are better than comparative example 1, and cost of material declines 5%~18%.
(11) embodiment 3~5 and comparative example 6 test grade by highest, but cost of material than comparative example 6 low 20%~
28%.
Embodiment described above is only that the preferred embodiment of the present invention is described, not to the model of the present invention
Enclose and be defined, on the premise of design spirit of the present invention is not departed from, technical side of the those of ordinary skill in the art to the present invention
The various modifications and improvement that case is made, it all should fall into the protection domain of claims of the present invention determination.
Claims (5)
- A kind of 1. fusion proof metal splash fabric, it is characterised in that:Form in the yarn of the fabric containing wool, denaturation nitrile Three kinds of synthetic fibre, non-flame resistant cellulose fibre fibers, the quality relative scale of three kinds of fibers are as follows:Wool/modacrylic:40%~240%;Non-flame resistant cellulose fibre/modacrylic:50%~120%.
- 2. the flame-retardant textile of fusion proof metal splash according to claim 1, it is characterised in that:Contain sheep in the fabric Three kinds of hair, modacrylic, non-flame resistant cellulose fibre fibers, the quality relative scale of three kinds of fibers are as follows:Wool/modacrylic:40%~240%Non-flame resistant cellulose fibre/modacrylic:50%~120%.
- 3. the flame-retardant textile of fusion proof metal splash according to claim 1 or 2, it is characterised in that:The non-flame resistant fibre Cellulose fiber does not include cotton fiber.
- 4. the flame-retardant textile of fusion proof metal splash according to claim 3, it is characterised in that:The fabric reaches EN ISO11612-2015 D1, D2, D3, E1, E2 or E3 protection level.
- 5. the flame-retardant textile of fusion proof metal splash according to claim 3, it is characterised in that:The fabric passes through EN ISO15025-2003A1 flame retardant test.