CN107512849A - Optical glass and optical element - Google Patents
Optical glass and optical element Download PDFInfo
- Publication number
- CN107512849A CN107512849A CN201710875119.7A CN201710875119A CN107512849A CN 107512849 A CN107512849 A CN 107512849A CN 201710875119 A CN201710875119 A CN 201710875119A CN 107512849 A CN107512849 A CN 107512849A
- Authority
- CN
- China
- Prior art keywords
- glass
- optical glass
- optical
- temperature
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of inexpensive optical glass for precision profiling, and the optical glass does not contain Gd2O3Component, density 4.2g/cm3Hereinafter, refractive index is 1.71~1.78, and Abbe number is 45~55, and transition temperature is less than 550 DEG C.The present invention is added without expensive Gd by the content of reasonable arrangement each component2O3, production cost is reduced, has saved resource.The transmittance of the optical glass of the present invention reaches corresponding wavelength X when 80%80For below 370nm;Crystallization ceiling temperature is below 1050 DEG C;Water resistance is used up to 1 grade suitable for precise compression molding.
Description
The application is to be directed to Application No. 201210480110.3, and the applying date is on November 23rd, 2012, entitled " optics
The divisional application of the application for a patent for invention of glass and optical element ".
Technical field
The present invention relates to the accurate die pressing optical glass that a kind of refractive index is 1.71~1.78, Abbe number is 45~55,
And the optical element made of the optical glass.
Background technology
In recent years, with the quick popularization and use of digital camera, video camera and camera mobile phone so that optical material
Also developed rapidly towards the direction of high precision int, miniaturization.To meet requirements above, optical design is carried out using non-spherical lens
As main flow.Increasingly it is taken seriously on Optical element manufacturing with low cost, the precise compression molding technology of high yield.
When carrying out precise compression molding, in order to which high-accuracy die face is replicated on glass products formed, it is necessary in high temperature
Under (generally 15~40 DEG C more than glass softening point temperature) extrusion forming glass preforms, at this moment shaping mould be exposed to high temperature in
And higher pressure is subjected to, even in protective atmosphere, casted die mould surface mold layer is still oxidized easily erosion.It is accurate
In compression molding, high-accuracy mould is main cost source, and mould cannot be realized using certain access times are not reached
The purpose of inexpensive high yield.In order to extend the mold use life-span, damage of the hot environment to mould is reduced, then is needed
Die mould temperature is reduced as much as possible.It is therefore desirable to which the transition temperature (Tg) of glass material is low as far as possible, this allows for being suitable to essence
The demand of the low softening point optical glass of close die mould is growing day by day.
It is cost-effective not only can be by extending the mould life-span, it is also crucial to reduce cost of material.
CN02155831.0 discloses a kind of optical glass, wherein containing expensive Gd2O3, cause the cost of the optical glass very
It is high.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of inexpensive optical glass for precision profiling, the optics glass
The density (ρ) of glass is 4.2g/cm3Hereinafter, refractive index (nd) is 1.71~1.78, and Abbe number (vd) is 45~55, transition temperature
(Tg) it is less than 550 DEG C.
The technical proposal for solving the technical problem of the invention is:Optical glass, Gd is not contained2O3Component, density are
4.2g/cm3Hereinafter, refractive index is 1.71~1.78, and Abbe number is 45~55, and transition temperature is less than 550 DEG C.
Further, its percentage by weight composition is:SiO2:1~10%, B2O3:22~35%, La2O3:26~38%,
ZrO2:1~8%, ZnO:20~30%, CaO:0~3%, SrO:0~3%, Ta2O5:0.1~5%, Y2O3:1~10%,
Li2O:0.1~3%.
Further, wherein:SiO2:2~5%.
Further, wherein:B2O3:25~30%, La2O3:30~35%.
Further, wherein:ZrO2:1~5%.
Further, wherein:ZnO:22~27%.
Further, wherein:Ta2O5:0.5~2.5%.
Further, wherein:Y2O3:3~7%.
Optical glass, its percentage by weight composition are:SiO2:1~10%, B2O3:22~35%, La2O3:26~38%,
ZrO2:1~8%, ZnO:20~30%, CaO:0~3%, SrO:0~3%, Ta2O5:0.1~5%, Y2O3:1~10%,
Li2O:0.1~3%.
Further, wherein:SiO2:2~5%.
Further, wherein:B2O3:25~30%, La2O3:30~35%.
Further, wherein:ZrO2:1~5%.
Further, wherein:ZnO:22~27%.
Further, wherein:Ta2O5:0.5~2.5%.
Further, wherein:Y2O3:3~7%.
Using gas preform made of above-mentioned optical glass.
Using optical element made of above-mentioned optical glass.
Using optical instrument made of above-mentioned optical glass.
The beneficial effects of the invention are as follows:The present invention is added without expensive by the content of reasonable arrangement each component
Gd2O3, production cost is reduced, has saved resource.The optical glass density (ρ) of the present invention is 4.2g/cm3Below;Refractive index
(nd) it is 1.71~1.78;Abbe number (vd) is 45~55;Transition temperature (Tg) is less than 550 DEG C;When transmittance reaches 80%
Corresponding wavelength X80For below 370nm;Crystallization ceiling temperature is below 1050 DEG C;Water resistance is up to 1 grade, suitable for precise compression molding
With.
Embodiment
Each component of optical glass of the present invention is described below, unless otherwise indicated, the ratio of each component content is
Represented with weight %.
SiO2It is the network generation oxide body to form glass, adds a certain amount of SiO2The high temperature viscosity of glass can be increased,
Improve the devitrification resistance property of glass.SiO2Content more than 10% when, the meltability of optical glass reduces, softening temperature rise.
Therefore SiO2Content be defined to 1~10%, preferably 2~5%.
As a kind of effective oxide for forming glass network structure, B2O3It is to obtain high refraction, the group of the lanthanides optics of low dispersion
The necessary component of glass.B in the present invention2O3The meltbility of glass can be efficiently modified, reduces smelting temperature and viscous flow temperature.When
B2O3When content is less than 22%, it is difficult to obtain the stable glass of property, devitrification resistance property is undesirable;But work as B2O3Content is higher than
When 35%, the refractive index of glass does not reach design object, while the chemical stability of glass can reduce.Therefore, B2O3Content limit
It is set to 22~35%, more preferably content is 25~30%.
La2O3It is high refraction, the main component of low-dispersion optical glass for mold, the refractive index and unobvious that can increase glass carry
The dispersion of high glass, in inventive formulation system, B2O3With La2O3Combination exist, the resistance to mistake of glass can be effectively improved
Permeability energy, improve the chemical stability of glass.Work as La2O3Content be less than 26% when, it is impossible to obtain the effect of the above;When it contains
When amount is more than 38%, the crystallization property of glass deteriorates, therefore its content is defined into 26~38%, and preferred content is 30~
35%.
ZrO2The viscosity, hardness and chemical stability of glass can be improved, reduces the thermal coefficient of expansion of glass.ZrO2Content
During more than 8%, glass infusibility, easy devitrification, and also chemical durability of glass deteriorates.Therefore ZrO2Content preferably 1~8%, more
Preferably 1~5%.
ZnO is the important component to form low-melting point optical glass, can reduce the thermal coefficient of expansion of glass, improve glass
Chemical stability, heat endurance and refractive index.When ZnO content is more than 30%, the easy devitrification of optical glass;When containing for ZnO
When amount is less than 20%, the transition temperature rise of optical glass.Therefore, ZnO content is preferably 20~30%, more preferably 22~
27%.
CaO has improvement stability, glass, and the effect of melting sources is helped during melting production, but its content is higher than
The tendency towards devitrification increase of glass when 3%, therefore CaO content is defined to 0~3%.
The effects of SrO in glass are similar to BaO, replace part BaO to accelerate the fusing and clarification of glass with SrO, drop
The tendency towards devitrification of low glass, when its content is higher than 3%, found difficulty, thus SrO contents be defined to 0~3%, preferably 0~
1%, more preferably it is added without.
Ta2O5Be to confer to the component of the high refraction of optical glass and low dispersion characteristics, can effective reinforcing glass stability,
But Ta2O5Content is high, the increase of glass cost.Therefore Ta2O5Content be preferably 0.1~5%, more preferably 0.5~2.5%.
Y2O3With the effect for improving refractive index, reducing dispersion, but if its content is excessive, then devitrification resistance property is drastically
Ground reduces.Therefore, Y2O3Preferred content be 1~10%, more preferably content be 3~7%.
Li2O can effectively reduce glass transformation temperature, be effectively improved the thawing ability of glass, reduce fusion temperature, simultaneously
It can also effectively reduce glass density;But deteriorate the processing performance of glass as its content Gao Shihui, the devitrification resistance of glass and
Chemical stability declines, so Li2O preferred content is 0.1~3%.
The performance of optical glass of the present invention is described below.
Density according to by《GB/T 7962.20-1987 colouless optical glass method of testing density measurement methods》Test.
Refractive index and Abbe number according to《The colouless optical glass method of testing refractive indexes of GB/T 7962.1-1987 and dispersion
Coefficient》Test.
Transition temperature (Tg) according to《GB/T7962.16-1987 colouless optical glass method of testings linear expansion coefficient, transformation
Temperature and sag temperature》Test, i.e.,:Sample is within the scope of certain temperature, and temperature often raises 1 DEG C, in sample
On expansion curve, low-temperature region and high-temperature area straight line portion are extended into intersecting, the temperature corresponding to its intersection point.
Glass is fabricated to the sample of 10mm ± 0.1mm thickness, test glass reaches wavelength corresponding to 80% in transmittance
λ80。
Using the crystallization property of temperature gradient furnace method measure glass, glass is made to 180 × 10 × 10mm sample, side is thrown
Light, it is put into the stove inside holding with thermograde and is taken out after 4 hours, under the microscope sight glass crystallization situation, glass occurs
Maximum temperature corresponding to crystal is the crystallization ceiling temperature of glass.
Water-fast effect stability DW(powder method) presses GB/T17129 method of testing, is calculated according to following formula:
DW=(B-C)/(B-A) × 100
In formula:DW- glass leaches percentage (%)
The quality (g) of B-filter and sample
The quality (g) of sample after C-filter and erosion
A-filter quality (g)
By the leaching percentage being calculated, by the stable D of the water-fast effect of optical glassWIt is divided into 6 classes see the table below.
By test, optical glass provided by the invention has following performance:Density (ρ) is 4.2g/cm3Below;Refraction
Rate (nd) is 1.71~1.78;Abbe number (vd) is 45~55;Transition temperature (Tg) is less than 550 DEG C;Transmittance reaches 80%
When corresponding wavelength X80For below 370nm;Crystallization ceiling temperature is below 1050 DEG C;Water resistance is up to 1 grade.
The present invention also provides a kind of optical element, by above-mentioned optical glass according to method shape well known to those skilled in the art
Into.Because described optical glass has high index of refraction and relatively low glass transformation temperature, therefore the optical element also has
High index of refraction and relatively low glass transformation temperature, can apply to the equipment such as digital camera, digital camera, camera cell phone.
Embodiment
In order to further appreciate that technical scheme, the embodiment of optical glass of the present invention will now be described.Should
It is noted that these embodiments do not limit the scope of the present invention.
The optical glass (embodiment 1~30) shown in 1~table of table 3 is by according to each embodiment shown in 1~table of table 3
Ratio weigh and hybrid optical glass common raw material (such as oxide, hydroxide, carbonate, nitrate and fluoride),
Mixed material is placed in platinum crucible, melted in 1100~1300 DEG C of temperature, and through melting, clarifying, stirring
After homogenizing, obtain no bubble and the homogeneous melt glass without undissolved material, by this melten glass in mould casting mold
And anneal and form.
The composition of the embodiment of the present invention 1~30 and refractive index (nd), Abbe number (vd), density (ρ), glass transformation temperature
(Tg), crystallization ceiling temperature, water resistance and transmittance reach corresponding wavelength X when 80%80Result together in 1~table of table 3
Represent.In these tables, the composition of each component is represented with weight %.
Table 1
Table 2
Table 3
From above-described embodiment as can be seen that the optical glass density (ρ) of the present invention is 4.2g/cm3Below;Refractive index (nd)
For 1.71~1.78;Abbe number (vd) is 45~55;Transition temperature (Tg) is less than 550 DEG C;Transmittance reaches corresponding when 80%
Wavelength X80For below 370nm;Crystallization ceiling temperature is below 1050 DEG C;Water resistance is used up to 1 grade suitable for precise compression molding.
Claims (11)
1. optical glass, it is characterised in that do not contain Gd2O3Component, density 4.2g/cm3Hereinafter, refractive index be 1.71~
1.78, Abbe number is 45~55, and transition temperature is less than 550 DEG C.
2. optical glass as claimed in claim 1, it is characterised in that it, which is formed, represents to contain by weight percentage:SiO2:1~
10%th, B2O3:22~35%, La2O3:26~38%, ZrO2:1~8%, ZnO:20~30%, Ta2O5:0.1~5%, Y2O3:1
~10%, Li2O:0.1~3%.
3. optical glass as claimed in claim 1, it is characterised in that its composition represents also to contain by weight percentage:CaO:0
~3%, SrO:0~3%.
4. optical glass, it is characterised in that it, which is formed, represents to contain by weight percentage:SiO2:1~10%, B2O3:22~
35%th, La2O3:26~38%, ZrO2:1~8%, ZnO:20~30%, CaO:0~3%, SrO:0~3%, Ta2O5:0.1~
5%th, Y2O3:1~10%, Li2O:0.1~3%.
5. optical glass, it is characterised in that its percentage by weight, which forms, is:SiO2:1~10%, B2O3:22~35%, La2O3:
26~38%, ZrO2:1~8%, ZnO:20~30%, CaO:0~3%, SrO:0~3%, Ta2O5:0.1~5%, Y2O3:1~
10%th, Li2O:0.1~3%.
6. the optical glass as described in Claims 1 to 4 any claim, it is characterised in that wherein:SiO2:2~5%;With/
Or B2O3:25~30%;And/or La2O3:30~35%;And/or ZrO2:1~5%;And/or ZnO:22~27%;And/or
Ta2O5:0.5~2.5%;And/or Y2O3:3~7%.
7. the optical glass as described in claim 4 or 5, it is characterised in that the refractive index of glass is 1.71~1.78, Abbe number
For 45~55.
8. the optical glass as described in claim 4 or 5, it is characterised in that the density of glass is 4.2g/cm3Hereinafter, transformation temperature
Spend for less than 550 DEG C.
9. using gas preform made of the optical glass described in any claim in claim 1~8.
10. optical element made of the optical glass as described in claim 1~8 any claim.
11. optical instrument made of the optical glass as described in claim 1~8 any claim.